Evidence for activated carrier mobility in organic solids
Activated carrier mobility confirmed in organic solids
Gutmann, F.↗
SEARCH · Search NASA
Results for “Carrier mobility”
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
Effective masses, relaxation times, and carrier mobilities in some chloride intercalants of graphite
The effective masses, carrier scattering times and carrier mobilities have been measured in selected graphite intercalation compounds using the Shubnikov-de Haas effect at a series of temperatures between 4 and 50 K. Effective masses are less than or equal to 0.1 of the free-electron mass, scattering times are about 10 to the -13th/s and carrier mobilities are on the order of 10,000 sq cm/V s.
Woollam, J. A.↗
Trap controlled minority-carrier mobility in heavily doped silicon
The activation behavior of the minority-carrier mobility and diffusivity in heavily doped (about 10 to the 20th per cu cm) Si(Si:As) was investigated in the temperature range, 20 - 350 K. Experimental results indicate that hole transitions between the valence band and localized shallow states give rise to the observed behavior. The activation energy is about 10 meV, which suggests that the localized states originate from band tails but does not rule out trapping at boron atoms in the compensated n(+) region.
Neugroschel, A.↗
Charge-carrier mobilities in Cd(0.8)Zn(0.2)Te single crystals used as nuclear radiation detectors
Charge-carrier mobilities were measured for the first time in Cd(0.8)Zn(0.2)Te single crystals using time-of-flight measurements of charge carriers produced by short (10 ns) light pulses from a frequency-doubled Nd:YAG laser (532 nm). The electron mobility displayed a T exp -1.1 dependence on the absolute temperature T in the range 200-320 K, with a room-temperature mobility of 1350 sq cm/V s. The hole mobility displayed a T exp -2.0 dependence in the same temperature range, with a room-temperature mobility of 120 sq cm/V s. Cd(0.8)Zn(0.2)Te appears to be a very favorable material for a room-temperature electronic nuclear radiation detector.
Burshtein, Z.↗
Minority-carrier mobility anomalies in low-resistivity silicon solar cells
Measurement of the minority-carrier mobility in the base region of a high-voltage metal-insulator-N-P solar cell (Green et al., 1984), as well as in other 0.1-ohm cm cells, provides direct proof that the high voltages measured for that cell are due not only to improved emitter characteristics but to an improved base region as well. The base characteristics are shown to be quite sensitive to the effects of diffusion-induced lattice stress originating in the emitter. The implications of these findings for the fabrication of high-efficiency cells are discussed.
Weizer, V. G.↗
The effect of minority carrier mobility variations on solar cell spectral response
Analysis of multistep diffused, high voltage 0.1 ohm-cm solar cells suggests that the increased voltage capability of these cells is correlated with localized variations in the base minority carrier mobility. An attempt to calculate the behavior of those cells revealed unexpected results. It is shown, contrary to what was expected, that spatial variations in the mobility effects severe changes in the short-circuit current and the spectral response. Variations in cell output as a result of imposing abrupt, linear, and exponential mobility variations are presented.
Weizer, V. G.↗
Multi-carrier mobile TDMA system with active array antenna
A multi-carrier time division multiple access (TDMA) is proposed for the future mobile satellite communications systems that include a multi-satellite system. This TDMA system employs the active array antenna in which the digital beam forming technique is adopted to control the antenna beam direction. The antenna beam forming is carried out at the base band frequency by using the digital signal processing technique. The time division duplex technique is applied for the TDM/TDMA burst format, in order not to overlap transmit and receive timing.
Suzuki, Ryutaro↗
The effect of minority carrier mobility variations on the performance of high voltage silicon solar cells
A multistep diffusion processing schedule is described which allows the attainment of high open circuit voltages in 0.1 ohm/cm silicon cells. The schedule consists of a deep primary diffusion, followed by an acid etch of emmitter surface which is then followed by a shallow secondary diffusion. A correlation is made between the observed voltage increases and the time of primary diffusion. Results indicate that as the primary diffusion time increases, the voltage rises monotonically.
Weizer, V. G.↗
Analysis of defect structure in silicon. Effect of grain boundary density on carrier mobility in UCP material
The relationships between hole mobility and grain boundary density were studied. Mobility was measured using the van der Pauw technique, and grain boundary density was measured using a quantitative microscopy technique. Mobility was found to decrease with increasing grain boundary density.
Dunn, J.↗
Measurement of minority carrier lifetime, mobility and diffusion length in heavily doped silicon
Carrier transport and recombination parameters in heavily doped silicon were examined. Data were presented for carrier diffusivity in both p- and n-type heavily doped silicon covering a broad range of doping concentrations from 10 to the 15th power to 10 to the 20th power atoms/cu cm. One of the highlights of the results showed that minority carrier diffusivities are higher by a factor of 2 in silicon compared to majority carrier diffusivities.
Swirhun, S. E.↗
Fully Printed High-Frequency Phased-Array Antenna on Flexible Substrate
To address the issues of flexible electronics needed for surface-to-surface, surface-to-orbit, and back-to-Earth communications necessary for manned exploration of the Moon, Mars, and beyond, a room-temperature printing process has been developed to create active, phased-array antennas (PAAs) on a flexible Kapton substrate. Field effect transistors (FETs) based on carbon nanotubes (CNTs), with many unique physical properties, were successfully proven feasible for phased-array antenna systems. The carrier mobility of an individual CNT is estimated to be at least 100,000 sq cm/V(dot)s. The CNT network in solution has carrier mobility as high as 46,770 sq cm/V(dot)s, and has a large current-density carrying capacity of approx. 1,000 mA/sq cm , which corresponds to a high carrying power of over 2,000 mW/ sq cm. Such high carrier mobility, and large current carrying capacity, allows the achievement of high-speed (>100 GHz), high-power, flexible electronic circuits that can be monolithically integrated on NASA s active phasedarray antennas for various applications, such as pressurized rovers, pressurized habitats, and spacesuits, as well as for locating beacon towers for lunar surface navigation, which will likely be performed at S-band and attached to a mobile astronaut. A fully printed 2-bit 2-element phasedarray antenna (PAA) working at 5.6 GHz, incorporating the CNT FETs as phase shifters, is demonstrated. The PAA is printed out at room temperature on 100-mm thick Kapton substrate. Four CNT FETs are printed together with microstrip time delay lines to function as a 2-bit phase shifter. The FET switch exhibits a switching speed of 0.2 ns, and works well for a 5.6-GHz RF signal. The operating frequency is measured to be 5.6 GHz, versus the state-of-the-art flexible FET operating frequency of 52 MHz. The source-drain current density is measured to be over 1,000 mA/sq cm, while the conventional organic FETs, and single carbon nanotube-based FETs, are typically in the mA to mA/sq cm range. The switching voltage used is 1.8 V, while the state-of-the-art flexible FET has a gate voltage around 50 V. The gate voltage can effectively control the source-drain current with an ON-OFF ratio of over 1,000 obtained at a low Vds bias of 1.8 V. The azimuth steering angles of PAA are measured at 0deg, -14.5deg, -30deg, and 48.6deg. The measured far-field patterns agree well with simulation results. The efficiency of the 2-bit 2-element PAA is measured to be 39 percent, including the loss of transmission line, FET switch, and coupling loss of RF probes. With further optimization, the efficiency is expected to be around 50-60 percent.
Chen, Yihong↗
Measurement of carrier transport and recombination parameter in heavily doped silicon
The minority carrier transport and recombination parameters in heavily doped bulk silicon were measured. Both Si:P and Si:B with bulk dopings from 10 to the 17th and 10 to the 20th power/cu cm were studied. It is shown that three parameters characterize transport in bulk heavily doped Si: the minority carrier lifetime tau, the minority carrier mobility mu, and the equilibrium minority carrier density of n sub 0 and p sub 0 (in p-type and n-type Si respectively.) However, dc current-voltage measurements can never measure all three of these parameters, and some ac or time-transient experiment is required to obtain the values of these parameters as a function of dopant density. Using both dc electrical measurements on bipolar transitors with heavily doped base regions and transients optical measurements on heavily doped bulk and epitaxially grown samples, lifetime, mobility, and bandgap narrowing were measured as a function of both p and n type dopant densities. Best fits of minority carrier mobility, bandgap narrowing and lifetime as a function of doping density (in the heavily doped range) were constructed to allow accurate modeling of minority carrier transport in heavily doped Si.
Swanson, Richard M.↗
Characterization of the transport properties of channel delta-doped structures by light-modulated Shubnikov-de Haas measurements
The transport properties of channel delta-doped quantum well structures were characterized by conventional Hall effect and light-modulated Shubnikov-de Haas (SdH) effect measurements. The large number of carriers that become available due to the delta-doping of the channel, leads to an apparent degeneracy in the well. As a result of this degeneracy, the carrier mobility remains constant as a function of temperature from 300 K down to 1.4 K. The large amount of impurity scattering, associated with the overlap of the charge carriers and the dopants, resulted in low carrier mobilities and restricted the observation of the oscillatory magneto-resistance used to characterize the two-dimensional electron gas (2DEG) by conventional SdH measurements. By light-modulating the carriers, we were able to observe the SdH oscillation at low magnetic fields, below 1.4 tesla, and derive a value for the quantum scattering time. Our results for the ratio of the transport and quantum scattering times are lower than those previously measured for similar structures using much higher magnetic fields.
Mena, R. A.↗
Multiple doping of silicon-germanium alloys for thermoelectric applications
It is shown that heavy doping of n-type Si/Ge alloys with phosphorus and arsenic (V-V doping interaction) by diffusion leads to a significant enhancement of their carrier concentration and possible improvement of the thermoelectric figure of merit. High carrier concentrations were achieved by arsenic doping alone, but for a same doping level higher carrier mobilities and lower resistivities are obtained through phosphorus doping. By combining the two dopants with the proper diffusion treatments, it was possible to optimize the different properties, obtaining high carrier concentration, good carrier mobility and low electrical resistivity. Similar experiments, using the III-V doping interaction, were conducted on boron-doped p-type samples and showed the possibility of overcompensating the samples by diffusing arsenic, in order to get n-type behavior.
Fleurial, Jean-Pierre↗
Measurement of minority-carrier drift mobility in solar cells using a modulated electron beam
A determination of diffusivity on solar cells is here reported which utilizes a one dimensional treatment of diffusion under sinusoidal excitation. An intensity-modulated beam of a scanning electron microscope was used as a source of excitation. The beam was injected into the rear of the cell, and the modulated component of the induced terminal current was recovered phase sensitively. A Faraday cup to measure the modulated component of beam current was mounted next to the sample, and connected to the same electronics. A step up transformer and preamplifier were mounted on the sample holder. Beam currents on the order of 400-pA were used in order to minimize effects of high injection. The beam voltage was 34-kV, and the cell bias was kept at 0-V.
Othmer, S.↗
Determination of the mobility profile in GaAs-MESFETs
A process for measuring charge carrier mobility for gallium-arsenide metal semiconductor field effect transistors is described in an attempt to optimize the relationship between this factor and production. The measuring procedure allows an actual determination of local mobility in the channel. The physical basis for the process and features of the measuring room are outlined. The measuring technique is described and recommendations are made for setting measuring parameters.
Prost, W.↗
Advanced methods for preparation and characterization of infrared detector materials
Crystals were prepared by the Bridgman-Stockbarger method with a wide range of crystal growth rates and temperature gradients adequate to prevent constitutional supercooling under diffusion-limited, steady-state, growth conditions. The longitudinal compositional gradients for different growth conditions and alloy compositions were calculated and compared with experimental data to develop a quantitative model of solute redistribution during the crystal growth of the alloys. Measurements were performed to ascertain the effect of growth conditions on radial compositional gradients. The pseudobinary HgTe-CdTe constitutional phase diagram was determined by precision differential-thermal-analysis measurements and used to calculate the segregation coefficient of Cd as a function of x and interface temperature. Experiments were conducted to determine the ternary phase equilibria in selected regions of the Hg-Cd-Te constitutional phase diagram. Electron and hole mobilities as functions of temperature were analyzed to establish charge-carrier scattering probabilities. Computer algorithms specific to Hg(1-x)CdxTe were developed for calculations of the charge-carrier concentration, charge-carrier mobilities, Hall coefficient, and Dermi Fermi energy as functions of x, temperature, ionized donor and acceptor concentrations, and neutral defect concentrations.
Broerman, J. G.↗
Pseudomorphic InGaAs/AlGaAs modulation-doped FET's with reduced low-frequency noise and thermally stable performance
A high-performance MODFET structure grown by MBE with the incorporation of a single quantum well In(0.15)Ga(0.85)As layer for the transport of two-dimensional electron gas has been critically examined for its thermal stability at 80 K and low-frequency noise form 0.01 to 10 to the 8th Hz. Experimental results indicate that the behavior of this device in both these respects is much superior when compared with the same behavior of conventional MODFETs. A maximum low-field carrier mobility of 29,000 sq cm/s at 80 K and an average carrier saturation velocity of 2 x 10 to the 7th cm/s at 300 K in a 1-micron gate device clearly indicate that the quality of the pseudomorphic quantum well (InGaAs) layer is either comparable or better than that of the usual GaAs buffer layer. The deep level spectra, obtained through photo-FET measurements, and the low-frequency noise spectra at different temperatures obtained for the new pseudomorphic and conventional MODFET's have clearly indicated that contributions from various deep levels present in the new structure are significantly reduced.
Liu, Shih-Ming↗