DOE OSTI2025

Metallurgical Analysis and Forward Modeling of Weld Distortion in SMR Containment Vessels

This work aimed to apply Sandia’s expertise in metallurgy and modeling to enable the use of hybrid laser arc welding for building nuclear reactor containment structures, via a collaboration with Holtec International. Experimental observations were coupled with finite element analysis to resolve microstructure development, mechanical properties, distortion, and residual stress in welds relevant to the production of the Holtec SMR-160. High residual stresses were observed in welds that were not subjected to preheat. Meanwhile, the microstructure of the welds generally exhibited a narrow heat affected zone relative to conventional arc welds. FEA appeared to be effective in simulating the thermal/mechanical conditions that occur during hybrid laser arc welding of simplified and instrumented test welds. Subsequently, FEA was used to perform sensitivity analyses for various weld geometries that would be prohibitively costly to assess with physical experiments. Insights from the study were used to inform Holtec’s welding process, and successful production welds were performed in 2025.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2021

Large-Scale Welding Process Simulation by GPU Parallelized Computing

The computational design of industrially relevant welded structures is extremely time consuming due to coupled physics and high nonlinearity. Previously, most welding distortion and residual stress simulations have been limited to small coupons and reduced order (from three-dimensional [3D] to two-dimensional [2D]), or inherent strain approximations were used for large structures. In this current study, an explicit finite element code based on a graphics processing unit was utilized to perform 3D transient thermomechanical simulation of structural components during welding. Laser brazing of aluminum alloy panels as representative of automotive manufacturing scenarios was simulated to predict out-of-plane distortion under different clamping conditions. The predicted deformation pattern and magnitude were validated by laser scanning data of physical assemblies. In addition, the code was used to investigate residual stresses developed during multipass arc welding of a nuclear industry pressurizer surge nozzle and subsequent welding repair where a 3D simulation was necessary. Taking the experimental data as reference, the 3D model predicted better residual stress distribution than a typical 2D asymmetrical model. Stress evolution in welding repair was also presented and discussed in this study. Furthermore, the efficient numerical model made it feasible to use integrated computational welding engineering to simulate welding processes for large-scale structures.

97 MATHEMATICS AND COMPUTING↗
DOE OSTI2022

ECAR-6330 Rev 0 Computational Fluid Dynamics Evaluation of Core Pressure Drop for the Primary Coolant Apparatus Test

PCAT is a thermal-hydraulic test loop for MARVEL reactor. The design gap thickness between the heater rods of PCAT core is 1.0 mm. The heater elements were manufactured within a straightness tolerance for the designed gap thickness, but several elements have been distorted out of tolerance during the welding process. The distortion of heater rods could lead to flow maldistribution and excessive hotspot temperature when the gap between two heater rods is too narrow. Wire-wraps are the spacer devices widely used in the sodium cooled fast reactor system to maintain the design fuel pitch. Generally, a wire spacer can enhance the turbulent heat transfer, but it increases the pressure drop, which is not desirable for a natural-circulation system like PCAT. Therefore, three short wire-wrap spacers per heater have been proposed to contain the core pressure drops and keep the heater-to-heater gap in an acceptable range. The objectives of this ECAR is to evaluate the PCAR core pressure drop with short wire spacers to confirm that the additional pressure drop due to the wire spacer will not disturb the natural circulation of the PCAT.

21 - SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLAN↗
DOE OSTI2022

ECAR-6415 Rev 0 CFD Analysis of the Primary Coolant Apparatus Test Core with Wire Spacers for Heterogeneous Power Distributions

Primary Coolant Apparatus Test (PCAT) is a thermal-hydraulic test loop for Microreactor Applications Research Validation and Evaluation (MARVEL) reactor. The heater elements were manufactured within a straightness tolerance for the designated gap thickness of 1.0 mm, but several elements have been distorted out of tolerance during the welding process. The distortion of heater rods can lead to flow maldistribution and excessive hotspot where the gap between two heater rods is too tight. In order to secure the heater-to-heater gap in an acceptable range, wire spacers are adopted for the PCAT. The wire spacers affect the thermal-hydraulic performance of the PCAT because they enhance the flow mixing among the flow subchannels in the core region. The objectives of this ECAR is to evaluate the effects of the wire spacers on the thermal-hydraulic performance of the PCAT core region by assuming several heterogeneous power distributions.

21 - SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLAN↗
DOE OSTI2021

17-7PH Housing Weld Report FY21

This report presents the work performed for welding 17-7PH stainless steel hemispheres, flanges, and accelerometer blocks. This includes weld development, microhardness measurements, calculated strengths, and distortion measurements after welding and heat treatment. The results of this report are utilized to propose a recommended welding procedure which was implemented for this experiment.

42 ENGINEERING↗
DOE OSTI2023

Develop a Fast Analysis Solver for Welding Sequence Optimization

During the shipbuilding manufacturing process, materials are exposed to significant stresses, as induced both thermally and mechanically, that alter the intended design and significantly affect the production schedule, labor hours (fitting, welding, rework, etc.), and material structural performance. The type and magnitude of deformation of a given structure depends on many factors such as the material, thickness and quality of components, the process heat input, preheat and inter-pass temperatures, type and size of welds, welding sequence and direction, location, sequence, and degree of fixturing. Numerical simulations using finite element analysis (FEA) have long been used to analyze welding-induced structural distortion. For large assemblies, transient thermal elastic-plastic analysis (TEPA) can take days or weeks to run, and optimization of welding sequence is not feasible. Simplified analysis methods were developed to reduce computational time. However, it is challenging to use these techniques to fully optimize welding sequencing because of their applied simplifications in modeling weld details. A fast analysis solver that could be used by the shipbuilding industry is being developed for optimizing welding sequences by taking full advantage of modern GPU-based HPC hardware and incorporating patented acceleration schemes. The accelerated processing factors are up to 2200 times greater for large, multi-pass welded structures.

Yang, Yu-Ping↗
DOE OSTI2025

Development, validation, and verification of multi-pass thermo-mechanical welding simulations using the open-source MOOSE framework: NeT TG4 benchmark weldment

This study develops and validates a sequentially coupled thermo-mechanical welding simulation for the three-pass 316L stainless steel NeT TG4 benchmark weldment using the open-source Multiphysics Object-Oriented Simulation Environment (MOOSE) and the Nuclear Engineering Material model Library (NEML). A diffused ellipsoidal heat source was calibrated against thermocouple data and weld macrographs to accurately model the fusion zone geometry and transient thermal fields. Material hardening is represented using the Lemaitre-Chaboche mixed isotropic-kinematic hardening model, while four annealing models - no annealing, single-stage at 1050 °C and 1300 °C, and two-stage at 800 °C/1300 °C - were implemented to assess the impact of annealing models on the accuracy of the predicted welding-induced plasticity, distortions, and residual stresses. The predictions were validated against experimental measurements and benchmarked against results from commercial software, demonstrating that thermo-mechanical MOOSE welding simulations achieve comparable accuracy with enhanced computational efficiency. This work highlights the potential of using open-source finite element frameworks like MOOSE for advanced manufacturing simulations.

Ji, Wendy [Australian Nuclear Science and Technolo↗
DOE OSTI2023

Modeling of Stress Distribution in Molten Salt Thermal Energy Storage Tanks for In-Service Central Receiver Power Plants

Failures in molten nitrate salts thermal energy storage tanks (TES) have been occurring in several concentrating solar power (CSP) plants around the world after a few months or years of operation. These failures are mainly related to a combination of high stress, corrosion, large deformation, and thermal cycling. Most of these failures are a consequence of the infancy of this technology; technical standards for design, fabrication, implementation, and operation of molten salt tanks operating at temperatures up to 565 degrees Celsius do not exist and most of current in-service tanks have been designed using the recommendations from the American Petroleum Institute (API) 650 and the American Society of Mechanical Engineers ASME section II standards, which are applicable for TES tanks operating at lower temperatures. We have developed a 3-dimensional model of a representative molten salt hot tank design that uses typical CSP plant operation conditions and allows determining the temperature and stress distribution in the tank. The model also considers the initial floor residual stresses and distortion after its welding fabrication. We have identified critical thermal gradients in the tank floor and shell and locations in the tank where the stresses are high and could become susceptible points for failure.

concentrating solar power↗
DOE OSTI2024

Adaptively remeshed multiphysical modeling of resistance forge welding with experimental validation of residual stress fields and measurement processes

Welding processes used in the production of pressure vessels impart residual stresses in the manufactured component. Computational modeling is critical to predicting these residual stress fields and understanding how they interact with notches and flaws to impact pressure vessel durability. Here, in this work, we present a finite element model for a resistance forge weld and validate it using laboratory measurements. Extensive microstructural changes, near-melt temperatures, and large localized deformations along the weld interface pose significant challenges to Lagrangian finite element modeling. The proposed modeling approach overcomes these roadblocks in order to provide a high-fidelity simulation that can predict the residual stress state in the manufactured pressure vessel; a rich microstructural constitutive model accounts for material recrystallization dynamics, a frictional-to-tied contact model is coordinated with the constitutive model to represent interfacial bonding, and adaptive remeshing is employed to alleviate severe mesh distortion. An interrupted-weld approach is applied to the simulation to facilitate comparison to displacement measures. Several techniques are employed for residual stress measurement in order to validate the finite element model: neutron diffraction, the contour method, and the slitting method. Model-measurement comparisons are supplemented with detailed simulations that reflect the configurations of the residual-stress measurement processes themselves. The model results show general agreement with experimental measurements, and we observe some similarities in the features around the weld region. Factors that contribute to model-measurement differences are identified. Finally, we conclude with some discussion of the model development and residual stress measurement strategies, including how to best leverage the efforts put forth here for other weld problems.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Failure Analysis for Molten Salt Thermal Energy Storage Tanks for In-Service CSP Plants

Thermal Energy Storage (TES) is a fundamental component in concentrating solar power (CSP) plants to increase the plant's dispatchability, capacity factor, while reducing the levelized cost of electricity. In central receivers CSP plants, nitrate molten salts have been used for several years for operation temperatures of up to 565 degrees C. Despite many efforts to advance nitrate salt to higher operation temperatures (even considering a replacement with molten chloride salts) to achieve higher energy conversion efficiencies, the 565 degrees C temperature is currently considered the state-of-the art. Although molten salt tanks have been broadly deployed in commercial CSP plants worldwide, several failures have been reported in these tanks after a few months or years of operation, causing significant economic loss and mistrust in CSP technologies. Most of these failures are associated with the infancy of the technology and multiple issues related to tank design, fabrication, commissioning, and aggressive operation. A technical standard dedicated to the design and fabrication of molten nitrate TES tanks does not exist today. Current in-service molten salt tanks have been generally designed based on the American Petroleum Institute's (API) 650 and ASME Section II standards. The API 650 code provides guidelines for dimensions and fabrication for oil storage tanks up to 260 degrees C. The ASME standard provides allowable stress values for various materials at a range of temperatures and conditions. Both standards seem to be limited for molten salt TES tanks where high temperatures, thermal cycling, and transient conditions are expected. In 2020, NREL released the Concentrating Solar Power Best Practices Study (NREL/TP-5500-75763) that summarized multiple issues in CSP plants, along with potential alternatives and recommendations to address those issues based on information collected from participants representing about 80% of operating CSP plants in the world. One of the recommendations from this study was the development of accurate and validated models to evaluate the plant's transient operation, capable of capturing the effect of short-term clouds and operator response, while being flexible in being adapted to various spatial and temporal resource data. The "Failure Analysis for Molten Salt Thermal Energy Tanks for In-Service CSP Plants" project was inspired on this recommendation and was focused on (1) the development and validation of a physics-based model for a representative, commercial-scale molten salt tank, (2) performing simulations to evaluate the behavior of the tank as a function of typical plant operation conditions, (3) understanding tank failures mechanisms, (4) determining the residual stress and distortion in the tank floor after welding fabrication and evaluating their impact in the stresses developed in the tank during operation, (5) assessing the impact of key operation parameters on the temperature and stress distribution, (6) conduct a preliminary evaluation of design features to reduce stress and improve tank's reliability, and (7) estimate the tank's service life based on the stress developed under diverse operation scenarios. From the analysis conducted in the project and presented in this report, it was found that maximum stresses surpassing the yield strength point of the stainless steel (SS) 347H are developed on the tank floor near the perimeter. These large stresses are strongly influenced by the initial residual stresses and distortion of the tank floor after welding fabrication. During operation, large stresses are developed in the tank floor at high operation temperatures with large salt inventory levels during transient operation. High stresses are also related to elevated temperature gradients in the tank floor that could be attributed to insufficient mixing within the salt inflow and the salt inventory. Based on the analysis, creep is the predominant failure mechanism. However, the large stress levels could favor the plastic deformation into buckles, and crack formation due to stress relaxation cracking during cycle operation. A lifetime below 3 years was estimated for the typical plant operation conditions and a specific initial residual stress and deformation distribution of the tank floor. The estimated life agrees with the service time to failure reported in several commercial molten salt tanks. Desing and operation guidelines can be extracted from the analysis presented in this report, which could be adopted by tank manufacturers and CSP operators to advance toward an ultimate solution for tank failures by reducing residual and operational stresses to achieve a tank service life of more than 30 years. Addressing failures in molten salt TES tanks is fundamental for the CSP industry's survivability, but it is also important for other industrial and power generation applications using this technology, including nuclear and concentrating solar thermal.

14 SOLAR ENERGY↗
DOE OSTI2025

Creep performance and microstructure of grade 91 steel weldments with integrated welding and thermal processing

Ferritic-Martensitic steel welds typically require post weld heat treatment (PWHT) to restore toughness and high temperature performance. This off-line thermal process reduces disparities between weld and base metal, but can cause distortion, cracking, or simply be impractical due to assembly size and joint non-uniformity. Here we show integrated welding and thermal processing applied to modified 9Cr-1Mo (Grade 91) steel, favored for advanced power generation applications, performed in real time through the addition of a secondary heat source near the primary weld head. Optimal integrated processing reduces weld fusion and heat affected zone hardness by 125 HV, approaching performance of conventional 730 °C, 60 min PWHT processing. Microstructures and mechanical performance are compared for mechanized GTAW welds, with equivalent lifetimes noted in cross-weld creep rupture tests up to 234 MPa at 550 °C, and up to 104 MPa at 650 °C. The integrated process was validated on a Grade 91 pressure vessel with multipass cold wire feed GTAW. After 550 °C, 71.4 bar thermomechanical cyclic testing, the maximum weld hardness is <350 HV.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Localized material compression to correct distortion in wire arc additive manufacturing

Wire Arc Additive Manufacturing (WAAM) is an advanced manufacturing technology which utilizes welding systems to generate three dimensional geometries in a layer-by-layer fashion. Distortion or warping of a print substrate and WAAM components due to thermally induced residual stresses is an ongoing challenge limiting the widespread adoption of WAAM technologies for producing components. In this manuscript, a novel approach is described to address thermal distortion in deposited components by applying lateral compressions along the length of the deposited material. To demonstrate this method, a series of single-track walls were printed and compressed at evenly spaced intervals using a modified hydraulic cutter tool. The jaws of the tool were modified to compress material rather than to shear it. A mathematical model was developed to relate the curvature of the deposited material to the volume of compression required to eliminate this distortion. Validation of this model was performed using 3D scan data to compare the change in wall curvature induced by compression to the volume of the applied compressions. Substrate deflection was also compared against a control wall, and implementation of wall compression reduced maximum deflections by 93% across a series of four depositions and subsequent compressions. Wall cross sections were also analyzed to determine the impact of compression on material hardness and grain structure. The results demonstrate that successively placed lateral compressions can effectively control and potentially eliminate bending distortion in printed parts. This methodology can be further developed to form a robust model for correction of thermally-induced distortion in WAAM components.

Additive manufacturing↗
DOE OSTI2023

Stress characterization for friction-stir-welded electric vehicle battery trays with application of neutron diffraction

The battery tray is an essential component that protects and controls battery-cell temperatures in electric and plug-in hybrid vehicles. The functional stress limit of the battery tray heavily depends on the residual stress acquired from the manufacturing process. Consequently, exceeding the stress limit of the battery tray during operation could compromise the battery-cell banks and may risk the vehicle's safety. Hence, understanding residual stress formation is vital for design and safety concerns. Here, in the current study, AA 6061-plates were friction stir welded to an A365 high-pressure die-cast battery tray to create sealed coolant channels in the battery tray. However, this multi-material lap friction stir weld introduces residual stress into the battery tray, resulting in distortion. This distortion was mitigated using burnishing or coining operations, though straightening the battery tray had initially unknown effects on the residual stress. Therefore, neutron diffraction was utilized to characterize residual stresses after straightening. The results indicate that the friction stir welding (FSW) operation generated residual stresses exceeding the yield strength of the material, consequently deforming the battery tray by ±3 mm from the pre-weld geometry. The burnishing operation reduced the residual stresses below the material's yield strength while restoring the tray to within ±0.75 mm of the pre-weld geometry. Similarly, the coining operation restored the battery tray to within ±0.75 mm of the pre-weld geometry, however, increasing the number of locations where the residual stress exceeds the yield strength of the material.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Power Density Distributions in Electron Beams

Measuring and controlling the power density distribution of electron beams used for welding is critical for producing repeatable welds and for transferring welding parameters between different machines. On any given machine, the power density distribution is controlled by defocusing the beam relative to its sharpest focused condition. However, measuring the power density distribution can be difficult due to the intense nature of welding beams and is further complicated by imperfect electron optics that can distort the beam, making it difficult to quantify. The enhanced modified Faraday cup (EMFC) diagnostic method was used here for beam analysis that utilizes computed tomography to reconstruct the beam’s power density distribution. These results were compared to the International Standards Organization (ISO) method for characterizing laser beams using a second-moment D4σ calculation. For ideal Gaussian-shaped beams, both methods would give the same result. However, for imperfect beams, the calculated D4σ diameter was shown to be about 25% larger relative to the FWe2 diameter measured by the EMFC due to the heavier weighting of data in the tails of the beam by D4σ. Finally, although both methods produce repeatable welds, it is important to understand the differences in the reported beam diameters, divergence angles, and beam parameter products when transferring parameters between machines.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Role of Computational Parameters on Predicting Self-Consistent Residual Stress and Distortion during Wire Arc Additive Manufacturing

Production of three-dimensional metallic parts through integration of an articulated robot and gas metal arc welding, also known as wire arc additive manufacturing (WAAM), can produce large-scale components with moderate geometrical complexity. This technology is particularly appealing due to its high deposition rates, scalability, and cost-effective feedstock compared to other AM processes. Despite its advantages, WAAM adoption is hindered by challenges in ensuring geometric conformity without extensive distortion, defect-free structures, and consistent mechanical properties. Finite element analysis (FEA) is often used to address the challenge of geometrical conformity. As the size of parts increases, the best practices for mesh size and temporal resolution known in the literature become computationally unviable. This research examined the effects of mesh and time-step resolutions during transient FEA of a large-scale (248 layers) metallic part. The impact of computational parameters on the thermal history, displacement, and residual stress distributions were evaluated. The results showed that predicted distortion was consistent across resolutions, while time-step length significantly affected predicted thermal history, and mesh size influenced residual stress distributions. To investigate this relationship further, directionally biased meshes were considered and analyzed. The results indicated that increasing mesh resolution perpendicular to the welding path yielded stress predictions that aligned closely with higher-resolution models while offering substantial computational savings. In conclusion, the significances of this research are related to verification and validation of WAAM models for widespread industrial adoption and pragmatic guidelines for optimizing computation parameters for balancing computational efficiency and predictive accuracy of residual stress and distortion.

Solsbee, Brandon [Univ. of Tennessee, Knoxville, T↗
DOE OSTI2022

Experimental studies of a high-gradient X-band welded hard-copper split accelerating structure

We report on recent research on high-gradient radio frequency (RF) accelerating structures indicates that the use of hard copper alloys provides improvement in high gradient performance over annealed copper. Such structures are made by bonding individually manufactured parts. However, there are no well-established bonding techniques that preserve the hardness, surface finish and cleanliness required for high gradient operation. To preserve the copper hardness, RadiaBeam has developed a novel high-gradient split accelerating structure, based on electron beam welding joining technique. This technique provides efficient bonding with strong, clean welds and minimal thermal loading, while maintaining a clean inner RF environment. Our RF design and fabrication methodology limits the small heat affected zone to the outer cavity envelop, with virtually no distortions or thermal loading of critical RF surfaces. It also incorporates provisions to precisely control the gap despite conventional issues with weld joint shrinkage. To date we have manufactured and validated an RF accelerating structure joined by electron-beam welding that incorporates a novel open split design to significantly reduce the assembly complexity and cost. In this paper, we will present the electromagnetic design of this structure, discuss bonding, and present the results of high-power tests, where the accelerating gradients of 140 MV m -1 with surface peak fields of 400 MV m -1 were achieved for flat-top pulse length of 600 ns with an RF breakdown rate of 10 -4 1/(pulsecm).

43 PARTICLE ACCELERATORS↗
DOE OSTI2026

Operational Parameter Database for Molten Salt Thermal Energy Storage Tank Modeling

The second generation of concentrated solar power (CSP) plants is characterized by the use of a central receiver (either cavity or external), two molten nitrate salt tanks (60 wt.% NaNO 3 and 40 wt.% KNO 3 ), and a steam Rankine power-generation cycle connected through a primary heat exchanger. Molten salt thermal energy storage (TES) tanks have been widely deployed in commercial CSP plants worldwide and have been essential for increasing plant dispatchability and capacity factor, while also reducing the levelized cost of electricity (LCOE). These systems enable energy storage at the gigawatt-hour scale, typically providing 6 to 17 hours of storage duration. Despite being a commercial technology, the multiple failures observed after only a few months or years of operation in plants around the world demonstrate the technology's relative infancy and highlight the need for further research to improve its reliability. The National Laboratory of the Rockies (NLR), in collaboration with industry partners and academic and research institutions, has been leading multiple projects funded by the U.S. Department of Energy (DOE). These projects focus on addressing molten salt tank failures by improving tank design and welding fabrication practices, evaluating new alloys and weld fillers, and providing guidelines for tank commissioning and safe operation. In particular, this report presents modeling results on the effect of key tank operation parameters during 60 minutes of operation, including the mass flow rate and temperature of the salt inflow, tank salt inventory temperature, and inventory level for a representative molten salt tank design. These results form a database of tank operation behaviors that captures the effects of each specific parameter during charging, charging/discharging, and discharging processes.

14 SOLAR ENERGY↗
DOE OSTI2024

Mitigation of distortion of Al/steel part under simulated paint baking condition: Experiment and numerical model studies

Multi-material joining of lightweight structures is essential to reduce vehicle weight for more energy savings and less greenhouse gas emission. However, mismatch of thermal expansion coefficient for dissimilar materials during the paint baking process can induce part distortion and joint failure for adhesive bonding. Here, in the present work, a thermomechanical model based on contact mechanics and large deformation theory was developed for dissimilar high-strength Al alloy and steel components to study the distortion mechanism and influential factors of the residual gap. The established model was used to optimize joint conditions, such as pitch distance and part geometry. When a weld pitch is shorter than 100 mm, the maximum gap between Al and steel part can be greatly reduced to 0.1 mm, and the local stress and plastic strain around the joint during the oven heating and cooling cycle are also substantially reduced compared with the long pitch case (900 mm). The numerical modeling results revealed that a comparable bending stiffness ratio between the steel and Al cross sections is critical to the minimization of gap and distortion under paint baking condition. Digital image correlation technique was used to measure the overall part distortion and local strain distribution that were used to validate the model prediction. Weld bonding (adhesive bonding with friction bit joining) process was successfully employed to join Al to steel component without gap opening in adhesive after the paint baking and cooling.

36 MATERIALS SCIENCE↗