To improve the economics of commercial nuclear reactors, nuclear vendors and utilities are seeking approval for increased burnup usage of the existing nuclear fleet. This is especially critical for meeting the clean energy initiative by the United States Government, Department of Energy (DOE). However, one of the key challenges the nuclear industry faces in this regard is that the regions exposed to high burnup and low temperatures exhibit a fine-grained microstructure with large bubbles known as high-burnup structure (HBS) [1]. The formation of HBS has been correlated to the diminished performance of the reactor, as well as fuel fragmentation and pulverization during transient and accidental conditions [2]. Therefore, it is paramount to understand the mechanisms for HBS formation along with its impact on the properties and performance of nuclear fuels. While existing programs, such as Nuclear Energy Advanced Modeling and Simulation (NEAMS) and Advanced Fuel Campaign (AFC) are focusing on evaluating the performance impact of HBS, the physical mechanisms contributing to HBS formation are still not fully understood. In addition, having predictive capabilities and sound understanding of the microstructural evolution of nuclear fuel is essential for accelerated development, qualification, and deployment of new nuclear materials and novel reactor designs for advanced nuclear reactors. There is a lack of consensus among researchers regarding the mechanisms leading to such restructuring observed in HBS. Grain subdivision due to polygonization versus recrystallization, continuous versus discrete recrystallization occurring in tandem or conjunction, etc., have been proposed and debated. In general, it is hypothesized that defect accumulation and dislocation interaction within the grains cause the realignment of dislocations into grain boundaries, leading to the new subgrain formation, which over time transforms into new grains. However, due to the lack of transient data, the importance of fission rate, irradiation, thermal, and stress history of the fuel on the restructuring could not be assessed. In situ microstructural evolution under various irradiation conditions is desired to bridge this gap. Alternatively, phase-field-based models have been developed to capture HBS formation via discrete recrystallization utilizing the classical nucleation approach [3–5]. However, in these models, the grain nucleation criteria are often defined based on empirical relations for burnup and fission gas density leading to dislocation density change. A mechanistic approach to capture the dislocation interaction with the microstructural features leading to grain subdivision is lacking.
11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗