DOE OSTI2022

CISCC Countermeasures for Spent Fuel Canisters in Concrete Casks

Aging management of spent fuel is an important issue worldwide. Chloride-induced stress corrosion cracking (CISCC) of welded canisters is particularly important for concrete casks, where it occurs in response to a combination of environmental, material, and residual stress factors. In this paper, we introduce a countermeasure to prevent the occurrence of CISCC by adjusting the flow rate of the cooling air into the concrete cask so that the canister surface temperature does not decrease below 100°C, which is a conservative deliquesce temperature threshold for CISCC occurrence. The flow adjustment device was installed in a cask model, and two tests were conducted under the heat rate conditions corresponding to those of an actual canister. In the first test, the device was operated under a condition where the canister surface temperature was below 100°C to verify whether it could increase the canister surface temperature to above 100°C. In the second test, the heat rate was decreased from a state where the canister surface temperature was above 100°C, to verify whether the device could maintain the canister surface temperature above 100°C. Good results were obtained in both cases. However, in the case of a low decay heat rate of spent fuel after extended dry storage, the temperature of the canister surface may decrease below 100°C even if no air supply is provided. Therefore, in this case, it may be necessary to take measures such as blocking air outlets.

Takeda, Hirofumi↗
DOE OSTI2020

Status Update: Deposition Modeling For SNF Canister CISCC

This report fulfills the M3 milestones M3SF-21PN010207025 & M3SF-20PN0102070412. During fiscal year (FY) 2020, Pacific Northwest National Laboratory (PNNL) worked to further develop the FY 2019 deposition and particle tracking models. This status report outlines these efforts and presents the progress made so far. Model development work is ongoing and is planned to continue in FY 2021. The FY 2020 model development included work on: Wind Effects. Model development and sensitivity studies, investigated how wind direction and speed affect deposition; Brownian Motion. Implementing Brownian Motion into existing models; Particle Size Variability. Depending on the particle composition, the diameter of the particle may vary with changes in relative humidity. Models were developed to analyze this; Multiphase and Fluid Film Modeling. Investigating canister surface wetting and drying, and how this effects overall deposition. Models were developed to analyze this; Difusophoresis. Performing initial work to implement diffusiophoresis into the existing models; Turbophoresis. Performing initial work to implement turbophoresis into the existing models. Much of this work will continue into FY21. The authors present initial results and discus current and future work.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2024

Remaining Life Prediction of SNF Storage Canisters Exposed to CISCC Environments

• DOE Standardized SNF Storage Canisters o DOE designed standard spent nuclear fuel (SNF) storage canisters for storage of DOE SNF. o DOE canisters are significantly different from commercial MultiPurpose Canisters (MPC) in size. o MPC canisters are large, a height = 15.8 ft, OD = 68”, WT = 0.5”. o DOE canisters are small with 18” / 24” diameter, 10’ / 15’ length. • Integrity Evaluation of DOE versus MPC Canisters o Many investigations have been performed for MPC canisters. o Limit investigations were performed for DOE standard canisters. Most were done at Idaho National Lab (INL). o DOE has sponsored integrity studies to evaluate weld integrity using drop tests and FEA simulations. o No evaluation on CISCC/service life of DOE canister in literature. o MPC canister: 4 axial welds, 1 center girth weld, 2 closing welds.

ZHU, Xiankui↗
DOE OSTI2025

Peening Techniques for Mitigating Chlorine-Induced Stress Corrosion Cracking of Dry Storage Canisters for Nuclear Applications

Fusion-welded austenitic stainless steel (ASS) was predominantly employed to manufacture dry storage canisters (DSCs) for the storage applications of spent nuclear fuel (SNF). However, the ASS weld joints are prone to chloride-induced stress corrosion cracking (CISCC), a critical safety issue in the nuclear industry. DSCs were exposed to a chloride-rich environment during storage, creating CISCC precursors. The CISCC failure leads to nuclear radiation leakage. Therefore, there is a critical need to enhance the CISCC resistance of DSC weld joints using promising repair techniques. This review article encapsulates the current state-of-the-art of peening techniques for mitigating the CISCC in DSCs. More specifically, conventional shot peening (CSP), ultrasonic impact peening (UIP), and laser shock peening (LSP) were elucidated with a focus on CISCC mitigation. The underlying mechanism of CISCC mitigation in each process was summarized. Finally, this review provides recent advances in surface modification techniques, repair techniques, and developments in welding techniques for CISCC mitigation in DSCs.

Chemistry↗
DOE OSTI2024

Assessing Uncertainty in Modeling Stress Corrosion Cracking

This report summarizes the collaboration between Sandia National Laboratories (SNL) and the Nuclear Regulatory Commission (NRC) to improve the state of knowledge on chloride induced stress corrosion cracking (CISCC). The foundation of this work relied on using SNL’s CISCC computer code to assess the current state of knowledge for probabilistically modeling CISCC on stainless steel canisters. This work is presented as three tasks. The first task is exploring and independently comparing crack growth rate (CGR) models typically used in CISCC modeling by the research community. The second task is implementing two of the more conservative CGR models from the first task into SNL’s full CISCC code to understand the impact of the different CGR models on a full probabilistic analysis while studying uncertainty from three key input parameters. The combined work of the first two tasks showed that properly measuring salt deposition rates is impactful to reducing uncertainty when modeling CISCC. The work in Task 2 also showed how probabilistic CGR models can be more appropriate at capturing aleatory uncertainty when modeling SCC. Lastly, appropriate and realistic input parameters relevant for CISCC modeling were documented in the last task as a product of the simulations considered in the first two tasks.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Cold Spray Deposition of 304L Stainless Steel to Mitigate Chloride-Induced Stress Corrosion Cracking in Canisters for Used Nuclear Fuel Storage

A feasibility study of the cold spray deposition process of 304L stainless steel on 304L stainless steel substrates as a mitigation method for chloride-induced stress corrosion cracking (CISCC) has been investigated under various substrate conditions. The study is aimed at the application of this technology to mitigate CISCC that may potentially occur in or nearthe fusion welded regions of stainless steel canisters in Dry Cask Storage System (DCSS) for used nuclear fuels. Spherical gas-atomized 304L stainless steel powder, in the size range of 25 µm to 44 µm, was used as a feedstock powder for the cold spray process. The powder was deposited on four types of 304L substrates with various surface conditions: as-polished, oxidized, cold-rolled, plates with prototypical CISCC. The effects of cold spray parameters on quality of cold spray coatings were investigated. Thickness, porosity, and phases in the as-deposited materials were evaluated using scanning electron microscopy (SEM) and X-ray diffraction (XRD), and correlated with microhardness and adhesion strength measured via micro-indentation and ASTM C633 pulling test, respectively. XRD analysis of the coatings was also conducted to examine the effects of cold spray condition on residual stress state in the coating. Detailed cross-sectional examination of coating/substrate interfaces was performed with transmission electron microscopy (TEM) equipped with energy dispersive spectroscopy (EDS). Dense and continuous coatings with good adhesion strength and hardness were produced for the various substrate conditions by adjusting cold spray parameters. The results demonstrate that cold spray stainless steel coating is a viable option to provide a physical barrier against CISCC in fusion weld regions of stainless steel in corrosive chloride salt-bearing environments.

Dry Cask Storage Systems, cold spray, 304L stainle↗
DOE OSTI2022

OVERVIEW OF PARTICLE DEPOSITION MODELS FOR SPENT NUCLEAR FUEL STORAGE SYSTEMS

Deposition models were built to evaluate contaminant deposition on spent nuclear fuel (SNF) canisters. The primary contaminant of concern is chloride, which is dispersed in the atmosphere and then deposits onto the canisters. During dry storage, the primary degradation process is likely to be Chloride Induced Stress Corrosion Cracking (CISCC) at the heat-affected zones of the canister welds. It is known that stainless steel canisters are susceptible to CISCC; however, the rate of chloride deposition onto the canisters is poorly known, based on sparse field data from a small number of sites. The models presented in this study could be useful for determining the rate of deposition on the canisters and the likelihood of CISCC to help with SNF canister ageing management. The deposition models were developed with the commercial computational fluid dynamics (CFD) code STAR-CCM+. Various deposition mechanisms were considered and incorporated into the models, and a sensitivity study was conducted to determine the most important mechanisms for deposition within a SNF storage system. The models included both a vertical and horizontal configuration storage system: NAC International’s Modular, Advanced Generation, Nuclear All-purpose STORage System (MAGNASTOR®) and a NUHOMS® horizontal storage module respectively. The resulting canister deposition on the horizontal canister is visually compared with inspection data taken onsite at the Calvert Cliffs Nuclear Power Plant. These models are preliminary, and development of the models will continue. Future validation exercises are currently being planned, including the Canister Deposition Field Demonstration (CDFD) effort funded by U.S. Department of Energy office of Nuclear Energy office of Spent Fuel Waste Science and Technology. The goal of the modeling presented is to demonstrate a potential modeling technique that could be used to plan and inform SNF canister ageing management programs with predictive models for the timing and occurrence of canister CISCC.

Suffield, Sarah R.↗
DOE OSTI2024

Study of Mechanical Properties, Microstructure, and Residual Stresses of AISI 304/304L Stainless Steel Submerged Arc Weld for Spent Fuel Dry Storage Systems

The confinement boundaries of spent nuclear fuel (SNF) canisters are typically fusion welded. Welded microstructures, strain hardening, and residual stresses combined with a chemically aggressive, chloride-rich environment led to concerns that the welded canister may be susceptible to chloride-induced stress corrosion cracking (CISCC). A comprehensive understanding of the modification of stainless steel (SS) metallurgical and mechanical properties by fusion welding could accelerate the predictive analysis of CISCC susceptibility. This paper describes a submerged arc welding (SAW) procedure that was developed and qualified on 12.7 mm (0.5 in.) thick AISI 304/304L SS to produce joints in a way similar to actual SNF canister manufacturing. This procedure has the potential to reduce the production cost and weld CISCC susceptibility by using fewer welding passes and lower heat input than current industrial applications. Global and local mechanical behaviors and properties, as well as residual stress distributions on the welded joint, were studied. The results indicate that hardness values in the fusion zone (FZ) and heat-affected zone (HAZ) are slightly higher than that of the base metal. Strain localization was presented in the HAZ before the tensile stress reached its maximum value, and then it shifted to the FZ. The specimen finally broke in the FZ. High tensile residual stresses exhibited in the FZ and the nearby HAZ suggest the highest CISCC-susceptible spots. The maximum tensile residual stresses were along the welding direction, indicating that if cracks occur, they would be perpendicular to the welding direction. This study involved developing and qualifying a SAW procedure for SNF canister production. The new procedure yielded cost savings (SAW working efficiency increased by about 80%), improved mechanical properties, and presented moderate residual stresses. Analysis revealed that the welded joint’s low-stress and high-stress damage assessments may be affected by shifts in the strain localization spot under loading.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2020

Investigation of Cold Spray as a Dry Storage Canister Repair and Mitigation Tool

The lack of a permanent spent nuclear fuel repository means utilities are faced with extending licenses for dry cask storage systems (DCSS) canisters far beyond their original 20-year license period. DCSS canisters are made from austenitic stainless steels (SSs) and fabricated using fusion welds. High heat input and melting associated with fabrication welds causes material around the weld to be susceptible to chloride-induced stress corrosion cracking (CISCC). The purpose of the work reported here is to investigate the use of cold spray for repair and mitigation of CISCC in DCSS canisters to ensure integrity far beyond their original license period. This report presents an analysis of cold spray for canister life extension, a summary of related efforts, relevant technology down selections, work accomplished, and future efforts relative to use of cold spray for repair and mitigation of CISCC in DCSS canisters.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2020

On residual stress analysis and microstructural evolution for stainless steel type 304 spent nuclear fuel canisters weld joint: Numerical and experimental studies

Chloride-induced stress corrosion cracking (CISCC) in the weldments of austenitic stainless steel canisters is one of the primary safety concerns during the dry storage of used nuclear fuel at Independent Spent Fuel Storage Installations in coastal areas. In order to evaluate the CISCC behavior in the canister, a 3D sequentially coupled thermo-mechanical finite element model was built to simulate the residual stresses induced by two intersecting longitudinal and circumferential multi-pass welds in austenitic stainless steel mockup canister. Weld-induced residual stresses from simulation were in good agreement with the experimental measurement results by deep-hole drilling and contour methods. Through-wall high tensile axial and hoop stresses were observed in both the fusion zone and heat affected zone (HAZ) in the longitudinal and circumferential weld, respectively. On the other hand, the microstructure within the weldments of 304 stainless steel mockup was characterized using optical microscopy, scanning electron microscopy, electron back-scattered diffraction and energy dispersive X-ray spectroscopy methods. A few amount of MnS inclusions in both the base metal and HAZ, and a lot of (Mn,Si) x O y inclusions in the fusion zone were found. Meanwhile, there is some α'-martensite in the base metal, while the martensite was reversed in the HAZ. In the fusion zone, there is a lot of δ-ferrite. The martensite reversion phenomenon was also verified by the combination of Feritscope test and thermal simulation, which could predict a martensite reversion temperature as 400C°. The welding residual stresses and microstructure analysis results could offer the instructive information for the prediction of CISCC behavior of the spent nuclear fuel canisters.

36 MATERIALS SCIENCE↗