Li/Ag 2 VO 2 PO 4 batteries: the roles of composite electrode constituents on electrochemistry
In this study, we utilize silver vanadium phosphorous oxide, Ag 2 VO 2 PO 4 , as a model system to systematically study the impact of the constituents of a composite electrode, including polymeric and conductive additives, on electrochemistry. Notably, although highly resistive, this bimetallic cathode can be discharged as a pure electroactive material in the absence of a conductive additive as it generates an in situ conductive matrix via a reduction displacement reaction resulting in the formation of silver metal nanoparticles. Also, three different electrode compositions were investigated: Ag 2 VO 2 PO 4 only, Ag 2 VO 2 PO 4 4 with binder, and Ag 2 VO 2 PO 4 with binder and carbon. Constant current discharge, pulse testing and impedance spectroscopy measurements were used to characterize the electrochemical properties of the electrodes as a function of depth of discharge. In situ EDXRD was used to spatially resolve the discharge progression within the cathode by following the formation of Ag 0 . Ex situ XRD and EXAFS modeling were used to quantify the amount of Ag 0 formed. Results indicate that the metal center reduced (V 5+ or Ag + ) was highly dependent on composite composition (presence of PTFE, carbon), depth of discharge (Ag 0 nanoparticle formation), and spatial location within the cathode. The addition of a binder was found to increase cell polarization, and the percolation network provided by the carbon in the presence of PTFE was further increased with reduction and formation of Ag 0 . Lastly, this study provides insight into the factors controlling the electrochemistry of resistive active materials in composite electrodes.