800H Weldments and Crack Growth Rates of CGR Alloys
Update on FY24 crack growth rate and 800H weldment testing.
36 MATERIALS SCIENCE↗
SEARCH · Search NASA
Results for “CGR”
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
Tropical extreme droughts drive long-term increase in atmospheric CO 2 growth rate variability
The terrestrial carbon sink slows the accumulation of carbon dioxide (CO 2 ) in the atmosphere by absorbing roughly 30% of anthropogenic CO 2 emissions, but varies greatly from year to year. The resulting variations in the atmospheric CO 2 growth rate (CGR) have been related to tropical temperature and water availability. The apparent sensitivity of CGR to tropical temperature ( ${{{{{{\rm{\gamma }}}}}}}_{{{{{{\rm{CGR}}}}}}}^{{{{{{\rm{T}}}}}}}$ ) has changed markedly over the past six decades, however, the drivers of the observation to date remains unidentified. Here, we use atmospheric observations, multiple global vegetation models and machine learning products to analyze the cause of the sensitivity change. We found that a threefold increase in ${{{{{{\rm{\gamma }}}}}}}_{{{{{{\rm{CGR}}}}}}}^{{{{{{\rm{T}}}}}}}$ emerged due to the long-term changes in the magnitude of CGR variability (i.e., indicated by one standard deviation of CGR; STD CGR ), which increased 34.7% from 1960-1979 to 1985-2004 and subsequently decreased 14.4% in 1997-2016. We found a close relationship (r 2 = 0.75, p < 0.01) between STD CGR and the tropical vegetated area (23°S – 23°N) affected by extreme droughts, which influenced 6-9% of the tropical vegetated surface. A 1% increase in the tropical area affected by extreme droughts led to about 0.14 Pg C yr -1 increase in STD CGR . The historical changes in STD CGR were dominated by extreme drought-affected areas in tropical Africa and Asia, and semi-arid ecosystems. The outsized influence of extreme droughts over a small fraction of vegetated surface amplified the interannual variability in CGR and explained the observed long-term dynamics of ${{{{{{\rm{\gamma }}}}}}}_{{{{{{\rm{CGR}}}}}}}^{{{{{{\rm{T}}}}}}}$ .
54 ENVIRONMENTAL SCIENCES↗
Effect of Water Chemistry on Crack Growth Rate in Neutron Irradiated X-750 and XM-19
The Advanced Test Reactor (ATR) National Science User Facility (NSUF) was used to study the effect of neutron damage on crack growth rates (CGR) under simulated boiling water reactor (BWR) water chemistry conditions using a fast neutron spectrum to accelerate the damage process. Nickel based Alloy X-750 and XM-19 were irradiated in the ATR center flux trap (CFT), with this experiment marking the first civilian project to utilize this position within the reactor. 0.4T-CT specimens were used to study crack growth rates for two sample fluences (~1.9 x 1020 n/cm2 and ~9.5 x 1020 n/cm2, E > 1MeV)) in both normal water chemistry (NWC) at 2.5 ppm O2 and hydrogen water chemistry (HWC) at ~80 ppb H2. CGR testing was conducted at a temperature of 288 °C. A decrease in CGR was observed for both alloys with the average ratio (CGR in NWC/CGR in HWC) being a factor of 281 for the XM-19 samples and a factor of 27.8 for the X-750 samples. Observed CGRs in this study showed little difference compared to non-irradiated samples (the non-irradiated XM-19 was 20% cold worked), suggesting limited sensitivity of these susceptible alloys to irradiation effects. Detailed results of CGR response to varying environmental electrochemical potential (ECP) and water purity will be presented in the context of crack growth mitigation in different water chemistries and the change in material behavior relative to non-irradiated samples of the material.
36 MATERIALS SCIENCE↗
Assessing Uncertainty in Modeling Stress Corrosion Cracking
This report summarizes the collaboration between Sandia National Laboratories (SNL) and the Nuclear Regulatory Commission (NRC) to improve the state of knowledge on chloride induced stress corrosion cracking (CISCC). The foundation of this work relied on using SNL’s CISCC computer code to assess the current state of knowledge for probabilistically modeling CISCC on stainless steel canisters. This work is presented as three tasks. The first task is exploring and independently comparing crack growth rate (CGR) models typically used in CISCC modeling by the research community. The second task is implementing two of the more conservative CGR models from the first task into SNL’s full CISCC code to understand the impact of the different CGR models on a full probabilistic analysis while studying uncertainty from three key input parameters. The combined work of the first two tasks showed that properly measuring salt deposition rates is impactful to reducing uncertainty when modeling CISCC. The work in Task 2 also showed how probabilistic CGR models can be more appropriate at capturing aleatory uncertainty when modeling SCC. Lastly, appropriate and realistic input parameters relevant for CISCC modeling were documented in the last task as a product of the simulations considered in the first two tasks.
36 MATERIALS SCIENCE↗
Effect of Water Chemistry on Crack Growth Rates in Neutron Irradiated X-750 and XM-19
The Advanced Test Reactor (ATR) National Science User Facility (NSUF) was used to study the effect of neutron damage on crack growth rates (CGR) under simulated boiling water reactor (BWR) water chemistry conditions using a fast neutron spectrum to accelerate the damage process. Nickel based Alloy X-750 and XM-19 were irradiated in the ATR center flux trap (CFT), with this experiment marking the first civilian project to utilize this position within the reactor. 0.4T-CT specimens were used to study crack growth rates for two sample fluences (~1.9 x 1020 n/cm2 and ~9.5 x 1020 n/cm2, E > 1MeV) in both normal water chemistry (NWC) at 2.5 ppm O2 and hydrogen water chemistry (HWC) at ~80 ppb H2. A decrease in CGR was observed with HWC for both alloys with the average ratio (CGR in NWC/CGR in HWC) being a factor of 281 for the XM-19 samples and a factor of 27.8 for the X-750 samples. Observed CGRs in this study showed little difference compared to non-irradiated samples (the non-irradiated XM-19 was 20% cold worked), suggesting limited sensitivity of these susceptible alloys to irradiation effects. The CGR response to varying environmental electrochemical potential (ECP) and water purity will be presented.
36 MATERIALS SCIENCE↗
Unusual characteristics of the carbon cycle during the 2015–2016 El Niño
The 2015–2016 El Niño was one of the strongest on record, but its influence on the carbon balance is less clear. Using Northern Hemisphere atmospheric CO 2 observations, we found both detrended atmospheric CO 2 growth rate (CGR) and CO 2 seasonal-cycle amplitude (SCA) of 2015–2016 were much higher than that of other El Niño events. The simultaneous high CGR and SCA were unusual, because our analysis of long-term CO 2 observations at Mauna Loa revealed a significantly negative correlation between CGR and SCA. Atmospheric inversions and terrestrial ecosystem models indicate strong northern land carbon uptake during spring but substantially reduced carbon uptake (or high emissions) during early autumn, which amplified SCA but also resulted in a small anomaly in annual carbon uptake of northern ecosystems in 2015–2016. This negative ecosystem carbon uptake anomaly in early autumn was primarily due to soil water deficits and more litter decomposition caused by enhanced spring productivity. Furthermore, our study demonstrates a decoupling between seasonality and annual carbon cycle balance in northern ecosystems over 2015–2016, which is unprecedented in the past five decades of El Niño events.
54 ENVIRONMENTAL SCIENCES↗
Effect of thermal aging and irradiation on microstructure and crack growth response of Alloy 690
Nickel-base Alloy 690 and the associated weld Alloys 52 and 152 are typically used for nozzle penetrations in replacement heads for pressurized water reactor (PWR) vessels, because of their excellent overall resistance to general corrosion and environmental degradation, primarily stress corrosion cracking (SCC). However, many of the existing PWRs reactors are expected to operate for 40-80 years. Likewise, advanced water-cooled small modular reactors (SMRs) will use Ni-Cr alloys and are expected to receive initial operating licenses for 60 years. Hence, the thermal stability of Ni-Cr alloys is a potential concern for the long-term performance of both existing and advanced nuclear plants, and possibly spent fuel storage containers. The objective of this research is to understand the microstructural changes occurring in high-Cr, Ni-based Alloy 690 during long time exposure to the reactor operating temperatures, and the effect of these changes on the service performance. One area of particular concern is the potential for long range ordering (LRO), i.e. formation of the intermetallic Ni 2 Cr phase under prolonged exposure to reactor temperatures and/or irradiation, which can increase strength, decrease ductility, and cause dimensional changes or lead to in-service embrittlement of components made with these alloys. Hence, this research focused on the microstructural evolution and the SCC response of Alloy 690 under accelerated thermal aging and irradiation conditions. The materials studied involved Alloy 690 from two sources: (i) Alloy 690 plate from an Alloy 152 dissimilar metal weld (DMW) joining the Alloy 690 plate to Alloy 533 LAS, aged at three different temperatures (370°C, 400°C and 450°C) for up to 75,000h (equivalent to 60 years of service), and (ii) specimens neutron-irradiated in the BOR-60 reactor up to 40 dpa. For aged Alloy 690 specimens, hardness was found to increase with aging time, however, the microstructural characterization by means of synchrotron X-ray did not find evidence of LRO. The microstructural characterization of neutron-irradiated specimens by TEM found no evidence of LRO either. Testing in a primary water environment of Alloy 690 specimens aged to a 60-year service equivalent revealed a fatigue and corrosion fatigue crack growth responses similar to those measured on the un-aged alloy. The SCC CGR response was also low. Overall, the two Alloy 690 heats investigated in this work, aged up to 60-year service equivalents or exposed to neutron irradiation up to 40 dpa, did not exhibit a deterioration in microstructure or performance.
22 GENERAL STUDIES OF NUCLEAR REACTORS↗
Effect of thermal aging on microstructure and crack growth response of Alloy 152 weld
Nickel-based Alloy 690 and the associated weld Alloys 52 and 152 are typically used for nozzle penetrations in replacement heads for pressurized water reactor (PWR) vessels, because of their excellent overall resistance to general corrosion and environmental degradation, primarily stress corrosion cracking (SCC). However, many of the existing PWRs are expected to operate for 40-80 years. Likewise, advanced water-cooled small modular reactors (SMRs) will use Ni-Cr alloys and are expected to receive initial operating licenses for 60 years. Hence, the thermal stability of Ni-Cr alloys is a potential concern for the long-term performance of both existing and advanced nuclear power plants, and possibly spent fuel storage containers. The objective of this research is to understand the microstructural changes occurring in high-Cr, Ni-based Alloy 152 weldments during long time exposure to the reactor operating temperatures, and the effect of these changes on the service performance. One area of particular concern is the potential for long range ordering (LRO), i.e. formation of the intermetallic Ni2Cr phase under prolonged exposure to reactor temperatures and/or irradiation, which can increase strength, decrease ductility, and cause dimensional changes or lead to in-service embrittlement of components made with these alloys. Hence, this research focused on the microstructural evolution and the SCC response of Alloy 152 under accelerated thermal aging. The materials studied involved three heats of Alloy 152 used to produce a dissimilar metal weld (DMW) joining an Alloy 690 plate to an Alloy 533 low alloy steel (LAS) plate, thermally aged at three different temperatures (370°C, 400°C and 450°C) for up to 75,000h (equivalent to 60 years of service). The microstructural characterization by means of synchrotron X-ray did not find evidence of LRO in any of the three heats aged to an equivalent of 60 years of service. Testing in a primary water environment of a heat of Alloy 152 aged at 370°C to a 60-year service equivalent revealed a fatigue and corrosion fatigue crack growth responses similar to those measured on the un-aged alloy. However, the SCC CGR response of the aged sample appears to show a deterioration in performance.
12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
Microtructure and Low-Cycle Fatigue Behavior of Additively Manufactured 316L Stainless Steel at 300°C
Metal additive manufacturing (AM) or 3D printing has the potential to transform the nuclear industry by producing high quality components faster and cheaper, thus enhancing the operating performance of current plants and advanced reactors. Two AM 316L tubes - intended to act as surrogates for complex components where nuclear equipment vendors are more likely to consider AM technologies - were printed using a Renishaw AM400 Laser Powder Bed Fusion (L-PBF) system. The porosity of the as-built material was found to be small, 0.06%. In prior research, the fatigue and corrosion fatigue crack growth rate (CGR) response of the AM specimens in the as-built condition was found to be similar to that expected for conventional alloys, and extremely resistant to stress corrosion cracking (SCC). The present research demonstrates that the low-cycle fatigue behavior of the AM material in air is similar to that of wrought stainless steel at LWR temperature. The data suggest that low porosity levels do not have a significant effect on the fatigue performance of AM materials. Taken together, all data generated to date demonstrate that the use of AM alloys in a nuclear environment is plausible. Additional research on environmental fatigue, crack initiation, and SCC needs to be conducted to provide the performance information needed to qualify AM materials for LWR applications.
36 MATERIALS SCIENCE↗
Effect of thermal aging on microstructure and stress corrosion cracking behavior of Alloy 152 weldment
Nickel-based Alloy 690 and the associated weld Alloys 52 and 152 are typically used for nozzle penetrations in replacement heads for pressurized water reactor (PWR) vessels, because of their excellent overall resistance to general corrosion and environmental degradation, primarily stress corrosion cracking (SCC). However, many of the existing PWRs are expected to operate for 40-80 years. Likewise, water-cooled small modular reactors (SMRs) will use Ni-Cr alloys and are expected to receive initial operating licenses for 60 years. Hence, the thermal stability of Ni-Cr alloys is a potential concern for the long-term performance of both existing and advanced nuclear power plants, and possibly spent fuel storage containers. The objective of this research is to understand the microstructural changes occurring in high-Cr, Ni-based Alloy 152 weldments during long time exposure to the reactor operating temperatures, and the effect of these changes on the service performance. One area of particular concern is the potential for long range ordering (LRO), i.e. formation of the intermetallic Ni2Cr phase under prolonged exposure to reactor temperatures and/or irradiation, which can increase strength, decrease ductility, and cause dimensional changes or lead to in-service embrittlement of components made with these alloys. Hence, this research focused on the microstructural evolution and the SCC response of Alloy 152 under accelerated thermal aging. The materials studied involved three heats of Alloy 152 used to produce a dissimilar metal weld (DMW) joining an Alloy 690 plate to an Alloy 533 low alloy steel (LAS) plate, thermally aged at three different temperatures (370°C, 400°C and 450°C) for up to 75,000h (equivalent to 60 years of service). The microstructural characterization by means of synchrotron X-ray conducted in small, 0.2 mm - step line scans in the high-deformation regions of the weld root – covering areas spanning from the weld heat affected zone (HAZ) in Alloy 690 to the weld and weld butter on LAS - did not show evidence of LRO in any of the three Alloy 152 heats aged to an equivalent of 60 years of service. Testing in a primary water environment of two heats of Alloy 152 aged at 370°C to a 60-year service equivalent revealed a fatigue and corrosion fatigue crack growth responses similar to those measured on the un-aged alloys. However, the SCC CGR response of the aged samples appears to show a deterioration in performance, confirming our previous observation.
36 MATERIALS SCIENCE↗
Effect of Thermal Aging on Microstructure and Stress Corrosion Cracking Behavior of an Alloy 152 1st Layer Butter Weldment
Nickel-based Alloy 690 and the associated weld Alloys 52 and 152 are typically used for nozzle penetrations in replacement heads for pressurized water reactor (PWR) vessels, because of their excellent overall resistance to general corrosion and environmental degradation, primarily stress corrosion cracking (SCC). However, many of the existing PWRs are expected to operate for 40- 80 years. Likewise, water-cooled small modular reactors (SMRs) will use Ni-Cr alloys and are expected to receive initial operating licenses for 60 years. Hence, the thermal stability of Ni-Cr alloys is critical for the long-term performance of both existing and advanced nuclear power plants, and possibly spent fuel storage containers. The objective of this research is to understand the microstructural changes occurring in high-Cr, Ni-based Alloy 152 weldments during long time exposure to the reactor operating temperatures, and the effect of these changes on the service performance. One area of particular concern is the potential for long range ordering (LRO), i.e. formation of the intermetallic Ni2Cr phase under prolonged exposure to reactor temperatures and/or irradiation, which can increase strength, decrease ductility, and cause dimensional changes or lead to in-service embrittlement of components made with these alloys. Hence, this research focused on the microstructural evolution and the SCC response of Alloy 152 under accelerated thermal aging. The materials studied involved three heats of Alloy 152 used to produce a dissimilar metal weld (DMW) joining an Alloy 690 plate to an Alloy 533 low alloy steel (LAS) plate, thermally aged at three different temperatures (370°C, 400°C and 450°C) for different durations up to 75,000h (equivalent to 60 years of reactor service). The microstructural characterization by means of synchrotron X-ray conducted in small, 0.2 mm - step line scans in the high-deformation regions of the weld root – covering areas spanning from the weld heat affected zone (HAZ) in Alloy 690 to the weld and weld butter on LAS - did not show evidence of LRO in any of the three Alloy 152 heats aged at 370°C and 450°C to an equivalent of 60 years of service. However, the first weld butter layer has high levels of deformation and is highly susceptible to SCC even in its non-aged condition. Nanohardness testing confirmed the extreme hardening with aging (ΔHV ≅ 100) at two locations within this weldment. In absence of LRO, hardening is suspected to be due to thermally-induced Cr carbide precipitation and coarsening. Testing in a primary water environment of the 1st layer of Alloy 152 weld butter aged at 370°C to a 60-year service equivalent revealed a fatigue and corrosion fatigue crack growth responses similar to those measured on the un-aged alloys. Similarly, the SCC CGR response of the aged weld butter does not appear to show a deterioration in performance, however, the difficult-to-test weldment geometry may affect the test results.
22 GENERAL STUDIES OF NUCLEAR REACTORS↗