Toughening Sm–Co sintered magnets via microstructure modification with additives
We report the mechanical properties of the brittle Smsingle bondCo permanent magnets are of great practical significance. However, studies on the magnets have mostly focused on their magnetic properties. This paper reports the modified microstructure and refined unimodal grain size, enhanced flexural strength, and magnetic properties of Sm 2 (Co,Fe,Cu,Zr) 17 sintered magnets doped with La 2 O 3 , MgO, and CaF 2 fine particulates. The correlations between microstructure, phase composition, and mechanical and magnetic properties were studied. Doping of a small amount (e.g., 0.5–3 wt%) of La 2 O 3 , MgO, or CaF 2 fine particulates could significantly refine the unimodal grain sizes of the Smsingle bondCo magnets via the Zener pinning effect. Moreover, doping significantly improved the flexural strengths σ of the magnets. For example, the σ values of the magnets with 0.5 wt% MgO, 1 wt% La 2 O 3 , and 1 wt% CaF 2 were approximately 65%, 63%, and 42% higher than that of the reference magnet, respectively. Micromechanical simulations revealed that the fine particles of La 2 O 3 could deflect crack growth, while the CaF 2 particles could attract or arrest cracks during the fracture process. The mechanical strengthening effect was mainly due to grain size refinement. The Smsingle bondCo magnets with 0.5–1.5 wt% CaF2 and 0.5 wt% La 2 O 3 exhibited excellent magnetic properties while doping 1–3 wt% La2O3 and 0.5–3 wt% MgO deteriorated magnetic performance. The rational design of CaF 2 - or La 2 O 3 -doped microstructure can be an economical and effective method for producing toughened Sm–Co sintered magnets with high magnetic performance.