Chemical stability enhancement of lithium conducting solid electrolyte plates using sputtered LiPON thin film

Sputter deposition of LiPON films directly onto high Li+ conductivity solid electrolyte plates has been investigated as a means to minimize the reactivity of the plates to metallic Li. The LiPON films were shown to effectively passivate the plates in contact with metallic Li, in contrast to unpassivated plates that reacted immediately in contact with Li metal.

LiPON lithium metals electrolyte plates↗

Chemical Passivation of Li(exp +)-Conducting Solid Electrolytes

Plates of a solid electrolyte that exhibits high conductivity for positive lithium ions can now be passivated to prevent them from reacting with metallic lithium. Such passivation could enable the construction and operation of high-performance, long-life lithium-based rechargeable electrochemical cells containing metallic lithium anodes. The advantage of this approach, in comparison with a possible alternative approach utilizing lithium-ion graphitic anodes, is that metallic lithium anodes could afford significantly greater energy-storage densities. A major impediment to the development of such cells has been the fact that the available solid electrolytes having the requisite high Li(exp +)-ion conductivity are too highly chemically reactive with metallic lithium to be useful, while those solid electrolytes that do not react excessively with metallic lithium have conductivities too low to be useful. The present passivation method exploits the best features of both extremes of the solid-electrolyte spectrum. The basic idea is to coat a higher-conductivity, higher-reactivity solid electrolyte with a lower-conductivity, lower-reactivity solid electrolyte. One can then safely deposit metallic lithium in contact with the lower-reactivity solid electrolyte without incurring the undesired chemical reactions. The thickness of the lower-reactivity electrolyte must be great enough to afford the desired passivation but not so great as to contribute excessively to the electrical resistance of the cell. The feasibility of this method was demonstrated in experiments on plates of a commercial high-performance solid Li(exp +)- conducting electrolyte. Lithium phosphorous oxynitride (LiPON) was the solid electrolyte used for passivation. LiPON-coated solid-electrolyte plates were found to support electrochemical plating and stripping of Li metal. The electrical resistance contributed by the LiPON layers were found to be small relative to overall cell impedances.

West, William↗

MoO3 Cathodes for High-Temperature Lithium Thin-Film Cells

MoO3 has shown promise as a cathode material that can extend the upper limit of operating temperature of rechargeable lithium thin-film electrochemical cells. Cells of this type are undergoing development for use as energy sources in cellular telephones, wireless medical sensors, and other, similarly sized portable electronic products. The LiCoO2 and LiMn2O4 cathodes heretofore used in these cells exhibit outstanding cycle lives (of the order of hundreds of thousands of cycles) at room temperature, but operation at higher temperatures reduces their cycle lives substantially: for example, at a temperature of 150 C, cells containing LiCoO2 cathodes lose half their capacities in 100 charge/discharge cycles. The superiority of MoO3 as a cathode material was demonstrated in experiments on lithium thin-film cells fabricated on glass slides. Each cell included a layer of Ti (for adhesion to the glass slide), a patterned layer of Pt that served as a cathode current collector, a cathode layer of MoO3, a solid electrolyte layer of Li3.3 PO3.8 N0.22 ("LiPON"), and an anode layer of Li. All the layers were deposited by magnetron sputtering except for the Li layer, which was deposited by thermal evaporation. These cells, along with similar ones containing LiCoO2 cathodes, were subjected to several tests, including measurements of specific capacity in charge/discharge cycling at a temperature of 150 C. The results of these measurements, plotted in the figure, showed that whereas specific capacity of the cells containing LiCoO2 cathodes faded to about half its initial value after only 100 cycles, the specific capacity of the cells containing the MoO3 cathodes faded only slightly during the first few hundred cycles and thereafter not only recovered to its initial value but continued to increase up to at least 5,500 cycles.

West, William↗