SEARCH · Search NASA
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
Computed materials data using density functional theory calculations. These calculations determine the electronic structure of bulk materials by solving approximations to the Schrodinger equation. For more information, see https://materialsproject.org/docs/calculations
Zinc-based batteries have attracted extensive attention in recent years, due to high safety, high capacities, environmental friendliness, and low cost compared to lithium ion batteries. However, the zinc anode suffers primarily from dendrite formation as a mode of failure in the mildly acidic system. Herein, we report on electrochemically deposited zinc (ED Zn) and copper-zinc (brass) alloy anodes, which are critically compared with a standard commercial zinc foil. The film electrodes are of commercially relevant thicknesses (21 and 25µM). The electrodeposited zinc-based anodes exhibit low electrode polarization (~0.025V) and stable cycling performance in 50 cycle consecutive experiments from 0.26-10 mA cm-2 compared to commercial Zn foil. Coulombic efficiencies at 1 mA cm-2 were over 98% for the electrodeposited zinc-based materials and were maintained for over 100 cycles. Furthermore, full cells with an electrodeposited Zn/brass anode, EMD MnO2 cathode, in 1M ZnSO4 + 0.1M MnSO4 delivered capacities of 96.3, and 163 mAh g-1, respectively, at a 100 mA g-1 compared to 92.1 mAh g-1 for commercial Zn. The zinc-based anodes also show better rate capability, delivering full cell capacities of 35.9 and 47.5 mAh g-1 at high current of up to 3 A g-1. Lastly, the electrodeposited zinc-based anodes show enhanced capacity for up to 100 cycles at 100 mA g-1, making them viable anodes for commercial use.
Zinc-MnO2 based batteries have acquired attention for grid-level applications, due to impressive theoretical performance, cost effectiveness and intrinsic safety. However, there are still many challenges that remain elusive due to the complex and controversial mechanisms of operation that hinders commercialization. In this work, the detailed redox processes that occur at the cathode during Zn-MnO2 battery operation are elucidated. Using a blend of structural and electrochemical techniques, the redox pairs that occur during operation are mechanistically studied while also showcasing the true impact of the electrolyte additive (0.1 M MnSO4) in a 1 M ZnSO4 electrolyte. An electrochemical quartz-crystal microbalance (EQCM) has been leveraged to reveal the effect of zinc hydroxy sulfate salt (Zn4SO4(OH)6·nH2O) and zinc manganese oxide (ZnxMnyOz) dissolution/deposition, which are believed to be major components during discharge and charge conditions. . These results provide insight not currently available, allowing a holistic view of the electrochemical reaction mechanisms during battery operation.
Mats of free-standing manganese oxide (MnxOy) nanowires have been fabricated as experimental electrode materials for rechargeable electrochemical power cells and capacitors. Because they are free-standing, the wires in these mats are electrochemically accessible. The advantage of the mat-of-nanowires configuration, relative to other configurations of electrode materials, arises from the combination of narrowness and high areal number density of the wires. This combination offers both high surface areas for contact with electrolytes and short paths for diffusion of ions into and out of the electrodes, thereby making it possible to charge and discharge at rates higher than would otherwise be possible and, consequently, to achieve greater power densities. The nanowires are fabricated in an electrolytic process in which there is no need for an electrode binder material. Moreover, there is no need to incorporate an electrically conductive additive into the electrode material; the only electrically conductive material that must be added is a thin substrate contact film at the anchored ends of the nanowires. Hence, the mass fraction of active electrode material is close to 100 percent, as compared with about 85 percent in conventional electrodes made from a slurry of active electrode material, binder, and conductive additive pressed onto a metal foil. The locations and sizes of the nanowires are defined by holes in templates in the form of commercially available porous alumina membranes. In experiments to demonstrate the present process, alumina membranes of various pore sizes and degrees of porosity were used. First, a film of Au was sputtered onto one side of each membrane. The membranes were then attached, variously, to carbon tape or a gold substrate by use of silver or carbon paste. Once thus attached, the membranes were immersed in a plating solution comprising 0.01 M MnSO4 + 0.03 M (NH4)2SO4. The pH of the solution was kept constant at 8 by addition of H2SO4 or NH4OH as needed. Mn(x)O(y) nanowires were potentiostatically electrodeposited in the pores in the alumina templates. Depending on the anodic deposition potentials, Mn(x)O(y) was deposited in various oxidation states [divalent (Mn3O4), trivalent (Mn2O3), or tetravalent (MnO2)]. The Mn(x)O(y) wires were made free-standing (see figure) by dissolving the alumina templates, variously, in KOH or NaOH at a concentration of 20 volume percent.