Creating Brønsted acidity at the SiO 2 -Nb 2 O 5 interface
Catalytically active acid sites associated with the silica-niobia interface were probed with a series of overcoated SiO 2 on Nb 2 O 5 (SiO 2 /Nb 2 O 5 ) mixed oxide materials prepared by deposition of tetraethyl orthosilicate onto niobic acid (Nb 2 O 5 nH 2 O) or calcined niobia (Nb 2 O 5 ). NH 3 TPD and pyridine DRIFTS studies indicated that the speciation of acid sites in the materials evolved as a function of SiO 2 loading, impacting the quantity and stability of Brønsted sites. Catalyst activity was highly dependent on SiO 2 loading in the liquid phase hydroalkoxylation of dihydropyran with n-octanol. At SiO 2 surface densities corresponding to approximately 1 Si per 2 surface Nb, the activity of these catalysts passed through a maximum approximately 20 times higher than the activity of calcined Nb 2 O 5 . We found that apparent reaction barriers measured over the most active SiO 2 /Nb 2 O 5 catalysts were 10 kJ/mol lower than those measured over niobic acid, suggesting that the OH features unique to the SiO 2 -Nb 2 O 5 interface were slightly more reactive than those on niobic acid.