Discovery of nanopore filling by gypsum in wellbore cement exposed to 17 MPa CO 2 under geologic carbon storage conditions
Here, this study investigates the pore structure evolution of the reaction zones in wellbore cement samples exposed to a CO 2 -rich solution in equilibrium with 17 MPa supercritical CO 2 over 14 days. Through advanced characterization methods of field emission SEM, Quantitative Evaluation of Minerals by Scanning Electron Microscopy (QEMSCAN), and micro-CT, a new mechanism of CO 2 -cement reaction involving filling of nanopores in the interior of cement by gypsum was revealed. Gypsum was formed by the liberation of SO 4 2− from ettringite (AFt) and monosulfate (AFm) caused by a decrease in pH. Based on these experimental observations, a new CO 2 -cement reaction model that incorporates four distinct reaction zones is developed. This model provides a comprehensive framework for understanding the spatial and temporal distribution of minerals in cement due to high pressure CO 2 —cement reactions. This study demonstrates that the major damage induced by high pressure CO 2 alteration occurs in the most exterior region of the cement. The interior region of the cement maintains its integrity due to nanopore filling by gypsum.