SCaN Network Ground Station Receiver Performance for Future Service Support

Objectives: Examine the impact of providing the newly standardized CCSDS Low Density Parity Check (LDPC) codes to the SCaN return data service on the SCaN SN and DSN ground stations receivers: SN Current Receiver: Integrated Receiver (IR). DSN Current Receiver: Downlink Telemetry and Tracking (DTT) Receiver. Early Commercial-Off-The-Shelf (COTS) prototype of the SN User Service Subsystem Component Replacement (USS CR) Narrow Band Receiver. Motivate discussion of general issues of ground station hardware design to enable simple and cheap modifications for support of future services.

Deep Space Network (DSN)↗

Self-Cleaning Cathodes for Endurance to Chromium Poisoning

Chromium (Cr) poisoning remains a significant issue in long-term solid oxide fuel cell (SOFC) operation. While the addition of Cr in the interconnect and balance-of-plant (BOP) materials is effective in improving their resistance to oxidation, it also causes the deposition of resistive phases in the air electrode and thus cell performance loss. Previous work has investigated the mitigation of chromium deposition using getters, Cr diffusion resistant coatings, and more chromium-tolerant air electrode materials. However, these mitigation strategies merely postpone the degradation of performance due to Cr poisoning. Additionally, some strategies require the replacement of components, e.g., use of getters. Here we investigated a new, in-situ Cr poisoning mitigation strategy.

30 DIRECT ENERGY CONVERSION↗

Minimizing Cr-Evaporation from Balance Of Plant Components By Utilizing Cost-Effective Alumina-Forming Austenitic Steels

A solid oxide fuel cell (SOFC) is a clean and efficient energy conversion device. The development of intermediate-temperature SOFCs has made it preferable to use metallic interconnects (MICs) to greatly reduce the cost and significantly increase the efficiency compared to ceramic interconnect materials. However, gaseous chromium species will evaporate from the chromium-containing layer formed on the surface of commonly used MICs and balance of plant (BoP) components. Volatile chromium species have been shown to form solid deposits which poison the cathodes of SOFCs, causing drastic cell performance degradation and thereby limiting commercialization. In order to alleviate the Cr poisoning and achieve long-term high performance of SOFC stacks, various Al 2 O 3 -forming austenitic (AFA) stainless steels applied at different temperatures are evaluated in this project. Based on our Phase I results (500 h operation), it is shown that on the AFAs, an alumina-based protective layer forms under high temperature that is invulnerable to water vapor effects and suppresses the diffusion of chromium and manganese which can prevent the generation of spinels on the alloy surface. Therefore, 310S, OC4 and OC5 at 800 °C and 625, OC11 and OC11LZ at 900 °C are selected to be tested in the Phase II long-term operation. From the results, we find that besides the lower Cr evaporation rates and better oxidation resistance of AFAs than benchmark alloys after short-term (500 h) operation, AFAs also possess the sturdy and compact alumina layer after a long-term operation (5000 h). A protective oxide layer is of great importance for the long-term high-temperature operation of structural materials. The high-temperature oxidation behavior of AFAs and commercial 310S and 625 alloys in Air + 10% H 2 O at 800 °C and 900 °C is systematically investigated. Severe breakaway oxidation and minor spallation are observed for the 310S and 625 after the long-term operation, while the AFAs show high oxidation resistance. It is found that the formation of a continuous alumina layer could greatly prevent the volatilization of chromium vapors. In addition, the corresponding evolving models are discussed. Chromium evaporation from BoP components in high-temperature environment could severely deteriorate the electrochemical performance of SOFC. Several methods were applied to evaluate the Cr evaporation rates of BoP after 500 h exposure at 800 °C to 900 °C in air with 10% H 2 O. An optimal method was designed to exclude the effect of silicon (Si) deposits from quartz tube and sodium (Na) deposits from the sodium carbonate on the oxidation process and the chemical interaction between Cr gaseous species and alumina tube which could provide further quantitative correlation of the evaporated Cr species quantities and degradation rates of SOFC. Based on the great performance of AFAs after long-term operation, AFAs are assembled with Anode-supported cells (ASC) to investigate the the Cr deposition of anode-supported cell under a constant current density of 0.5 A cm -2 at 800 °C with AFA alloys compared with commercial alloys. In addition, the anodic and cathodic processes are deconvoluted by distribution of relaxation times (DRT) method which are comprehensively discussed. It is found out that the voltage exhibited a slight decrease of 5.09 % and 1.54 % in the presence of OC11 and OC11LZA alloy, respectively. However, a considerable decrease of 22.14 % and 12.06 % was determined in the presence of 310S and 625 alloy, respectively. AFAs possessing the low-cost, low Cr evaporation rates and the high oxidation resistance will make it of great potential to replace the existing BoP components.

01 COAL, LIGNITE, AND PEAT↗

Minimizing Cr-Evaporation from Balance of Plant Components by Utilizing Cost-Effective Alumina-Forming Austenitic Steels

A solid oxide fuel cell (SOFC) is a clean and efficient energy conversion device. The development of intermediate-temperature SOFCs has made it preferable to use metallic interconnects (MICs) to greatly reduce the cost and significantly increase the efficiency compared to ceramic interconnect materials. However, gaseous chromium species will evaporate from the chromium-containing layer formed on the surface of commonly used MICs and balance of plant (BoP) components. Volatile chromium species have been shown to form solid deposits which poison the cathodes of SOFCs, causing drastic cell performance degradation and thereby limiting commercialization. In order to alleviate the Cr poisoning and achieve long-term high performance of SOFC stacks, various Al2O3-forming austenitic (AFA) stainless steels applied at different temperatures are evaluated in this project. Based on our Phase I results (500 h operation), it is shown that on the AFAs, an alumina-based protective layer forms under high temperature that is invulnerable to water vapor effects and suppresses the diffusion of chromium and manganese which can prevent the generation of spinels on the alloy surface. Therefore, 310S, OC4 and OC5 at 800 °C and 625, OC11 and OC11LZ at 900 °C are selected to be tested in the Phase II long-term operation. From the results, we find that besides the lower Cr evaporation rates and better oxidation resistance of AFAs than benchmark alloys after short-term (500 h) operation, AFAs also possess the sturdy and compact alumina layer after a long-term operation (5000 h). A protective oxide layer is of great importance for the long-term high-temperature operation of structural materials. The high-temperature oxidation behavior of AFAs and commercial 310S and 625 alloys in Air + 10% H 2 O at 800 °C and 900 °C is systematically investigated. Severe breakaway oxidation and minor spallation are observed for the 310S and 625 after the long-term operation, while the AFAs show high oxidation resistance. It is found that the formation of a continuous alumina layer could greatly prevent the volatilization of chromium vapors. In addition, the corresponding evolving models are discussed. Chromium evaporation from BoP components in high-temperature environment could severely deteriorate the electrochemical performance of SOFC. Several methods were applied to evaluate the Cr evaporation rates of BoP after 500 h exposure at 800 °C to 900 °C in air with 10% H 2 O. An optimal method was designed to exclude the effect of silicon (Si) deposits from quartz tube and sodium (Na) deposits from the sodium carbonate on the oxidation process and the chemical interaction between Cr gaseous species and alumina tube which could provide further quantitative correlation of the evaporated Cr species quantities and degradation rates of SOFC. Based on the great performance of AFAs after long-term operation, AFAs are assembled with Anode-supported cells (ASC) to investigate the the Cr deposition of anode-supported cell under a constant current density of 0.5 A cm -2 at 800 °C with AFA alloys compared with commercial alloys. In addition, the anodic and cathodic processes are deconvoluted by distribution of relaxation times (DRT) method which are comprehensively discussed. It is found out that the voltage exhibited a slight decrease of 5.09 % and 1.54 % in the presence of OC11 and OC11LZA alloy, respectively. However, a considerable decrease of 22.14 % and 12.06 % was determined in the presence of 310S and 625 alloy, respectively. AFAs possessing the low-cost, low Cr evaporation rates and the high oxidation resistance will make it of great potential to replace the existing BoP components.

36 MATERIALS SCIENCE↗

Controlling magnetostructural transition and magnetocaloric effect in multi-component transition-metal-based materials

Proper coupling between structural and magnetic transitions is critical for the emergence and control of magnetocaloric effects in solids. We examine the influence of minor substitutional doping (replacing Mn by Cr and Al by Sn) and interstitial doping with B on the magnetic, structural, and magnetocaloric properties of recently discovered Mn 0.5 Fe 0.5 NiSi 0.94 Al 0.06 alloy exhibiting a giant magnetocaloric effect near room temperature. We demonstrate that magnetocaloric properties of the base compound can be controlled and, in some cases, improved by chemical substitutions. First-principles computations elucidate how small changes in the composition affect properties in this family of compounds and, thus, provide useful guidance for the selection of suitable doping elements for such materials. Here the magnetic-field-induced entropy change measured for Mn 0.5 Fe 0.5 NiSi 0.94 Al 0.06 B 0.005 is –22 J/kg K near room temperature for the applied magnetic field of 2 T, and it is among the highest known values for this class of materials.

36 MATERIALS SCIENCE↗

Petrology of Chondrule Rims in Yamato-791498 and Asuka-881828, the Least-Altered CR Chondrites in the Japanese NIPR Collection

CR chondrites are a group of car-bonaceous chondrites with well-preserved records of formation of their components in the solar nebula. The CR chondrites have undergone a wide range of aqueous alteration from nearly anhydrous (CR2.8 or CR3.0) to extensive recrystallization of primary minerals, including replacement of coarse-grained silicates in chondrules (CR2.0). At the same time, CRs have experienced only minor thermal metamorphism except for rare CR6 samples. Identifying minimally altered CR chondrites is a priority because they preserve (1) relatively pristine records of the solar nebula and (2) minerals and textures at the beginning stages of aqueous alteration. Here we report the petrologic characteristics of Y-791498 and A-881828 as the least aqueously altered CR chondrites in the Japanese NIPR meteorite collection. Previous studies have shown that fine-grained rims on chondrules are indicators of incipient alteration of primitive CR chondrites, there-fore we focus on rims around chondrules in the two meteorites.

Komatsu, M.↗

Understanding Trace Iron and Chromium Incorporation During Gibbsite Crystallization and Effects on Mineral Dissolution

Incorporation of pollutants, e.g., heavy metals, or critical elements, e.g., lithium, as impurities in mineral phases can significantly affect their mobility or sequestration in the environment. Even when present at low concentrations, impurities can alter the solubility and reactivity of the host mineral. Here, in this study, we investigate the incorporation of trace amounts of iron (Fe 3+ ) and chromium (Cr 3+ ) during the crystal growth of the aluminum (Al 3+ ) hydroxide, gibbsite, a major component of bauxite ores, an important soil mineral, and a dominant mineral phase in stored radioactive wastes. Using a comprehensive suite of analytical techniques, we show that both Cr 3+ and Fe 3+ can be incorporated into the gibbsite lattice during coprecipitation by replacing Al 3+ in octahedral sites. These small amounts are consistent with limited to no structural isomorphism shared between Al 3+ and Cr 3+ /Fe 3+ hydroxide precipitates, nor room temperature miscibility of their isostructural M 2 O 3 oxide forms, in contrast with oxyhydroxide forms where Al 3+ and Fe 3+ share similar structural topologies. Despite the limited uptake of Cr 3+ /Fe 3+ , we show that these impurities have significant implications for gibbsite dissolution behavior. The limited uptake of Cr 3+ /Fe 3+ (e.g. 0.43% Cr 3+ and 0.4% Fe 3+ ), we show that these impurities have significant implications for gibbsite dissolution behavior and subsequent reactivity in complex environments.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

NASA and ESA Collaboration on Hexavalent Chrome Alternatives - Pretreatments with Primers Screening Final Test Report

Hexavalent chromium (hex chrome or Cr(VI)) is a widely used element within applied coating systems because of its self-healing and corrosion-resistant properties. The replacement of hex chrome in the processing of aluminum for aviation and aerospace applications remains a goal of great significance. Aluminum is the major manufacturing material of structures and components in the space flight arena. The National Aeronautics and Space Administration (NASA) and the European Space Agency (ESA) are engaged in a collaborative effort to test and evaluate alternatives to hexavalent chromium containing corrosion coating systems. NASA and ESA share common risks related to material obsolescence associated with hexavalent chromium used in corrosion-resistant coatings. In the United States, Occupational Safety and Health Administration (OSHA) studies have concluded that hexavalent chromium is carcinogenic and poses significant risk to human health. On May 5, 2011, amendments to the Defense Federal Acquisition Regulation Supplement (DFARS) were issued in the Federal Register. Subpart 223.73 prohibits contracts from requiring hexavalent chromium in deliverables unless certain exceptions apply. Subpart 252.223-7008 provides the contract clause prohibiting contractors and subcontractors from using or delivering hexavalent chromium in a concentration greater than 0.1 percent by weight for all new contracts associated with supplies, maintenance and repair services, and construction materials. ESA faces its own increasingly stringent regulations within European directives such as Registration, Evaluation, Authorization and Restriction of Chemical (REACH) substances and the Restriction of Hazardous Substances Directive (RoHS) which have set a mid-2017 sunset date for hexavalent chromium. NASA and ESA continue to search for an alternative to hexavalent chromium in coatings applications that meet their performance requirements in corrosion protection, cost, operability, and health and safety, while typically specifying that performance must be equal to or greater than existing systems. The overall objective of the collaborative effort between NASA TEERM and ESA is to test and evaluate coating systems (pretreatments, pretreatments with primer, and pretreatments with primer and topcoat) as replacements for hexavalent chrome coatings in aerospace applications. This objective will be accomplished by testing promising coatings identified from previous NASA, ESA, Department of Defense (DOD), and other project experience. Additionally, several new materials will be analyzed according to ESA-identified specifications.

coating↗

NASA and ESA Collaboration on Hexavalent Chrome Alternatives: Pretreatments Only Final Test Report

Hexavalent chromium (hex chrome or CR(VI)) is a widely used element within applied coating systems because of its self-healing and corrosion-resistant properties. The replacement of hex chrome in the processing of aluminum for aviation and aerospace applications remains a goal of great significance. Aluminum is the major manufacturing material of structures and components in the space flight arena. The National Aeronautics and Space Administration (NASA) and the European Space Agency (ESA) are engaged in a collaborative effort to test and evaluate alternatives to hexavalent chromium containing corrosion coating systems. NASA and ESA share common risks related to material obsolescence associated with hexavalent chromium used in corrosion-resistant coatings.

RoHS↗

Applied Research and Development to Support Open Water Testing at PacWave – Task 5: Development of additively manufactured, functionally graded, corrosion resistant clads for wave energy applications

In this task, we focused on developing corrosion-resistant claddings for wave energy applications. Wave energy systems are exposed to saline conditions, which are corrosive to many metallic structural materials (e.g., carbon steel). Corrosion-resistant (stainless) steels are typically alloyed with >18% chromium (Cr) and >8% nickel (Ni), which dramatically raises material costs and can hinder the development of wave energy systems; thus, coatings are a necessary corrosion protection method for most. Non-metallic coatings (paint, epoxy) have shorter service lives, limited resistance to mechanical stress and wear, plus additional costs of inspection and eventual replacement. Therefore, overlay stainless steel (SS) claddings have a cost-effective use case for protecting components from corrosion, particularly for those that may be subject to mechanical stress / wear and with long service lives.

16 TIDAL AND WAVE POWER↗

Heterogeneous creep deformation behavior of functionally graded transition joints (GTJs)

Dissimilar metal welds (DMWs) made between ferritic steels and austenitic alloys are used extensively in high-temperature power plant components. These DMWs experience premature creep failure in the ferritic steel’s heat affected zone (HAZ), close to the weld interface. Steep variations in microstructure and chemical composition across the dissimilar weld interface have been the contributing factors for the failure. Graded transition joints (GTJs), developed by functionally grading the chemical composition in layers, have been proposed as potential candidates to replace DMWs. In this research, GTJ coupons were fabricated between 2.25Cr-1Mo steel and Alloy 800H base material using two filler materials: (i) Inconel 82 and (ii) P87. These samples were aged at 600°C for 2000h to accelerate high-temperature microstructural evolution seen in service conditions, before subjecting them to short-term (~1 month) creep tests. Surface strains were measured using digital image correlation (DIC) technique to extract creep strain rates at different locations within GTJs. Both the GTJs exhibited heterogeneous creep strain distribution. Creep strain accumulated in the FGHAZ of 2.25Cr-1Mo steel, similar to type IV failure associated with Cr-Mo steel weldments. Microstructure based creep model framework was developed to describe the discrete creep strain rates observed in various 2.25Cr-1Mo steel regions of GTJs.

36 MATERIALS SCIENCE↗

Friction and Wear Characteristics of a Modified Composite Solid Lubricant Plasma Spray Coating

LCR304 is a solid lubricant coating composed of Ni-10Cr, Cr2O3, BaF2-CaF2 and Ag and developed for dimensional stability in high temperature air. This coating is a modification of PS304, which differs in that the Ni-Cr constituent contains 20wt% Cr. The tribological characteristics of LCR304 were evaluated by pin-on-disk and foil air bearing rig testing from 25 to 650 C and compared to previous test results with PS304. For both tests, the friction coefficient decreased as temperature increased from 25 to 650 C. Wear generally decreased with increasing temperature for all pin-on-disk tests. LCR304 coated components produced the least wear of Inconel X-750 counterface materials at 427 and 650 C. These results indicate that the LCR304 coating has potential as a replacement for PS304 in, for example, low cycle (minimum wear) applications where dimensional stability is imperative.

Stanford, M. K.↗

What Are Space Exposure Histories Telling Us about CM Carbonaceous Chondrites?

Chondrites are chemically primitive and carbonaceous (C) chondrites are potentially the most primitive among them because they mostly escaped thermal metamor-phism that affected the other chondrite groups and ratios of their major, non-volatile and most of the volatile elements are similar to those of the Sun. Therefore, C chondrites are ex-pected to retain a good record of the origin and early history of the solar system. Carbonaceous chondrites are chemically differentiated from other chondrites by their high Mg/Si ratios and refractory elements, and have experienced various degrees of aqueous alteration. They are subdivided into eight subgroups (CI, CM, CO, CV, CK, CR, CB and CH) based on major element and oxygen isotopic ratios. Their elemental ratios spread over a wide range though those of ordinary and enstatite chondrites are relatively uniform. It is critical to know how many sepa-rate bodies are represented by the C chondrites. In this study, CM chondrites, the most abundant carbona-ceous chondrites, are examined. They are water-rich, chon-drule- and CAI-bearing meteorites and most of them are brec-cias. High-temperature components such as chondrules, iso-lated olivine and CAIs in CMs are frequently altered and some of them are replaced by clay minerals and surrounded by sul-fides whose Fe was derived from mafic silicates. On the basis of degrees of aqueous alteration, CMs have been classified into subtypes from 1 to 2, although Rubin et al. [1] assigned subtype 1 to subtype 2 and subtype 2 to subtype 2.6 using various petrologic properties. The classification is based on petrographic and mineralogic properties. For example, though tochilinite (2[(Fe, Mg, Cu, Ni[])S] 1.57-1.85 [(Mg, Fe, Ni, Al, Ca)(HH)2]) clumps are produced during aqueous alteration, they disappear and sulfide appears with increasing degrees of aqueous alteration. Cosmic-ray exposure (CRE) age measurements of CM chondrites reveal an unusual feature. Though CRE ages of other chondrite groups range from several Myr to tens of Myr, CMs exposure ages are not longer than 7 Myr with one-third of the CM having less than 1 Myr CRE age. For those CM chondrites that have CRE ages <1 Myr, there are two discern-able CRE peaks. Because a CRE age reflects how long a me-teorite is present as a separate body in space, the peaks pre-sumably represent collisional events on the parent body (ies) [2]. In this study we defined 4 distinct CRE age groups of CMs and systematically characterized the petrography in each of the 4 CRE age groups to determine whether the groups have significant petrographic differences, with such differences probably reflecting different parent body (asteroid) geological processing, or multiple original bodies.

Takenouchi, A.↗

6.26 Low Cost Basalt Fiber for Automotive Applications

Vehicle lightweighting is an essential component to the automotive industry to improve fuel economy of internal combustion engine (ICE) vehicles to meet ever improving emission standards and to improve the range of electric vehicles (EV). Composite materials offer high specific modulus and specific strength, which makes them appealing for these light weighting efforts. Sheet molding compounds (SMC) are particularly interesting from an automotive perspective because of the relatively low cost and high volume of producing SMC parts. Traditionally, composite materials for automotive application are glass fiber reinforced because of the attractive price - performance ratio, but basalt fibers are a cost and recycling competitive reinforcement alternative in this market. The aim of this project was to examine the feasibility of utilizing basalt fiber for automotive applications. More specifically, an effort was made to examine different fiber sizings on basalt fiber combined with vinyl-ester (VE) resin, and their performance as part of an SMC process. In addition to offering vehicle lightweighting with fiber reinforced polymer composites, basalt fiber is a fully recyclable material and thus supports the IACMI technical goal of: Demonstrate that the technology is capable at a sufficient scale for >80% recyclability or reuse of fiber reinforced polymer composites in five years into useful components with projected cost and quality at commercial scale competitive with virgin materials on a pathway to 95% recyclability or reuse starting in ten years. Three different fiber sizings were applied to a continuous roving of basalt fiber and compared to a traditional Electrical/Chemical Resistance (E-CR) glass fiber that is typically used in these types of applications. Fiber tows were examined for Loss on Ignition percentage (LOI%), Tex, and tow strength. Some sizings clearly outperformed others, and the ability to process these fibers on a pilot scale SMC line was demonstrated. A test plan for the manufacturing and mechanical testing of SMC panels was developed. This work continues outside the time frame allocated for this project. When this work is completed, it will be added to this report and posted as Appendix C. Glass fiber reinforced SMC materials have already proven feasible as a light weighting method for traditionally steel parts like the Volkswagen (VW) Atlas lift-gate (Figure 1); this project team is seeking the feasibility of basalt fiber as a drop-in replacement for glass fiber reinforced SMC. Sizing development for basalt fibers has proven that the mechanical properties are better than E-glass and closer to S-glass, which makes it an interesting material for SMC applications. Better mechanical properties translate to less material needed to achieve load case requirement for target applications. The business case has already been demonstrated for 100,000 parts per year of glass fiber reinforced SMC Atlas lift-gates compared to traditional steel manufacturing processes. Reduced overhead and assembly costs are offset by glass fiber SMC higher cost per kg beyond 100,000 parts per year, which is still a relatively low volume for the automotive industry. For basalt fiber reinforced SMC to become feasible for automotive applications, the price-performance ratio has to be precisely determined. Based on the mechanical performance it is possible to establish a range of applications and technical solutions in which the potential of basalt SMC can be utilized, while the price of the material can be used to compile the business case for such applications. Based on these business cases and the sustainability indicators, glass fiber reinforcement (or other) materials can be directly substituted. Volkswagen’s commitment to reducing carbon emissions cannot be understated. Basalt fiber shows promise of reducing the carbon footprint in SMC materials, especially if sizing optimizations can be made with thermoplastic based SMC. To fully realize the value of basalt fiber reinforced materials, a lifecycle cost analysis should be performed on basalt’s production and recycling, and then compared against E-glass. From this assessment, a true judgement can be made on the commercialization potential of this material. Figure 1. Example of Fiber Reinforced Polymer Composite Liftgate As a conclusion, we can state that Mafic basalt fiber is not a direct replacement for E-glass or E-CR glass based on price, but should be considered a technical solution when E-glass does not provide adequate performance in a composite design and S-glass, aramid and carbon fibers are too costly. Mafic basalt fiber can be placed on the high-performance fiber spectrum next to S-glass for performance but at one third the price. It should be considered for more technically challenging structural designs wherein the performance can demonstrate 20-25% performance enhancement over E-glass to elicit more strength or a weight reduction. Both Michelman and Mafic produce thermoplastic sizings which, in combination with Nylon and polypropylene resin and fibers, can further advance high speed composite implementations while maintaining an eco-friendly manufacturing process.

36 MATERIALS SCIENCE↗

Effect of Thermal Aging on Microstructure and Stress Corrosion Cracking Behavior of an Alloy 152 1st Layer Butter Weldment

Nickel-based Alloy 690 and the associated weld Alloys 52 and 152 are typically used for nozzle penetrations in replacement heads for pressurized water reactor (PWR) vessels, because of their excellent overall resistance to general corrosion and environmental degradation, primarily stress corrosion cracking (SCC). However, many of the existing PWRs are expected to operate for 40- 80 years. Likewise, water-cooled small modular reactors (SMRs) will use Ni-Cr alloys and are expected to receive initial operating licenses for 60 years. Hence, the thermal stability of Ni-Cr alloys is critical for the long-term performance of both existing and advanced nuclear power plants, and possibly spent fuel storage containers. The objective of this research is to understand the microstructural changes occurring in high-Cr, Ni-based Alloy 152 weldments during long time exposure to the reactor operating temperatures, and the effect of these changes on the service performance. One area of particular concern is the potential for long range ordering (LRO), i.e. formation of the intermetallic Ni2Cr phase under prolonged exposure to reactor temperatures and/or irradiation, which can increase strength, decrease ductility, and cause dimensional changes or lead to in-service embrittlement of components made with these alloys. Hence, this research focused on the microstructural evolution and the SCC response of Alloy 152 under accelerated thermal aging. The materials studied involved three heats of Alloy 152 used to produce a dissimilar metal weld (DMW) joining an Alloy 690 plate to an Alloy 533 low alloy steel (LAS) plate, thermally aged at three different temperatures (370°C, 400°C and 450°C) for different durations up to 75,000h (equivalent to 60 years of reactor service). The microstructural characterization by means of synchrotron X-ray conducted in small, 0.2 mm - step line scans in the high-deformation regions of the weld root – covering areas spanning from the weld heat affected zone (HAZ) in Alloy 690 to the weld and weld butter on LAS - did not show evidence of LRO in any of the three Alloy 152 heats aged at 370°C and 450°C to an equivalent of 60 years of service. However, the first weld butter layer has high levels of deformation and is highly susceptible to SCC even in its non-aged condition. Nanohardness testing confirmed the extreme hardening with aging (ΔHV ≅ 100) at two locations within this weldment. In absence of LRO, hardening is suspected to be due to thermally-induced Cr carbide precipitation and coarsening. Testing in a primary water environment of the 1st layer of Alloy 152 weld butter aged at 370°C to a 60-year service equivalent revealed a fatigue and corrosion fatigue crack growth responses similar to those measured on the un-aged alloys. Similarly, the SCC CGR response of the aged weld butter does not appear to show a deterioration in performance, however, the difficult-to-test weldment geometry may affect the test results.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

Effect of thermal aging on microstructure and stress corrosion cracking behavior of Alloy 152 weldment

Nickel-based Alloy 690 and the associated weld Alloys 52 and 152 are typically used for nozzle penetrations in replacement heads for pressurized water reactor (PWR) vessels, because of their excellent overall resistance to general corrosion and environmental degradation, primarily stress corrosion cracking (SCC). However, many of the existing PWRs are expected to operate for 40-80 years. Likewise, water-cooled small modular reactors (SMRs) will use Ni-Cr alloys and are expected to receive initial operating licenses for 60 years. Hence, the thermal stability of Ni-Cr alloys is a potential concern for the long-term performance of both existing and advanced nuclear power plants, and possibly spent fuel storage containers. The objective of this research is to understand the microstructural changes occurring in high-Cr, Ni-based Alloy 152 weldments during long time exposure to the reactor operating temperatures, and the effect of these changes on the service performance. One area of particular concern is the potential for long range ordering (LRO), i.e. formation of the intermetallic Ni2Cr phase under prolonged exposure to reactor temperatures and/or irradiation, which can increase strength, decrease ductility, and cause dimensional changes or lead to in-service embrittlement of components made with these alloys. Hence, this research focused on the microstructural evolution and the SCC response of Alloy 152 under accelerated thermal aging. The materials studied involved three heats of Alloy 152 used to produce a dissimilar metal weld (DMW) joining an Alloy 690 plate to an Alloy 533 low alloy steel (LAS) plate, thermally aged at three different temperatures (370°C, 400°C and 450°C) for up to 75,000h (equivalent to 60 years of service). The microstructural characterization by means of synchrotron X-ray conducted in small, 0.2 mm - step line scans in the high-deformation regions of the weld root – covering areas spanning from the weld heat affected zone (HAZ) in Alloy 690 to the weld and weld butter on LAS - did not show evidence of LRO in any of the three Alloy 152 heats aged to an equivalent of 60 years of service. Testing in a primary water environment of two heats of Alloy 152 aged at 370°C to a 60-year service equivalent revealed a fatigue and corrosion fatigue crack growth responses similar to those measured on the un-aged alloys. However, the SCC CGR response of the aged samples appears to show a deterioration in performance, confirming our previous observation.

36 MATERIALS SCIENCE↗

Effect of thermal aging and irradiation on microstructure and crack growth response of Alloy 690

Nickel-base Alloy 690 and the associated weld Alloys 52 and 152 are typically used for nozzle penetrations in replacement heads for pressurized water reactor (PWR) vessels, because of their excellent overall resistance to general corrosion and environmental degradation, primarily stress corrosion cracking (SCC). However, many of the existing PWRs reactors are expected to operate for 40-80 years. Likewise, advanced water-cooled small modular reactors (SMRs) will use Ni-Cr alloys and are expected to receive initial operating licenses for 60 years. Hence, the thermal stability of Ni-Cr alloys is a potential concern for the long-term performance of both existing and advanced nuclear plants, and possibly spent fuel storage containers. The objective of this research is to understand the microstructural changes occurring in high-Cr, Ni-based Alloy 690 during long time exposure to the reactor operating temperatures, and the effect of these changes on the service performance. One area of particular concern is the potential for long range ordering (LRO), i.e. formation of the intermetallic Ni 2 Cr phase under prolonged exposure to reactor temperatures and/or irradiation, which can increase strength, decrease ductility, and cause dimensional changes or lead to in-service embrittlement of components made with these alloys. Hence, this research focused on the microstructural evolution and the SCC response of Alloy 690 under accelerated thermal aging and irradiation conditions. The materials studied involved Alloy 690 from two sources: (i) Alloy 690 plate from an Alloy 152 dissimilar metal weld (DMW) joining the Alloy 690 plate to Alloy 533 LAS, aged at three different temperatures (370°C, 400°C and 450°C) for up to 75,000h (equivalent to 60 years of service), and (ii) specimens neutron-irradiated in the BOR-60 reactor up to 40 dpa. For aged Alloy 690 specimens, hardness was found to increase with aging time, however, the microstructural characterization by means of synchrotron X-ray did not find evidence of LRO. The microstructural characterization of neutron-irradiated specimens by TEM found no evidence of LRO either. Testing in a primary water environment of Alloy 690 specimens aged to a 60-year service equivalent revealed a fatigue and corrosion fatigue crack growth responses similar to those measured on the un-aged alloy. The SCC CGR response was also low. Overall, the two Alloy 690 heats investigated in this work, aged up to 60-year service equivalents or exposed to neutron irradiation up to 40 dpa, did not exhibit a deterioration in microstructure or performance.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

Effect of thermal aging on microstructure and crack growth response of Alloy 152 weld

Nickel-based Alloy 690 and the associated weld Alloys 52 and 152 are typically used for nozzle penetrations in replacement heads for pressurized water reactor (PWR) vessels, because of their excellent overall resistance to general corrosion and environmental degradation, primarily stress corrosion cracking (SCC). However, many of the existing PWRs are expected to operate for 40-80 years. Likewise, advanced water-cooled small modular reactors (SMRs) will use Ni-Cr alloys and are expected to receive initial operating licenses for 60 years. Hence, the thermal stability of Ni-Cr alloys is a potential concern for the long-term performance of both existing and advanced nuclear power plants, and possibly spent fuel storage containers. The objective of this research is to understand the microstructural changes occurring in high-Cr, Ni-based Alloy 152 weldments during long time exposure to the reactor operating temperatures, and the effect of these changes on the service performance. One area of particular concern is the potential for long range ordering (LRO), i.e. formation of the intermetallic Ni2Cr phase under prolonged exposure to reactor temperatures and/or irradiation, which can increase strength, decrease ductility, and cause dimensional changes or lead to in-service embrittlement of components made with these alloys. Hence, this research focused on the microstructural evolution and the SCC response of Alloy 152 under accelerated thermal aging. The materials studied involved three heats of Alloy 152 used to produce a dissimilar metal weld (DMW) joining an Alloy 690 plate to an Alloy 533 low alloy steel (LAS) plate, thermally aged at three different temperatures (370°C, 400°C and 450°C) for up to 75,000h (equivalent to 60 years of service). The microstructural characterization by means of synchrotron X-ray did not find evidence of LRO in any of the three heats aged to an equivalent of 60 years of service. Testing in a primary water environment of a heat of Alloy 152 aged at 370°C to a 60-year service equivalent revealed a fatigue and corrosion fatigue crack growth responses similar to those measured on the un-aged alloy. However, the SCC CGR response of the aged sample appears to show a deterioration in performance.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗