Polymer toughness is typically dictated by the entanglement density. Here we demonstrate a new paradigm via polymer-grafted nanocomposites that couples segmental dynamics with the entanglement concept for enhanced toughness at high deformation rates.
A comparison is made between fracture toughness KIc as measured by recommended ASTM procedures and crack arrest toughness KIa as measured on more than 100 bolt-loaded double-cantilever beam (DCB) specimens from 7075, 7050, and 7049 alloy plates. Close agreement was found between the two values, KIa being on the average less than KIc over a specified range. This indicates that a simplified test based on a bolt-loaded DCB specimen could be used for quality control, lot release, and screening purposes. Measurements of crack length and specimen deflection are all that are required. The specimens do not have to be fatigue precracked, nor is a tensile machine needed.
A description is presented of studies which have been conducted to establish an improved technology base for a use of the sharply notched cylindrical specimen in quality assurance tests of aluminum alloy products. The results are presented of an investigation of fundamental variables associated with specimen preparation and testing, taking into account the influence of the notch root radius, the eccentricity of loading, the specimen diameter, and the notch depth on the sharp notch strength. Attention is given to the statistical procedures which are necessary to establish correlations between the sharp notch strength and the plane-strain fracture toughness for high-strength aluminum alloys.
Explore the source record for details and available documents.
The potential application of metallic glasses (MGs) as structural materials demands accurate measurements of their toughness and the understanding of the underlying factors affecting it. Currently, it is challenging to precisely measure the toughness of MGs, especially ductile MGs. Measured toughness values are widely scattered, even for MGs with identical compositions. That is attributed to the combined effect of intrinsic and extrinsic factors including processing, sample geometries, and loading conditions. A fundamental understanding of the influences of these elements is thus of great significance. In the present study, molecular dynamics simulations are performed to investigate the influence of intrinsic and extrinsic effects on the fracture toughness of CuZr MGs. In particular, focused is placed on the effects of cooling rate, notch shape and size, strain rate, and temperature. The results indicate that the fracture toughness of a MG scales with the cooling rate used to prepare it. This is attributed to increased free volume content generated at high cooling rates, which enhances plastic deformation and amplifies the associated energy dissipation during plastic deformation events. Fracture toughness also increases with the strain rate, arguably due to strain rate-induced crack extension delay. Overall, the results demonstrate that the largest fracture toughness are achieved when MG samples are fabricated at high cooling rates and subjected to high strain rate deformation. In addition, results suggest that the fracture toughness decreases with increasing temperature, due to the significant decrease in strength. Here, the correlations revealed between these crucial intrinsic and extrinsic parameters and the calculated MG fracture toughness support the development of a framework to understand the root of the discrepancies in the measurement of the toughness of MGs and provide insights into the design of tough MGs for structural applications.
Efforts are underway to replace superalloys used in the hot sections of gas turbine engines with materials possessing better mechanical and physical properties. Alloys based on the intermetallic NiAl have demonstrated potential; however, they generally suffer from low fracture resistance (toughness) at room temperature and from poor strength at elevated temperatures. Directional solidification of NiAl alloyed with both Cr and Mo has yielded materials with useful toughness and elevated-temperature strength values. The intermetallic alloy NiAl has been proposed as an advanced material to extend the maximum operational temperature of gas turbine engines by several hundred degrees centigrade. This intermetallic alloy displays a lower density (approximately 30-percent less) and a higher thermal conductivity (4 to 8 times greater) than conventional superalloys as well as good high-temperature oxidation resistance. Unfortunately, unalloyed NiAl has poor elevated temperature strength (approximately 50 MPa at 1027 C) and low room-temperature fracture toughness (about 5 MPa). Directionally solidified NiAl eutectic alloys are known to possess a combination of high elevated-temperature strength and good room-temperature fracture toughness. Research has demonstrated that a NiAl matrix containing a uniform distribution of very thin Cr plates alloyed with Mo possessed both increased fracture toughness and elevated-temperature creep strength. Although attractive properties were obtained, these alloys were formed at low growth rates (greater than 19 mm/hr), which are considered to be economically unviable. Hence, an investigation was warranted of the strength and toughness behavior of NiAl-(Cr,Mo) directionally solidified at faster growth rates. If the mechanical properties did not deteriorate with increased growth rates, directional solidification could offer an economical means to produce NiAl-based alloys commercially for gas turbine engines. An investigation at the NASA Glenn Research Center at Lewis Field was undertaken to study the effect of the directional solidification growth rate on the microstructure, room temperature fracture toughness, and strength at 1027 C of a Ni-33Al-31Cr-3Mo eutectic alloy. The directionally solidified rates varied between 7.6 and 508 millimeters per hour Essentially fault-free, alternating (Cr, Mo)/NiAl lamellar plate microstructures (left photograph) were formed during growth at and below 12.7 mm/hr, whereas cellular microstructures (right photograph) with the (Cr, Mo) phase in a radial spokelike pattern were developed at faster growth rates. The compressive strength at 1027 C continuously increased with increasing growth rate and did not indicate a maxima as was reported for directionally solidified Ni-33Al-34Cr. Surprisingly, samples with the lamellar plate microstructure (left photograph) possessed a room-temperature fracture toughness of approximately 12 MPa(sup square root of m), whereas all the alloys with a cellular microstructure had a toughness of about 17 MPa(sup square root of m). These results are significant since they clearly demonstrate that Ni-33Al-31Cr-3Mo can be directionally solidified at much faster growth rates without any observable deterioration in its mechanical properties. Thus, the potential to produce strong, tough NiAl-based eutectics at commercially acceptable growth rates exists. Additional testing and alloy optimization studies are underway.
In this paper, the data reduction equations for common delamination toughness tests are rederived for use with specimens which have bonded doublers. The common toughness tests considered here are the double cantilever beam (DCB) for mode I toughness; the end notch flexure (3ENF) and 4 point ENF (4ENF) for mode II toughness; and the mixed mode bending (MMB) test for testing under combined mode I and mode II loading. Because the addition of the doublers changes the bending stiffness of the specimens, these data reduction equations may need to be corrected. Doublers were added to the delamination test specimens to solve a premature failure problem. Delamination toughness is normally tested using a beam with an imbedded insert so that one end of the specimen is split into two arms. If the specimen is too thin, or if the toughness of the material is too high, an arm of the specimen may fail in bending before the delamination grows. When this occurs, the toughness of the material cannot be determined. To delay the bending failure so that delamination growth occurs, doubler plates were bonded to both top and bottom surfaces of the specimen. A doubler parameter, beta, which describes how much the use of doubler plates changed the ratio of full thickness to delaminated bending stiffnesses, was defined. When changes to the data reduction equations were required, the changes were minor when written in terms of the beta parameter. The doubler plate technique was demonstrated by measuring the mixed-mode fracture toughness of a carbon-carbon composite using test specimens which would otherwise have failed before delamination growth occurred. The doubler plate technique may solve several problems that can be encountered when testing delamination fracture toughness.
Uniaxial and ball burst toughness for eight commercial polyethylene balloon films have been investigated and compared. Uniaxial toughness was measured in both machine and transverse directions using a rectangular sample 25.4 mm wide by 50.8 mm gage length with an average nominal thickness of 20.32 microns (0.8 mils). Ball burst toughness was measured using a ball burst test fixture with 127 mm hole diameter and 50.8 mm ball diameter resulting in a 0.4 ball to hole diameter ratio. Both the size and shape of the deformed area were observed and the ball burst toughness was calculated based on the deformed area of the film instead of the full area. Specimens were tested at 23 C and -80 C and cross head speed was maintained at 508 mm per minute. The uniaxial toughness were in general, higher than the ball burst toughness. The toughness of the films varied from 12 to 365 MPa when measured uniaxially and from 24 to 73 MPa when measured in the ball burst test. Further investigation showed an apparent correlation between film performance in flight as measured by its stress index and its toughness.
Composite sandwich structures will be used in many future applications in aerospace, marine and offshore industries due to the fact that the strength and stiffness to mass ratios surpass any other structural type. Sandwich structure also offers advantages over traditional stiffened panels such as ease of manufacturing and repair. During the last three decades, sandwich structure has been used extensively for secondary structure in aircraft (fuselage floors, rudders and radome structure). Sandwich structure is also used as primary structure in rotorcraft, the most common example being the trailing edge of rotor blades. As with other types of composite construction, sandwich structure exhibits several types of failure mode such as facesheet wrinkling, core crushing and sandwich buckling. Facesheet/core debonding has also been observed in the marine and aerospace industry. During this failure mode, peel stresses applied to an existing facesheet/core debond or an interface low in toughness, results in the facesheet being peeled from the core material, possibly leading to a significant loss in structural integrity of the sandwich panel. In an incident during a test on a liquid hydrogen fuel tank of the X-33 prototype vehicle, the outer graphite/epoxy facesheet and honeycomb core became debonded from the inner facesheet along significant areas, leading to failure of the tank. As a consequence of the accident; significant efforts were made to characterize the toughness of the facesheet/core bond. Currently, the only standardized method available for assessing the quality of the facesheet/core interface is the climbing drum peel test (ASTM D1781). During this test a sandwich beam is removed from a panel and the lip of one of the facesheets is attached to a drum, as shown in Fig. 1. The drum is then rotated along the sandwich beam, causing the facesheet to peel from the core. This method has two major drawbacks. First, it is not possible to obtain quantitative fracture data from the test and so the results can only be used in a qualitative manner. Second, only sandwich structure with thin facesheets can be tested (to facilitate wrapping of the facesheet around the climbing drum). In recognition of the need for a more quantitative facesheet/core fracture test, several workers have devised experimental techniques for characterizing the toughness of the facesheet/core interface. In all of these cases, the tests are designed to yield a mode I-dominated fracture toughness of the facesheet/core interface in a manner similar to that used to determine mode I fracture toughness of composite laminates. In the current work, a modified double cantilever beam is used to measure the mode I-dominated fracture toughness of the interface in a sandwich consisting of glass/phenolic honeycomb core reinforced with graphite epoxy facesheets. Two specimen configurations were tested as shown in Fig 2. The first configuration consisted of reinforcing the facesheets with aluminum blocks (Fig. 2a). In the second configuration unreinforced specimens were tested (Fig. 2b). Climbing drum peel tests were also conducted to compare the fracture behavior observed between this test and the modified double cantilever beam. This paper outlines the test procedures and data reduction strategies used to compute fracture toughness values from the tests. The effect of specimen reinforcement on fracture toughness of the facesheet/core interface is discussed.
In the 1990’s, the Heavy Section Steel Irradiation Program at the ORNL performed investigation of the shape of the fracture toughness master curve for reactor pressure vessel steel highly embrittled because of irradiation exposure. A radiation-sensitive reactor pressure vessel (RPV) weld with intentionally enhanced copper content, designated KS-01, has been characterized in terms of static initiation (KJc) and Charpy impact toughness in the unirradiated and irradiated conditions. The objective of this original project was to investigate the ability of highly embrittled material to maintain the shape of the unirradiated transition fracture toughness curve, as well as to examine the ability of the Charpy 41-J shift to predict the fracture toughness shift at such high level of embrittlement. Irradiation of this weld was performed at the University of Michigan Ford Reactor in the new HSSI irradiation-anneal-reirradiation (IAR) facility. Broken specimens from that project have been saved in ORNL storage. To verify applicability of Mini-CT specimens for fracture toughness characterization of RPV materials as part of the DOE Light Water Reactor Sustainability Program, Mini-CT specimens were machined from broken Charpy specimens and tested according to ASTM E1921 standard. As result of this study, the fracture toughness of this weld derived by testing Mini-CT specimens in the unirradiated and irradiated conditions is compared to previously reported fracture toughness derived by large number of conventional specimens.
The feasibility of using ultrasonic attenuation measurements to rank tungsten carbide alloys according to their fracture toughness was demonstrated. Six samples of cobalt-cemented tungsten carbide (WC-Co) were examined. These varied in cobalt content from approximately 2 to 16 weight percent. The toughness generally increased with increasing cobalt content. Toughness was first determined by the Palmqvist and short rod fracture toughness tests. Subsequently, ultrasonic attenuation measurements were correlated with both these mechanical test methods. It is shown that there is a strong increase in ultrasonic attenuation corresponding to increased toughness of the WC-Co alloys. A correlation between attenuation and toughness exists for a wide range of ultrasonic frequencies. However, the best correlation for the WC-Co alloys occurs when the attenuation coefficient measured in the vicinity of 100 megahertz is compared with toughness as determined by the Palmqvist technique.
Laminates with various proportions of 0 deg, 45 deg, and 90 deg plies were fabricated from T300/5208 and T300/BP-907 graphite/epoxy prepreg tape material. The fracture toughness of each laminate orientation or lay-up was determined by testing center-cracked specimens, and it was also predicted with the general fracture-toughness parameter. The predictions were good except when crack-tip splitting was large, at which time the toughness and strengths tended to be underpredicted. By using predictions, a parametric study was also made of factors that influence fracture toughness. Fiber and matrix properties as well as lay-up were investigated. Without crack-tip splitting, fracture toughness increases in proportion to fiber strength and fiber volume fraction, increases linearly with E(22)/E(11), is largest when the modulus for non-0 deg fibers is greater than that of 0 deg fibers, and is smallest for 0(m)/90(p)(s) lay-ups. (The E(11) and E(22) are Young's moduli of the lamina parallel to and normal to the direction of the fibers, respectively). For a given proportion of 0 deg plies, the most notch-sensitive lay-ups are 0(m)/90(p)(s) and the least sensitive are 0(m)/45(n)(s) and alpha(s). Notch sensitivity increases with the proportion of 0 deg plies and decreases with alpha. Strong, tough matrix materials, which inhibit crack-tip splitting, generally lead to minimum fracture toughness.
Plane strain fracture toughness (K sub IC) was evaluated for Weldalite (tm) 049 with and without TiB2 reinforcement. For the nonreinforced variant, changes in toughness were measured for various aging conditions and lithium levels. Toughness testing was carried out on fatigue precracked compact tension (CT) specimens at 24 C, as per ASTM standard E-399. Toughness was measured as a function of aging time at 160 C for the two Weldalite 049(1.3) heats. The composition of these heats differed only in that 0.03 wt pct. Ti was added to one as an additional grain refiner. Both heats showed a decrease in toughness with increasing aging time, although toughness values for one were significantly higher than for the other. This greater toughness may be due to a subtle change in the grain size resulting for the presence of Ti or, alternatively, to differences in texture or substructure formed during extrusion.
Zirconia with 3 mol% yttria (3Y-TZP) has been used for dental crowns and bridges due to its excellent mechanical behavior. Performing fracture toughness testing on this nanograin material, however, can be a challenge. For reliable results, fracture toughness testing requires an extremely sharp notch in the test specimen that closely approximates a very sharp crack. This study was to investigate an alternative method to produce nanometer-sized notches, which are less than the average grain size of 3Y-TZP, during the preparation of single-edge V-notched beam specimens and report the resulting fracture toughness value. We present a method using focused ion beam (FIB) milling to fabricate nanometer-sized notches in 3Y-TZP. The notch tip is <100 nm wide, which is smaller than the grain size, and is consistent throughout the thickness of the specimen. The FIB-notched specimens show a much reduced average fracture toughness of 5.64 ± 1.14 MPa√m compared to 8.90 ± 0.23 MPa√m for the specimens without FIB-notches. The FIB-milling did not appear to create any monoclinic phase prior to fracture toughness testing. Fractures originated at the FIB-notches, and the notch size can be readily identified post-mortem using a microscope. A considerable amount of tetragonal-to-monoclinic phase transformation was observed throughout the fracture surfaces. FIB milling provides an alternative method to fabricate nanometer-sized notches that are smaller than the grain size of tetragonal zirconia polycrystal. The fracture toughness determined using FIB-notches was ~5.64 MPa√m, smaller than the specimens with V-notches fabricated using saw blades.
High explosive materials, and in particular insensitive high explosive (IHE) materials, are of significant interest. TATB-based LX-17 and PBX 9502 are two IHE’s and mechanical properties are an important metric of performance. In this work we present, for the first time, a study of fracture as a function of temperature and displacement rate and starter crack length on billet pressed IHE materials using a standard three point bend technique. We demonstrated that the technique can yield consistent results over time by measuring samples from the same lots 4 years later and observed that the fracture toughness of LX-17 and PBX 9502 are similar. We also determined the temperature dependence for different starter crack lengths and found that the fracture toughness generally decreases with larger starter crack sizes and temperatures. For the LX-17, where a wide temperature range of -60 C to 50 C was investigated, the impact of temperature on fracture toughness between -20 C and 23 C was less than expected. For the PBX 9502 we observed the difference in fracture toughness values between -20 C and 23 C did depend on the particular lot, and also there was a tendency of the fracture toughness to scale with the tensile strength. We also investigated the effect of a lower displacement rate and observed that while the impact on the fracture toughness was relatively small, the samples surprisingly did not break (fail) after exceeding the peak load. We took advantage of this to perform x-ray computed tomography (CT) of the samples to image crack propagation in the intact samples. We observed that cracks were generally straight and unaffected by the microstructure in the LX-17, in contrast to the PBX 9502 where the direction of the cracks would frequently change and were likely influenced by the underlying microstructure.