Microstructural features underpinning the mechanical behavior of powder metallurgy Cr-based alloys
Refractory materials such as Cr-based alloys offer the potential of enhanced elevated temperature performance but have been limited by their poor formability. However, powder metallurgy has been shown to be a viable pathway to fabricate these alloys. Nanophase separation sintering (NPSS) in particular has been used in the literature to accelerate the densification of powder metallurgy Cr- and W-based alloys. Here, we explore microstructure evolution during NPSS in a binary Cr 85 Ni 15 alloy consolidated via (i) cold pressing & pressureless sintering and (ii) hot isostatic pressing followed by hot extrusion & hot upsetting, and the role of these different processing routes on resulting material properties. The alloy lacked room temperature tensile ductility regardless of consolidation process, with multi-length scale characterization, including scanning electron microscopy, transmission electron microscopy, atom probe tomography, X-ray diffraction, and uniaxial tensile testing, revealing that brittleness was due to intrinsically poor Cr grain boundary cohesion. Tensile testing conducted at 760 °C showed marked strength reduction for the extruded & upset (94 %) condition compared to the pressed & sintered (18 %). The formation of orthorhombic CrNi 2 intermetallics functioned as precipitate strengtheners and prevented elevated temperature softening in the pressed and sintered condition. The findings offer foundational insights into aiding the future development of Cr-based alloys.