DOE OSTI2023

Pressureless sintering of dual-phase, high-entropy boride–carbide ceramics

Here, dual-phase, high-entropy boride–carbide ceramics were densified by pressureless sintering. Relative densities up to approximately 96% were obtained for ceramics containing about 30 vol% high-entropy boride and 70 vol% high-entropy carbide. Isostatic pressing at 200 MPa resulted in higher relative densities of both the green bodies and final ceramics compared to uniaxial pressing. The highest relative density of 96.3% was achieved for a ceramic that was isostatically pressed at 200 MPa and sintered at 2300°C for 2 h. Grain sizes of the resulting ceramics were approximately 2 µm. This is the first report of pressureless sintering of dual-phase, high-entropy boride–carbide ceramics.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Pressureless sintering of lithium hydride

Lithium Hydride is a material of growing importance for addressing technological challenges related to nuclear fusion, long-term human space travel, and thermal energy storage. Pressureless sintering provides a straightforward, scalable approach to produce dense LiH parts of all sizes and shapes. Pressed LiH green compacts were sintered at heating rates from 2.5 to 20 °C/min to 650 °C, yielding densities up to 96 ± 1.4 %, with densification initiating at 500 °C. Here, a validated master sintering curve was constructed with a sintering apparent activation energy of 135 kJ/mol. X-ray diffraction and simultaneous thermal analysis revealed Li 2 O formation from 300 – 550 °C and decomposition of LiH into Li metal at 550 °C, each reflected as deviations in the master sintering curve. Computed tomography after thermal treatment to 550 °C showed the formation of corrosion products, and after thermal treatment to 650 °C LiH reduction to Li most significantly at exposed surfaces.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Pressureless Sintering of Pre-Alloyed Nanostructured Bainitic Steel Powders

A recent study shows that powder metallurgy and pressureless sintering are a viable pathway to realize full-density bulk components of nanostructure bainitic steels. A scalable, pressureless supersolidus liquid phase sintering (SLPS) approach to process nanostructured bainitic steel is evaluated. Furthermore, to address the oxidation issues associated with the mechanical alloying of elemental powders, powder atomization is used to produce pre-alloyed nanostructured bainitic steel powders.

mechanical alloying↗
DOE OSTI2023

Synthesis, sintering, and grain growth kinetics of Hf 6 Ta 2 O 17

Here Aasystematic study of the solid-state synthesis, pressureless sintering, and grain growth kinetics of Hf 6 Ta 2 O 17 is presented. The ideal conditions for solids-state synthesis of Hf 6 Ta 2 O 17 powder with minimal particle necking was 1250 °C for 2 h in air. The resultant powder has an average particle size of 210 ± 70 nm. The combined synthesis and ball-milling procedure produces highly sinterable Hf 6 Ta 2 O 17 powder, achieving > 97 % of theoretical density after pressureless sintering at 1600 °C for 2 h in air. The grain growth mechanism was sensitive to processing conditions, appearing to be primarily driven by surface diffusion below 1600 °C and grain boundary diffusion above 1650 °C. The respective activation energies for grain growth were found to be Q S = 659 ± 79 kJ mol -1 and Q GB = 478 ± 63 kJ mol -1 .

36 MATERIALS SCIENCE↗
DOE OSTI2020

Tape casting and characterizations of MgO ceramics

Herein we report a high density MgO ceramic substrate produced by the tape casting technology. The tape casting formulation and process produced a uniform tape free of cracking. Y 2 O 3 and SiO 2 were used as the sintering aid for the pressureless sintering of the green tape. X-ray diffraction phase identification indicates that MgO is the main phase, while both Y 2 O 3 and SiO 2 sintering aids react with MgO to form MgY 4 Si 3 O 13 as the second phase. Liquid phase sintering occurs in the temperature range from 1030°C to ~1500°C, which is confirmed by the simultaneous Thermal Gravitation Analysis/ Differential Scanning Calorimeter (TGA/DSC) and the percent linear shrinkage and densification. A 96.5% theoretical density was achieved by presureless sintering at 1650°C for 2 hours, which was further increased to a fully dense structure using hotisostatic- pressing(HIP) at 1650°C and 207 MPa in argon. Scanning electron microscopy (SEM) and energy dispersive(EDS) spectroscopic analysis on the HIP’ed sample show that MgY 4 Si 3 O 13 is located at the MgO grain boundary and the sample has a fully dense structure. The refractive indices and extinction coefficient were measured on the HIP’ed sample along with thermal properties and dielectric properties. Thermal diffusivity and heat capacity were measured to calculate the thermal conductivity.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Compositional Exploration of Additively Manufactured Ultra-High-Temperature Ceramic Composites for Use in Concentrated Solar Power Plant Heat Exchangers

The DOE has research interest in new technologies for high temperature concentrated solar power plants. Our project this summer was to explore the use of additively manufactured ultra-high-temperature ceramics in a heat exchanger. The heat exchanger would transfer heat between a molten chloride salt and supercritical CO 2 . We selected 22 compositions to test and were able to mix 14 of these compositions. We sintered these compositions using pressureless sintering and direct current sintering. We also conducted high temperature TGA on some ceramic samples. We also performed preliminary binder jet additive manufacturing trials with tungsten carbide powder. Our work so far points towards one of our titanium diboride samples being promising, but much more research needs to be done.

14 SOLAR ENERGY↗
DOE OSTI2020

Microstructure evolution during binder jet additive manufacturing of H13 tool steel

H13 is one of the most used tool steels for both hot and cold work tooling applications. Binder jet additive manufacturing offers the potential to deposit complex tools at scale due to larger powder bed sizes and faster deposition rates. However, to date there is no published literature on the sintering of H13 to full densification. Here, we discuss the pressureless sintering of binder jet AM H13 steel to full densification via supersolidus liquid phase sintering (SLPS) while presenting appropriate process windows (1360 °C – 1380 °C) for densification without distortion. The process windows have been rationalized based on thermodynamic calculations of liquid volume fractions with temperature. We show that higher binder saturation results in higher carbon retention and subsequently early liquid formation that can initiate the sintering process at lower temperatures. We report abnormal grain growth during sintering and found that the solidification phase transformations play a critical role on microstructural evolution and must be considered to accurately model the kinetics of SLPS.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Predicting sintering window during supersolidus liquid phase sintering of steels using feedstock analysis and CALPHAD

Binder jet 3D printing results in carbon pickup from the binder at the inter-particle regions during binder burnout. The excess carbon lowers the solidus temperature of the green part locally during supersolidus liquid phase sintering (SLPS). Currently, thermodynamic calculations rely on the use of bulk powder compositions to predict the sintering window. This can overestimate the sintering temperature since the local increase in carbon on powder surfaces is not accounted for, that can locally lower the solidus temperature during SLPS. Here we show that using the inputs from feedstock and binder analysis, the excess carbon and hence the sintering window for the alloy can be predicted using CALPHAD. We present a case study on applying the proposed approach for pressureless sintering of binder jet additive manufactured (BJAM) of H13 steel via SLPS.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Microstructural features underpinning the mechanical behavior of powder metallurgy Cr-based alloys

Refractory materials such as Cr-based alloys offer the potential of enhanced elevated temperature performance but have been limited by their poor formability. However, powder metallurgy has been shown to be a viable pathway to fabricate these alloys. Nanophase separation sintering (NPSS) in particular has been used in the literature to accelerate the densification of powder metallurgy Cr- and W-based alloys. Here, we explore microstructure evolution during NPSS in a binary Cr 85 Ni 15 alloy consolidated via (i) cold pressing & pressureless sintering and (ii) hot isostatic pressing followed by hot extrusion & hot upsetting, and the role of these different processing routes on resulting material properties. The alloy lacked room temperature tensile ductility regardless of consolidation process, with multi-length scale characterization, including scanning electron microscopy, transmission electron microscopy, atom probe tomography, X-ray diffraction, and uniaxial tensile testing, revealing that brittleness was due to intrinsically poor Cr grain boundary cohesion. Tensile testing conducted at 760 °C showed marked strength reduction for the extruded & upset (94 %) condition compared to the pressed & sintered (18 %). The formation of orthorhombic CrNi 2 intermetallics functioned as precipitate strengtheners and prevented elevated temperature softening in the pressed and sintered condition. The findings offer foundational insights into aiding the future development of Cr-based alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Enhancing thermal conductivity of UO 2 with the addition of UB 2 via conventional sintering techniques

We report that uranium dioxide has been the primary fuel type used in light water reactors for more than 40 years and proven to be reliable and robust. However, the Fukushima-Daiichi nuclear accident has motivated new work evaluating fuels with characteristics promoting accident tolerance, including enhanced thermal conductivity. Recently, additives have been investigated to increase thermal conductivity, but research has been largely focused on non-fissile additions. This study investigated the use of fissile additives to not only increase the thermal conductivity but also increase the uranium loading. Uranium diboride was chosen as the additive for this study due to its promising corrosion behavior as well as its significantly higher thermal conductivity at 573 K (25 Wm -1 K -1 ) when compared to UO 2 (7 Wm -1 K -1 ). Uranium diboride powder was fabricated via the arc melting technique and a ball milling process prior to mixing with UO 2 in a 90/10 wt% UO 2 /UB 2 ratio. Green bodies were made using a uniaxial die and subjected to a traditional pressureless sintering technique at 2073 K in argon. Sintered samples were analyzed via laser flash analysis for thermal diffusivity and differential scanning calorimetry for specific heat capacity in order to calculate thermal conductivity. The samples displayed an increase of 36-55% in thermal conductivity between 323 K and 1273 K when compared to the benchmark samples (pure UO 2 ) as reported in open literature.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2020

Direct selective laser sintering of hexagonal barium titanate ceramics

Abstract A direct selective laser sintering (SLS) process was combined with a laser preheating procedure to decrease the temperature gradient and thermal stress, which was demonstrated as a promising approach for additive manufacturing of BaTiO 3 ceramics. The phase compositions in BaTiO 3 ceramics fabricated by SLS were investigated by X‐ray and neutron diffractions. The surface morphologies and cross‐section microstructures were characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). A dense hexagonal h‐BaTiO 3 layer was formed on the surface and extended to a depth of 500 μm, with a relative density higher than 97% and absence of pores or microcracks. SLS resulted in the formation of the high‐temperature phase, h‐BaTiO 3 , which was retained at room temperature possibly due to the high cooling rate. The grain boundaries of SLSed h‐BaTiO 3 ceramics consist of a Ti‐rich secondary phase. Compared with that of the pressureless sintered t‐BaTiO 3 ceramics, the Vickers hardness of SLSed h‐BaTiO 3 is 70% higher.

Zhang, Xiang↗
DOE OSTI2024

Processing and characterization of the homologous Zr x Ta 2 O 2x+5 series

In this study, Zr x Ta 2 O 2x+5 (ZTOx) was systematically studied to determine ideal solid-state synthesis and pressureless sintering conditions. For Zr 6 Ta 2 O 17 (ZTO6) and other compositions with values of x in ZTOx the optimal synthesis temperature of 1100 °C with 1 h dwell time was optimal. XRD phase analysis of the homologous series indicated that for ZTOx, x = 5, 6, 7, and 8 were within the phase stability field while x = 4 and x = 9 were outside the phase stability field. Unit cell lattice parameters changed anisotropically with Zr:Ta ratio with an overall <0.1% change in unit cell volume across the solid solution. Some Raman modes red shifted while others blue shifted, indicating competing tensile and compressive strains. Sintering of ZTOx required a progressively higher temperature as Zr-content increased despite the same starting powder grain sizes and synthesis temperature. Higher Vickers hardness for Zr-rich (12.7–12.8 GPa) than Ta-rich Zr x Ta 2 O 2x+5 (11.6–11.7 GPa) disappeared when accounting for different sintering temperatures. Indentation toughness was similar for all compositions (1.2–1.4 MPa m 1/2 ). Properties of Zr x Ta 2 O 2x+5 series indicate tunability of Zr:Ta composition ratio while maintaining the structure and room temperature mechanical properties comparable to Hf 6 Ta 2 O 17 and 8 mol% yttria stabilized zirconia ceramics.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Direct ink writing of boron carbide monoliths

Direct ink writing – an extrusion-based additive manufacturing process – followed by pressureless sintering was investigated to produce boron carbide monoliths. The effects of ceramic powder loading and Pluronic binder concentration on the rheology of boron carbide pastes were studied and linked to both processing behaviour and final outcome in terms of sintered density and hardness. The effects of printing parameters, in particular orifice diameter and printing speed, were also investigated. Reducing the size of the extrusion nozzle from 584 μm to 406 μm led to significantly better shape retention, lower surface roughness, as well as higher density and hardness. A 203 μm printing orifice was also trialled but was unsuccessful due to faster drying kinetics that occurred with smaller ceramic struts resulting in rapid warping and nozzle clogging. Carbon-black – 8 wt% relative to B 4 C – acted as an effective sintering aid to increase both density and hardness. After optimisation of feedstock and printing parameters, few-layer samples (3–5 layers) had a density as high as ~ 97 % TD and a hardness of ~ 30 GPa. On the other hand, 18-layer specimens had a sintered density of ~ 87 % TD, despite a fully dense microstructure, due to the formation of a 3D array of inter-strut pores. Nevertheless, several issues that arose during manufacturing and post-processing were detrimental to the density and structural integrity of printed specimens; these issues were identified, discussed, and suggestions for future work are provided in this report.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Resin chemistry and particle size influence on stereolithography with silicon carbide

Stereolithography (SLA) is an established process able to produce high resolution polymer parts with complex geometries. Silicon carbide (SiC) has uses in a variety of applications, but traditionally was difficult to manufacture into complex geometries. There have been advances in producing SiC through SLA using a SiC-derived ceramic such as silicon oxycarbide (SiOC). In this study, a slurry using a commercially available resin as the base material with additional modifiers was investigated to create a SiC slurry ready for pressureless sintering. The effects of photoinitiator, dispersant and a bimodal distribution of SiC particle sizes was studied using a design of experiments (DOE). A slurry with a bimodal distribution of 70 % coarse and 30 % fine SiC powder at 40 % solids loading by volume was prepared and successfully printed. Rheology measurements show the slurry to have viscoelastic shear thinning behavior below the recommended 1000 Pas necessary for printing. Printing parameters for the new material on a commercially available SLA printer were studied parametrically. The laser marking speeds found to print the slurry was 260 mm/s and 130 mm/s. A slurry and printing parameters were determined to produce a green part with a proposed debinding cycle.

Herd, Tien [ORNL]↗
DOE OSTI2024

UHT-CAMANCHE: Ultra-High Temperature Ceramic Additively Manufactured Compact Heat Exchangers

The conceptual basis for this project is the convergence of advanced ultra-high temperature ceramic materials and additive manufacturing technologies to produce compact ceramic heat exchangers with complex internal flow path geometries. Task areas were broadly divided into materials and manufacturing development, heat exchanger design, component testing, and techno-economic analysis. Technical challenges included the design and commissioning of new test facilities, improving feature resolution and deposition rate of ceramic additive manufacturing techniques, establishing process-structure-property relationships in additively manufactured ultra-high temperature ceramics, and assessing high temperature materials compatibility in CO 2 environments. The primary candidate material evaluated in this work is a composite comprising zirconium diboride (ZrB2) with 30 vol. % silicon carbide (SiC) which was selected based on its desirable combination of high temperature mechanical properties, high thermal and electrical conductivities, and oxidation resistance. High solids loaded ZrB2-SiC pastes suitable for extrusion-based additive manufacturing were developed for the first time as part of this work. Materials compatibility studies indicate this material oxidizes in CO 2 to form a protective borosilicate scale which transforms to pure silica above 1000°C. Parts made by additive manufacturing displayed enlarged grain sizes produced by pressureless sintering as compared to hot-press sintering. Increases in microstructural coarseness have outsized effect on oxidation performance up to 1400°C due to incomplete oxidation of coarse large diameter SiC particles resulting in lower amounts of silica that apparently inhibit protective scale formation. Additive manufacturing as a forming technique did not appear to significantly affect thermal conductivity, hardness, or elastic modulus, though flexural strength was reduced by half or more as compared to traditionally hot-pressed materials. This effect was attributed to the presence of strength-limiting flaws (ca. 40 microns in size) originating from extrudate inhomogeneities that could potentially be eliminated with further process improvements. Attempts to attain economies of scale for production of multi-kilowatt scale heat exchangers by ceramic additive manufacturing proved difficult. Lack of automation and a modest extrusion rate while retaining fine feature resolution made the overall process labor intensive and limited experimental throughput. A number of full-scale components were taken through post-process heat treatments including drying, binder burnout, and sintering; however, none survived without significant flaws or cracks. Therefore, no operational data from a newly installed heat exchanger test loop were able to be obtained during the performance period. Continued research and development is recommended to improve economic feasibility of ceramic additive manufacturing by standardizing the use of advanced sensors, artificial intelligence, and automation tools to reduce associated labor costs and accelerate production rates. The materials and manufacturing techniques demonstrated in this work are likely to find applications in defense and energy applications.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗
DOE OSTI2023

Fracture‐Resistant and Thermally Insulating Ultrahigh‐Temperature Carbide Foams

Dense ultrahigh‐temperature ceramics (UHTCs) carbides are recognized as potential materials for thermal protection systems (TPS) owing to properties beyond existing structural materials’ capabilities. Recent advances in UHTCs have enabled the development of multiscale porous microstructures. Herein, it is highlighted that the porosity in UHTCs are no longer treated as a defect but as a functional property specifically tailored for thermal insulation. It is a promising solution to design and fabricate bulk UHTC foams via a freeze‐drying (FD) approach followed by calibrated pressureless spark plasma sintering. Herein, monolithic TaC and HfC UHTC foams and their composite show the partial solid–solution formation of (Ta, Hf)C with porosity ≥50%. TaC–HfC foam (≈80–92 N) shows an intermediate load‐bearing capability compared to monolithic TaC (≈120–135 N) and HfC (≈28–35 N) foams, with no evident cracking on the sample surface. The thermal conductivity of partial solid‐solution TaC–HfC foam increases up to fivefold compared to parent UHTC foams. In the results, solid solutions’ efficacy and pores’ unidirectionality in providing thermal insulation to TaC–HfC while maintaining its high‐load bearing capability are illustrated. In conclusion, the developed technique establishes a new paradigm shift in UHTCs, expanding their potential for TPS in extreme environments.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Multi-scale characterization of supersolidus liquid phase sintered H13 tool steel manufactured via binder jet additive manufacturing

Additive manufacturing (AM) of H13 tool steel by binder jet 3D printing (BJ3DP) followed by pressureless supersolidus liquid phase sintering (SLPS) provides a low-cost alternative manufacturing method for components with intricate geometric features. However, the microstructure-mechanical property relationships for BJ3DP-SLPS produced H13 tool steel are not well understood, which makes it challenging to develop printing and post-processing methods that maximize part performance. In this work, we leverage atom probe tomography and transmission electron microscopy along with thermodynamic calculations to rationalize the microstructure-mechanical property relationships in as-sintered BJ3DP H13 tool steel. Here, we report for the first time, the presence of a continuous eutectic film-like carbide in H13 along with the more commonly observed cuboidal MX carbides in the prior liquid channels of the microstructure. Further, atom probe tomography revealed the interconnected nature of the MX carbides that appear to be discrete in two-dimensional micrographs. These continuous eutectic carbides and interconnected MX carbides result in brittle failure of the material. Characterization of these microstructural features will be critical in developing appropriate post-processing heat treatments for the improved mechanical performance of BJ3DP H13.

36 MATERIALS SCIENCE↗