NASA NTRS1985

Strain isolated ceramic coatings

Plasma sprayed ceramic coatings are used in gas turbine engines to improve component temperature capability and cooling air efficiency. A compliant metal fiber strain isolator between a plasma sprayed ceramic coating and a metal substrate improves ceramic durability while allowing thicker coatings for better insulation. Development of strain isolated coatings has concentrated on design and fabrication of coatings and coating evaluation via thermal shock testing. In thermal shock testing, five types of failure are possible: buckling failure im compression on heat up, bimetal type failure, isothermal expansion mismatch failure, mudflat cracking during cool down, and long term fatigue. A primary failure mode for thermally cycled coatings is designated bimetal type failure. Bimetal failure is tensile failure in the ceramic near the ceramic-metal interface. One of the significant benefits of the strain isolator is an insulating layer protecting the metal substrate from heat deformation and thereby preventing bimetal type failure.

Tolokan, R. P.↗
NASA NTRS1988

Designing Ceramic Coatings

Report summarizes design of ceramic coats for metal parts in heat engines. Ceramic coat used to reduce transfer of heat from hot gas to cylinder wall, piston, turbine blade, or other internally-cooled metal part. Enables use of higher gas temperatures needed for higher efficiencies, permits use of less cooling air, or extends life of metal part by reducing temperature.

Mcdonald, G.↗
NASA NTRS1982

Advanced ceramic coating development for industrial/utility gas turbine applications

The effects of ceramic coatings on the lifetimes of metal turbine components and on the performance of a utility turbine, as well as of the turbine operational cycle on the ceramic coatings were determined. When operating the turbine under conditions of constant cooling flow, the first row blades run 55K cooler, and as a result, have 10 times the creep rupture life, 10 times the low cycle fatigue life and twice the corrosion life with only slight decreases in both specific power and efficiency. When operating the turbine at constant metal temperature and reduced cooling flow, both specific power and efficiency increases, with no change in component lifetime. The most severe thermal transient of the turbine causes the coating bond stresses to approach 60% of the bond strengths. Ceramic coating failures was studied. Analytic models based on fracture mechanics theories, combined with measured properties quantitatively assessed both single and multiple thermal cycle failures which allowed the prediction of coating lifetime. Qualitative models for corrosion failures are also presented.

Andersson, C. A.↗
NASA NTRS2013

Nano-Ceramic Coated Plastics

Plastic products, due to their durability, safety, and low manufacturing cost, are now rapidly replacing cookware items traditionally made of glass and ceramics. Despite this trend, some still prefer relatively expensive and more fragile ceramic/glassware because plastics can deteriorate over time after exposure to foods, which can generate odors, bad appearance, and/or color change. Nano-ceramic coatings can eliminate these drawbacks while still retaining the advantages of the plastic, since the coating only alters the surface of the plastic. The surface coating adds functionality to the plastics such as self-cleaning and disinfectant capabilities that result from a photocatalytic effect of certain ceramic systems. These ceramic coatings can also provide non-stick surfaces and higher temperature capabilities for the base plastics without resorting to ceramic or glass materials. Titanium dioxide (TiO2) and zinc oxide (ZnO) are the candidates for a nano-ceramic coating to deposit on the plastics or plastic films used in cookware and kitchenware. Both are wide-bandgap semiconductors (3.0 to 3.2 eV for TiO2 and 3.2 to 3.3 eV for ZnO), so they exhibit a photocatalytic property under ultraviolet (UV) light. This will lead to decomposition of organic compounds. Decomposed products can be easily washed off by water, so the use of detergents will be minimal. High-crystalline film with large surface area for the reaction is essential to guarantee good photocatalytic performance of these oxides. Low-temperature processing (<100 C) is also a key to generating these ceramic coatings on the plastics. One possible way of processing nanoceramic coatings at low temperatures (< 90 C) is to take advantage of in-situ precipitated nanoparticles and nanostructures grown from aqueous solution. These nanostructures can be tailored to ceramic film formation and the subsequent microstructure development. In addition, the process provides environment- friendly processing because of the aqueous solution. Low-temperature processing has also shown versatility to generate various nanostructures. The growth of low-dimensional nanostructures (0-D, 1-D) provides a means of enhancing the crystallinity of the solution-prepared films that is of importance for photocatalytic performance. This technology can generate durable, fully functional nano-ceramic coatings (TiO2, ZnO) on plastic materials (silicone, Teflon, PET, etc.) that can possess both photocatalytic oxide properties and flexible plastic properties. Processing cost is low and it does not require any expensive equipment investment. Processing can be scalable to current manufacturing infrastructure.

Cho, Junghyun↗
NASA NTRS1976

Effect of ceramic coating of JT8D combustor liner on maximum liner temperatures and other combustor performance parameters

The effect of ceramic coating of a JT8D combustor liner was investigated at simulated cruise and takeoff conditions with two fuels of widely different aromatic contents. Substantial decreases in maximum liner temperatures and flame radiation values were obtained with the ceramic-coated liner. Small reductions in exhaust gas smoke concentrations were observed with the ceramic-coated liner. Other performance parameters such as combustion efficiency and emissions of unburned hydrocarbons, CO, and NOx were not affected significantly. No deterioration of the ceramic coating was observed after about 6 hours of cyclic operation including several startups and shutdowns.

Butze, H. F.↗
NASA NTRS1985

Fabrication of strain-isolated ceramic coated combustor components

The use of strain-isolated ceramic coated material to produce an AGT1500 combustor scroll-shaped transition duct which requires no air for film cooling is investigated. The scroll receives the exhaust of the can-style combustor liner and turns it into the annular inlet of the high pressure gas producer turbine nozzle. Strain-isolation of plasma sprayed thermal barrier coating is achieved by placing a compliant pad between the structural base metal and the ceramic coating. The compliant pad is brazed to the metal structure. In order to achieve a good braze bond, the strain-isolating compliant pad and base metal must be closely matched in shape and tightly fixtured for joining. The complex geometry of the AGT1500 scroll makes it impractical to attack pads to the supporting structure in its finished shape. Instead the pads are brazed to flat stock and post-formed into scroll sections. While test samples were successfully post-formed, plasma sprayed, and subjected to cyclic heating, the forming of full scale parts by normal methods resulted in tearing of the Hastelloy-X base metal because of embrittlement by the braze material. Several solutions were explored which finally resulted in the successful forming of full scale scroll parts.

Rutter, S.↗
NASA NTRS1983

Thermal stress fracture of ceramic coatings

Thermal stress failures of ceramic coatings are discussed in terms of fracture mechanics concepts. The effects of transient and residual stresses on single and multiple cycle failure mechanisms are considered. A specific example of a zirconia thermal barrier coating is presented and its endurance calculated using the proposed relationships.

Andersson, C. A.↗
NASA NTRS1986

Impact-Resistant Ceramic Coating

Refractory fibers more than double strength of coating. Impact strengths of ceramic coatings increase with increasing whisker content. Silicon carbide whiskers clearly produce largest increase, and improvement grows even more with high-temperature sintering. Coating also improves thermal and mechanical properties of electromagnetic components, mirrors, furnace linings, and ceramic parts of advanced internal-combustion engines.

Wheeler, W. H.↗
NASA NTRS1948

Cooling of gas turbines IX : cooling effects from use of ceramic coatings on water-cooled turbine blades

The hottest part of a turbine blade is likely to be the trailing portion. When the blades are cooled and when water is used as the coolant, the cooling passages are placed as close as possible to the trailing edge in order to cool this portion. In some cases, however, the trailing portion of the blade is so narrow, for aerodynamic reasons, that water passages cannot be located very near the trailing edge. Because ceramic coatings offer the possibility of protection for the trailing part of such narrow blades, a theoretical study has been made of the cooling effect of a ceramic coating on: (1) the blade-metal temperature when the gas temperature is unchanged, and (2) the gas temperature when the metal temperature is unchanged. Comparison is also made between the changes in the blade or gas temperatures produced by ceramic coatings and the changes produced by moving the cooling passages nearer the trailing edge. This comparison was made to provide a standard for evaluating the gains obtainable with ceramic coatings as compared to those obtainable by constructing the turbine blade in such a manner that water passages could be located very near the trailing edge.

HEAT TRANSMISSION - METALS↗
NASA NTRS1982

Advanced ceramic coating development for industrial/utility gas turbines

A program was conducted with the objective of developing advanced thermal barrier coating (TBC) systems. Coating application was by plasma spray. Duplex, triplex and graded coatings were tested. Coating systems incorporated both NiCrAly and CoCrAly bond coats. Four ceramic overlays were tested: ZrO2.82O3; CaO.TiO2; 2CaO.SiO2; and MgO.Al2O3. The best overall results were obtained with a CaO.TiO2 coating applied to a NiCrAly bond coat. This coating was less sensitive than the ZrO2.8Y2O3 coating to process variables and part geometry. Testing with fuels contaminated with compounds containing sulfur, phosphorus and alkali metals showed the zirconia coatings were destabilized. The calcium titanate coatings were not affected by these contaminants. However, when fuels were used containing 50 ppm of vanadium and 150 ppm of magnesium, heavy deposits were formed on the test specimens and combustor components that required frequent cleaning of the test rig. During the program Mars engine first-stage turbine blades were coated and installed for an engine cyclic endurance run with the zirconia, calcium titanate, and calcium silicate coatings. Heavy spalling developed with the calcium silicate system. The zirconia and calcium titanate systems survived the full test duration. It was concluded that these two TBC's showed potential for application in gas turbines.

Vogan, J. W.↗
NASA NTRS1979

Ceramic coating effect on liner metal temperatures of film-cooled annular combustor

An experimental and analytical investigation was conducted to determine the effect of a ceramic coating on the average metal temperatures of full annular, film cooled combustion chamber liner. The investigation was conducted at pressures from 0.50 to 0.062. At all test conditions, experimental results indicate that application of a ceramic coating will result in significantly lower wall temperatures. In a simplified heat transfer analysis, agreement between experimental and calculated liner temperatures was achieved. Simulated spalling of a small portion of the ceramic coating resulted in only small increases in liner temperature because of the thermal conduction of heat from the hotter, uncoated liner metal.

Claus, R. W.↗
NASA NTRS1980

Comparative evaluation of insulating properties of plasma-sprayed ceramic coatings

A simple method for evaluating the thermal insulating capability of ceramic coatings was devised. It is based on monitoring the temperature of the uncoated back surface of a thin superalloy disk while its front surface, coated with the ceramic material, is exposed to the high-temperature environment of an electric muffle furnace. The results obtained indicate that zirconia containing 8 wt% Y2O3 is a better thermal insulator than barium zirconate or calcium orthosilicate.

Zaplatynsky, I.↗
NASA NTRSDate not supplied

Wear-Resistance Investigations on Ceramic Coatings for Lunar Dust Mitigation

Lunar dust has posed a major challenge to exploration efforts due to abrasion and impact. This work focuses on fundamental studies on ceramic coatings as candidates for enhanced resistance to impact and wear. As a first step, standard and modified approaches to the method of abrasion testing were explored for options to incorporate lunar regolith as wear media, the effects of which were presented for AL6061-T6 control samples. Following this, wear results for air plasma-sprayed (APS) alumina coatings were investigated due to their superior strength and surface hardness. In addition, APS 8 wt % yttria-stabilized zirconia (8YSZ) coatings were studied for their strength and martensitic transformation toughness. Measurements were made by assessing the mass loss, with a standard scale at various intervals. In addition, surface roughness was measured with a profilometer and features identified with a high-resolution microscope. The findings demonstrated that wear media has a distinct effect on the abrasion. The alumina coatings demonstrated improved wear over 8YSZ. However, the tailorability of 8YSZ makes it an attractive option to continue to modify as a wear-resistant coating to protect against lunar dust abrasion. The results of these measurements provide insight into the wear behavior of future directions in candidate ceramic coatings for the harsh lunar environment.

ceramic coatings↗
NASA NTRSDate not supplied

Wear-Resistance Investigations on Ceramic Coatings for Lunar Dust Mitigation

Lunar dust has posed a major challenge to exploration efforts due to abrasion and impact. This work focuses on fundamental studies on ceramic coatings as candidates for enhanced resistance to impact and wear. As a first step, standard and modified approaches to the method of abrasion testing were explored for options to incorporate lunar regolith as wear media, the effects of which were presented for AL6061-T6 control samples. Following this, wear results for air plasma-sprayed (APS) alumina coatings were investigated due to their superior strength and surface hardness. In addition, APS 8 wt % yttria-stabilized zirconia (8YSZ) coatings were studied for their strength and martensitic transformation toughness. Measurements were made by assessing the mass loss, with a standard scale at various intervals. In addition, surface roughness was measured with a profilometer and features identified with a high-resolution microscope. The findings demonstrated that wear media has a distinct effect on the abrasion. The alumina coatings demonstrated improved wear over 8YSZ. However, the tailorability of 8YSZ makes it an attractive option to continue to modify as a wear-resistant coating to protect against lunar dust abrasion. The results of these measurements provide insight into the wear behavior of future directions in candidate ceramic coatings for the harsh lunar environment.

ceramic coatings↗
NASA NTRS1980

Development of improved-durability plasma sprayed ceramic coatings for gas turbine engines

An investigation is reported of improving the durability of plasma sprayed ceramic coatings for the vane platforms in the JT9d turbofan engine. The program aims for reduced fuel consumption of commercial aircraft engines; the use of improved strain tolerant microstructures and control of the substrate temperature during coating application are being evaluated. The initial burner rig tests at temperatures up to 1010 C indicated that improvements in cyclic life greater than 20:1 over previous ceramic coatings were achieved. Three plasma sprayed coating systems applied to first stage vane platforms in the high pressure turbine were subjected to a 1000-cycle JT9D engine endurance test with only minor damage occurring to the coatings.

Sumner, I. E.↗
NASA NTRS1985

Cyclic stress analysis of ceramic coated gas turbine seals

Through the use of the Finite Element Method, the cyclic thermomechanical response of ceramic coated gas turbine parts is considered. The analysis includes temperature dependent elastic-plastic-creep material properties and cyclic thermal loads. To demonstrate the cyclic thermomechanical response, a ceramic coated outer gas path seal is studied. The analysis will estimate the significant residual stress field created by the cyclic thermal loads.

Padovan, Joe↗