DOE OSTI2025

Irradiation-induced formation of G-phase precipitates and M 2 X carbides in self-ion irradiated HT-9

Ferritic-martensitic steels with high chromium content are a promising material group for advanced nuclear systems due to their high temperature strength and good irradiation tolerance. HT-9 is an optimized and often-studied alloy in this group, but additional studies are required on its radiation response under extreme conditions to be experienced in various types of nuclear reactors, especially with respect to phase stability under irradiation. Self-ion irradiation of HT-9 by 5 MeV Fe ions was used to simulate neutron-induced behavior reaching peak doses of 100 and 300 dpa at temperatures ranging from 450 to 550 °C. M 23 C 6 carbides that existed prior to irradiation were found to remain stable under all examined irradiation conditions. As irradiation progressed at 450 and 500 °C, however, formation of spherical-like G-phase precipitates and needle-like M 2 X carbides was observed. G-phase precipitates were found to be enriched in Ni, Si, and Mn, and show no interface segregation, whereas needle-like M 2 X carbides were rich in Cr and Mo and clearly displayed interface segregation of Ni and Si. M 2 X carbide formation is believed to be assisted by vacancies, while G-phase precipitation is thought to be assisted by interstitials. Finally, this difference in defect-mediated formation leads to a difference in distribution with depth. M 2 X carbides are distributed over shallower depths than that of G-phase precipitates, consistent with defect imbalance predictions that consider the influence of the injected interstitial effect.

atom probe tomography↗
DOE OSTI2021

Evolution of {delta}ferrite in a CF3 cast stainless steel upon neutron irradiation to 3, 5, 10, 20, and 40 dpa

The microstructural evolution of delta ferrite in a CF3 cast stainless steel irradiated to 3, 5, 10, 20, and 40 dpa with two dose rates was studied with atom probe tomography (APT) and transmission electron mi-croscopy. Spinodal decomposition and G-phase precipitates induced by neutron irradiation and thermal aging were quantified systematically. The neutron irradiation significantly enhances the spinodal decom-position in delta ferrite as both the spinodal wavelength (i.e. a characteristic repeat distance) and am-plitude (i.e. magnitude of elemental concentration fluctuation) increase after irradiation. The wavelength only varies slightly when the dose increases from 5 to 40 dpa, while the amplitude increases dramatically from 10 to 20 dpa and starts to saturate before 20 dpa. The dose rate and irradiation temperature also have a notable effect on the spinodal wavelength and amplitude. The study shows that higher dose rate promotes a larger wavelength at given irradiation doses. Regarding the G-phase precipitates, a slightly lower irradiation temperature would result in a smaller mean size of G-phase precipitates, while a lower irradiation dose rate would lead to a larger G-phase precipitates at a given temperature and dose. Over-all, the spinodal decomposition and G-phase precipitates in the delta ferrite continue to evolve with the increasing dose beyond 10 dpa. This study confirms that the formation of G-phase precipitates at the in-terdomain region between alpha and alpha-prime is facilitated by the Si and Mo atoms rejected from Fe rich alpha phase and the Ni and Mn atoms rejected from Cr rich alpha-prime phase. Neutron irradiation plays a dominant role in the ferrite instability, and the effect of prior thermal aging at 400 degrees C for 10,000 hours is negligible as the dose is 3 dpa and above.

duplex stainless steel↗
DOE OSTI2021

Modified microstructures in proton irradiated dual phase 308L weldment filler material

In this study, the effect of proton irradiation on the microstructure of δ ferrite—γ austenite mixed phase 308L filler material in a 508–304 dissimilar metal weldment was investigated over a depth of 0 to 10 µm. Ni–Si–Mn G-phase precipitates were observed with SEM and TEM in δ ferrite but not in γ austenite. Our density functional theory based calculations show that the G/Fe interface energy in δ-Fe is significantly lower than that in γ-Fe (0.35 versus 1.25 J/m 2 ), which provides a thermodynamics-based explanation for our experimental observations of preferential formation of G-phase in δ ferrite. STEM-EDS, TEM dark field imaging, and diffraction patterns confirmed the Ni–Si–Mn enriched precipitates were G-phase precipitates with a stoichiometry of Mn 6 Ni 16 Si 7 . Intragranular voids and Ni–Si enriched clusters were observed in irradiated γ austenite. Additionally, Ni and Si segregation was observed along the void interfaces. In both cases, Ni–Si clusters and segregation to voids, selected area diffraction patterns did not reveal the existence of a second phase. Proton irradiation induced Cr depletion and Si and Ni enrichment at γ-γ austenite grain boundaries that was characterized with STEM/EDS.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Measurement of G-phase volume fraction and number density in duplex stainless steels using transmission electron microscopy

Duplex stainless steels (DSS) have a high toughness and strength due the presence of both austenitic and ferritic phases. These alloys have had limited use in power production applications due to thermal embrittlement caused by spinodal decomposition and development of G-phase precipitates in the ferrite. Lean grade DSS alloys (e.g., 2101, 2003) may offer improved thermal stability due to the reduction of Cr- and Ni-equivalent elements when compared to standard grade compositions (e.g., 2205, 2209). The abundance of the G-phase was measured in five duplex stainless steels, three wrought alloys (2101, 2003, 2205) and their matching filler metals (2101-w, 2209-w), after aging at 427 °C for 1000 h and 10,000 h. The G-phase volume fraction, number density, size, and precipitate spacing were found using quantitative analysis of transmission electron microscopy dark field images and the composition of G-phase precipitates on other clusters were characterized with atom probe tomography (APT). In the welded alloys, the G-phase was found to develop rapidly, relative to the wrought material. A positive correlation was found between the nickel equivalent composition of the alloy and the G-phase volume fraction. The alloys 2205, 2209, and 2101-w, which are higher in Cr and Ni, all showed significant G-phase precipitation, further strengthening the hypothesis that lean grade DSS alloys are more thermally stable against precipitation in the ferrite. Electron diffraction showed a secondary phase present in the 2101 wrought alloy at 10,000 h, but it was not crystallographically consistent with the G-phase; APT showed the presence of nanoclusters rich in both nickel and copper for this alloy. In conclusion, no secondary phases or clusters were found in 2003 after 10,000 h of aging, so it may be a candidate alloy for applications that require long-life times at high operating temperatures.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Irradiated Microstructure of Zorita Materials

Reactor baffle plate materials were harvested from the decommissioned Zorita nuclear power reactor after 38 years of service and were characterized with transmission electron microscope. The samples were Type 304 stainless steels and had been irradiated to 0.05, 16.9, ad 48.6 dpa. Faulted dislocation loops, voids, and irradiation-induced precipitates were observed in this material. While dislocation loops were the dominant irradiation defects for all samples, small voids and precipitates were also observed at 16.9 and 48.6 dpa, but not at 0.05 dpa. The size of dislocation loops increased with irradiation dose and saturated below 16.9 dpa. The loop density continued to increase between 16.9 and 48.6 dpa. For voids, both the density and mean size were small, and the volume swelling was negligibly small even at 48.6 dpa. In addition, carbides or G-phase precipitates were detected at 16.9 and 48.6 dpa, and a complex dose dependence was observed. A range of irradiation hardening was estimated at each dose, and the resulting yield strengths were consistent with the previous tensile results measured from the Halden and BOR-60 specimens.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2021

Evolution of the role of molybdenum in duplex stainless steels during thermal aging: From enhancing spinodal decomposition to forming heterogeneous precipitates

Thermal aging of ferrite in duplex stainless steels leads to a complex microstructural evolution that can give way to large deleterious changes in mechanical properties. The microstructural evolution mechanisms that happen concurrently are strongly linked to minor changes in composition. By characterizing duplex stainless steels with various compositions over a range of aging conditions, it was revealed that adding a modest amount of Mo to cast austenitic stainless steel (such as changing from grade CF3 to grade CF3M) not only increases the kinetics of spinodal decomposition and Ni-Si-Mn-rich G-phase precipitation, but it also forms a separate Mo-rich phase. At shorter equivalent aging times, Mo segregates from Fe and towards Cr accelerating spinodal decomposition. At longer aging times, Mo enriches in the Ni-Si-Mn clusters before phase separating into an adjoined Mo-rich cluster. We found that these phase changes and precipitation events result in a rather steep drop in fracture and impact toughness. These results will inform the design of similar alloys for use at high temperatures.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Void swelling of conventional and composition engineered HT9 alloys after high-dose self-ion irradiation

Ferritic/martensitic (F/M) steels are being considered as potential structural materials for next generation nuclear reactors, and variants of the alloy HT9 are some of the most promising candidates. In this study, two conventional and two composition engineered HT9 alloys were irradiated using 3.5 MeV Fe 2+ up to 600 peak displacement-per-atom (dpa) at 450 °C. Void swelling and microstructure evolution were characterized for each alloy and compared. The two conventional HT9 alloys (INL and ACO3) showed similar void swelling behavior due to their similar elemental composition and processing conditions. The INL HT9 exhibited a maximum of 2.4% swelling and the ACO3 HT9 showed a maximum of 2.8% swelling at 342 and 393 average local dpa, respectively. On the other hand, the two-composition engineered HT9 alloys with varying N contents (10 ppm for low N and 440 ppm for high N) showed disparate swelling behavior. The low N HT9 exhibited a maximum of 4.6% swelling, while the high N HT9 showed a maximum of 0.7% swelling at 342 average local dpa. Changes in the N content also affected Ni/Si rich G-phase formation. The low N HT9 showed a larger size and lower density of G-phase precipitates compared with the high N HT9 after 600 peak dpa irradiation. This study compares the void swelling behavior of the ion irradiated four current HT9 alloys to extremely high doses, with the void swelling data from neutron irradiated HT9 alloys. Furthermore, the comparison lends critical insights into how well these current alloys can withstand high neutron fluxes in future reactors, especially since the low N and high N HT9 alloys have never been exposed to such high doses before.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Phase instabilities in austenitic steels during particle bombardment at high and low dose rates

Disruption of phase stability by energetic particle bombardment is a major challenge in designing advanced radiation-tolerant alloys and ion beam processing of nanocomposites. Particularly, ballistic dissolution susceptibility of different solute nanocluster species in alloys is poorly understood. Here, low dose rate neutron irradiations were conducted on a Fe-Cr-Ni based austenitic steel in the BOR-60 reactor (9.4 × 10 -7 dpa/s, 318 °C) followed by accelerated dose rate ion irradiations at multiple temperatures ( 10 -3 dpa/s, 380 – 420 °C). Using atom probe tomography, the stability of radiation-enhanced Cu-rich and radiation-induced Ni-Si-Mn-rich nanoclusters was evaluated. During neutron irradiation, Cu-rich clusters nucleated with their core concentrations progressively increasing with dose, while Ni-Si-Mn-rich clusters formed and evolved into G-phase precipitates. Ion irradiations dramatically altered the nanoclusters. Cu-rich clusters were ballistically dissolved, but Ni-Si-Mn-rich clusters remained stable and coarsened with dose at 400 and 420 °C, highlighting that different nanocluster species in a single microstructure can have innately distinct ballistic dissolution susceptibilities. Solute-specific recoil rates were incorporated into the Heinig precipitate stability model, which shows that in addition to radiation-enhanced diffusion, recovery from ballistic dissolution depends on solute concentration gradient near cluster interfaces. Finally, the combined experimental-modeling study quantified the critical temperatures and damage rates where ballistic dissolution dominates for each cluster species.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Detecting Thermally Induced Spinodal Decomposition with Picosecond Ultrasonics in Cast Austenitic Stainless Steels

Given the existential climate crisis faced by mankind and the world, the lifetime and sustainability of nuclear reactors as a carbon-free source of renewable energy depend on the susceptibility of their structural components to environmental degradation. In particular, critical components for light water reactors (LWRs) evolve over decades in service, losing ductility and toughness due to thermal and irradiation aging. Techniques to monitor their health cannot be easily applied in the field due to their destructive, expensive, or immobile nature. Thus, non-destructive evaluation (NDE) methods are sought to monitor and evaluate the health of major LWR components such as core barrels, steam generator tubes, or primary coolant pipes and are often required by policy, such as NRC policy #10-CFR-50.65. In this work we demonstrate the use of gigahertz, non-contact ultrasonics to gauge the state of cast austenitic stainless steels (CASS), used in some of the largest components in LWR primary systems. We do so by linking changes in their surface acoustic wave (SAW) characteristics using transient grating spectroscopy (TGS) to transmission electron microscopy (TEM)-verified evidence of spinodal decomposition and G-phase precipitation. In this thesis, thermal aging is shown to induce SAW peak splitting in spinodally decomposed CASS alloys, correlated strongly with lowered toughness and decreased ductility. Furthermore, statistical testing on the number of SAW peak splits observed show that the second SAW peak significantly appears more frequently and is significantly different in frequency in comparison to counts and frequencies measured in unaged specimens. The ability of this technique to non-destructively detect microstructural degradation at a distance in a predictive manner in the case of CASS motivates extending gigahertz ultrasonics to detect other LWR material degradation modes as an in-vessel inspection technique, such as reactor pressure vessel (RPV) embrittlement. This allows for the greater use of NDE techniques for confident monitoring of LWR structural material health to 80 years and beyond, saving costs by minimizing structural replacements until needed and maximizing energy production by preventing early decommission until necessary.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Phase Transformation of Thermally Aged and Neutron Irradiated Duplex Stainless Steel Used in LWRs. Final report

The lifetime of reactor components made of duplex stainless steels can be limited by the embrittlement from thermal aging, neutron irradiation or a synergistic effect between thermal aging and neutron irradiation. There is still a large scientific knowledge gap in understanding the phase evolution in duplex stainless steels upon thermal aging with or without neutron irradiation, the synergistic effect between thermal aging and neutron irradiation, and the impacts of structural evolution on material mechanical responses. In this project, totally, five major tasks were completed through this project: a) the in-situ WAXS tensile tests of thermally aged cast duplex stainless steels, b) the EXAFS investigation of thermally aged cast austenitic stainless steel and welds of austenite sainless steel, c) the characterization of irradiation effect on neutron irradiated CASS using APT, d) characterize the ferrite hardening of neutron irradiated CASS using nanoindentation, and e) the FEM modelling to validate the in-situ WAXS tensile tests and to simulate the stress/strain distribution during deformation for thermally aged duplex stainless steel. In summary, the thermal aging without neutron irradiation can significantly increase the strength of ferrite phase through the spinodal decomposition and G-phase precipitations. The in-situ X-ray experiments show that the hardening effect in ferrite phase can significantly alter the load partition between the ferrite and austenite phases. Atom probe tomography characterizations on samples irradiated to 0.08, 3, 5, 10, 20, and 40 dpa shows that neutron irradiation has dominated the microstructural evolution after 3 dpa, and the spinodal decomposition has saturated yet even at 40 dpa based on the quantified wavelength and amplitude.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2020

Nitrogen effects on radiation response in 12Cr ferritic/martensitic alloys

Ferritic/martensitic steels are one of the best candidates for structural materials for high dose applications in next generation nuclear reactors. The composition of structural materials must be optimized for reliable service during irradiation. This study reports the effect of interstitial nitrogen on radiation response in 12Cr ferritic/martensitic HT9 steels having a controlled nitrogen concentration. Results show that a high amount of ‘free’ nitrogen in the matrix stabilizes the interstitial clusters which leads to (i) larger loop sizes (ii) lower loop density and (iii) slightly reduced radiation induced hardening. It also affects diffusion mechanism of Ni and formation of Ni/Si-rich precipitates.

36 MATERIALS SCIENCE↗