Residual Strains in an Additively Processed Ni-based Superalloy Transpiration-Cooled Aerodynamic Leading Edge Structure using Neutron Diffraction

Selective Laser Melting (SLM) is a well-known additive manufacturing method based on a layer-by-layer building process that is capable of fabricating gas turbine Ni-based superalloy parts with complex and integrated cooling geometries that are typically not achievable using conventional casting methods. However, the impact of residual stress concentration on SLM component life is a concern. In this work, residual strains present at room temperature in an SLM Inconel 718 generic aerodynamic leading edge segment with transpiration cooling were investigated using neutron diffraction at Oak Ridge National Laboratory. This study reveals that areas of the part where complex cooling holes were printed exhibit residual tensile strains that can be detrimental to its integrity. The study paves the way for future studies of the design of cooling hole geometries and manufacturing parameters that achieve improved cooling while minimizing stress concentration effects.

Fouliard, Quentin↗

Direct observations and characterization of crack closure during microstructurally small fatigue crack growth via in-situ high-energy X-ray characterization

This study provides direct observation of the crack closure mechanism of a naturally occurring, tortuous, 3D microstructurally small fatigue crack (SFC) in additively manufactured Inconel 718. In-situ non-destructive characterization is performed using high-energy X-ray diffraction techniques to capture the evolution of the 3D microstructure and micromechanical response in the vicinity of the crack front. Based on the stress state of twelve grains analyzed at the crack tip, the crack closure events of the SFC front was found to be spatially heterogeneous with respect to loading progression governed by the local stress state of the grains (specifically the stress reversal from compression to tension). From this analysis, three grains that displayed different degrees of crack closure were further investigated, based on the orientation of the crack relative to the grains and the associated modality of crack growth. The stress normal to the crack plane and the associated degree of Mode I crack behavior were correlated with events of the crack opening earlier during the loading cycle. This was further corroborated by diffraction spot spreading analysis that quantified the crystallographic lattice distortion caused by the opening crack. Additionally, the detailed characterization of the opening behavior of the grains located at the crack tip and their associated states of stress elucidates the mechanism governing crack closure and will inform future modeling efforts of this phenomenon.

36 MATERIALS SCIENCE↗