Detailed characterizaton and formulation studies were performed on a methyltriakoxysilane hydrolysate as a binder for thermal control coatings. The binder was optimized by varying hydrolysis temperature, time, catalyst type, and water concentration. The candidate coating formulations, based on this binder with TiO2 pigment, were optimized via a detailed series of sprayed test panels that included the parameters of binder/pigment ratio, ethanol content, pigment particle size, coating thickness and cure conditions. A typical optimized coating was prepared by acetic acid catalyzed hydrolysis of methyltriethoxysilane with 3.25 mol-equivalents of water over a 24 hour period at room temperature. The resulting hydrolysate was directly mixed with pre-milled TiO2 (12 grams pigment/26 grams binder) to yield a sprayable consistency. Panels were sprayed to result in a nominal cure coating thickness of 2 mils. Cure was affected by air drying for 24 hr at room temperature plus 72 hr at 150 F. These coatings are typically extremely tough and abrasion-resistant, with an absorptance (alpha) of 0.20 and emittance (e) of 0.89. No significant coating damage was observed in the mandrel bend test, even after exposure to thermal cycling from -160 to 160 F. Vacuum exposure of the coatings for 930 hours at 1 equivalent UV sun resulted in no visible degradation and no significant increase in absorptance.