DOE OSTI2023

The Effect of Dopant Concentration and Annealing Treatments on N-Type Iodine Doped CdTe

We report properties of highly conducting n-type cadmium telluride single crystals doped with iodine (CdTe:I). These crystals were grown with dopant concentrations in the range of 10^17 cm-3 to 10^19 cm-3 by Modified Vertical Bridgman (MVB) melt growth. Post-growth dopant activation, including Cd annealing, Te annealing, and rapid thermal annealing (RTA), was applied to improve free carrier density. The structural, optical, and electrical properties were analyzed by Glow Discharge Mass Spectroscopy (GDMS), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), Photoluminescence Spectroscopy (PL), optical absorption, Hall measurements, Capacitance-Voltage (CV) measurements, and time-resolved photoluminescence (TRPL). The results indicate that Cd annealing is the most effective activation method to get 100% donor activation (n is approximately 2 x 10^18 cm-3), which is close to the room temperature solubility limit of iodine. This leads to the lowest resistivity and the highest mobility. Moreover, this data suggests a potential role of Cd vacancy-related defects on electrical self-compensation.

annealing↗
DOE OSTI2021

Mapping Current Collection in Cross Section: The Case of Copper-Doped CdTe Solar Cells

For decades, copper has been used to improve the performance of cadmium telluride thin film solar cells. However, it has also been shown to be the main cause of metastability in CdTe. Recently a low activation energy has been reported for the thermal diffusion of Cu in CdTe explaining the ease of motion that it has under moderate temperatures. The community consensus is that copper segregates to the absorber grain boundaries, where it's either beneficial or detrimental to device performance depending on its concentration. Using nanoscale X-ray micrsocopy and a two-dimensional drift-diffusion model we present a preliminary correlation between local copper distribution and electrical performance of a single-junction CdTe/CdS solar cell.

CdTe↗
DOE OSTI2024

Carrier Dynamics and Photoluminescence in Antimony-Doped CdTe and CdSeTe

Arsenic (As)-doped graded Cd(Se,Te) photovoltaics have achieved record efficiency of 22.4%, but further increases in efficiency have been limited by doping activation of only ~1% and radiative voltage losses of ~100 meV. Antimony (Sb) can also act as a p-type dopant of Cd(Se,Te) but has received relatively little attention. We measured carrier dynamics and photoluminescence of Sb-doped CdTe and CdSeTe films grown by vapor-transport deposition, with dopant activation up to ~20% Time resolved terahertz (TRTS) and photoluminescence (TRPL) data were fit by simulating the semiconductor equations, revealing bulk lifetimes of >20 ns in CdTe:Sb and >65 ns in CdSeTe:Sb and surface recombination velocities <1000 cm/s at alumina interfaces. We also qualitatively compare transients and PL spectra of doped and undoped films, with no apparent variation associated with hole concentrations up to 1015 cm-3. Preliminary variable temperature steady state photoluminescence (VT-SSPL) indicates dominant band-gap emission in CdSeTe:Sb and no evidence of potential fluctuations with Sb-doping up to this hole concentration.

14 SOLAR ENERGY↗
DOE OSTI2020

Imaging hole-density inhomogeneity in arsenic-doped CdTe thin films by scanning capacitance microscopy

We report nanometer-scale hole-density imaging in As-doped CdTe films by scanning capacitance microscopy (SCM). The hole-density profiling is validated by contrasting a CdTe cross-section sample made by molecular-beam epitaxy with systematically increased As doping in a staircase pattern over the range of 10 15 -10 18 /cm 3 within a single film. In polycrystalline films, the carrier distribution is significantly nonuniform, with inhomogeneity ranging from several hundred nm to several um and hole density varying by one order of magnitude (low 10^16 to low 10 17 /cm 3 ). This nonuniformity is distributed randomly, independent of the grain structure and grain boundaries (GBs). Kelvin probe force microscopy (KPFM) maps the surface potential and is correlated to cathodoluminescence (CL) and SCM by imaging over identical areas. Higher potential and lower CL intensity are found on GBs but not by SCM contrast; this indicates positive GB charging and recombination, but not GB-specific hole-density changes. The overall KPFM potential image is in rough agreement with the SCM carrier distribution and indicates band-edge potential fluctuations. Nonuniform carrier concentration, potential fluctuations, and defect recombination can all cause voltage and performance loss in As-doped CdTe solar technology.

14 SOLAR ENERGY↗
DOE OSTI2020

Defect Study of Group V Doped CdTe By Thermoelectric Effect Spectroscopy

Shallow acceptors in single crystal CdTe induced by Group V (P, As, and Sb) doping are identified by thermoelectric effect spectroscopy (TEES). Understanding defects in Group V doped CdTe is critical to improving and controlling the acceptor density and lifetime in the absorber material which is an important factor determining the open circuit voltage and efficiency in CdTe solar cells.

14 SOLAR ENERGY↗
DOE OSTI2020

Nanometer-Scale Imaging of Inhomogeneous Active Charge Carriers in Arsenic-Doped CdTe Thin Films

We report nanometer-scale imaging of active carrier distribution of As-doped CdTe films by scanning capacitance microscopy (SCM). We developed SCM sample preparation for CdTe by ion-milling followed by thermal processing. The nanometer-resolution carrier delineation for CdTe was validated by imaging on a CdTe cross-section sample made by a molecular beam epitaxy layer stack with As-doping concentrations of 10^15 ~10^18 /cm 3 . We found that the carrier distribution in As-doped films was significantly nonuniform, with inhomogeneity ranging from sub-um to a few um and concentration variation of one order of magnitude (low 10^16 to low 10^17 /cm 3 ). This nonuniformity is distributed randomly, independent of grain structure and grain boundary (GB). We used Kelvin probe force microscopy (KPFM) and cathodoluminescence (CL) to further map the surface potential and radiative illumination on the same area as the SCM image. Higher potential and lower CL intensity were found on GBs but not on SCM contrast, illustrating positive GB charging and GB recombination but not GB-distinguished doping. The overall KPFM potential image is in rough agreement with the SCM carrier distribution, in terms of Fermi-level position relative to the bandgap edge - thus resulting in the band-edge potential fluctuation. Nonuniform carrier concentration, potential fluctuation, and defect recombination can all together cause the Voc deficit of the As-doped CdTe device.

14 SOLAR ENERGY↗
DOE OSTI2020

Correlative nm-Scale Nonuniformity of Active Charge Carriers and Electrical Potential Along Both the Plane-View and Depth Directions in Group-V-Doped CdTe Thin Films: Preprint

We report nanometer-scale imaging on inhomogeneous distributions of active carrier and electrical potential in an As-doped CdTe film along both plane-view and film-depth directions. Despite Se grading, the SCM imaging does not show a clear variation of carrier concentration along the depth of the film. Instead, we observe carrier concentration variations of about 1 order of magnitude (high 1015 to low 1017/cm3) with inhomogeneous spatial regions ranging from a few hundred nm to a few ?m. This nonuniformity is distributed randomly in both the film lateral and vertical directions, independent of grain structure and GBs. We further mapped the surface potential using Kelvin probe force microscopy (KPFM). Higher potential was found on GBs, illustrating positive GB charging but not GB-specific carrier concentration. The results indicate that this suite of techniques can help identify nonuniform carrier concentration and potential fluctuations that can contribute to Voc deficits in GrV-doped CdTe devices.

CdTe thin film photovoltaics↗
DOE OSTI2021

Developing a Low Cost, High Volume and Scalable Manufacturing Technology for Undoped and Heavily P-Type Doped CdTe Feedstock Materials (Final Report)

The goal of this project was to establish a cost-effective and scalable production approach of feedstock (CdTe and Cd-Se-Te) for the solar industry, with the material properties necessary to improve performance and reduce costs. The primary focus was to develop a CdTe synthesis and growth process that pushed the p-type doping of CdTe to previously unattainable levels, while creating a path to scalable production. In our approach, the first step was bulk CdTe growth doped with Group V dopants (P, As, and Sb) using the Modified Vertical Bridgman (MVB) and high Pressure Bridgman (HPB) techniques, and the second step was examination of films deposited by Close-Spaced Sublimation (CSS) and Vapor Transport Deposition (VTD) using this specialized feedstock.

14 SOLAR ENERGY↗
DOE OSTI2026

Design and simulation of n -type solar cells based on an iodine-doped CdTe absorber using SCAPS-1D

The performance of conventional p-type CdTe solar cells has plateaued in recent years, motivating exploration of n-type absorbers. Here, we evaluate a homojunction solar cell employing iodine-doped CdTe (CdTe:I) as the absorber in a Ti 3 C 2 T x MXene/p-CdTe:As/n-CdTe:I/indium structure through SCAPS-1D simulations and prototype devices. Optimized simulations predict efficiencies above 25% for thin CdTe:I absorbers (~0.7 μm). In contrast, the first prototype achieved only ~1.36% efficiency with V OC = 0.48 V, J SC = 6.45 mA/cm 2 and FF = 43.8%. When the simulation is adjusted to match the actual device structure, and the effective illumination is reduced to account for front-side light loss, the predicted V OC (0.48 V) and JSC (6.74 mA/cm 2 ) closely reproduce the experimental values. This suggests that the device performance is primarily limited by reduced front-side photon transmission and other material non-idealities. These results highlight the promise of iodine-doped n-type CdTe and identify clear pathways for further efficiency improvement.

14 SOLAR ENERGY↗
DOE OSTI2023

Quantifying carrier dynamics and PL characterization of antimony-doped CdTe and CdSeTe

Our team has achieved ~20% doping activation of CdSeTe with antimony (Sb), whose shallow acceptor level makes it a viable alternative to As.1,2 Arsenic (As)-doped graded CdSeTe photovoltaics have achieved record efficiencies of 22.3%. Remaining challenges include doping activation of only ~2% in polycrystalline films and radiative voltage losses of ~100 mV. Here we use (transient) terahertz and photoluminescence spectroscopy of CdTe:Sb and CdSeTe:Sb to show sufficiently long bulk lifetimes to enable high-efficiency devices. Early results also indicate dominant bandgap emission in CdSeTe:Sb and a lack of potential fluctuations with Sb-doping that have proven detrimental for As-doped films. While more work is needed, these results show significant promise for Sb doping.

14 SOLAR ENERGY↗
DOE OSTI2024

Quantifying carrier dynamics and PL characterization of antimony-doped CdTe and CdSeTe

Our team has achieved ~20% doping activation of CdSeTe with antimony (Sb), whose shallow acceptor level makes it a viable alternative to As.1,2 Arsenic (As)-doped graded CdSeTe photovoltaics have achieved record efficiencies of 22.3%. Remaining challenges include doping activation of only ~2% in polycrystalline films and radiative voltage losses of ~100 mV. Here we use (transient) terahertz and photoluminescence spectroscopy of CdTe:Sb and CdSeTe:Sb to show sufficiently long bulk lifetimes to enable high-efficiency devices. Early results also indicate dominant bandgap emission in CdSeTe:Sb and a lack of potential fluctuations with Sb-doping that have proven detrimental for As-doped films. While more work is needed, these results show significant promise for Sb doping.

14 SOLAR ENERGY↗
DOE OSTI2020

Growth and Characterization of Arsenic-Doped CdTe 1-x Se x Single Crystals Grown by the Cd-Solvent Traveling Heater Method

The photovoltaic performance of CdTe solar cells is mainly limited by low doping and short minority carrier lifetime. Group-V element doping and Se-alloying have a significant impact on tuning these fundamental CdTe properties. In this paper, we report the growth of p-type As-doped, Cd-rich CdTe 1-x Se x single crystals using metallic Cd as the solvent in the traveling-heater method. The structural and electrical properties of CdTe1-xSex are examined for different Se concentrations. CdTe 1-x Se x single crystals (0 ≤ x ≤ 0.5) with zincblende structure indicate homogeneous composition. The 10 17 cm-3 As-doping activation efficiency can be maintained at close to 50% for x ≤ 0.2. Se alloying leads to bulk minority carrier lifetime exceeding 30 ns for samples doped near 1017 cm -3 . These results help us to overcome the current roadblocks in device performance.

14 SOLAR ENERGY↗