NASA NTRS1961

Structural and High-Temperature Tensile Properties of Special Pitch-Coke Graphites

The room-temperature structural properties and the tensile properties up to 5000 F (275O C) were determined for ten grades of specially prepared petroleum-coke coal-tar-pitch graphites which were graphitized at 5430 F (3000 C). One impregnation with coal-tar pitch increased the bulk density from 1.41 to 1.57 g/cm3 and the maximum strength at 4500 F (2500 C) from 4000 to 5700 psi. None of the processing parameters studied had a marked effect on the closed porosity or the X-ray structure or the per cent graphitization. The coarse-particle filler resulted in the lowest coefficient of thermal expansion and the fine-particle filler in the highest coefficient. A marked improvement in uniformity of tensile strength was observed. A standard-deviation analysis gave a one-sigma value of approximately 150 psi for one of these special grades and values of 340-420 psi for three commercial grades.

GRAPHITE↗

NASA NTRS1972

CMB-13 research on carbon and graphite

The effects of grinding on Santa Maria coke are considered, as well as the production of resin-bonded graphite from the coke. Kynol fibers, properties and purities of coal tar pitches, carbonization of resin components, synthesis of gamma BL (4-furfuryl 2-pentenoic acid gamma lactone), and a glass-like carbon powder for use as a filler are also discussed. The hydrogen contents of commercial cokes and graphites are tabulated, and a quantimet image-analyzing computer and its operation are described.

Smith, M. C.↗

NASA NTRS1973

Oxidation resistance of selected mechanical carbons at 650 deg C in dry flowing air

Oxidation experiments were conducted with several experimental mechanical carbons at 650 C in air flowing at 28 cu cm/sec (STP). Experiments indicate that boron carbide addition and zinc phosphate treatment definitely improved oxidation resistance. Impregnation with coal tar pitch before final graphitization had some beneficial effect on oxidation resistance and it markedly improved flexure strength and hardness. Graphitization temperature alone did not affect oxidation resistance, but with enough added boron carbide the oxidation resistance was increased although the hardness greatly decreased.

Allen, G. P.↗

NASA NTRS1982

Integral throat entrance development, qualification and production for the Antares 3 nozzle

Although design analyses of a G-90 graphite integral throat entrance for the Antares 3 solid rocket motor nozzle indicated acceptable margins of safety, the nozzle throat insert suffered a thermostructural failure during the first development firing. Subsequent re-analysis using properties measured on material from the same billet as the nozzle throat insert showed negative margins. Carbon-carbon was investigated and found to result in large positive margins of safety. The G-90 graphite was replaced by SAI fast processed 4-D material which uses Hercules HM 10000 fiber as the reinforcement. Its construction allows powder filling of the interstices after preform fabrication which accelerates the densification process. Allied 15V coal tar pitch is then used to complete densification. The properties were extensively characterized on this material and six nozzles were subjected to demonstration, development and qualification firings.

Clayton, F. I.↗