Titanium Carbide MXene Hole Contacts for CdTe Photovoltaics

CdTe is a high‐efficiency thin‐film photovoltaic technology that has seen tremendous commercial success over the past decade. Yet despite the improvement of other device characteristics, the fabrication of an ohmic hole back contact layer has remained a challenge due to the high ionization potential of CdTe, which limits the external potential that can be feasibly reached even as other characteristics of the device improve. MXenes, a family of 2D materials with rapidly growing scientific and commercial interest, offer a promising route to forming low‐cost, low‐barrier contacts due to their demonstrated high work function, metallic conductivity, and facile solution processing from benign solvents. Here, it is shown that Ti 3 C 2 T x MXene films processed from an aqueous colloidal dispersion can perform as a highly efficient hole contact material for CdTe solar cells, resulting in high power‐conversion efficiencies. The role of the Schottky barrier formation in Ti 3 C 2 T x ‐contacted CdTe devices is probed, and potential pathways for the future development of this potent combination of materials are elucidated. The modularity of the expansive MXene family of materials presents a promising strategy for developing next‐generation hole contacts for CdTe solar cells.

14 SOLAR ENERGY↗

Cracked Film Lithography with CuGaO x Buffers for Bifacial CdTe Photovoltaics

Abstract Bifacial CdTe solar cells with greater power density than the monofacial baselines are demonstrated by using a CuGaO x rear interface buffer that passivates while reducing sheet resistance and contact resistance. Inserting CuGaO x between the CdTe and Au increases mean power density from 18.0 ± 0.5 to 19.8 ± 0.4 mW cm −2 for one sun front illumination. However, coupling CuGaO x with a transparent conductive oxide leads to an electrical barrier. Instead, CuGaO x is integrated with cracked film lithography (CFL)‐patterned metal grids. CFL grid wires are spaced narrowly enough (≈10 µm) to alleviate semiconductor resistance while retaining enough passivation and transmittance for a bifacial power gain: bifacial CuGaO x /CFL grids generate 19.1 ± 0.6 mW cm −2 for 1 sun front + 0.08 sun rear illumination and 20.0 ± 0.6 mW cm −2 at 1 sun front + 0.52 sun rear—the highest reported power density at field albedo conditions for a scaled polycrystalline absorber.

14 SOLAR ENERGY↗

Analysis of CdTe photovoltaic cells for ambient light energy harvesting

This paper investigates the suitability of CdTe photovoltaic cells to be used as power sources for wireless sensors located in buildings. We fabricate and test a CdTe photovoltaic cell with a transparent conducting oxide front contact that provides for high photocurrents and low series resistance at low light intensities and measures the photovoltaic response of this cell across five orders of magnitude of AM1.5G light intensity. Efficiencies of 10% and 17.1% are measured under ~1 W m -2 AM1.5G and LED irradiance respectively, the highest values for a CdTe device under ambient lighting measured to date. We use our results to assess the potential of CdTe for internet of things devices from an optoelectronic, as well as a techno-economic perspective, considering its established manufacturing know-how, potential for low-cost, proven long-term stability and issues around the use of cadmium.

14 SOLAR ENERGY↗

Roadmap to 100 GWDC: Scientific and supply chain challenges for CdTe photovoltaics

This roadmap highlights pathways to expand the CdTe module manufacturing capacity per year to 100 GW DC by 2030 by improving Te extraction from existing supply chains, minimizing Te usage in modules by leveraging thinner absorbers, and focusing research efforts in key areas to improve module efficiencies. Both scientific and supply chain innovations will be necessary to maintain the high compound annual growth rate of the CdTe photovoltaic (PV) industry and cement its role as a key technology for multi-TW-scale PV deployment.

14 SOLAR ENERGY↗

Environmentally improved CdTe photovoltaic recycling through novel technologies and facility location strategies

Abstract Photovoltaic waste is projected to reach up to 78 million tons across globally dispersed locations through 2050. Current recycling infrastructure is inadequate to process these waste volumes responsibly. This necessitates commercializing novel, environmentally advantageous photovoltaic recycling technologies that improve upon incumbent industrial operations. CdTe photovoltaic recycling is a promising candidate for improvements as 25,000 tons of spent modules are recycled worldwide annually. This paper evaluates the operational performance and compares six novel technologies, the incumbent technology used in industry and one technology which extends the incumbent process across ten environmental impact categories. The tradeoff between incurring a transportation burden (ship or road) to recycle in a large‐scale centralized facility with a higher operational efficiency and avoiding transportation by recycling in a small‐scale decentralized facility with a lower operational efficiency is evaluated. Thermal delamination to eliminate the ethylene vinyl acetate and separate the photovoltaic glass panels is preferable to the incumbent mechanical process across nine environmental impact categories and decreases the climate‐change impact of CdTe photovoltaic recycling by 23%. Bath and probe sonication are ineffective for delamination, and the use of organic solvents is more environmentally burdensome than the incumbent mechanical process. Centralized recycling with shipping is environmentally preferable than with road‐based transportation. For every 100‐km increase in road transportation from the decentralized to the centralized facility, the inventory requirement in the centralized facility should be 6% lower than the decentralized facility for centralized recycling to have a lower climate‐change impact than decentralized recycling. The corresponding value for shipping is 0.4%.

Ravikumar, Dwarakanath↗

Copper iodide nanoparticles as a hole transport layer to CdTe photovoltaics: 5.5 % efficient back-illuminated bifacial CdTe solar cells

We report the role of copper iodide (CuI) nanoparticles (NPs) as a hole transport layer (HTL) in cadmium sulfide/cadmium telluride (CdS/CdTe) photovoltaics. These CuI NPs were prepared using solution processing at room temperature and used to fabricate monofacial and bifacial CdTe solar cells with different back contacts. Using CuI/Au as the back contact, the device efficiency reached to 14.8% with outstanding fill factor (FF) of 79.2%. Replacing the gold (Au) electrode with sputtered transparent indium tin oxide (ITO), a CuI/ITO back contact yielded photoconversion efficiencies (PCEs) of 11.6% and 5.5% under front and back illumination respectively. Bifacial devices (CdTe/ITO) without the CuI NP HTL have an efficiency of 7.0% and 1.0% for front and back illumination, respectively. For CuI/ITO, a current collection of 12.0 mAcm -2 was observed upon back illumination which significantly improved over an ITO-only back contact (5.0 mAcm -2 ). The PCE obtained from back illumination was enhanced when using CuI NPs as the HTL due to the reduced back barrier height, and improved back interface as determined by temperature dependent current vs. voltage characteristics and impedance spectroscopy analysis. The improvement in device performance of the bifacial configuration is a significant step forward toward realizing thin film photovoltaic modules which harvest energy incident on the rear of the module.

36 MATERIALS SCIENCE↗

Sputtered Aluminum Oxide and p+ Amorphous Silicon Back-Contact for Improved Hole Extraction in Polycrystalline CdSexTe1-x and CdTe Photovoltaics

A thin layer of Al 2 O 3 at the back of CdSe x T e1-x /CdTe devices is shown to passivate the back interface and drastically improve surface recombination lifetimes and photoluminescent response. Despite this, such devices do not show an improvement in open-circuit voltage (VOC.) Adding a p + amorphous silicon layer behind the Al 2 O 3 bends the conduction band upward, reducing the barrier to hole extraction and improving collection. Further optimization of the Al 2 O 3 , amorphous silicon (a-Si), and indium-doped tin oxide (ITO) layers, as well as their interaction with the CdCl 2 passivation process, are necessary to translate these electro-optical improvements into gains in voltage.

14 SOLAR ENERGY↗

Doping CdSexTe1-x/CdTe Graded Absorber Films with Arsenic for Thin-Film Photovoltaics

CdTe thin-film photovoltaics have demonstrated some of the lowest costs of electricity generation owing to its low material cost and ease of manufacturing. However, the full potential of polycrystalline CdTe photovoltaics can only be realized if the open-circuit voltage can be increased beyond 1 V Open-circuit voltage ~850-900 mV has been consistently observed for state-of-the-art polycrystalline CdTe solar cells. Open-circuit voltage of over 1V has been demonstrated for single crystal CdTe devices by doping with Group V elements. Therefore, this study is aimed at understanding behavior of polycrystalline CdTe devices with arsenic doping, its activation and process and performance optimization in order to overcome current voltage limitations in CdTe solar cells.

14 SOLAR ENERGY↗

Copper Defects and Charge Collection in Cadmium Telluride Photovoltaic Devices

In CdTe photovoltaic devices, the CdTe layer must be doped with Cu to reduce its resistivity, increase carrier lifetime, and improve hole transport. However, the Cu concentration is typically very low around the interfaces and within the CdTe layer, making it difficult to determine the influence Cu has on charge transport at the nanoscale; Cu concentrations are difficult to detect due to low ionization probability of Cu atoms [1]. Here, we use synchrotron X-ray microscopy to probe the nanoscale distribution of Cu and correlate it to local charge collection in CdTe photovoltaic devices. We demonstrate Cu segregation around grain boundaries, and, using cross-section charge collection measurements and transport modelling, show recombination center concentration in the CdTe layer dictates the interface at which charge collection occurs. The work gives insights on how Cu distributes in CdTe photovoltaic systems, and an understanding of how these distributions affect charge transport.

Walker, Trumann↗

Data for "Gold-Induced Chemical Perturbations in CdTe-Based Photovoltaic Cells"

Back contacting p-type CdTe has been identified as one of the major areas of loss in CdTe photovoltaic (PV) power conversion efficiency (PCE). In research settings, Au is a common contact material due to its ease of use and decent performance. This work provides a detailed investigation into using gold for back contacting As-doped, CdCl2 treated, polycrystalline CdTe that has been exposed to air after absorber processing, another routine practice. First, X-ray photoemission spectroscopy (XPS) is used to determine the native oxide to be 1.6 nm of CdTeO3 using a combination of angle-resolved XPS and the cadmium modified Auger parameter. During gold metallization of CdTe, oxygen and oxidized tellurium are eliminated from the thin CdTeO3 native oxide. The fate of the released oxygen and possibly cadmium and tellurium are not known, but these reaction byproducts can enter the absorber bulk or grain boundaries, stay at the interface, or dissolve in the Au. Interfacial hole barriers between CdTe and Au are measured for samples with and without the native oxide present prior to metallization. Results show that the thin CdTeO3 alleviates the downward band bending by 40 meV from 470 meV to 430 meV even though it is consumed during interface formation. The implications of these chemical reactions on the device are assessed through photoluminescence (PL) spectroscopy which shows losses in internal open circuit voltage (iVoc) from 820 meV to 795 meV, carrier lifetime from 123 ns to 45 ns, and PL quantum yield from 2.9x10-5 to 1.2x10-5. Modeling time-resolved PL lifetimes demonstrates the back surface recombination velocity due to metallization reduces minority carrier lifetimes. These results identify the native oxide and show that it plays an important role in mediating downward band bending along with how the back interface reaction can negatively impact device-scale parameters and reduce PV PCE.

14 SOLAR ENERGY↗

Gold-Induced Chemical Perturbations in CdTe-Based Photovoltaic Cells

Back-contacting p-type CdTe has been identified as one of the major areas of loss in CdTe photovoltaic (PV) power conversion efficiency (PCE). In research settings, Au is a common contact material due to its ease of use and decent performance. This work provides a detailed investigation into using gold for back contacting As-doped, CdCl 2 -treated, polycrystalline CdTe that has been exposed to air after absorber processing, another routine practice. First, X-ray photoemission spectroscopy (XPS) is used to determine the native oxide to be 1.6 nm of CdTeO 3 by using a combination of angle-resolved XPS and the cadmium-modified Auger parameter. During gold metallization of CdTe, oxygen and oxidized tellurium are eliminated from the thin CdTeO 3 native oxide. The fates of the released oxygen and possibly cadmium and tellurium are not known, but these reaction byproducts can enter the absorber bulk or grain boundaries, stay at the interface, or dissolve in the Au. Interfacial hole barriers between CdTe and Au are measured for samples with and without the native oxide present prior to metallization. Results show that the thin CdTeO 3 alleviates the downward band bending by 40 meV from 470 to 430 meV even though it is consumed during interface formation. The implications of these chemical reactions on the device are assessed through photoluminescence (PL) spectroscopy, which shows losses in internal open circuit voltage (iVoc) from 820 to 795 meV, carrier lifetime from 123 to 45 ns, and PL quantum yield from 2.9 × 10 −5 to 1.2 × 10 −5 . Modeling timeresolved PL lifetimes demonstrates the back surface recombination velocity due to metallization reduces minority carrier lifetimes. These results identify the native oxide and show that it plays an important role in mediating downward band bending along with how the back interface reaction can negatively impact device-scale parameters and reduce PV PCE.

14 SOLAR ENERGY↗

Cadmium Telluride Accelerator Consortium (CTAC)

The United States is the leader in cadmium telluride (CdTe) photovoltaic (PV) manufacturing, and CdTe is the second most-deployed solar technology in the world. The CdTe Accelerator Consortium (CTAC) was formed to enhance U.S. technology leadership and competitiveness in CdTe photovoltaics (PV) including increasing cell efficiencies, decreasing module costs, and maintaining or increasing domestic CdTe PV material and module production. Leadership for the 3-year consortium was selected by an NREL team through a competitive solicitation. CTAC was formally announced on August 1st by U.S. Secretary of Energy Jennifer M. Granholm and U.S. Representative Marcy Kaptur at an event held at University of Toledo. We will give an overview of CTAC research directions along with their goals and activities. We can also discuss how CTAC relates to the National Renewable Energy Laboratory (NREL) and to the U.S. Manufacturing of Advanced Cadmium Telluride Photovoltaics Consortium (US-MAC). Visit our poster to find out who leads CTAC and how you can get involved.

costs↗

Exceeding 200 ns Lifetimes in Polycrystalline CdTe Solar Cells

CdTe photovoltaics has achieved one of the lowest levelized costs of electricity among all energy sources. However, for decades, carrier lifetimes have been inferior to those of other prevalent solar cell materials. This quality has inhibited common methods to improve solar cell efficiency such as back-surface fields, electron reflectors, or bifacial solar cells. In this work, a significant increase in carrier lifetime to values exceeding 200 ns in fully functional CdTe solar cells is demonstrated. The increased lifetime is achieved by large CdSeTe grains at the absorber/emitter interface, intragrain passivation in the absorber layer, and chemical passivation by forming nanoscale oxidized tellurium species at the transparent conducting oxide interface. The carrier lifetime is correlated to the open-circuit voltage and enables paths for back-surface manipulation and novel cell architectures to further improve CdTe photovoltaic performance.

14 SOLAR ENERGY↗

The nanoscale distribution of copper and its influence on charge collection in CdTe solar cells

For decades, Cu has been the primary dopant in CdTe photovoltaic absorbers. Typically, Cu acceptor concentrations in these devices are on the order of 1 1014 cm-3, which has made it notoriously difficult to directly correlate nanoscale Cu distributions to the local charge transport properties of these devices. To measure and correlate these properties, measurement techniques require high sensitivity to elemental concentration, large penetration depth, and operando compatibility. Techniques such as secondary-ion mass spectroscopy and X-ray energy dispersive spectroscopy are widely adopted to measure Cu concentrations, but they are limited by penetration depth, sensitivity, or spatial resolution. Additionally, they lack the operando capabilities required to correlate one-to-one Cu concentrations to electrical performance. In this work, correlative X-ray microscopy is used to investigate the spatial distribution of Cu and its impact on charge collection through the depth and breadth of CdTe photovoltaic devices. Plan-view, nanoscale X-ray fluorescence maps clearly demonstrate the spatial segregation of copper around regions thought to be CdTe grain boundaries. Complementary cross-section imaging unveils the transition of the maximum charge-collection efficiency from the ZnTe-CdTe interface to the CdS-CdTe interface as a function of Cu incorporation. The copper concentration through the depth of the CdTe layer is characterized by slow and fast diffusion components, and cross-section charge-transport modeling shows that the experimentally obtained charge collection can be explained by the modeled acceptor distribution through the depth of the CdTe layer.

14 SOLAR ENERGY↗

CdTe Core: Final Technical Report (FTR)

CdTe is presently the cost-leading thin-film PV technology, directly competing with Si at scale, even when domestically manufactured. While an impressive technology, its efficiency remains much below the detailed balance limit with the largest cause due to its low photovoltage and fill factor. To realize gains, the carrier concentration, minority carrier lifetime, and interface recombination all need to be improved simultaneously over historic levels. Using a new defect chemistry (group V doping instead of copper) has been identified as a viable route using single crystal systems. This project focused on implementing this new defect chemistry in scalable, polycrystalline thin-film photovoltaic CdTe devices with tasks focusing improvements to the front interface, absorber, and rear interface as well as capability development & stakeholder engagement. The goal of the project was to establish a strategy using devices, test structures, detailed characterization, and modeling to quantify the sources of losses in state-of-the-art CdTe photovoltaic devices. Using this strategy and advanced synthesis, losses at the front interface, absorber, and rear interface were worked on in parallel. The final objective was to significantly improve the voltage deficit in CdTe devices to enable improvements in photovoltage and efficiency that can be implemented by industry in the near-term. Over the course of the project, the team developed new characterization techniques, analysis, and modeling which were then applied to state-of-the-art materials generated internally and collaboratively. In particular to enable rapid progress, NREL worked closely with First Solar where NREL grew complete devices as well as ones that interleaved process steps where First Solar had completed different steps such as absorber growth or absorber growth and activation using their baseline methods. Using detailed characterization and analysis including photoemission, photoluminescence, and scanning probe techniques enabled understanding of the loss pathways and area for improvements in our own and First Solar s materials. Ultimately, this contributed to the first series of new world record CdTe efficiencies since 2016, culminating in a 23.1% certified cell that was P-doped along with As-doped cells of similar performance. Internally, NREL improved the statistical variation in baseline As-doped devices and improved average photovoltage by over 100 mV. This was done through an improvement in absorber quality, changed front interface, and improved back contact. In addition to materially improving the fabrication processes at NREL, characterization, analysis, and modeling were developed and disseminated. NREL also played a pivotal role in community building over the course of this project working closely with the Cadmium Telluride Accelerator Consortium. NREL worked in a series of collaborations with academic and industry partners, leveraging knowledge and innovations from this project, as well as helped organize a series of workshops to ensure rapid progress in the field. Working closely with the academic community has led to a dissemination of knowledge; working with First Solar as increased US competitiveness First Solar expanded domestic production to ~10 GW and opened new facilities.

14 SOLAR ENERGY↗

Cadmium Telluride Photovoltaics Accelerator Consortium Solicitation: Request for Proposals Information

Cadmium telluride photovoltaics (CdTe PV) is a leading PV technology built on U.S. innovations that currently holds significant market share within domestic utility scale PV systems. In order to keep pace with a highly competitive and innovative global PV module market, CdTe manufacturing needs readily adaptable advances at the cell and module levels that simultaneously enable higher conversion efficiencies and manufacturing cost reductions without risking long-term module durability. In pursuit of this goal, the Department of Energy (DOE) Solar Energy Technologies Office (SETO) has asked the National Renewable Energy Laboratory (NREL) to launch and support a Consortium to accelerate domestic CdTe technology development through a competitive solicitation process. NREL will competitively select a CdTe Consortium with the goals of enhancing U.S. competitiveness and expanding domestic CdTe PV material and module production through 2030. NREL will provide coordination and oversight through development of technical scopes, review of technical proposals, subcontract support, and review of deliverables along with research support to the Consortium. The new Consortium is expected to include major U.S. companies and universities that possess strong technology development, transfer, and validation capabilities. The research and analysis output of the CdTe Consortium will inform purchasing, design, deployment, and operations decisions of companies in the domestic CdTe PV supply chain, leading to increased material and module production in the U.S.

41 EE - Solar Energy Technologies Office (EE-4S)↗

Life-cycle costing assessment of back contact doping and encapsulation alternatives for increasing the life expectancy of CdTe PV modules (Final Report)

Contribution of Research to the State-of-Knowledge This research produced comparative sustainability evaluations of back contact doping and encapsulation alternatives considered by First Solar for decreasing degradation and increasing the life of the cadmium telluride (CdTe) photovoltaic (PV) modules. Technical Effectiveness and Economic Feasibility of Methods Investigated A holistic life-cycle-assessment of the alternatives considered for longer module operational lives, showed that they add between 0.2% and 2% to environmental impact indicators at the cradle-to-gate module level, but at the cradle-to-grave system level, alternative materials offer only benefits (i.e., environmental impact indicator decreases) to the public and the environment. Parallel experimental studies at First Solar showed that the use of the considered alternative materials did not impact the effectiveness of the current module recycling separations and material recovery processes. Furthermore, the increment on the module manufacturing cost due to using alternative materials was estimated to be negligible (i.e., >1%) and longer module lives more than compensate cost increases. Specifically, increase of the current warranted module life of 30 years to 50 years, would decrease the levelized cost of electricity (LCOE) from $40/MWh to $24/MWh for utility-scale installations in the US-SW, the economic feasibility of the considered alternatives is assured. Benefit to the Public With decreasing degradation from the current ~0.3%/year of Series 6 modules to less than 0.2%/year, the public will be benefited by longer photovoltaic operational lives, and therefore. In addition, the requirement for end-of-life management is shifted from 30 years to 40 or 50 years, with profound benefits to the public and the environment.

14 SOLAR ENERGY↗