NASA NTRS2023

Effect of Loading Rate on the Open Hole Compression Strength of Quasi-Isotropic Carbon/Epoxy Laminates

This study was undertaken to examine how well the 0.05 inch/min loading rate typically used to develop allowables for open hole compression strength of carbon/epoxy laminates represents structures that may experience a much lower loading rate (such as civil engineering structures) or a much higher loading rate (such as a rocket interstage at liftoff). The Composite Materials Handbook-17 (CMH-17) suggests developing strength allowables at the coupon level (lowest level of the “building block” approach) and using a rigorous statistical analysis to arrive at a strength allowable upon which the structure is to be further designed at higher levels of the building block pyramid. But do these coupon level tests truly represent meaningful stresses at which the composite in the final structure can withstand considering the effects of loading rate? Open hole compression (OHC) strength was chosen for this study since most structures are designed to some damage tolerance criteria and OHC strength testing is rather simple to perform. A quasi-isotropic lay-up was chosen since this is a very common lay-up sequence. The results show that for structures that experience a very small loading rate (0.0005 in/min) the allowables developed at the standard 0.05 in/min loading rate are higher than what the composite can withstand at this lower loading rate. Conversely, at a high loading rate of 10 in/min the strength values found at the standard test rate of 0.05 in/min are slightly lower and not “in family” using the statistics suggested in CMH-17. These results question if standardized test rates are reliable, at least to the fidelity of being “in family” per CMH-17. Some creep rupture tests were also performed to demonstrate that OHC strength values could be lower than the slowest test speed used in this study (0.0005 in/min).

open hole compression strength↗
NASA NTRS1988

Loading rate sensitivity of open hole composites in compression

The results are reported of an experimental study on the compressive, time-dependent behavior of graphite fiber reinforced polymer composite laminates with open holes. The effect of loading rate on compressive strength was determined for six material systems ranging from brittle epoxies to thermoplastics at both 75 F and 220 F. Specimens were loaded to failure using different loading rates. The slope of the strength versus elapsed time-to-failure curve was used to rank the materials' loading rate sensitivity. All of the materials had greater strength at 75 F than at 220 F. All the materials showed loading rate effects in the form of reduced failure strength for longer elapsed-time-to-failure. Loading rate sensitivity was less at 220 F than the same material at 70 F. However, C12000/ULTEM and IM7/8551-7 were more sensitive to loading rate than the other materials at 220 F. AS4/APC2 laminates with 24, 32, and 48 plies and 1/16 and 1/4 inch diameter holes were tested. The sensitivity to loading rate was less for either increasing number of plies or larger hole size. The failure of the specimens made from brittle resins was accompanied by extensive delaminations while the failure of the roughened systems was predominantly by shear crippling. Fewer delamination failures were observed at the higher temperature.

Lubowinski, Steve J.↗
NASA NTRS1990

Loading rate sensitivity of open-hole composite specimens in compression

The results are reported of an experimental study on the compressive, time-dependent behavior of graphite fiber reinforced polymer composite laminates with open holes. The effect of loading rate on compressive strength was determined for six material systems ranging from brittle epoxies to thermoplastics at both 75 F and 220 F. Specimens were loaded to failure using different loading rates. The slope of the strength versus elapsed time-to-failure curve was used to rank the materials' loading rate sensitivity. All of the materials had greater strength at 75 F than at 220 F. All the materials showed loading rate effects in the form of reduced failure strength for longer elapsed-time-to-failure. Loading rate sensitivity was less at 220 F than the same material at 70 F. However, C12000/ULTEM and IM7/8551-7 were more sensitive to loading rate than the other materials at 220 F. AS4/APC2 laminates with 24, 32, and 48 plies and 1/16 and 1/4 inch diameter holes were tested. The sensitivity to loading rate was less for either increasing number of plies or larger hole size. The failure of the specimens made from brittle resins was accompanied by extensive delaminations while the failure of the roughened systems was predominantly by shear crippling. Fewer delamination failures were observed at the higher temperature.

Lubowinski, S. J.↗
NASA NTRS1986

Loading rate effect on interlaminar fracture toughness of a thermoplastic composite

A study was undertaken to investigate the loading rate effect on delamination fracture initiation toughness of a thermoplastic composite. For this purpose, double cantilever beam specimens of graphite/PEEK were tested in a displacement controlled mode using an Instron tensile test machine. Specimens were loaded at various crosshead speeds ranging from 0.05 cm/min to 100 cm/min. The interlaminar fracture toughness was found to decrease with increasing loading rate, and this decrease was more than one hundred percent over the five decades of loading rate employed.

Mall, S.↗
NASA NTRS2003

Effect of Elevated Temperature and Loading Rate on Delamination Fracture Toughness

The effects of temperature and loading rate on delamination growth were studied. The delamination fracture toughness of IM7/K3B was measured at 149 C, 177 C, and 204 C. At each temperature the tests were performed with a variety of loading rates so that the delamination initiated over the range of time from 0.5 sec to 24 hrs. The double cantilever beam (DCB) test was used to measure fracture toughness. The results showed that the delamination resistance is a complicated function of both time and temperature with the effect of temperature either increasing or decreasing the fracture toughness depending on the time scale. The results also showed that the fracture toughness changed by as much as a factor of three as the time scale changed over the five orders of magnitude tested.

Reeder, J. R.↗
NASA NTRS2021

On the Loading Rate Dependence of Environment-assisted Cracking in Sensitized AA5456-H116 Exposed to Marine Environments

The influence of the applied loading rate (dK/dt) on the environment-assisted cracking (EAC) behavior of sensitized AA5456-H116 in 0.6 M NaCl at applied potentials ranging from −800 to −900 mV_SCE is assessed via a rising-K testing framework. The applied potential strongly affects the dK/dt-dependence of EAC with results suggesting a minimal influence for potentials more positive than −830 mVSCE and a stronger dK/dt-dependence for potentials more negative than −830 mV_SCE. Crack growth rates measured using rising versus static K testing are compared, which demonstrates that rising K methods consistently yield conservative EAC metrics with increased efficiency.

Al-Mg↗
NASA NTRS1959

Investigation of the Maximum Spin-Up Coefficients of Friction Obtained During Tests of a Landing Gear Having a Static-Load Rating of 20,000 Pounds

An experimental investigation was made at the Langley landing loads track to obtain data on the maximum spin-up coefficients of friction developed by a landing gear having a static-load rating of 20,000 pounds. The forward speeds ranged from 0 to approximately 180 feet per second and the sinking speeds, from 2.7 feet per second to 9.4 feet per second. The results indicated the variation of the maximum spin-up coefficient of friction with forward speed and vertical load. Data obtained during this investigation are also compared with some results previously obtained for nonrolling tires to show the effect of forward speed.

Batterson, Sidney A.↗
NASA NTRS1989

Effects of loading rate and temperature on dynamic fracture of ceramic matrix composites

A hybrid experimental-numerical procedure was used to determine the dynamic fracture initiation toughnesses and the dynamic stress intensity factors of alumina, TiB2-particulate/SiC-matrix, and SiC(w)/Al2O3-matrix composites at room and elevated temperatures under static and impact loadings. The dynamic fracture initiation toughnesses at room and elevated temperatures were greater than the corresponding static fracture toughness. The crack velocity versus the dynamic stress intensity factor relations showed minor differences due to temperature changes but significant differences due to the change in loading rates.

Yang, K. H.↗
NASA NTRS1966

Tensile-strength apparatus applies high strain-rate loading with minimum shock

Tensile-strength testing apparatus employs a capillary bundle through which a noncompressible fluid is extruded and a quick-release valve system. This apparatus applies the test loads at relatively constant very high strain rates with minimal shock and vibration to the tensile specimen and apparatus.

Cotrill, H. E., Jr.↗
NASA NTRS2001

Effect of Load Rate on Ultimate Tensile Strength of Ceramic Matrix Composites at Elevated Temperatures

The strengths of three continuous fiber-reinforced ceramic composites, including SiC/CAS-II, SiC/MAS-5 and SiC/SiC, were determined as a function of test rate in air at 1100 to 1200 C. All three composite materials exhibited a strong dependency of strength on test rate, similar to the behavior observed in many advanced monolithic ceramics at elevated temperatures. The application of the preloading technique as well as the prediction of life from one loading configuration (constant stress-rate) to another (constant stress loading) suggested that the overall macroscopic failure mechanism of the composites would be the one governed by a power-law type of damage evolution/accumulation, analogous to slow crack growth commonly observed in advanced monolithic ceramics. It was further found that constant stress-rate testing could be used as an alternative to life prediction test methodology even for composite materials, at least for short range of lifetimes and when ultimate strength is used as the failure criterion.

Choi, Sung R.↗
NASA NTRS2001

Effect of Load Rate on Tensile Strength of Various CFCCs at Elevated Temperatures: An Approach to Life Prediction Testing

Strength of three continuous fiber-reinforced ceramic composites, including SiC/CAS-11, SiC/MAS-5 and SiC/SiC, was determined as a function of test rate in air at 1100 - 1200 C. All three composite materials exhibited a strong dependency of strength on test rate, similar to the behavior observed in many advanced monolithic ceramics at elevated temperatures. The application of the preloading technique as well as the prediction of life from one loading configuration (constant stress-rate) to another (constant stress loading) suggested that the overall macroscopic failure mechanism of the composites would be the one governed by a power-law tyw of damage evolution/accumulation, analogous to slow crack growth commonly observed in advanced monolithic ceramics. It was further found that constant stress-rate testing could be used as an alternative to life prediction test methodology even for the composite materials at least for the short range of lifetime.

Choi, Sung R.↗
NASA NTRS1986

Effect of loading rate on dynamic fracture of reaction bonded silicon nitride

Wedge-loaded, modified tapered double cantilever beam (WL-MTDCB) specimens under impact loading were used to determine the room temperature dynamic fracture response of reaction bonded silicon nitride (RBSN). The crack extension history, with the exception of the terminal phase, was similar to that obtained under static loading. Like its static counterpart, a distinct crack acceleration phase, which was not observed in dynamic fracture of steel and brittle polymers, was noted. Unlike its static counterpart, the crack continued to propagate at nearly its terminal velocity under a low dynamic stress intensity factor during the terminal phase of crack propagation. These and previously obtained results for glass and RBSN show that dynamic crack arrest under a positive dynamic stress intensity factor is unlikely in static and impact loaded structural ceramics.

Liaw, B. M.↗
NASA NTRS2020

An Improved Plastically Dilatant Unified Viscoplastic Constitutive Formulation for Multiscale Analysis of Polymer Matrix Composites Under High Strain Rate Loading

Polymer matrix composites are commonly used to fabricate energy-absorbing structures expected to experience impact loading. As such, a detailed understanding of the dynamic response of the constituent materials is necessary. Since the rate, temperature, and pressure dependence of carbon fiber reinforced polymer matrix composites are primarily manifestations of the rate, temperature, and pressure dependence of the polymer matrix, it is crucial that the constitutive behavior of the matrix be accurately characterized. In this work, an existing unified viscoplastic constitutive formulation is extended to ensure thermodynamic consistency and to more accurately account for the tension-compression asymmetry observed in the response of polymeric materials. A new plastic potential function is proposed, and elementary loading conditions are utilized to determine relations between model constants to ensure nonnegative plastic dissipation, a necessary thermodynamic requirement. Expressions for plastic Poisson’s ratios are derived and are bounded by enforcing nonnegative plastic dissipation. The model is calibrated against available experimental data from tests conducted over a range of strain rates, temperatures, and loading cases on a representative thermoset epoxy; good correlation between simulations and experimental data is obtained. Temperature rises due to the conversion of plastic work to heat are computed via the adiabatic heat energy equation. The viscoplastic polymer model is then used as a constitutive model in the generalized method of cells micromechanics theory to investigate the effects of matrix adiabatic heating on the high strain rate response of a unidirectional composite. The thermodynamic consistency of the model ensures plastic dissipation can only cause an increase in temperature. Simulation results indicate that significant thermal softening due to the conversion of plastic work to heat is observed in the composite for matrix dominated deformation modes.

Impact loading↗
NASA NTRS1987

Portable, Controlled-Load-Rate Tension Tester

Tensile-testing machine for ceramic and foam materials has selfcontained air supply with built-in airflow controller. New machine easily moved to point of use, and loads applied automatically at constant rate of increase, without fluctuations caused by manual control of supply pressure. Eliminates impact after failure of specimen so it does not damage itself. Potential applications of machine include tensile tests of large composite parts that contain localized defects and adhesion tests of virtually any bonded structure.

Jamieson, R. S.↗
NASA NTRS2018

Effect of Control Mode and Load Rate on Fracture Toughness of Brittle Ceramics

The effects of control mode and rate on the fracture toughness of ceramics were measured by using chevron-notched flexure specimen in accordance with ASTM C1421. The use of stroke control gave consistent results with about 2% variation in measured fracture toughness for a very wide range of rates (0.005 to 0.5 mm/min). Use of strain or CMOD control gave an approximately 5% variation over a very wide range of rates, with the measurements being a function of rate. However, the effect was eliminated by use of dry nitrogen, implying a stress corrosion effect rather than a stability effect. With the use of nitrogen for strain control, fracture toughness values were within about 1% over a wide range of rates (1 to 80 micro-epsilon/sec.). CMOD or strain control did allow stable crack extension well past maximum load, and thus is preferred for energy calculations. The effort is being used to confirm recommendations in ASTM International standard C1421 on fracture toughness measurement.

control mode↗
NASA NTRS2019

Progressive Damage and Failure Analysis of Bonded Composite Joints at High Energy Dynamic Impacts

Both wing and fuselage structures utilize bonded composite joints for structural efficiency in modern commercial and military aircraft. To ensure compliance with certification requirements mechanical fasteners are typically used as a failsafe mechanism for appropriate strength in the event of complete stiffener disbond. However, the use of fasteners decreases the structural efficiency of the structure by adding weight. This establishes the requirement to better exploit the efficiency of bonded structures and fully understand the failure behavior of adhesively bonded composite structures, particularly when subjected to elevated loading rates due to high energy dynamic impacts (HEDI). For this reason, the NASA Advanced Composite Consortium (ACC) HEDI team developed an experimentation and numerical modeling program for high rate loading of composite joints. In the present work, the response of adhesively bonded composite joints subjected to elevated loading rates is studied numerically and validated against experimental results. Due to dynamic considerations of experiments, the idea of wedge insert was extended to use with Split Hopkinson Pressure Bar (SHPB) testing techniques. Mode-I and Mode-II test configurations were simulated to evaluate the capability of two continuum damage material (CDM) models in LS-DYNA, namely MAT162 and MAT261. Three different levels of fidelity were considered to investigate the level of detail required to numerically predict the failure behavior and the results from high fidelity analysis are presented.

MAT261↗
NASA NTRS1994

Substorm recurrence during steady and variable solar wind driving: Evidence for a normal mode in the unloading dynamics of the magnetosphere

Farrugia et al (1993) have recently studied substorm activity driven by the passage of an interplanetary magnetic cloud during which the interplanetary magnetic field turned southward for approximately 18 hours. It was shown that both the epsilon and the VB(sub s) parameters varied slowly on the timescale of a substorm but changed considerably over the interval as a whole. The substorm occurrence rate did not reflect the variation in magnetospheric energy loading rate as measured by these parameters but, rather, remained roughly constant with a 50-min average period. Klimas et al. (1992) showed that the Faraday loop analog model of geomagnetic activity predicts this single unloading rate under various constant loading rates. However, various model parameters were adjusted to yield a 1-hour unloading period in agreement with the Bargatze et al. (1985) linear prediction filters and in approximate agreement with the Farrugia et al. (1993) results. It has since been found necessary to add a slow relaxation mechanism to the Faraday loop model to allow for its approach to a ground state during long periods of inactivity. It is proposed that the relaxation mechanism is provided by slow convection of magnetic flux out of the magnetotail to the dayside magnetosphere. In addition, a rudimentary representation of magnetotail-ionosphere coupling has been added to enable comparison of model output to measured AL. The present study is of the modified Faraday loop model response to solar wind input from the Bargatze et al. data set with comparison of its output to concurrent AL. This study has removed the degree of freedom in parameter choice that had earlier allowed adjustments toward the 1-hour unloading period and has, instead, yielded the 1-hour unloading period under various constant loading rates. It is demonstrated that the second peak of the bimodal Bargatze et al. linear prediction filters at approximately equal 1-hour lag and the approximately constant substorm recurrence rate observed by Farrugia et al. can be interpreted as both being due to the existence of a normal unloading recurrence period in the dynamics of the magnetosphere.

Klimas, A. J.↗