NASA NTRS1982

Effects of heating rate on density, microstructure, and strength of Si3N4-6 wt.% Y2O3 and a beta-prime sialon

The effects of the heating rate during sintering/firing on the final density, microstructure, and strength of Si3N4-6 wt% Y2O3 and beta-prime sialon, sintered for four hours at 1750 C, are examined. In Si3N4-6 wt% Y2O3 increasing the heating rate from 7 C/min to 25 C/min to 90 C/min results in a corresponding decrease in the final density from 3.01 g/cu cm to 2.92 g/cu cm to 2.76 g/cu cm. In the beta-prime sialon composition all three heating rates produce an equivalent final density of 3.13 g/cu cm. All heating rates in both compositions produce nonhomogeneous microstructures. The room-temperature strength of Si3N4-6 wt% Y2O3 increases from 372 to 510 MPa with increased density, while the corresponding strengths for the betaprime sialon at equivalent densities are 345 to 445 MPa.

Campbell, S. S.↗
NASA NTRS1989

Strength of hot isostatically pressed and sintered reaction bonded silicon nitrides containing Y2O3

The hot isostatic pressing of reaction bonded Si3N4 containing Y2O3 produced specimens with greater room temperature strengths than those by high pressure nitrogen sintering of the same material. Average room temperature bend strengths for hot isostatically pressed reaction bonded silicon nitride and high pressure nitrogen sintered reaction bonded silicon nitride were 767 and 670 MPa, respectively. Values of 472 and 495 MPa were observed at 1370 C. For specimens of similar but lower Y2O3 content produced from Si3N4 powder using the same high pressure nitrogen sintering conditions, the room temperature strength was 664 MPa and the 1370 C strength was 402 MPa. The greater strengths of the reaction bonded silicon nitride materials in comparison to the sintered silicon nitride powder material are attributed to the combined effect of processing method and higher Y2O3 content.

William A Sanders↗
NASA NTRS1995

Elevated temperature creep properties of NiAl cryomilled with and without Y2O3

The creep properties of lots of NiAl cryomilled with and without Y2O3 have been determined in compression and tension. Although identical cryomilling procedures were used, differences in composition were found between the lot ground with 0.5 vol% yttria and the lot ground without Y2O3. Compression testing between 1000 and 1300 K yielded similar creep strengths for both materials, while tensile creep rupture testing indicated that the yttria-containing alloy was slightly stronger than the Y2O3-free version. Both compression and tensile testing showed two deformation regimes; whereas the stress state did not affect the high stress exponent (n approximately equals 10) mechanism, the low stress exponent regime n was approximately 6 in tension and approximately 2 in compression. The strengths in tension were somewhat less than those measured in compression, but the estimated activation energies (Q) of approximately 600 kJ/mol for tensile testing were closer to the previously measured values (approximately 700 kJ/mol) for NiAl-AlN and very different from the Q's of 400 and 200 kJ/mol for compression tests in the high and low stress exponent regimes, respectively. A Larson-Miller comparison indicated that cryomilling can produce an alloy with long-term, high-temperature strength at least equal to conventional superalloys.

Whittenberger, J. Daniel↗
NASA NTRS1999

The Effect of Microstructure on Mechanical Properties of Directionally Solidified Al2O3/ZrO2(Y2O3) Eutectic

The eutectic architecture of a continuous reinforcing phase within a higher volume fraction phase or matrix can be described as a naturally occurring in-situ composite. Here we report the results of experiments aimed at identifying the sources of high temperature creep resistance and high levels of strength in a two phase Al2O3/ZrO2(Y2O3) system. The mechanical properties of two phase Al2O3/ZrO2(Y2O3) eutectic are superior to those of either constituent alone due to strong constraining effects provided by the coherent interfaces and microstructure. The AlO3/ZrO2(Y2O3) eutectic maintains a low energy interface resulting from directional solidification and can produce strong and stable reinforcing phase/matrix bonding. The phases comprising a eutectic are thermodynamically compatible at higher homologous temperatures than man-made composites and as such offer the potential for superior high temperature properties.

Sayir, Ali↗
NASA NTRS2001

Calculation of Phase Equilibria in the Y2O3-Yb2O3-ZrO2 System

Rare earth oxide stabilized zirconias find a wide range of applications. An understanding of phase equilibria is essential to all applications. In this study, the available phase boundary data and thermodynamic data is collected and assessed. Calphad-type databases are developed to completely describe the Y2O3-ZrO2, Yb2O3-ZrO2, and Y2O3-Yb2O3 systems. The oxide units are treated as components and regular and subregular solution models are used. The resultant calculated phase diagrams show good agreement with the experimental data. Then the binaries are combined to form the database for the Y2O3-Yb2O3-ZrO2 psuedo-ternary.

Jacobson, Nathan S.↗
NASA NTRS2002

Thermodynamic Assessment of the Y2o3-yb2o3-zro2 System

Yttria-zirconia (Y2O3-ZrO2) is the most widely used of the rare earth oxide-zirconia systems. There are numerous experimental studies of the phase boundaries in this system. In this paper, we assess these data and derive parameters for the solution models in this system. There is current interest in other rare earth oxide-zirconia systems as well as systems with several rare earth oxides and zirconia, which may offer improved properties over the Y2O3-ZrO2 system. For this reason, we also assess the ytterbia-zirconia (Yb2O3-ZrO2) and Y2O3-Yb2O3-ZrO2 system.

Jacobson, Nathan S.↗
NASA NTRS2003

Thermal Conductivity and Stability of HfO2-Y2O3 and La2Zr2O7 Evaluated for 1650 Deg C Thermal/Environmental Barrier Coating Applications

HfO2-Y2O3 and La2Zr2O7 are candidate thermal and environmental barrier coating (T/EBC) materials for gas turbine ceramic matrix composite (CMC) combustor applications because of their relatively low thermal conductivity and high temperature capability. In this paper, thermal conductivity and high temperature stability of hot-pressed and plasma sprayed specimens with representative partially-stabilized and fully-cubic HfO2-Y2O3 compositions and La2Zr2O7 were evaluated at temperatures up to 1700 C using a steady-state laser heat-flux technique. Sintering behavior of the plasmasprayed coatings was determined by monitoring the thermal conductivity increases during a 20-hour test period at various temperatures. Durability and failure mechanisms of the HfO2-Y2O3 and La2Zr2O7 coatings on mullite/SiC hexoloy or SiC/SiC CMC substrates were investigated at 1650 C under thermal gradient cyclic conditions. Coating design and testing issues for the 1650 C thermal/environmental barrier coating applications are also discussed.

Zhu, Dong-Ming↗
NASA NTRS1990

Thermal Conductivity and Temperature Limits of Electron-Beam Physical-Vapor-Deposited ZrO2-7wt%Y2O3 Thermal Barrier Coating

The electron-beam physical-vapor-deposited (EB-PVD) ZrO2-7wt%Y2O3 thermal barrier coating has been widely used to protect engine hot section components in modem aircraft engines. Thermal conductivity and the conductivity increases due to sintering and phase changes are important coating design parameters. There is a need to characterize the coating thermal conductivity behavior and temperature limits, in order to potentially take full advantage of the coating capability. In addition, since the ZrO2-7wt%Y2O3 coating is often used as a baseline coating for the development of advanced lower thermal conductivity and higher temperature capability coatings, a thorough evaluation of the coating conductivity behavior at future higher engine operating temperatures will be useful for more accurately assessing the benefit gained from the new coating systems. In this study, thermal conductivity behavior of EB-PVD ZrO2-7wt%Y2O3 coating has been systematically investigated as a function of temperature (up to 2600 F) and time under steady-state and cyclic test conditions using a laser heat-flux technique. Thermal conductivity change kinetics were determined under realistic engine high temperature thermal gradient conditions, and correlated to the coating microstructural and phase changes. The thermal conductivity prediction models have been established in terms of heat flux, time, and testing temperatures.

Zhu, Dongming↗
NASA NTRS1980

Effect of thermal cycling on ZrO2-Y2O3 thermal barrier coatings

The paper studies the comparative life of plasma-sprayed ZrO2-Y2O3 thermal barrier coatings on NiCrAlY bond coats on Rene 41 in short (4 min) and long (57 min) thermal cycles at 1040 C in a 0.3-Mach flame. Attention is given to determining the effect of short- and long-duration cycles on ZrO2-Y2O3 coatings, the cause of any cycle frequency effects, and methods to improve tolerance to thermal stress. Short cycles greatly reduced the life of the ceramic coating in terms of time at temperatures as compared to longer cycles, the failed coating indicating compressive failure. The experiments and stress calculations show that repeatedly subjecting a ceramic coating to high rates of initial heating has a more destructive influence on the coating than sustained operation at temperature. The effect of such thermal compressive stresses might be minimized through coating deposition and thickness control and by turbine cycle measurement to keep starting heating rates below critical values.

Mcdonald, G.↗
NASA NTRS1981

Effect of CeO2, MgO and Y2O3 additions on the sinterability of a milled Si3N4 with 14.5 wt% SiO2

The sinterability of alpha Si3N4 with 0-5.07 equivalent per cent of CeO2, MgO, or Y2O3 has been studied in the temperature range 1650-1820 C by density measurements and X-ray diffraction analysis. Maximum densities were obtained in the range 1765-1820 C and were 99.6% of theoretical with 2.5% CeO2; 98.5% of theoretical with 1.24 to 1.87% MgO, and 99.2% of theoretical with 2.5% Y2O3. Densities 94% or more of theoretical value were obtained with as little as 0.62 equivalent per cent additive.

Arias, A.↗
NASA NTRS1982

Effect of fuel to air ratio on Mach 0.3 burner rig hot corrosion of ZrO2-Y2O3 thermal barrier coatings

A Mach 0.3 burner rig test program was conducted to determine how the fuel to air mass ratio affects the durability of ZrO2-Y2O3/Ni-16Cr-6Al-0.31Y thermal barrier coating systems in combustion products containing 5 ppm Na and 2 ppm V. As the fuel to air mass ratio was increased from 0.039 to 0.049, the durability of ZrO2-6Y2O3, ZrO2-8Y2O3 and ZrO2-12Y2O3 coatings decreased. ZrO2-8Y2O3 coatings were approximately 2X and 1.3X more durable than ZrO2-12Y2O3 and ZrO2-6Y2O3 coatings respectively at the fuel to air mass ratio of 0.039. The number of one hour cycles endured by ZrO2-8Y2O3 coatings varied from averages of 53 to 200 for the fuel to air mass ratios of 0.049 and 0.039, respectively. At the fuel to air mass ratio of 0.049, all ZrO2-Y2O3 coated specimens failed in 40 to 60 one hour cycles

Hodge, P. E.↗
NASA NTRS1983

Sintering, properties and fabrication of Si3N4 + Y2O3 based ceramics

Pure silicon nitride shows a remarkable resistance to sintering without the use of densification additives. The present investigation is concerned with results which show the effect of chemical content on sinterability, taking into account the composition, raw material impurities, and processing contaminants. Aspects of sintering are discussed along with strength characteristics, and oxidation relations. Attention is given to phase field I and II materials, phase field III and IV materials, tungsten carbide and oxidation at 600 C, and studies involving shape fabrication by injection molding. It was found that in sintering Si3N4 + Y2O3 an increase in the amount of Y2O3 and, in particular, the addition of Al2O3 enhances the fluidity of the liquid phase.

Quackenbush, C. L.↗
NASA NTRS1983

Analysis of grain boundary phase devitrification of Y2O3- and Al2O3-doped Si3N4

The present study has the objective to show that a Fourier Transform IR (FTIR) spectrometer in a single-beam reflection mode can be used for direct comparison of fractured vs nonfractured Si3N4 surfaces. This can be done because the FTIR method permits a digital summation of nearly 1000 scans of the fracture surface. Commercial-grade Si3N4, Y2O3, and Al2O3 were used in the study. The samples were heat treated in a vacuum induction heating furnace at either 1000 C for 10 h or 1200 C for 10 h each. Use of Fourier transform IR reflection spectroscopic analysis and X-ray diffraction shows that 10 h at 1200 C is sufficient to devitrify the amorphous grain boundary phase of Si3N4 containing 15 percent Y2O3 + 2 percent Al2O3 densification aids.

Hench, L. L.↗
NASA NTRS1980

Effect of thermal cycling on ZrO2-Y2O3 thermal barrier coatings

A study was made of the comparative life of plasma sprayed ZrO2-Y2O3 thermal barrier coatings on NiCrAlY bond coats on Rene 41 in short (4 min) and long (57 min) thermal cycles to 1040 C in a 0.3 Mach flame. Short cycles greatly reduced the life of the ceramic coating in terms of time at temperature as compared to longer cycles. Appearance of the failed coating indicated compressive failure. Failure occurred at the bond coat-ceramic coat junction. At heating rates greater than 550 kw/sq m, the calculated coating detachment stress was in the range of literature values of coating adhesive/cohesive strength. Methods are discussed for decreasing the effect of high heating rate by avoiding compressive stress.

Mcdonald, G.↗
NASA NTRS1982

Effect of Y2O3 and Al2O3 on the oxidation resistance of Si3N4

Oxidation of cold-pressed and sintered Si3N4 containing 15 wt% Y2O3 and 2, 4, 6, and 8% Al2O3 is observed at temperatures as low as 1000 C with IR reflection spectroscopy. Concentrations of Al2O3 in excess of 4% greatly retard the rate of oxidation and alter the mechanism of surface attack by promoting formation of a glassy layer on the surface containing mixed oxynitride bonds. The glassy layer retards heterogeneous attack and reduces the effect of an oxidation transition temperature between 1000 and 1100 C for these materials.

Hench, L. L.↗
NASA NTRS1982

Some inelastic effects of thermal cycling on ZrO2-Y2O3 materials

An analysis has been developed which relates the effects of inelastic behavior of Y2O3 stabilized ZrO2 (YSZ) materials. The results show these materials to be sensitive to small changes in temperature and are supported by measurements of inelastic behavior in disk and bar specimens at temperatures as low as 1010 C (1850 F). At higher thermomechanical loads, the test specimens can deform to strains greater than 1 percent and for bar specimens, with sufficient strength, to remain bonded to the metallic substrate.

Hendricks, R. C.↗
NASA NTRS1983

Anisotropic thermal expansion effects in plasma-sprayed ZrO2-8 percent Y2O3 coatings

The thermal expansion properties of plasma-sprayed ZrO2-8-wt pct Y2O3 coatings, detached from the substrate, have been examined. Coatings were heat-treated in air or in argon. Anisotropic effects in the longitudinal (planar to the substrate surface) and transverse (perpendicular to the substrate surface) directions were measured and related to the coating structure. The thermal expansion coefficient of the coating is discussed in terms of the material's properties, such as the crack network and interlamellar boundary distribution. A precise model for the expansion behavior of coatings still needs attention, since no description of all of the contributing variables exists. A quantitative analysis of thermal properties of coatings will aid in future design and modeling of coating systems.

Berndt, C. C.↗
NASA NTRS1983

Grain-boundary phases in hot-pressed silicon nitride containing Y2O3 and CeO2 additives

Auger electron spectroscopy in conjunction with X-ray powder diffraction and scanning electron microscopy is used to analyze the grain-boundary phases of Y2O3- and CeO2-doped Si3N4 hot-pressed materials in order to demonstrate that the additives concentrate predominantly in the grain boundaries of Si3N4 in the form of various oxynitride phases. A high oxygen content observed in sample fracture surfaces was found to be consistent with the existence of an oxygen-enriched phase in the grain boundaries. The presence of yttrium and cerium in the fracture surfaces and an overall increase in the O/N ratio imply that the additive oxides are predominantly concentrated in the intergranular phases.

Guha, J. P.↗