NASA NTRS1986

Effect of adherend thickness and mixed mode loading on debond growth in adhesively bonded composite joints

Symmetric and unsymmetric double cantilever beam (DCB) specimens were tested and analyzed to assess the effect of: (1) adherend thickness, and (2) a predominantly mode I mixed mode loading on cyclic debond growth and static fracture toughness. The specimens were made of unidirectional composite (T300/5208) adherends bonded together with EC3445 structural adhesive. The thickness was 8, 16, or 24 plies. The experimental results indicated that the static fracture toughness increases and the cyclic debond growth rate decreases with increasing adherend thickness. This behavior was related to the length of the plastic zone ahead of the debond tip. For the symmetric DCB specimens, it was further found that displacement control tests resulted in higher debond growth rates than did load control tests. While the symmetric DCB tests always resulted in cohesive failures in the bondline, the unsymmetric DCB tests resulted in the debond growing into the thinner adherend and the damage progressing as delamination in that adherend. This behavior resulted in much lower fracture toughness and damage growth rates than found in the symmetric DCB tests.

Mangalgiri, P. D.↗
NASA NTRS1980

Analysis and test of bonded single lap joints with preformed adherends

A theoretical and experimental study has been conducted to investigate the load transfer of a single lap joint where the adherends have been preformed so that the angle between the line of action of the applied in-plane force and the bond line is reduced. The preforming of the adherend reduces the moment resultant in the adherend at the edge of the overlap region which reduces both the maximum peel and shear stresses in the adhesive, and gives a more uniform shear distribution in the adhesive. An increase in static load transfer of up to 120 percent has been shown, and several orders of magnitude increase in fatigue life have been achieved with modest preform angles. Thus, sizeable benefits can be obtained in the fatigue life or additional load capacity of bonded single lap joints by preforming the adherends.

Sawyer, J. W.↗
NASA NTRS1984

Effect of preforming adherends on static and fatigue strength of bonded composite single-lap joints

An analytical and experimental investigation was conducted on bonded composite single-lap joints with the adherends performed to reduce the angle between the line of action of the applied in-plane force and the bondline. A classical closed-form solution was used to analyze the composite joints with various preform angles and overlap lengths. The adherends of the test specimens were preformed before bonding, during the layup and curing process. Static tests were conducted for preform angles of 0, 5, 10, and 15 deg and overlap lengths of 0.75, 1.75, 2.75, and 3.75 in. A limited fatigue study was conducted for specimens with a 2.75-in. overlap and a preform angle of 5 deg. Results of the analysis showed that preforming the adherends of bonded composite single-lap joints significantly reduced the shear and peel stress concentrations in the adhesive. Experimental results showed that preforming the adherends significantly increased their static and fatigue strength and thus increased the load level for which bonded composite single-lap joints can be designed.

Sawyer, J. W.↗
DOE OSTI2023

Plasma treatment on both adhesive tape and adherends for significantly enhanced CFRTP-related adhesive joints

Unlike existing literature that primarily concentrates on either the plasma treatment of adherends alone or solely on adhesive surfaces, this work leverages plasma modification of both adhesive in tape form and adherend surfaces to largely enhance the interfacial bonding between a thermoset-based adhesive tape and carbon-fiber-reinforced thermoplastic polymer (CFRTP) for structural bonding applications. Here, by conducting single lap shear tests on adhesively-bonded AA6061-CFRPPA (carbon-fiber-reinforced polyphthalamide) dissimilar joints, it is shown that the plasma treatment of adherends alone can increase the lap shear strength (LSS) of the joints by approximately 200% compared to non-treated counterparts. An additional plasma treatment of adhesive tape surfaces leads to even higher LSS improvement, reaching up to 315%, due to the formation of a denser crosslinked network of covalent bonds and a reduced area fraction of interfacial voids at the CFRPPA/adhesive interface. The highest plasma-enhanced LSS of the metal-CFRTP dissimilar joints rivals that of metal-metal joints, which is typically stronger than the joints associated with fiber-reinforced polymers. This study is important for achieving strong CFRTP-related structural components bonded using adhesive tape, providing better compatibility with plasma treatment and other joining methods like riveting compared to adhesive paste or liquid.

36 MATERIALS SCIENCE↗
NASA NTRS1975

Effect of polymer properties and adherend surfaces on adhesion

The surface properties associated with good adhesive joints were evaluated in terms of application of adhesive bonding in aerospace technology. The physical and chemical nature was determined of Ti and Al adherend surfaces after various surface treatments, and the effects on fracture surfaces of high temperature aging, and variations in amide, anhydride, and solvent during polymer synthesis. The effects were characterized of (1) high temperature during shear strength testing, (2) fiber-reinforced composites as adherends, (3) acid/base nature of adherends, (4) aluminum powder adhesive filler, and (5) bonding pressure.

Dwight, D. W.↗
NASA NTRS2003

Analysis Method for Inelastic, Adhesively Bonded Joints with Anisotropic Adherends

A one-dimensional analysis method for evaluating adhesively bonded joints composed of anisotropic adherends and adhesives with nonlinear material behavior is presented in the proposed paper. The strain and resulting stress field in a general, bonded joint overlap are determined by using a variable-step, finite-difference solution algorithm to iteratively solve a system of first-order differential equations. Applied loading is given by a system of combined extensional, bending, and shear forces that are applied to the edge of the joint overlap. Adherends are assumed to behave as linear, cylindrically bent plates using classical laminated plate theory that includes the effects of first-order transverse shear deformation. Using the deformation theory of plasticity and a modified von-Mises yield criterion, inelastic material behavior is modeled in the adhesive layer. Results for the proposed method are verified against previous results from the literature and shown to be in excellent agreement. An additional case that highlights the effects of transverse shear deformation between similar adherends is also presented.

Smeltzer, Stanley S., III↗
DOE OSTI2022

The Roles of Interface, Adherend, and Adhesive in Plasma- and Other-treated Joints of Metals and FRP Materials Under Shear Deformation

This work investigated the role of interface, adherend, and adhesive in adhesively-bonded metal-metal, metal-CFRTP, and CFRTP-CFRTP combinations with plasma-treated surfaces under shear deformation. To this end, aluminum alloys (AA5052 and AA6061) and short-carbon-fiber-reinforced polyamide 66 (CFRPA66) were used as examples and performed through single lap shear testing. The results showed that air plasma surface treatment can improve the shear behavior of adhesively-bonded AA5052-CFRPA66 and CFRPA66-CFRPA66 joints with about 20% enhanced lap shear strength compared to non-treated cases. Failure surface morphology of plasma-treated CFRPA66 adherend confirmed this improvement by showing an increased amount of adhesive failure than interfacial failure between CFRPA66 and adhesive. But this is not true for AA5052-AA6061 joints with plasma-treated surfaces exhibiting almost no enhanced lap shear strength. This study also showed the importance of selecting a proper surface modification method for the enhancement of adhesive-bonded structures under shear deformation through the analysis of the results in this study and in the literature. For fiber-reinforced polymers (FRPs), improving FRP/adhesive interface may be prioritized via different surface modification methods (e.g., plasma, chemical coating, etc.) than adhesive modification methods. However, for surface-cleaned metals, toughening adhesive via different enhancement methods (e.g., nano-particles, chemical enhancement, etc.) may be more important than improving metal/adhesive interface. These insightful results are valuable in the area of multi-materials joining.

Qiao, Yao↗
NASA NTRS1985

Bonding and nondestructive evaluation of graphite/PEEK composite and titanium adherends with thermoplastic adhesives

Bonded single overlap shear specimens were fabricated from Graphite/PEEK (Polyetheretherketone) composite adherends and titanium adherends. Six advanced thermoplastic adhesives were used for the bonding. The specimens were bonded by an electromagnetic induction technique producing high heating rates and high-strength bonds in a few minutes. This contrasts with conventionally heated presses or autoclaves that take hours to process comparable quality bonds. The Graphite/PEEK composites were highly resistant to delamination during the testing. This allowed the specimen to fail exclusively through the bondline, even at very high shear loads. Nondestructive evaluation of bonded specimens was performed ultrasonically by energizing the entire thickness of the material through the bondline and measuring acoustic impedance parameters. Destructive testing confirmed the unique ultrasonic profiles of strong and weak bonds, establishing a standard for predicting relative bond strength in subsequent specimens.

Hodges, W. T.↗
NASA NTRS1987

Sodium hydroxide anodization of Ti-Al-4V adherends

The use of sodium hydroxide anodization (SHA) for Ti-6Al-4V adherends is examined. The SHA surface is evaluated using SEM, X-ray photoelectron spectroscopy, and Auger electron spectroscopy. The SHA procedures of Kennedy et al. (1983) were employed in this experiment. The photomicrographs of the SHA (sandblasted) and PSHA (sandblasted and pickled) oxide surface reveal that the two surfaces differ. The PSHA is patchy and similar to a chromic acid anodization surface and the porosity of the PSHA is more uniform than the SHA surface. The compositions of the surfaces are studied. It is noted that SHA is an effective pretreatment for Ti-6Al-4V adherends.

Filbey, Jennifer A.↗
NASA NTRS1988

Deformations and strains in a thick adherend lap joint

Displacement fields in a thick adherend lap joint were measured by high-sensitivity moire interferometry. Contour maps of in-plane U and V displacements were obtained across adhesive and adherend surfaces. Loads ranged from a modest load to a near-failure load. Quantitative results are given for displacements and strains in the adhesive and along the adhesive/adherend boundary lines. The results show nearly constant shear strain in the adhesive, nonlinear strains as a function of load or average shear stress, and viscoelastic or time-dependent response. Longitudinal normal strains in the adhesive are nearly two orders of magnitude less than the shear strains. With its subwavelength displacement resolution and high spatial resolution, moire interferometry is especially well suited for deformation studies of adhesive joints.

Post, D.↗
NASA NTRS1989

Tensile behavior of bonded scarf joints between composite adherends

Tensile tests of bonded scarf joints indicate that shallow angle joints are sensitive to slight adherend tip bluntness. For scarf angles ranging from 9.2 to 1.1 degrees stress concentrations from blunt adherend tips significantly limit the increased strength expected from larger bond area. The bonded joints fail by two failure modes depending on the scarf angle. Although most of the joints in this study were scarfed by a surface grinder, small angle scarfs can be cut very accurately with a hand held rotary bur.

Adkins, David W.↗
NASA NTRS1990

Methods of using fluoroepoxy compounds as adhesives for fluoroplastic adherends and products made therefrom

Fluoroepoxy compounds are made by reacting a fluoroepoxy resin with an effective curing agent, such as an adduct amine, and, while the compound is sufficiently liquid to wet a fluoroplastic surface, it may be applied to a fluoroplastic adherend, such as a Teflon, to be employed as an adhesive, to form various fluoroplastic products, without requiring any surface treatment of the adherend. The compounds are intentionally formulated with high fluorine contents, normally above 46% by weight, preferably for bonding fluoroplastics with a high F-content, above 55% by weight.

Lee, Sheng Y.↗
NASA NTRS2026

Thermal Inspection for the Assessment of Adhesively Bonded Metal Adherends

Certification of adhesively bonded structures is currently a challenge for aircraft manufacturers. The ability to certify bonds in primary structure can reduce dependence on fasteners and this will enable more efficient manufacturing. For example, drilling holes and installing fasteners in bonded joints can be a potentially significant bottleneck in airframe manufacturing. In addition, fasteners increase the airframe weight and can add stress concentration areas. Reducing fastener count can accelerate manufacturing and improve aircraft performance. NASA is currently investigating nondestructive evaluation (NDE) techniques to assess bond integrity. For example, bond thickness influences bond strength and therefore NDE techniques are being investigated to determine bond thickness. For bonded metal structures, there is a large difference in the thermal diffusivity between the 7075 aluminum alloy metal adherends and aircraft grade adhesive. Multi-layered thermal models show a large variation in the thermal response for bondline adhesive thicknesses that vary from 100 to 300 microns for adherend thicknesses of 0.163 cm. Experimental through-transmission thermal measurements reveal promise to quantitatively characterize the bondline thickness. Results were validated with X-ray computed tomography and optical microscopy measurements, and influence of porosity on the thermal model and measurements are investigated.

X-ray computed tomography↗
NASA NTRS1976

Effect of polymer properties and adherend surfaces on adhesion

High temperature polymer surface characteristics associated with joint strength were evaluated. Selected samples represented composite adherends, aluminum filler and fiber glass carrier cloth. Detailed analysis of fractured joint surfaces revealed unique characteristics typical of the specific adhesive formulations and test conditions. A fracture mechanism model was developed for correlating macroscopic shear strength and microstructure of fracture surfaces. Applications were made to unpublished data on polyimides and fluoropolymers.

Dwight, D. W.↗
NASA NTRS1985

Characterization of mode 1 and mixed-mode failure of adhesive bonds between composite adherends

A combined experimental and analytical investigation of an adhesively bonded composite joint was conducted to characterize both the static and fatigue beyond growth mechanism under mode 1 and mixed-mode 1 and 2 loadings. Two bonded systems were studied: graphite/epoxy adherends bonded with EC 3445 and FM-300 adhesives. For each bonded system, two specimen types were tested: a double-cantilever-beam specimen for mode 1 loading and a cracked-lapshear specimen for mixed-mode 1 and 2 loading. In all specimens tested, failure occurred in the form of debond growth. Debonding always occurred in a cohesive manner with EC 3445 adhesive. The FM-300 adhesive debonded in a cohesive manner under mixed-mode 1 and 2 loading, but in a cohesive, adhesive, or combined cohesive and adhesive manner under mode 1 loading. Total strain-energy release rate appeared to be the driving parameter for debond growth under static and fatigue loadings.

Mall, S.↗
NASA NTRS1986

Characterization of mode I and mixed-mode failure of adhesive bonds between composite adherends

A combined experimental and analytical investigation of an adhesively bonded composite joint was conducted to characterize both the static and fatigue beyond growth mechanism under mode 1 and mixed-mode 1 and 2 loadings. Two bonded systems were studied: graphite/epoxy adherends bonded with EC 3445 and FM-300 adhesives. For each bonded system, two specimen types were tested: a double-cantilever-beam specimen for mode 1 loading and a cracked-lapshear specimen for mixed-mode 1 and 2 loading. In all specimens tested, failure occurred in the form of debond growth. Debonding always occurred in a cohesive manner with EC 3445 adhesive. The FM-300 adhesive debonded in a cohesive manner under mixed-mode 1 and 2 loading, but in a cohesive, adhesive, or combined cohesive and adhesive manner under mode 1 loading. Total strain-energy release rate appeared to be the driving parameter for debond growth under static and fatigue loadings.

Mall, S.↗
NASA NTRS2004

Nonlinear Analysis of Bonded Composite Single-LAP Joints

This study presents a semi-analytical solution method to analyze the geometrically nonlinear response of bonded composite single-lap joints with tapered adherend edges under uniaxial tension. The solution method provides the transverse shear and normal stresses in the adhesive and in-plane stress resultants and bending moments in the adherends. The method utilizes the principle of virtual work in conjunction with von Karman s nonlinear plate theory to model the adherends and the shear lag model to represent the kinematics of the thin adhesive layer between the adherends. Furthermore, the method accounts for the bilinear elastic material behavior of the adhesive while maintaining a linear stress-strain relationship in the adherends. In order to account for the stiffness changes due to thickness variation of the adherends along the tapered edges, their in-plane and bending stiffness matrices are varied as a function of thickness along the tapered region. The combination of these complexities results in a system of nonlinear governing equilibrium equations. This approach represents a computationally efficient alternative to finite element method. Comparisons are made with corresponding results obtained from finite-element analysis. The results confirm the validity of the solution method. The numerical results present the effects of taper angle, adherend overlap length, and the bilinear adhesive material on the stress fields in the adherends, as well as the adhesive, of a single-lap joint

Oterkus, E.↗