Results for “Crack growth”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 19 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1987

Random loading fatigue crack growth: Crack closure considerations

The prediction of fatigue crack growth is an important element of effective fracture control for metallic structures and mechanical components, especially in the aerospace industry. The prediction techniques available and applied today are mostly based on fatigue crack growth measurements determined in constant amplitude testing. However, while many service loadings are constant amplitude, many more loadings are random amplitude. An investigation to determine which statistics of random loadings are relevant to fatigue crack closure was conducted. The fundamentals of random processes and crack closure are briefly reviewed, then the relevance of certain random process parameters to the crack closure calculation are discussed qualitatively. A course for further research is outlined.

Ortiz, Keith↗
NASA NTRS1983

Measurement and analysis of critical crack tip processes associated with variable amplitude fatigue crack growth

Crack growth retardation following overloads can result in overly conservative life predictions in structures subjected to variable amplitude fatigue loading when linear damage accumulation procedures are employed. Crack closure is believed to control the crack growth retardation, although the specific closure mechanism is debatable. Information on the relative contributions to crack closure from: (1) plasticity left in the wake of the advancing crack and (2) crack tip residual stresses is provided. The delay period and corresponding crack growth rate transients following overloads are systematically measured as a function of load ratio (R) and overload magnitude. These responses are correlated in terms of the local 'driving force' for crack growth as measured by crack tip opening loads and delta K sub eff. The latter measurements are obtained using a scanning electron microscope equipped with a cyclic loading stage; measurements are quantified using a relatively new stereoimaging technique. Combining experimental results with analytical predictions suggests that both plastic wake and residual stress mechanism are operative, the latter becoming predominate as R increases.

Hudak, S. J., Jr.↗
DOE OSTI2024

CONSTRAINT-INDEPENDENT CONSTANT CTOA DETERMINATION FOR DUCTILE STABLE CRACK GROWTH

Crack tip opening angle (CTOA) has been used as a reliable fracture toughness parameter for decades to characterize stable ductile crack growth for thin-walled aerospace structures in the low-constraint conditions. Recently, the CTOA parameter was also applied to the pipeline industry, and a CTOA test standard ASTM E3039 was thus developed for testing a critical constant CTOA. Research showed that the constant CTOA can reasonably describe fracture toughness required to arrest a dynamic crack propagation for a modern gas pipeline. However, the CTOA fracture criterion requires constraint-independent CTOA toughness against stable ductile crack growth. ASTM E3039 recommends a drop weight tearing test (DWTT) specimen for CTOA testing. Since a shallow crack is used, DWTT measured CTOA may depend on constraint level at the crack tip. To understand if it is the case, this paper evaluates the critical CTOA for a set of fracture toughness tests on single edge notched bend (SENB) specimens with shallow and deep cracks based on four CTOA estimation models. In which, the Ln(P)-LLD linear fit model is similar to that used by ASTM E3039 in the CTOA calculation. Fracture test data for X80 pipeline steel and HY80 structural steel are considered in the CTOA evaluation. The results show that the four CTOA models can determine a crack size-independent constant CTOA over stable ductile crack growth for the SENB specimens. As a result, CTOA determined by ASTM E3039 is constraintindependent and transferable to use for an actual crack propagating in a gas pipeline.

Zhu, Xian-Kui↗
NASA NTRS1983

A critical study of the crack closure effect on near-threshold fatigue crack growth

Crack closure in the near-crack-tip region has been considered to be an important contribution to the development of a crack-growth threshold for macroscopic cracks. Recent analytical work, however, has suggested that closure well back of the tip may be the controlling factor. In order to check on this possibility, material has been machined away far behind the crack tip in order to eliminate long-range closure. Removal of this material did not eliminate the threshold, but did lower the threshold level by approximately 10 percent for tests conducted on 6.3 mm-thick X7090-T6 powder metallurgy aluminum alloy.

Minakawa, K.↗
NASA NTRS1995

Fatigue Crack Growth and Crack Bridging in SCS-6/Ti-24-11

Interfacial damage induced by relative fiber/matrix sliding was found to occur in the bridged zone of unidirectional SCS-6/Ti-24Al-11Nb intermetallic matrix composite specimens subjected to fatigue crack growth conditions. The degree of interfacial damage was not uniform along the bridged crack wake. Higher damage zones were observed near the machined notch in comparison to the crack tip. The interfacial friction shear strength tau(sub f) measured in the crack wake using pushout testing revealed lower values than the as-received interface. Interfacial wear also reduced the strength of the bridging fibers. The reduction in fiber strength is thought to be a function of the magnitude of relative fiber/matrix displacements ind the degree of interfacial damage. Furthermore, two different fiber bridging models were used to predict the influence of bridging on the fatigue crack driving force. The shear lag model required a variable tau(sub f) in the crack wake (reflecting the degradation of the interface) before its predictions agreed with trends exhibited by the experimental data. The fiber pressure model did an excellent job in predicting both the FCG data and the DeltaCOD in the bridged zone even though it does not require a knowledge of tau(sub f).

Ghosn, Louis J.↗
NASA NTRS1974

The effect of pre-stress cycles on fatigue crack growth - An analysis of crack growth mechanism

Cyclic prestress increases subsequent fatigue crack growth rate in 2024-T351 aluminum alloy. This increase in growth rate, caused by the prestress, and the increased rate, caused by temper embrittlement as observed by Ritchie and Knott (1973), cannot be explained by the crack tip blunting model alone. Each fatigue crack increment consists of two components, a brittle and a ductile component. They are controlled by the ductility of the material and its cyclic yield strength, respectively.

Kang, T. S.↗
NASA NTRS1990

Simulation of crack growth and crack closure under large cyclic plasticity

The propagation of a crack during cyclic loading with large plasticity was simulated using a finite element method. The numerical procedure included the determination of crack closing and opening by examining the contact condition of the crack surfaces in the plasticity iteration. The method was applied to the growth of cracks in Alloy 718 single edge notch specimens at 538 C subject to strain cycling under both nominally elastic and elastoplastic conditions. The results show, among other things, that the crack closure and opening stresses become more compressive as the loading becomes more plastic, and that, under a given control condition, the closure and opening stresses become less compressive as the crack propagates.

Kim, K. S.↗
DOE OSTI2024

Summary of Alloy 617 and Alloy 709 Elevated Temperature Crack Growth Test Results from the Planned FY24 Crack Growth Test Activities

This report covers the results from crack growth rate testing performed at Idaho National Laboratory in the fiscal year 2024. It includes two creep crack growth rate tests and two creep-fatigue crack growth rate tests. Results are shown for each of these tests, included crack growth measured during the test using direct current potential drop, and measurements based off of the fracture surface. Load line displacement, as well as load, were also collected during the tests. Detailed analysis of the results will continue into the next fiscal year, however, a number of potential improvements to the equipment and testing procedures were identified that will increase testing reliability and throughput, as well as decrease complications with the analysis.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

Results of Initial Alloy 617 High Temperature Crack Growth Testing

Crack propagation data can provide valuable insights when performing a safety evaluation for a component. Alloy 617 is qualified in Section III, Division 5 of the American Society of Mechanical Engineers (ASME) Boiler and Pressure Vessel Code (BPVC) for elevated-temperature nuclear service up to 950°C. Little is known, however, about subcritical crack-growth phenomena in Alloy 617. Previous crack-growth studies of Alloy 617 did not investigate temperatures across the range which is currently qualified in Section III, Division 5. High-temperature crack-growth testing in air and in reactor-grade helium can provide data for establishing the crack-growth correlations in support of an ASME BPVC Section XI high-temperature flaw evaluation Code Case. Idaho National Laboratory (INL) has previously performed crack-growth testing, but the equipment requires revitalization. This report provides the status of crack-growth testing in Alloy 617 at INL.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2023

Inversion-based correction of Double-Torsion (DT) subcritical crack growth tests for crack profile geometry

Because of its simplicity and the ability to produce a stable, slow-propagating crack, the Double-Torsion (DT) method has been used widely for investigating the critical and subcritical propagation of a slow-propagating tensile (mode-I) crack. However, to determine the complex relationship between the crack velocity $\mathcal{v_c}$ vs. the strain energy release rate $\mathscr{G}$ (or the stress intensity factor K) from laboratory measurements, several corrections must be made to account for the impact of sample and crack geometry. Particularly, DT test typically produces a crack with a curved edge profile instead of a straight line, causing the local $\mathcal{v_c}$ and $\mathscr{G}$ vary along the crack front. The experimentally measured $\mathcal{v_c}$ and $\mathscr{G}$ data merely reflect collective, averaged behavior of the crack. This makes inversion for the intrinsic, “true” crack growth kinetics necessary, based upon the knowledge of the crack geometry. Simple and effective correction methods have been proposed and validated for the slow, chemical-reaction-controlled part (Region I) of the $\mathcal{v_c}$-$\mathscr{G}$ curve. However, reliable methods for the highly nonlinear, transport-dominated part (Region II) and its sudden transition to the dynamic propagation part (Region III) are still lacking. Here we propose a method for determining the intrinsic $\mathcal{v_c}$-$\mathscr{G}$ relationship across all three Regions based upon DT test data, using a simple model function and its numerical inversion. The performance of this approach is examined and demonstrated using both synthetic and laboratory data for subcritical crack growth in soda lime glass.

42 ENGINEERING↗
NASA NTRS2003

Fatigue Crack Growth Rate and Stress-Intensity Factor Corrections for Out-of-Plane Crack Growth

Fatigue crack growth rate testing is performed by automated data collection systems that assume straight crack growth in the plane of symmetry and use standard polynomial solutions to compute crack length and stress-intensity factors from compliance or potential drop measurements. Visual measurements used to correct the collected data typically include only the horizontal crack length, which for cracks that propagate out-of-plane, under-estimates the crack growth rates and over-estimates the stress-intensity factors. The authors have devised an approach for correcting both the crack growth rates and stress-intensity factors based on two-dimensional mixed mode-I/II finite element analysis (FEA). The approach is used to correct out-of-plane data for 7050-T7451 and 2025-T6 aluminum alloys. Results indicate the correction process works well for high DeltaK levels but fails to capture the mixed-mode effects at DeltaK levels approaching threshold (da/dN approximately 10(exp -10) meter/cycle).

Forth, Scott C.↗
NASA NTRS2015

On the Crack Bifurcation and Fanning of Crack Growth Data

Crack growth data obtained from ASTM load shedding method for different R values show some fanning especially for aluminum alloys. It is believed by the authors and it has been shown before that the observed fanning is due to the crack bifurcation occurs in the near threshold region which is a function of intrinsic properties of the alloy. Therefore, validity of the ASTM load shedding test procedure and results is confirmed. However, this position has been argued by some experimentalists who believe the fanning is an artifact of the test procedure and thus the obtained results are invalid. It has been shown that using a special test procedure such as using compressively pre-cracked specimens will eliminate the fanning effect. Since not using the fanned data fit can result in a significantly lower calculated cyclic life, design of a component, particularly for rotorcraft and propeller systems will considerably be impacted and therefore this study is of paramount importance. In this effort both test procedures i.e. ASTM load shedding and the proposed compressive pre-cracking have been used to study the fatigue crack growth behavior of compact tension specimens made of aluminum alloy 2524-T3. Fatigue crack growth paths have been closely observed using SEM machines to investigate the effects of compression pre-cracking on the crack bifurcation behavior. The results of this study will shed a light on resolving the existing argument by better understanding of near threshold fatigue crack growth behavior.

Forman, Royce G.↗
DOE OSTI2024

Application of C ( t )-Integral Solutions in Extending ASME BPVC Section XI Division 2 Code Case N-934 for Transient Creep Crack Growth

Creep crack growth is a phenomenon which arises in damaged metallic structures under combined primary and secondary loads in the creep regime. The High Temperature Flaw Evaluation Code Committee of the American Society of Mechanical Engineers Boiler and Pressure Vessel Code (BPVC) is evaluating methods in extending Code Case N-934 to capture transient creep crack growth. Here, this paper provides context and basic examples on the selected approach to transient creep crack growth methods based on the C(t)-integral. The basis for selected C(t)-integral solution as analytical method is established, including an overview of its derivation. Practical assessments of a crack growing under creep conditions in a realistic component are conducted to illustrate the analytical approach. Additional considerations in the application of the analytical methods and limitations are discussed.

36 MATERIALS SCIENCE↗
NASA NTRS1992

Program Analyzes Crack-Growth Data

Crack Growth Rate Data Analysis program used for cyclis crack-growth testing of compact tension specimens. Program digitizes data on crack-opening displacement vs. load and reduces these into data on crack-growth rate vs. stress-intensity excursion. Written in HP BASIC.

Demonet, Charles M.↗
NASA NTRS1997

Use of Marker Bands for Determination of Fatigue Crack Growth Rates and Crack Front Shapes in Pre-Corroded Coupons

Groups of striations called marker bands generated on a fatigue fracture surface can be used to mark the position of an advancing fatigue crack at known intervals. A technique has been developed that uses the distance between multiple sets of marker bands to obtain a vs. N, crack front shape, and fatigue crack growth rate data for small cracks. This technique is particularly usefull for specimens that require crack length measurements during testing that cannot be obtained because corrosion obscures the surface of the specimen. It is also useful for specimens with unusual or non-symmetric shapes where it is difficult to obtain accurate crack lengths using traditional methods such as compliance or electric potential difference in the early stages of testing.

Willard, S. A.↗