DOE OSTI2025

Characterization of Recrystallized Grains During Static Recrystallization of Hot-Compressed Mg–Zn–Ca Alloys Using In Situ Far-Field High-Energy Diffraction Microscopy

In this study, we explored the effect of Zn content on the static recrystallization of three 80 pct hot-compressed alloys, Mg–0.5Zn–0.1Ca wt pct (ZX050), Mg–1Zn–0.1Ca wt pct (ZX10), and Mg–3.2Zn–0.1Ca wt pct (ZX30), using far-field high-energy microscopy (ff-HEDM). Individual recrystallized grains were tracked and their 3D centroid, relative volume, and grain-averaged crystallographic orientation were measured during annealing. These measurements were used to compare the recrystallization kinetics and texture evolution of recrystallized grains in ZX alloys as a function of the Zn content. Fully recrystallized microstructures were observed for the ZX30 and the ZX10 alloys after annealing at 230 °C and 330 °C, respectively. In contrast, only a partially recrystallized microstructure for the ZX050 alloy was observed after > 1 hour of annealing at 430 °C. The resistance to recrystallization with decreasing Zn content was also confirmed by detecting faster growth rates of recrystallized grains in the ZX10 and ZX30 alloys, and slower growth rates in the ZX050 alloy. The significant recrystallization texture weakening of the ZX10 and ZX30 alloys and the development of a basal texture in the ZX05 alloy were described based on the orientation dependency of nucleation and growth of recrystallized grains. The analysis demonstrated that texture weakening was associated with increasing Zn content in Mg–Zn–Ca alloys.

Roumina, Reza [Univ. of Michigan, Ann Arbor, MI (U↗
DOE OSTI2024

Multiscale in-situ characterization of static recrystallization using dark-field X-ray microscopy and high-resolution X-ray diffraction

Abstract Dark-field X-ray microscopy (DFXM) is a high-resolution, X-ray-based diffraction microstructure imaging technique that uses an objective lens aligned with the diffracted beam to magnify a single Bragg reflection. DFXM can be used to spatially resolve local variations in elastic strain and orientation inside embedded crystals with high spatial (~ 60 nm) and angular (~ 0.001°) resolution. However, as with many high-resolution imaging techniques, there is a trade-off between resolution and field of view, and it is often desirable to enrich DFXM observations by combining it with a larger field-of-view technique. Here, we combine DFXM with high-resolution X-ray diffraction (HR-XRD) applied to an in-situ investigation of static recrystallization in an 80% hot-compressed Mg–3.2Zn–0.1Ca wt.% (ZX30) alloy. Using HR-XRD, we track the relative grain volume of > 8000 sub-surface grains during annealing in situ. Then, at several points during the annealing process, we “zoom in” to individual grains using DFXM. This combination of HR-XRD and DFXM enables multiscale characterization, used here to study why particular grains grow to consume a large volume fraction of the annealed microstructure. This technique pairing is particularly useful for small and/or highly deformed grains that are often difficult to resolve using more standard diffraction microstructure imaging techniques.

36 MATERIALS SCIENCE↗
DOE OSTI2023

An Integrated Simulation of Multiple-Pass U-10Mo Alloy Hot Rolling and Static Recrystallization

To achieve a desired microstructure and minimize the thickness variation in rolled foils, researchers must understand the effects of foil fabrication process variables on microstructure evolution. We developed an integrated simulation of deformation and recrystallization that employs the finite element method (FEM) and the kinetic Monte Carlo (KMC) Potts model, respectively, to investigate microstructure evolution during multiple-pass hot rolling and heat treatment in polycrystalline U-10Mo fuel. Scanning electron microscopy and electron backscatter diffraction images of microstructures were directly used as input in FEM calculation of deformation, and the calculated strains were used to determine the driving force of nucleation and growth of recrystallized grains in the Potts model. Grain structures predicted by the Potts model were used to update the grain structure and material properties for FEM. Simulation alternated between FEM and the Potts model to simulate grain structure evolution during multiple rolling and heat treatments. The initial model parameters were determined by benchmarking the recrystallization kinetics against experimental data. Then, the model was applied to predict the grain structure evolution. Results showed that our model can capture the coupling between deformation and recrystallization and can quantitatively reproduce the observed U-10Mo recrystallization and grain growth kinetics. The simulation results demonstrated that the developed model can predict U-10Mo grain structures as a function of initial microstructure and foil fabrication parameters.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Multimodal Analysis of Spatially Heterogeneous Microstructural Refinement and Softening Mechanisms in Three-Pass Friction Stir Processed Al4Si Alloy

Multiple thermally and thermomechanically induced microstructural refinement mechanisms can be activated in metallic alloys when subjected to solid phase processing methods such as friction stir processing (FSP). In this work, we provide detailed descriptions of the relationship between region-specific microstructural refinement mechanisms and the variation in microhardness, through a systematic and multimodal microstructural characterization of an FSP-processed 75% cold-rolled Al-4 at.% Si model binary alloy. Spatially resolved high-energy synchrotron X-ray diffraction, electron backscattered diffraction, and scanning transmission electron microscopy were used to understand the spatially heterogeneous microstructural evolution due to FSP. Results provide insights into how mechanisms such as static recovery, static recrystallization, dynamic recovery and recrystallization, geometric and continuous dynamic recrystallization, and particle-stimulated static or dynamic grain nucleation may occur heterogeneously in the microstructure as a function of the distance from the stir zone in processed alloys, directly influencing the degree of softening. The systematic analysis of microstructures and hardness in the FSP-processed model binary alloy given in this work highlights the rich microstructural domains that can be uniquely harnessed through solid phase processing of metallic alloys.

Al4Si, Friction Stir Processing, Geometric Dynamic↗
DOE OSTI2021

Prediction of softening kinetics and recrystallization texture in non-isothermally annealed bulged tubes using CPFEM and CA models

A hierarchically coupled cellular automata (CA) model, crystal plasticity finite element method (CPFEM), and thermal finite element (FE) model is developed to predict the softening kinetics of the bulged steel tube during non-isothermal annealing. Through the developed model, the kinetics of softening mechanisms including static recovery (SRV) and static recrystallization (SRX), as well as the recrystallization texture are predicted. Later, the Johnson-Mehl-Avrami-Kohnogorov (JMAK) model based on the predicted SRX data is developed to interpret the recrystallization behavior of the material. To perform this study, diverse experimental tests including tube hydroforming (THF), annealing, uniaxial tensile test, hardness test, as well as microstructure observations through optical microscopy and Electron Backscatter Diffraction (EBSD) tests on steel tube are performed. The obtained experimental data are utilized to calibrate and verify the implemented CPFEM model for simulation of THF process, thermal FE model for prediction of the local temperature over annealing time, and CA algorithm for modeling of the softening kinetics and texture evolution throughout the annealing process. The study shows that the predicted deformation characteristics, softening kinetics, recrystallization texture and temperature profile during non-isothermal annealing are in good agreement with experimental data. During the annealing process, a total of four stages for the kinetics of softening mechanisms is observed: No softening; SRV only; SRV dominant; and SRX dominant. During the progress of SRX, the behavior of recrystallization is abruptly changed, confirming that two different mechanisms are controlling the kinetics of transformation.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Coupling Thermomechanical Processing and Alloy Design to Improve Textures in Mg-Zn-Ca Sheet Alloys

Abstract The effect of Ca and Zn additions on the microstructure and texture evolution during thermomechanical processing of Mg-Zn-Ca sheet alloys was systematically investigated and quantified. Plane strain compression testing in a Gleeble thermomechanical simulator was used to physically simulate a 10-pass rolling schedule, while allowing for careful control and monitoring of the processing parameters. Textures in the as-deformed ternary alloy samples demonstrate a weak maximum basal intensity and spreading in the transverse direction. Increasing the Zn content to 3.2 wt.% in the ternary alloys resulted in samples that exhibited weak textures in the as-deformed state. Importantly, static recrystallization (SRX) during post-deformation annealing of these alloys promoted a desirable annular texture, with the c -axis tipped from the normal direction and a lower basal texture intensity. The evolution in texture during SRX is associated with as-deformed microstructures with broad grain orientation spreads and a low degree of recrystallization.

36 MATERIALS SCIENCE↗
DOE OSTI2024

The 650 °C Tensile Deformation of Graded IN718-René41 Superalloy Fabricated by Laser Blown-Powder Directed Energy Deposition

The microstructure and 650 °C tensile properties of a compositionally graded IN718-René41 (718-R41) superalloy fabricated by laser blown-powder directed energy deposition (DED-LB/M) are investigated to understand structure–property relationships and baseline tensile properties. Digital Image Correlation (DIC), in situ neutron diffraction, and conventional characterization techniques are performed to study the as-built and heat-treated states. The applied heat treatment generates static recrystallization and equiaxed grains in 718-rich compositions, while R41-rich compositions remain partially or un-recrystallized possibly influenced by a higher MC carbide fraction (>0.5%). The yield strengths of the 718 and R41 sections in the heat-treated state are comparable to wrought forms but the graded compositions show weakness due to unoptimized heat treatment. Diffraction elastic constants first decrease and then increase along the 718-R41 composition gradient, while a small difference is observed between the as-built and heat-treated states and γ, γ′ phases. Overall, the compositionally graded region shows a smooth transition in the elastic properties. Grain-level load transfer from the (220) to (200) grains shows compositional dependence, and qualitatively agrees with DIC-measured macroscopic yield strength. Within the (200) grains, the γ/γ′ phases deform elastically until the γ phase yields and afterwards, the γ′ phase takes load from the γ phase.

Huang, Shenyan (ORCID:0000000196528114)↗
DOE OSTI2024

Tensile Deformation of DED Graded IN718-René41 Superalloy at 650°C by in-situ Neutron Diffraction and Digital Image Correlation

A compositionally graded material comprised IN718 (718, γ'/γ" strengthened superalloy) and René41 (R41, a medium γ' strengthened superalloy) was fabricated using laser blown-powder directed energy deposition (DED/LB-M). Hot gas path components that require high and low temperature capabilities at different locations may benefit from such graded superalloy, potentially eliminating the use of welded or mechanically joined components and reducing cost. In the present work, microstructure and 650°C tensile behavior of 718-R41 graded superalloy in as-built and heat-treated states are investigated by Digital Image Correlation (DIC), in-situ neutron diffraction, coupled with conventional characterization techniques. The applied heat treatment generates static recrystallization and equiaxed grains in 718 rich compositions, while R41 rich compositions remain partially or un-recrystallized. Yield strengths of 718 and R41 sections in heat-treated state are comparable to wrought forms but the graded compositions show weakness. From neutron experiment, diffraction elastic constants and single crystal elastic constants are calculated, which show small difference between the as-built and heat-treated states and between the γ and γ' phases. Grain-level load transfer from the (220) grains to (200) grains is found to be composition dependent, and qualitatively agrees with DIC measured macroscopic yield strength. Within the (200) grains, the γ/γ' phases deform elastically until the γ phase yields and afterwards the γ' phase takes load from γ phase.

digital image correlation↗
DOE OSTI2021

Measuring residual stress in Ti-6Al-4V with HR-EBSD, using reference patterns from annealed material

In this study, elastic strain and residual stress values in an engineering material were determined by high-resolution EBSD (HR-EBSD) using reference patterns from annealed, recrystallized material. Specifically, rolled Ti-6Al-4V sheet was analyzed using HR EBSD in both an as-annealed and a strained state, the latter established via a static two-point bend fixture. The commercial software CrossCourt4 (CC4) was used to evaluate the relative intragranular strain tensor components of the alpha grains mapped by HR-EBSD. The intragranular reference patterns identified in each grain by the software were then replaced with similarly-oriented patterns from scans of the as-annealed, recrystallized material. The CC4 analysis was then repeated to provide calibrated strain and residual stress values. Elastic strains on the order of 10–3 were detected, with corresponding residual stress values on the order of 1 GPa. Subsequent analyses using high energy synchrotron x-ray diffraction showed good correlation with the elastic strains measured by HR-EBSD using the annealed reference patterns. Additionally, the maximum macroscopic stress analytically predicted for two-point bending was in agreement with the residual stress observed. Good repeatability of the methodology and insight into the state of individual grains were also observed. The findings provide encouraging evidence that accurate intragranular and long-range residual stress measurements of engineering significance can be made with HR-EBSD using a physical reference pattern library.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Creep Deformation and Dynamic Grain Growth in an Interstitial-Free Steel

Dynamic grain growth is demonstrated to be much faster than static grain growth in a body-centered-cubic, interstitial-free steel sheet material at 850°C. Dynamic grain growth occurs during concurrent plastic deformation at elevated temperature, whereas static grain growth occurs during static annealing. Grain growth during steady-state plastic flow in tension at 850°C to a true strain of 0.2 at a true-strain rate of 10 -4 s -1 doubled grain size, while static annealing for the same time produced no increase in grain size. This is described as dynamic normal grain growth (DNGG) because no abnormally large grains were observed. The recrystallized microstructure of the steel demonstrated a log-normal distribution of grain sizes. DNGG produced bimodal grain size distributions that deviate from the theoretical expectation of a simple shift to larger sizes during normal growth. The bimodal distributions contained a remnant of small grains that were not consumed during grain growth. DNGG produced a crystallographic texture that is unique from both the recrystallized material and that produced by lattice rotation alone. DNGG strengthened the {111}⟨110⟩ and {111}⟨112⟩ components of the strong γ-fiber component in the original recrystallization texture. Lattice rotation from tensile deformation, by contrast, strengthened the α-fiber components that intersect the original γ-fiber.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Solute effects upon dislocation motion and recovery in Mg alloys (Final Report)

The objective the research was to develop a firmer understanding of the interactions between substitutional solute atoms and dislocations within Mg alloys. These interactions govern the absolute and relative mobilities of various types of dislocations in Mg (e.g., basal < a>, non-basal < a>, and pyramidal < c+a>). Furthermore, they have an impact on dislocation recovery processes (e.g., cross-glide, climb, rearrangement, and annihilation). Ultimately, solute-dislocation interactions strongly impact a) strain hardening, b) strain rate sensitivity, c) plastic anisotropy of textured polycrystals, d) texture evolution, e) dislocation substructures evolution, and even f) recrystallization behavior. It is broadly known that Mg alloys exhibit poor low temperature formability. Since formability is largely governed by properties (a) – (c) in this list, it is critical to develop a better understanding of solute-dislocation interactions, if one hopes to improve the situation. While the theory of static solute strengthening is well developed, especially for alloys with face centered cubic (FCC) crystal structures, there are outstanding questions related to applications to hexagonal close packed (HCP) crystal structures and dynamic strain aging (DSA) in materials of various structures. DSA has far-reaching implications for metal formability and, in the case of Mg alloys, appears to correlate with the so-called rare-earth (RE) texture which has been shown to benefit formability. The Portevin-Le Chatelier (PLC) effect, and associated negative strain rate sensitivity, occur at higher temperatures (>100℃) in Mg alloys as compared with similar Al alloys, even though they have similar melting points and solute diffusivities. Our preliminary research has shown that modern, physics-based models of DSA can be tuned to describe the behavior of Mg alloys if a rather higher activation enthalpy is assumed for cross-core diffusivity. While this partially explains the delay in DSA to higher temperatures, it is also hypothesized that this delay is due in part to the intrinsically more thermally activated (rate sensitive) nature of non-basal < a> dislocation motion which is required for macroscopic flow of Mg alloys, whereas octahedral slip in many FCC metals like aluminum is essentially athermal at room temperature. It was originally proposed to employ a combination of in-situ diffraction-based experimental characterization to validate existing theory. It was envisioned to perform in-situ transmission electron microscopy (TEM) to assess individual dislocation behavior and in-situ high-energy X-ray diffraction (HEXRD) techniques which were showing great promise for elucidating collective dislocation behavior, 2 including recovery, especially if the contributions to various forms of diffraction peak broadening (𝜂𝜂,𝜔𝜔,and 2𝜃𝜃) can be effectively integrated. Finally, it was envisioned to perform discrete dislocation dynamics (DDD) modeling approaches to aide in the interpretation of both TEM and HEXRD experiments. In the end, mechanical tests were performed on more complex Mg alloys which exhibited evidence of dynamic strain aging, and this led to the establishment of another project. Mechanical test data obtained at McMaster University served as the basis of an assessment of the applicability of Bazinski’s “stress equivalence” theory of solute strengthening to polycrystalline alloys of Mg. Although we did not succeed in applying the approach to Mg alloys, we did develop expertise with the HEXRD approach using a BCC, β-Ti alloy and demonstrated numerous new capabilities that may be applied to any polycrystalline material in collaboration with researchers at CHESS and around the world: (1) assessment of details of the elastoplastic transition (yielding) using a combination of HEXRD and full-field polycrystal plasticity modeling, (2) the first-ever experimental observation of strong stress rotation within the individual grains of a polycrystalline material, and (3) a comprehensive analysis of the grain-level dislocation density evolution based upon diffraction peak broadening along 𝜂𝜂,𝜔𝜔,and 2𝜃𝜃 directions. This final aspect allowed us to confirm that dislocations were gliding on multiple plane types and not restricted to {110} type planes, and it also provided clues as to why some grains were unloading during straining, with surprising implications for our understanding of the effects of geometrically necessary dislocations (GNDs). Finally, graduate student, Mohammed Shabana, developed a MATLAB code which confirmed the conclusions of Prof. Catalin Picu (Rensallear Polytechnic Institute, RPI) regarding the effect of solute-trapped, forest dislocations on the breaking stress of Lomer lock junctions in FCC metal alloys. He applied the same anisotropic line-tension model to a variety of dislocation junction configurations and found an inconsistency in the widely cited results of Dupuy and Fivel regarding the Hirth Lock, and he outlined an approach to extend these finding to HCP Mg alloys that we are still pursuing with discretionary fundings at UVA.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Quasi-static and dynamic response of a Cu/Nb composite following equal channel angular extrusion

The article presents a study of the plastic properties of a Cu–18%Nb composite following equal channel angular extrusion under both low- and high-strain rate loadings. The microstructures are characterized by optical and scanning electron microscopy as well as electron backscatter diffraction. Comparisons are also made with a Cu–50%Nb laminate made by accumulative roll bonding. Textures obtained within the respective phases in the extruded composite closely mimic those previously reported for the pure components alone (Cu, Nb). Grain sizes of the major phase (Cu) exhibit broad distributions, due largely to partial recrystallization during the extrusion process. Further re-crystallization is obtained within localized deformation bands produced at high strain rates (3 × 10 3 s –1 ). While the degree of anisotropy and the strain rate sensitivity of the composite response are similar to those of pure Cu after extrusion, the strength levels of the composite are somewhat greater, falling broadly between those obtained in the pure components after extrusion to comparable plastic strains. Furthermore, the implications for selection of composite composition and processing for achieving higher strengths are briefly discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Understanding Microstructural Effects on Dynamic Performance Towards the Development of Shock Metamaterials

With the recent advances in additive manufacturing (AM), long-range periodic lattice assemblies are being developed for vibration and shock mitigation components in aerospace and military applications with unique geometric and topological structures. There has been extensive work in understanding the static properties associated with varying topology of these lattice architectures, but there is almost no understanding of microstructural affects in such structures under high-strain rate dynamic loading conditions. Here we report the shock behavior of lattices with varying intrinsic grain structures achieved by post process annealing. High resolution 316L stainless steel lattices were 3D printed by a laser-powder bed fusion machine and characterized by computed tomography. Subsequent annealing resulted in stress-relieved and recrystallized lattices. Overall the lattices had strong cubic texture aligning with the x-, y- and z-directions of the build with a preference outside the build direction (z). The recrystallized sample had more equiaxed polygonal grains and a layer of BCC ferrite at the surface of the structure approximately 1 grain thick. Upon dynamic compression the as-deposited lattice showed steady compaction behavior while the heat-treated lattices exhibit negative velocity behavior indicative of failure. We attribute this to the stiffer BCC ferrite in the annealed lattices becoming damaged and fragmenting during compression.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Development of Corrosion Resistant Coatings for Structural Materials for Liquid Fueled Molten Salts Reactors Applications (Final Report)

Current structural alloys, code certified for the MSRs temperature ranges, contain high levels of chromium, making them highly susceptible to molten halide salt corrosion. One potential solution to circumvent the need for code certification of novel alloys, which is expensive and time consuming, is to design claddings that will protect the underlying code certified materials from corrosion damage during operation. In this work, we examined the corrosion of Ni and Cu electroplated, Ni and CuNi weld overlay, Mo-laser clad, and carburized claddings on SS316H for use in molten salt reactor environments. After characterization of the cladded materials (Task 1), static corrosion tests were used to assess corrosion resistance of the claddings in typical molten fluoride salts (Task 2). The corrosion tests were performed in molten FLiNaK at 700°C up to 1000 hours. Pre- and post-corrosion Scanning Electron Microscopy (SEM), energy-dispersive-spectroscopy (EDS), Transmission Electron Microscopy (TEM), X-ray Diffraction (XRD) and glow-discharge-optical-emission-spectroscopy (GDOES) were performed on cladding cross-sections and surfaces to evaluate degradation. The Cu and Ni electroplated samples, as well as the carburized samples, showed excellent corrosion resistance relative to the bare SS316H. To assess high temperature cladding stability, ageing experiments were performed at temperatures up to 900 C in inert atmosphere for the electroplated and carburized samples and a diffusion model was developed to predict long term cladding behavior (Task 3). It was found that the Cu cladding was basically insensitive to the high temperature ageing, except for small secondary phases forming at the interface. On the other hand, the Ni electroplated cladding experienced significant interdiffusion. Nevertheless, the gain in corrosion resistance for a 100μm Ni electroplated cladding is phenomenal, with more than 50% reduction in chromium dissolution from the substrate material for the first 15 years of salt exposure at 700°C. To assess radiation resistance and phase stability, high-temperature 4MeV Ni heavy ion irradiation was performed across the cladding/substrate interface up to 50 displacement-per-atom (DPA) at 500°C and 700°C to assess the phase stability and irradiation behaviors of the electroplated systems (Task 4). The Ni and Cu electroplated systems did not experience void swelling at the contrary to the SS316H substrate due to their nanocrystalline nature. Some level of recrystallization was observed in the cladding, as well as radiation induced segregation and enhanced diffusion. The interface acted as a potent sink for point defects with the presence of a void denuded zone. The mechanical properties of the claddings were assessed using thermal shock, micro-indentation, nano-indentation, and four-point bend testing experiments (Task 5). These experiments were performed on the claddings in as-received, corroded, irradiated, and thermally aged states to determine the effects of typical molten salt reactor environments on cladding integrity. No significant mass loss was observed after repeated thermal shocks. While the electroplated samples softened after high-temperature ageing, irradiation hardening compensate this effect, such that there is little different with the as-received materials. The results of these experiments suggest that the electroplated (copper/nickel) show the greatest promise for application in molten salt reactor development. These claddings prevented any chromium dissolution from occurring during the static corrosion experiments. Additionally, they demonstrated favorable properties for high temperature diffusion, phase stability, interfacial mechanical properties, and irradiation resistance. Weld-overlay cladding are also of great interest and could reach properties similar to the electroplated samples upon optimization (especially with multiple weld passes). The carburized SS316H showed excellent behavior as well, but more work needs to be done to assess their long-term stability. Finally, the Mo-laser clad system was not pursued further due to the manufacturing challenges. It is also worth noting that the Ni cladding systems should behave relatively well in terms of weldability since the Ni-weld overlay microstructure and associated corrosion rate are sound. While the NiCu weld-overlay has even lower corrosion rates than the Ni-weld overlay, more studies on welding of Cu-electroplated systems are necessary since Cu clusters are known to embrittle steels.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Unraveling the Crystallization Kinetics of 2D Perovskites with Sandwich-Type Structure for High-Performance Photovoltaics

2D perovskite solar cells with high stability and high efficiency have attracted significant attention. A systematical static and dynamic structure investigation is carried out to show the details of 2D morphology evolution. A dual additive approach is used, where the synergy between an alkali metal cation and a polar solvent leads to high-quality 2D perovskite films with sandwich-type structures and vertical phase segregation. Such novel structure can induce high-quality 2D slab growth and reduce internal and surface defects, resulting in a high device efficiency of 16.48% with enhanced continuous illumination stability and improved moisture (55-60%) and thermal (85°C) tolerances. Transient absorption spectra reveal the carrier migration from low n to high n species with different kinetics. An [PbI 6 ] 4- octagon coalescence transformation mechanism coupled with metal and organic cations wrapped is proposed. By solvent vapor annealing, a recrystallization and reorientation of the 2D perovskite slabs occurs to form an ideal structure with improved device performance and stability.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Dynamic Shear Deformation of a Precipitation Hardened Al 0.7 CoCrFeNi Eutectic High-Entropy Alloy Using Hat-Shaped Specimen Geometry

Lamellar eutectic structure in Al 0.7 CoCrFeNi high-entropy alloy (HEA) is emerging as a promising candidate for structural applications because of its high strength-ductility combination. The alloy consists of a fine-scale lamellar fcc + B2 microstructure with high flow stresses > 1300 MPa under quasi-static tensile deformation and >10% ductility. The response to shear loading was not investigated so far. This is the first report on the shear deformation of a eutectic structured HEA and effect of precipitation on shear deformation. A split-Hopkinson pressure bar (SHPB) was used to compress the hat-shaped specimens to study the local dynamic shear response of the alloy. The change in the width of shear bands with respect to precipitation and deformation rates was studied. The precipitation of L1 2 phase did not delay the formation of adiabatic shear bands (ASB) or affect the ASB width significantly, however, the deformed region around ASB, consisting of high density of twins in fcc phase, was reduced from 80 μm to 20 μm in the stronger precipitation strengthened condition. We observe dynamic recrystallization of grains within ASBs and local mechanical response of individual eutectic lamellae before and after shear deformation and within the shear bands was examined using nano-indentation.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Phase stability of a eutectic high entropy alloy under extremes of pressures and temperatures

Additively manufactured high-entropy alloys are of interest because of their unique combination of high yield strength and large ductility achieved with far-from-equilibrium crystalline phases and micro/nanostructure morphology. We report on the phase transformation and thermal equation of state of the eutectic high-entropy alloy (EHEA) Al 18 Co 20 Cr 10 Fe 10 Ni 40 W 2 , produced by laser powder-bed fusion (L-PBF). The EHEA was studied in a large-volume Paris–Edinburgh cell using energy-dispersive x-ray diffraction to a pressure of 5.5 GPa and a temperature of 1723 K. Static compression studies in diamond anvil cells using angle-dispersive x-ray diffraction extended the high-pressure structural data to 317 GPa at ambient temperature. The initial dual-phase nanolamellar face-centered cubic (FCC) and body-centered cubic (BCC) structure of Al 18 Co 20 Cr 10 Fe 10 Ni 40 W 2 transforms into a single FCC phase under high pressure, with the BCC-to-FCC phase transformation completing at 9 ± 2 GPa. The FCC phase remained stable up to the highest pressure of 317 GPa. The measured thermal equation of state for the FCC phase of Al 18 Co 20 Cr 10 Fe 10 Ni 40 W 2 is presented up to 5.5 GPa and 1473 K. We observed melting of the EHEA at 1698 ± 25 K at a pressure of 5.5 GPa, and the recrystallized sample shows an increased fraction of the CsCl-type (B2) phase at ambient conditions following release from the high-pressure high-temperature state. The BCC-to-FCC phase transition completion pressure is correlated with the nanolamellae thickness of the BCC layer in this diffusion-less transformation at ambient temperature.

36 MATERIALS SCIENCE↗