DOE OSTI2023

Origin of age softening in the refractory high-entropy alloys

Refractory high-entropy alloys (RHEAs) are emerging materials with potential for use under extreme conditions. As a newly developed material system, a comprehensive understanding of their long-term stability under potential service temperatures remains to be established. This study examined a titanium-vanadium-niobium-tantalum alloy, a promising RHEA known for its superior high-temperature strength and room-temperature ductility. Using a combination of advanced analytical microscopies, Calculation of Phase Diagrams (CALPHAD) software, and nanoindentation, we investigated the evolution of its microstructure and mechanical properties upon aging at 700°C. Trace interstitials such as oxygen and nitrogen, initially contributing to solid solution strengthening, promote phase segregation during thermal aging. As a result of the depletion of solute interstitials within the metal matrix, a progressive softening is observed in the alloy as a function of aging time. This study, therefore, underscores the need for a better control of impurities in future development and application of RHEAs.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Development and characterization of a low-density TiNbZrAlTa refractory high entropy alloy with enhanced compressive strength and plasticity

A new refractory high entropy alloy (RHEA) is designed by combining refractory elements Nb and Ta with Ti, Zr, and Al, resulting in a (TiNbZr) 89 (AlTa) 11 alloy composition with a low-density of 6.0 g/cm 3 . The novel RHEA features a BCC matrix with B2 and Zr 5 Al 3 nano precipitates, exhibiting a compressive yield strength of ~890 MPa and specific yield strength of ~148.3 MPa g -1 cm 3 . Remarkably, the alloy demonstrates excellent compressive plasticity of ~70% at 298 K. As the temperature increases to 873 K, 1073 K, and 1273 K, the yield strength of the RHEA gradually decreases to ~610 MPa, ~ 210 MPa, and ~ 60 MPa, respectively. These results indicate that this novel RHEA showcases a combination of good specific strength and plasticity. Post-compression, B2, and Zr 5 Al 3 phases are observed. In conclusion, the second-phase particles dispersed throughout the grains hinder dislocation motion and contribute to the formation of sub-grain boundaries during hot compression.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Refractory high entropy alloy compact heat exchanger

Several innovative technologies, including pressure-drop minimization, advanced refractory high entropy alloys, and advanced manufacturing can provide a compact heat exchanger that extends the state-of-the-art heat-exchanger operating range. The compact heat exchanger can reduce pressure drop losses by 100 to 500%, while retaining most of the heat transfer. The compact heat exchanger can be fabricated from refractory high entropy alloys that have favorable corrosion, thermal fatigue, and creep properties at high temperatures and pressures. Therefore, the compact heat exchanger using high entropy alloys can operate at >800° C. and 80 bars.

Kustas, Andrew↗
DOE OSTI2025

Bi‐Continuous W‐Rich Refractory High Entropy Alloy‐Cu Composite: Toward Material Innovation of Nuclear Reactor Coolant System

Abstract Refractory high‐entropy alloys (RHEAs) are considered promising candidate materials for next‐generation nuclear reactors due to their superior mechanical strength, irradiation resistance, and thermal stability at high temperatures. However, the significant positive heat of mixing between refractory alloying elements and Cu, commonly used in cooling systems, poses challenges in forming composite structures. This study addresses the issue using a liquid metal dealloying (LMD) process. A precursor alloy (WTaVTi) with a directional dendrite‐interdendrite structure is fabricated and reacted with molten Cu at 1200 °C for 96 h. This approach produced a RHEA‐Cu composite with a stable interface between RHEA (W 31.5 Ta 30.9 V 21.4 Ti 14.3 ) and Cu, featuring a spontaneously formed W‐rich interlayer that enhances interfacial bonding. The composite showed excellent irradiation resistance, with 30% less swelling under α‐ion irradiation than pure W. It also exhibited low thermal conductivity at room temperature, but reached ≈120 W m −1 ·K −1 at ≈650 °C, surpassing pure W. This temperature‐dependent rise in κ, with a positive gradient of +0.075 W m −1 ·K − 2 , is attributed to decreasing diffuse mismatch at elevated temperatures. The large‐scale reaction and stable microstructure achieved through LMD process highlight its industrial potential. This work offers a strategy for developing high‐performance materials by combining RHEA's radiation resistance with Cu's thermal conductivity for extreme environments.

Chemistry↗
DOE OSTI2024

Rapid Design of Cost-Effective Refractory High Entropy Alloys Strengthened by Precipitation

Funded by the ARPA-E ULTIMATE program, this project aims to develop cost-effective refractory high entropy alloys (RHEAs) for gas turbine blades applications at 1300 degree Celsius and above. The alloy design focuses on carbides precipitation strengthening in a strong and ductile solid solution BCC matrix. The goal is to achieve balanced mechanical properties including room temperature ductility & fracture toughness and high temperature strength and creep resistance, while maintaining comparable oxidation resistance and densities to Ni-base superalloys. To accelerate alloy design, multiscale modeling including CALPHAD and first-principles density functional theory (DFT) calculations and machine learning are performed. Specifically, high throughput phase diagram calculations and screening are carried out using CALPHAD; DFT calculations are performed to predict intrinsic ductility, grain boundary strengthening potential, coefficient of thermal expansion (CTE) and temperature-dependent elastic constants. Temperature dependent yield stress, creep strain and CTE are also predicted using machine learning. Down-selected alloys are synthesized in small buttons of about 250g using arc melting for rapid evaluation on microstructure and mechanical properties before employing plasma arc melting and additive manufacturing for producing large ingots. Preliminary computational and experimental results of this project will be presented and future direction in RHEA development will be discussed.

high temperature materials↗
DOE OSTI2025

Shear strength of a refractory high entropy alloy MoNbTaVW under high pressure

Radial X-ray diffraction (R-XRD) was performed in situ using a Panoramic Diamond Anvil Cell on the refractory high entropy alloy MoNbTaVW. The lattice parameters were determined through a Le Bail fit using a body centered cubic (BCC) lattice of symmetry $Im$$\overline{3}$$m$ (international space group number 229). Upper and lower bounds to the shear strength were determined up to 80 GPa nonhydrostatically using copper as a pressure standard. The equation of state was derived at the magic angle ψ = 54.7° and yielded a bulk modulus of K 0 = 220.8 ± 1.65 GPa. The experimental lattice parameters and bulk modulus match closely with corresponding density functional theory (DFT) calculations. The BCC phase remains stable up to the highest pressure of 80 GPa studied and is shown to be elastically anisotropic. The shear strength was found to saturate around 70 GPa with a value of τ = 1.75 GPa, and the shear moduli are presented in different limits of iso-strain and iso-stress.

36 MATERIALS SCIENCE↗
DOE OSTI2026

High-throughput oxidation screening and down-selection of refractory high entropy alloys in the Al-Cr-Mo-Nb-Ta-Ti system

Rapid experimentation and characterization are ever-present needs in the discovery of high entropy alloys. High entropy alloy systems are difficult to survey with systematic composition sweeps using traditional synthesis methods. The number of distinct compositions in even a four-element system is experimentally intractable. Exploration of these, and higher-element systems, necessitates thermodynamic prediction coupled with an automated sample creation method and a rapid screening methodology to effectively down-select alloys with targeted properties. As a result, a high-throughput method for evaluating the oxidation performance of refractory high entropy alloys was developed and tested. The six-element system of aluminum, chromium, molybdenum, niobium, tantalum, and titanium was evaluated for single phase stability and short-duration oxidation resistance. Target compositions were initially determined via thermodynamic predictions of single-phase stability across a wide temperature range. A twenty-five-sample build plate was produced using directed energy deposition additive manufacturing. After fabrication, the twenty-five 1 cm 3 samples were heat treated and characterized for composition and phase identification. The build plate was exposed to a high temperature oxidizing environment at 1000 °C for three hours. After oxidation, the composition, morphology, and chemistry of the oxides formed were characterized. Of the twenty-five samples produced, nine exhibited a favorable oxidation response, from which a single-phase BCC alloy at a composition of Al 13 Cr 7 Mo 19 Nb 18 Ta 26 Ti 17 was identified as the alloy with the most protective oxidation coating with a thin, adherent oxide scale. Finally, the complete experimental down-selection—from machine setup to final alloy identification—required approximately 45 labor hours, demonstrating a rapid validation for alloy discovery.

Additive manufacturing↗
DOE OSTI2024

Bayesian blacksmithing: discovering thermomechanical properties and deformation mechanisms in high-entropy refractory alloys

Finding alloys with specific design properties is challenging due to the large number of possible compositions and the complex interactions between elements. This study introduces a multi-objective Bayesian optimization approach guiding molecular dynamics simulations for discovering high-performance refractory alloys with both targeted intrinsic static thermomechanical properties and also deformation mechanisms occurring during dynamic loading. The objective functions are aiming for excellent thermomechanical stability via a high bulk modulus, a low thermal expansion, a high heat capacity, and for a resilient deformation mechanism maximizing the retention of the BCC phase after shock loading. Contrasting two optimization procedures, we show that the Pareto-optimal solutions are confined to a small performance space when the property objectives display a cooperative relationship. Conversely, the Pareto front is much broader in the performance space when these properties have antagonistic relationships. Density functional theory simulations validate these findings and unveil underlying atomic-bond changes driving property improvements.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Thermodynamic assessment of the quaternary WTaCrV refractory high entropy alloy as a means to guide experimental approaches

The deployment of fusion energy poses challenges for materials in plasma facing components to withstand high temperatures and thermal gradients, particle implantation and neutron damage. The current material of choice is tungsten, although property degradation limits its consideration in future fusion reactors. Hence, materials with better resistance to harsh environments need to be developed for fusion energy to become a reality. High entropy alloys are being explored as potential candidates with some compositions showing good radiation resistance to defect cluster formation. One of these materials is the WTaCrV system, although only one composition has been tested under ion irradiation. In this work, we study the thermodynamic properties of the entire quaternary alloy composition range. Coupling first principles calculations, cluster expansion approaches, and Monte Carlo methods, we access the free energy functionals, short-range ordering as a function of temperature, and atomic configurations that can be compared to experimental observations. We use this data to inform experiments into compositions with higher propensity to form solid solutions, instead of phase separating. With this formalism we have developed thermodynamic database (TDB) files that can be used to plot quaternary phase diagrams.

Cluster Expansion↗
DOE OSTI2023

The microstructure and He + ion irradiation behavior of novel low-activation W-Ta-Cr-V refractory high entropy alloy for nuclear applications

Microstructure and nanohardness of a nearly equimolar W-Ta-Cr-V high entropy alloy (HEA), as well as its irradiation response under He + irradiation, were investigated. The single-phase body-centered cubic nanostructured alloy with a 1 µm thick layer was fabricated on a silicon substrate using a magnetron sputtering method. The HEA film has a complex microstructure consisting of micrometric domains that exhibit internal nanostructure controlled by their crystal orientation. The measured nanohardness of the W-Ta-Cr-V alloy is 13 ± 2 GPa, which significantly exceeds the hardness of nanocrystalline tungsten as a result of the high solid-solution strengthening effect. In order to evaluate the irradiation resistance of the HEA film, the material was irradiated with 200 keV He + ions at room temperature, with two different ion fluences: 1 × 10 16 and 5 × 10 16 ions/cm 2 . Using transmission electron microscopy, a high density of extremely fine He bubbles is observed that were uniformly distributed in the matrix. The increase of He + ion fluence increased the density of bubbles, whereas their size remained at a similar level, which indicates that the damage proceeds by the nucleation of additional He bubbles, not by their growth.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Integrated design of aluminum-enriched high-entropy refractory B2 alloys with synergy of high strength and ductility

Refractory high-entropy alloys (RHEAs) are promising high-temperature structural materials. Their large compositional space poses great design challenges for phase control and high strength-ductility synergy. The present research pioneers using integrated high-throughput machine learning with Monte Carlo simulations supplemented by ab initio calculations to effectively navigate phase selection and mechanical property predictions, developing single-phase ordered B2 aluminum-enriched RHEAs (Al-RHEAs) demonstrating high strength and ductility. These Al-RHEAs achieve remarkable mechanical properties, including compressive yield strengths up to 1.7 gigapascals, fracture strains exceeding 50%, and notable high-temperature strength retention. They also demonstrate a tensile yield strength of 1.0 gigapascals with a ductility of 9%, albeit with B2 ordering. Furthermore, we identify valence electron count domains for alloy ductility and brittleness with the explanation from density functional theory and provide crucial insights into elemental influence on atomic ordering and mechanical performance. The work sets forth a strategic blueprint for high-throughput alloy design and reveals fundamental principles governing the mechanical properties of advanced structural alloys.

Science & Technology - Other Topics↗
DOE OSTI2026

Additively manufactured refractory high-entropy alloys with superior radiation resistance

Refractory high-entropy alloys (RHEAs) are promising candidates for next-generation nuclear and high-temperature applications. Among many approaches to manufacture RHEAs, additive manufacturing (AM) represents the most recent and advanced metal manufacturing method which allows near-net-shape manufacturing to reduce material waste and post-processing time. However, performance of AM RHEAs under complex irradiation conditions remains largely unexplored. Here, in this study, we demonstrate for the first time the response of directed energy deposition (DED) AM quaternary RHEAs (HfTaVW, CrTaVW) subjected to sequential dual-beam ion irradiation, consisting of helium pre-implantation followed by high-dose heavy ion bombardment. Compositions of DED AM RHEAs were selected using Monte Carlo (MC) simulations based on a cluster expansion (CE) Hamiltonian parameterized by density functional theory (DFT). Post-irradiation microstructural characterization revealed that the AM RHEA maintained remarkable stability, with suppressed helium bubble growth and reduced defect accumulation compared to conventional alloys. Even at high doses (∼100 dpa), the alloy exhibited no void swelling, a low density of dislocation loops, and no evidence of severe degradation. These results highlight the intrinsic ability of AM-derived microstructures and multicomponent chemistry to synergistically mitigate irradiation effects. Our findings establish AM RHEAs as a class of materials with superior resistance to radiation damage under conditions relevant to advanced fusion and fission environments and demonstrate the importance of sequential ion beam studies in evaluating their long-term performance.

36 MATERIALS SCIENCE↗