Results for “White etching cracks”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

10 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2023

The effect of current and lambda on white-etch-crack failures

White etching cracks (WECs) have been associated with premature failure of wind turbine roller bearings. Various drivers for the generation of WECs have been identified such as loading conditions, slip, steel quality, lubrication, hydrogen embrittlement, corrosion fatigue cracking, and stray electrical currents passing through the surface. Here, in this work, a benchtop test rig utilizing a three-ring-on-roller test configuration was used to investigate the effect of electrical current and operation in different lubricating regimes, defined by lambda (λ), on high-quality bearing steel samples tested in a commercially available power transmission EP gear lubricant. It was observed that there is an inverse correlation between the magnitude of electric current applied to the ring/ roller system and time-to-failure. Higher current magnitudes lead to shorter time-to-failure than lower current magnitudes, with macropitting as the main failure mode. Sub-surface investigation revealed the presence of WECs in all cases. For the same current magnitude, tests conducted in boundary and mixed lubrication regimes showed that time-to-failure increased as lambda increased, and the tests resulted in WEC related macropits, whereas tests conducted in near-hydrodynamic regime resulted in surface damage with no macropit. It was also noted that a shift toward near-hydrodynamic lubrication resulted in a distinct surface distress on the roller surface. Furthermore, there seems to be a transition in the mixed regime during which the surface distress occurred. The damage on the surface of the test samples resembled non-spatially, periodic, groove-like corrugations and, in some cases, crater-like depressions. Sub-surface imaging, performed by sequential sectioning, revealed the presence of WECs in all cases, and broad, branching cracks that were more prevalent under the more severe boundary conditions.

17 WIND ENERGY↗
DOE OSTI2021

A proposed criteria to identify wind turbine drivetrain bearing loads that induce roller slip based white-etching cracks

In this article, the type of roller slip behavior that may result in the formation of white-etching cracks (WECs) in wind turbine gearbox bearings is identified. A new hypothesis based on the inner raceway normal contact load magnitude at the time of roller slip is proposed as the probable cause of WECs. For this purpose, the maximum normal contact loads are identified when roller slip occurs in high-speed shaft bearings at different mean wind speeds. Subsequently, the annual probability of occurrence of the maximum normal loads are obtained. The probability of maximum load under slip exceeding a limit probability is hypothesized as a probable cause for WEC. In order to apply the proposed hypothesis, two different wind turbines high-speed shaft bearings are used: the cylindrical roller bearing of the General Electric 1.5 SLE turbine and the tapered roller bearing of Vestas V52 turbine. Both the chosen bearings are on the generator side of the high-speed shaft. For both turbines, measurement data together with analytical models are used for identifying the slip and the maximum normal contact loads. We propose forecasting the probability of exceedance of a threshold maximum normal contact load level during slip to identify the possibility for inducing WECs.

17 WIND ENERGY↗
DOE OSTI2021

WhiteWind: White Etching Crack (WEC) Bearing Failures in Wind Turbine: Cooperative Research and Development, CRADA Number CRD-18-00758 (Final Report)

A WEC is a particularly aggressive, unpredictable and wide spread rolling element bearing failure mode that is common for large multi-megawatt (MW) wind turbines. WEC is considered the single most expensive failure mode for all wind turbine components, and there is currently no commercial solution. The Technical University of Denmark (DTU) is leading the WhiteWind project to investigate WECs through funding provided by the Innovation Fund Denmark. Other project partners include Vestas, SKF, Expanite, Rheinisch-Westfalische Technische Hochschule Aachen University (RWTH Aachen), and Argonne National Laboratory. The objective of the overall project is to develop a new surface engineered WEC-resistant bearing material using novel surface engineering techniques that shall provide a commercially competitive alternative to existing wind turbine bearings. NREL will support the project by providing existing measured bearing loads and validating models of drivetrain loads.

17 WIND ENERGY↗
DOE OSTI2021

The effect of electrical current on premature failures and microstructural degradation in bearing steel

Premature failures associated with microstructural degradation, i.e. white etching cracks (WECS), are becoming commonplace as applications are requiring tribological components to operate under extreme conditions. Although the specific drivers of WECs are still debated, the failures are often found in applications where cyclic loading is combined with added energy from stressors such as slip, impacts, or stray current. The aim of the current work is to elucidate effect that variable current has on premature failure. Numerous commercially available lubricants were tested, and both lubricant base oil type and additive package were found to have an effect on WEC failure time.

Bearing failure↗
DOE OSTI2021

Gaining Insights in Loading Events for Wind Turbine Drivetrain Prognostics

Wind energy is one of the largest sources of renewable energy in the world. To further reduce the operations and maintenance (O&M) costs of wind farms, it is essential to be able to accurately pinpoint the root causes of different failure modes of interest. An example of such a failure mode that is not yet fully understood is white etching cracks (WEC). This can cause the bearing lifetime to be reduced to 5–10% of its design value. Multiple hypotheses are available in literature concerning its cause. To be able to validate or disprove these hypotheses, it is essential to have historic high-frequency measurement data (e.g., load and vibration levels) available. In time, this will allow linking to the history of the turbine operating data with failure data. This paper discusses the dynamic loading on the turbine during certain events (e.g., emergency stops, run-ups, and during normal operating conditions). By combining the number of specific events that each turbine has seen with the severity of each event, it becomes possible to assess which turbines are most likely to show signs of damage.

49 EE - Wind and Water Power Program - Wind (EE-4W↗
DOE OSTI2020

Boride-Carbon Hybrid Technology to Produce Ultra-Wear and Corrosion Resistant Surfaces for Applications in Harsh Conditions (Final Technical Report)

Engineered functional surfaces play an important role to enable new products and manufacturing processes that can endure harsh service conditions such as high impact and contact loads, highly abrasive wear, extreme temperatures, and corrosive environments. Engineered surfaces can also be instrumental to improving the efficient use of energy by reducing frictional losses and extending service life. The main objective of this project was to develop a hybrid surface engineering technology that combines the advantages of a novel ultrafast boriding process with the next generation of superhard carbon coatings. The hypothesis was that this hybrid process will offer an unprecedented combination of wear and corrosion resistance, low frictional losses and affordability for treated parts so that it can be utilized in many applications. During this project, a duplex process was developed that combines the advantages of ultra-fast electrochemical boriding with those of hard tetrahedral amorphous carbon coatings. Both technologies can be combined to form a hybrid technology that is characterized by low friction and wear properties combined with corrosion and fatigue resistance. Good adhesion of both layers to each other was one main goal of this project, that has been achieved with HF1 adhesion through the Rockwell-C adhesion test. In this project, the mechanical properties of the hybrid coating were modeled through a finite-element analysis approach. We can conclude that the FEA model resembles the actual samples and be utilized to predict mechanical behavior under impacts. Based on this model, application-oriented load conditions can be simulated for optimal layer design regarding thickness and mechanical properties. To exemplify, one conclusion that can be drawn from the nanoindentation model is a boride layer thickness of 50 µm is sufficient to effectively support the carbon coating on the identified AISI 1045 low carbon steel substrate material. The duplex treatment yields wear rates as low as 6 x 10 -8 mm 3 N -1 m -1 and a coefficient of friction of 0.14 when tested against a steel counter face in a ball-on-disk test setup. On the other hand, the wear rate of the only-borided AISI 1045 steel was 5 x 10 -5 mm 3 N -1 m -1 , about three orders of magnitude higher than the duplex coating. At the same time, duplex treated samples experience corrosion resistance, which could not be achieved with single-layer carbon coatings. The developed surface treatment withstands a 3-hour exposure to 15% HCl, while the only carbon coated counter sample shows severe delamination of the coating due to pin hole corrosion. The boride layer is chemically stable and pin hole free because it is formed through an electrochemical process under high current densities (700 mA/cm 2 ) and high temperature. Additionally, the hybrid coating led to at least 3x increase in fatigue strength of the steel substrate, which exceeds the target performance of 30% improvement. There are numerous potential applications for the duplex coatings. A representative application is bearing ball coatings for off-shore windmills. Compared to currently employed surface technologies in this field, the initial costs of applying our technology might be higher due to more process steps but the performance benefits lead to an increased life time of treated parts, which will lower the maintenance and replacement costs in the long-term. To validate the technology for this specific application, the team is currently investigating the process of white etching crack initiation of the duplex coating in collaboration with ANL. Overall, this project successfully validated that the boride-carbon hybrid technology can withstand harsh conditions. One possible approach to commercialization under consideration is to transfer the technology to a startup or an existing coatings company.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Gearbox Reliability Collaborative 1.5 (GRC1.5) Project: Joint Industry Megawatt Scale Gearbox Field Tests: Cooperative Research and Development (Final Report) CRADA Number CRD-16-00608

A new DOE/NREL industry collaboration called the Gearbox Reliability Collaborative 1.5 (GRC1.5) will undertake field testing on a commercial multi-megawatt wind turbine gearbox to collect loading data as installed in the turbine to thoroughly characterize gearbox loads and responses during actual in-field conditions. A chief outcome is to provide publicly available operational loading data to the industry. This will provide a greater understanding of steady-state, transient, and fault response for both the input and output of the gearbox; thus, facilitating improvements in the gearbox components, lubrication system, power converter or turbine controller.

17 WIND ENERGY↗
DOE OSTI2024

GRC1.5 Project: Joint Industry Megawatt Scale Gearbox Field Tests (Final Report)

A new DOE/NREL industry collaboration called the Gearbox Reliability Collaborative (GRC) 1.5 will undertake field testing on current commercial multi-megawatt wind turbine gearboxes to collect loading data from installed turbines to thoroughly characterize gearbox input loads and responses during actual in-field conditions. A chief outcome is to provide operational loading data relative to the most common failure modes. This will provide a greater understanding of steady-state, transient, and fault response for both the input and output of the gearbox, thus facilitating improvements in the gearbox, power converter or turbine controller.

17 WIND ENERGY↗
DOE OSTI2022

Effects of Water Contamination on Micropitting and Rolling Contact Fatigue of Bearing Steels

Abstract In this research, the effects of water contamination in oil were investigated on two kinds of failures that occur in bearing steel: micropitting and rolling contact fatigue. Whereas the presence of water in the oil had little effect on the generation of surface wear in these experiments, increases in the occurrences of micropitting and rolling contact fatigue were observed due to the presence of either dissolved or free water in lubricants. Additionally, the presence of white etching matter at crack interfaces was observed and evaluated. The experimental results showed that water content can be considered as a significant factor that accelerates the formation of micropitting and fatigue cracks in rolling bearings.

Engineering↗
DOE OSTI2020

Isothermal oxidation of zirconium using steam

Oxidation of zirconium and its alloys under any atmosphere is generally characterised by a protective and non-protective stage. During the protective stage, the kinetics of oxidation are quasi-parabolic, while the oxide scale formed on the surface of the metal is black, compact, and protective in nature. For the non-protective stage, the oxidation rate becomes linear, while the protective oxide film turns into a deteriorated white scale. Breakaway is known as the transition point from protective to non-protective stage. The actual mechanism leading to breakaway of zirconium is still a matter of controversy, however some of the most common factors affecting breakaway are the following: - Impurities on the metal (Carbon, Oxygen, Nitrogen); - Oxidizing atmosphere (Presence of H{sub 2}O (g) or N{sub 2} (g)); - Sample preparation (Chemically etched or polished); - Temperature (LWR, LOCA). This research investigates the effect of temperature on 'breakaway' when zirconium is oxidized isothermally in steam for 60 min at 800 and 900 deg. C using thermogravimetric and optical microscopic imaging techniques. 1. Steam isothermal oxidations were performed on zirconium at 800 and 900 deg. C using a Thermogravimetric Analyzer (TGA). 2. Log-log plots of mass gain vs time were obtained from thermogravimetric results to calculate the reaction orders (n) and reaction rate constants (K) during oxidation. 3. Results of the kinetics of reaction were correlated with optical microscopic images form Light Microscope (LM) and Scanning Electron Microscope (SEM). Breakaway depends very strongly on temperature. At 800 deg. C, the weight gain followed a cubic-parabolic behaviour with evidence of a protective oxide film. On the other hand, oxidation at 900 deg. C showed signs of breakaway since the oxide film was cracked and oxidation rate was almost linear throughout the reaction.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗