DOE OSTI2024
The conceptual basis for this project is the convergence of advanced ultra-high temperature ceramic materials and additive manufacturing technologies to produce compact ceramic heat exchangers with complex internal flow path geometries. Task areas were broadly divided into materials and manufacturing development, heat exchanger design, component testing, and techno-economic analysis. Technical challenges included the design and commissioning of new test facilities, improving feature resolution and deposition rate of ceramic additive manufacturing techniques, establishing process-structure-property relationships in additively manufactured ultra-high temperature ceramics, and assessing high temperature materials compatibility in CO 2 environments. The primary candidate material evaluated in this work is a composite comprising zirconium diboride (ZrB2) with 30 vol. % silicon carbide (SiC) which was selected based on its desirable combination of high temperature mechanical properties, high thermal and electrical conductivities, and oxidation resistance. High solids loaded ZrB2-SiC pastes suitable for extrusion-based additive manufacturing were developed for the first time as part of this work. Materials compatibility studies indicate this material oxidizes in CO 2 to form a protective borosilicate scale which transforms to pure silica above 1000°C. Parts made by additive manufacturing displayed enlarged grain sizes produced by pressureless sintering as compared to hot-press sintering. Increases in microstructural coarseness have outsized effect on oxidation performance up to 1400°C due to incomplete oxidation of coarse large diameter SiC particles resulting in lower amounts of silica that apparently inhibit protective scale formation. Additive manufacturing as a forming technique did not appear to significantly affect thermal conductivity, hardness, or elastic modulus, though flexural strength was reduced by half or more as compared to traditionally hot-pressed materials. This effect was attributed to the presence of strength-limiting flaws (ca. 40 microns in size) originating from extrudate inhomogeneities that could potentially be eliminated with further process improvements. Attempts to attain economies of scale for production of multi-kilowatt scale heat exchangers by ceramic additive manufacturing proved difficult. Lack of automation and a modest extrusion rate while retaining fine feature resolution made the overall process labor intensive and limited experimental throughput. A number of full-scale components were taken through post-process heat treatments including drying, binder burnout, and sintering; however, none survived without significant flaws or cracks. Therefore, no operational data from a newly installed heat exchanger test loop were able to be obtained during the performance period. Continued research and development is recommended to improve economic feasibility of ceramic additive manufacturing by standardizing the use of advanced sensors, artificial intelligence, and automation tools to reduce associated labor costs and accelerate production rates. The materials and manufacturing techniques demonstrated in this work are likely to find applications in defense and energy applications.
32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗