SEARCH · Search NASA
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
Ta2C is trigonal omega structured and crystallizes in the trigonal P-3m1 space group. The structure is two-dimensional and consists of one Ta2C sheet oriented in the (0, 0, 1) direction. Ta is bonded in a distorted T-shaped geometry to three equivalent C atoms. All Ta–C bond lengths are 2.20 Å. C is bonded to six equivalent Ta atoms to form edge-sharing CTa6 octahedra.
Five experimental tantalum alloy compositions containing 13-18% W+Re+Hf solid solution solute additions with dispersed phase strengthening achieved by carbon or nitrogen additions were prepared as 1.4 inch diameter ingot processed to 3/8 inch diameter rod and evaluated. Elevated temperature tensile and creep strength increased monotonically with increasing solute content. Room temperature elongation decreased for 20% to less than 2% as the solute content was increased above 16%. Phase identification indicated that the precipitating phase in the carbide containing alloys was Ta2C.
Metallurgical condition was shown to have a significant effect on the creep properties of ASTAR-811C (Ta-8W-1Re-0.7Hf-0.025C) sheet. Cold worked material exhibited creep rates 30 times higher than solution annealed material and 10 times greater than for recrystallized material. Both grain size and the carbide morphology changes as the final annealing temperature was raised from 3000 F to 3600 F. However, the lowest creep rates were achieved for material which retained the high temperature form of the Ta2C precipitate. Samples with GTA weldments had essentially identical properties as recrystallized base metal. Cooling rates from 3600 F of 5, 50, and 800 F deg/min. had little effect on the 2000 and 2400 F creep behavior of ASTAR-811C.
The reaction between a sputtered-deposited Ta film (320 nm thick) and a single crystalline (001) beta-SiC substrate induced by vacuum annealing at temperatures of 600-1200 C for 1 h (30 min at 1100 C) is investigated by 3 MeV He(+2) backscattering spectrometry, x-ray diffraction, secondary ion mass spectrometry, and transmission and scanning electron microscopies. No significant reaction is observed at 800 C or at lower tempertures. At 900 C, the main product phases are Ta2C and carbon-stabilized Ta5Si3. A minor amount of unreacted Ta is also present. After annealing at 1000 C, all the tantalum has reacted; the reaction zone possesses a multilayered structure of beta-SiC/TaC/carbon-stabilized Ta5Si3/alpha-Ta5Si3/Ta2C. The diffusion path at 1000 C is plotted on the isothermal section of the Ta-Si-C phase diagram. At 1100 C, the reacted layer has an interface with the SiC substrate that is still quite flat but has a rough surface due to the formation of macroscopic voids within the reacted layer. The equilibrium products predicted by the phase diagram are TaC and TaSi2. This final state is reached by annealing at 1200 C for 1 h. At that point, the reacted layer has a latterally very uneven structure and morphology.
Power electronics materials are poised to play a critical role in fulfilling next generation energy needs, with up to 90% of future energy demand predicted to flow through power electronics at some point.[1] Among a number of candidate materials, AlxGa1-xN is the strongest, having bipolar dopability, thermal and chemical stability, an ultra-wide bandgap, and demonstrated experimental feasibility. However, AlGaN growth is limited by a lack of lattice-matched substrates, ultimately stunting material quality at higher thicknesses needed for power electronics applications. Further, high power applications increasingly call for fully vertical device structures, necessitating a conductive substrate. [1] Recently our group identified the (111) plane of TaC as a conductive surface lattice-matched to Al0.55Ga0.45N, taking inspiration from prior work of AlN and GaN binaries on carbide and boride substrates. [2,3,4] In this talk we demonstrate the growth of (111)-oriented TaC by RF sputtering. We investigate the interface of TaC with sapphire and SiC substrates and identify means to suppress competing Ta2C nucleation in order to stabilize (111)-oriented TaC. Potential stacking sequences are identified with respect to crystal structure and observed twinning in the TaC films. We next assess structural changes and film recrystallization that results from face-to-face annealing of TaC thin films at high temperatures above 1500 degrees Celsius. Changes to grain structure and domain size are assessed by x-ray diffraction and surface morphology is explored using atomic force microscopy. Figure 1 shows significant improvements to in- and out-of-plane strain following annealing along with the formation of terraced step edges at the film surface. Strain as a function of material composition and thickness is considered, as this may play a major role in future nucleation of AlGaN layers.
Power electronics materials are poised to play a critical role in fulfilling next generation energy needs, with up to 90% of future energy demand predicted to flow through power electronics at some point. AlxGa1-xN ranks high among candidate materials, having bipolar dopability, thermal and chemical stability and an ultra-wide bandgap. However, AlGaN growth is limited by a lack of lattice-matched substrates, ultimately stunting material quality at higher thicknesses needed for power electronics applications. Further, high power applications increasingly call for fully vertical device structures, necessitating a conductive substrate. Recently our group identified the (111) plane of TaC as a conductive surface lattice-matched to Al0.55Ga0.45N, taking inspiration from prior work of AlN and GaN binaries on carbide and boride substrates. In this talk we demonstrate the growth of (111)-oriented TaC by RF sputtering. We investigate the interface of TaC with sapphire and SiC substrates and identify means to suppress competing Ta2C nucleation in order to stabilize (111)-oriented TaC. Potential stacking sequences are identified with respect to crystal structure and observed twinning in the TaC films. We next assess structural changes and film recrystallization that results from face-to-face annealing of TaC thin films at high temperatures above 1500 degrees C. Changes to grain structure and domain size are assessed by x-ray diffraction and surface morphology is explored using atomic force microscopy. Figure 1 shows significant improvements to in- and out-of-plane strain following annealing along with the formation of terraced step edges at the film surface. Strain as a function of material composition and thickness is considered, as this may play a major role in future nucleation of AlGaN layers. (1) R. J. in a face-to-face configuration, as illustrated in the schematic at left. Kaplar et al 2017, ECS J. Solid State Sci. Technol. 6 Q3061; (2) D. M. Roberts et al 2022, https://arxiv.org/abs/2208.11769; (3) T. Aizawa et al 2008, J Crys Growth 310, 1 22; (4) R. Liu et al 2002, Appl. Phys. Lett. 81, 3182-3184.