Sila’s ultra-low volume change silicon anode material was utilized to achieve high cycle life and calendar life with improved electrolyte formulations, simultaneously achieving the required 1000 cycles and 10 year calendar life required in an electric vehicle battery, while also enabling >900 Wh/L and >350 Wh/kg cell level energy density.
Voltage-hold (V-hold) protocols have shown promise toward calendar lifetime analysis of cells with graphite (Gr) and silicon (Si) anodes. In this work, repeat V-holds are performed on Gr and Si cells paired with lithium iron phosphate cathodes to delineate their beneficial role in formation and conditioning. We find that V-hold at the top of charge supplements constant current cycling in conditioning the cell to higher capacities for both Gr and Si cells after the first V-hold. A reduced order model provides the irreversible capacity proportions of each V-hold. With each repeat V-hold, parasitic loss of lithium to the solid electrolyte interphase (SEI) decreases on both Gr and Si cells. Gr cells show the square-root-of-time capacity loss behavior within 200 h of V-hold, indicative of its fast relaxation and low impact of reference performance test cycles on the SEI growth. Lifetime estimates from repeat V-holds on Gr can reach years. Si exhibits longer transition times from kinetic to diffusion-limited SEI growth, evidenced by the 400 h and 200 h holds showing square-root-of-time and linear behavior, respectively. Lifetime predictions from repeat V-holds on Si only reach 1–2 months, highlighting its limitations. Recommended duration of V-holds for Si cells should be ≥400 h.
Silicon (Si) is one of the most promising anode materials for the next generation lithium-ion batteries (LIBs). Although significant progresses have been made on the cycle life of Si-based LIBs, their calendar-life is still far less than those required for electrical vehicle applications. Here, in this work, the fundamental mechanisms behind the limited calendar life of Si-LIBs have been investigated. It is found that the unstable interphase layers formed on electrodes during the formation/cycling of batteries using conventional electrolyte with fluoroethylene carbonate (FEC) additive are responsible for the rapid impedance-increase of Si-LIBs during storage at elevated temperature (55°C). By using an FEC-free localized high concentration electrolyte (lithium bis(fluorosulfonyl)imide:ethyl propionate:ethylene carbonate:1,1,2,2-tetrafluoroethyl-2,2,3,3-tetrafluoropropyl ether (1:2.8:0.2:1 by mol.) with 1 wt.% lithium difluorophosphate), stable interphase layers formed on electrodes can effectively block the crosstalk between cathode and anode, minimize the impedance increase of Si||LiNi 0.6 Mn 0.2 Co 0.2 (NMC622) batteries during storage at elevated temperature (55°C), therefore largely improve their calendar life. Si||NMC622 batteries using this electrolyte also demonstrated a high-capacity retention of ~92.4% after 500 cycles at 45°C with well-preserved electrode structure. Hence, this novel electrolyte is a good candidate to extend the cycling life and calendar life of Si-LIBs.
The expansion of renewable technologies and electrification of the transportation sector is driving increased demand for next-generation battery materials that provide higher power and energy density with superior cycling and calendar life stability. Silicon (Si) has a theoretical capacity nearly 10x that of graphite, and is therefore a promising anode material candidate to meet these rigorous performance demands. While leading Si anode battery demonstrations are approaching target metrics for cycle life, a series of complex and interrelated modes of reactivity lead to reduced calendar life and therefore challenge practical adoption of these materials. Deconvoluting the degradation processes that impact Si calendar life is critical to informing the rational and accelerated design of improved Si materials. In the present work, we employ novel sampling techniques and GC-MS-FID characterization to measure gas-phase composition during initial Si cycling, which we tie to selective mechanisms of Si passivation. We utilize a tiered analysis approach to identify and quantify the gas-phase reaction products associated with three advanced Si material candidates under practical operating conditions. Ex situ analysis of Si powders (pure chemical reactivity) is coupled with nondestructive in situ sampling of Si electrodes in a practical pouch-cell format (coupled chemical and electrochemical reactivity). We link the observed gas-phase species evolution to electrochemical behavior and measured calendar life of the three Si materials. Further, we evaluate the voltage-resolved evolution of gas-phase species for one such Si nanomaterial, where nonmonotonic gas generation implies competition between passivating reaction pathways. The measured gas-phase compositional data serves as a critical input for our advanced electrochemical SEI models to identify favorable vs unfavorable reaction pathways to stabilize Si. In addition to bolstering a fundamental understanding of Si reactivity, the present approach informs specific and quantifiable gas-phase metrics tied to calendar life improvements in Si, which can streamline and accelerate the process of next-generation material development.
This study evaluates novel electrolytes tailored for Si-containing anodes to promote calendar-life. Drawing inspiration from advancements in electrolytes for Li-metal cells, the work investigates correlations between predicted electrolyte properties and measured electrochemical performance using several machine-learning models. By leveraging machine learning and advanced modeling techniques, this study aims to establish predictive frameworks that accelerate calendar-aging experiments and inform rational electrolyte design for Si-containing cells. In the present study, fifteen different electrolytes are evaluated in a Si-containing cell using an accelerated calendar-life protocol. For each electrolyte considered, 87 properties (features) from the Advanced Electrolyte Model were produced to identify key property/performance relationships. In this study, the best performing electrolytes were generally those formulations that included non-coordinating fluoroether solvents, and the most predictive features for long-term calendar-life were features related to salt concentration and electrolyte viscosity as well as early capacity, ionic conductivity, and Coulombic efficiency measurements. The framework developed in this study correlating electrolyte properties to measured electrochemical performance is expected to accelerate electrolyte design for Si-containing anodes and ultimately enable high-energy-density, long-life Li-ion batteries.
Silicon is widely recognized as the most promising upgrade for graphite anodes due to its much higher capacity, natural abundance, and ability to be directly applied in the slurry-based, roll-to-roll production lines. However, in addition to the fast capacity decay, silicon anodes also suffer from inferior calendar life in practical applications due to the unstable solid-electrode interface (SEI). Until now, strategies to effectively improve the calendar life by tailored SEIs remain largely unclear, especially in high-Si content, zero-graphite anodes. Here, silicon anodes with superior calendar life are developed by adding small concentrations of multivalent salts into the baseline electrolyte. The Ca additive reacts with the F ions in the electrolyte, forming a layer of nanocrystalline CaF 2 that is closely coated around the silicon particles. The CaF 2 -enabled new SEI is strong and dense, which effectively protects the silicon core from side reactions, leading to lower capacity decay after calendar aging at high voltage. More importantly, the Ca additive is effective universally for all available commercial silicon or SiO sources. This study provides a feasible and low-cost solution for developing silicon anodes with long calendar life, paving the way towards commercially viable silicon anodes.
This study will analyze calendar life aging performance of two 18650 lithium ion cell models deployed in human space flight applications. Test conditions of voltage and temperature were selected based on product application. The cell test campaign includes storage of a cell model produced in April 2007 and initial calendar life performance for a cell produced in December 2013. Mechanistic aging models will be considered. The results of this study are applicable to applications requiring extended low state of charge storage and low cycle life.
Silicon-based anodes promise an increase in energy density for Li-ion batteries, yet they suffer from a poor calendar life. Researchers have posited that fluorinated lithium salt forms reactive side products that destroy the solid electrolyte interphase (SEI), even without cycling. HF is one such reactive side product formed from trace water contamination in the electrolyte. Some electrolytes, such as localized high concentration electrolytes (LHCEs) may improve cell stability in highly reactive systems, such as Li metal and Si. In the present study, LHCEs containing 200-300 ppm of water retained up to 8% greater capacity (1200-1300 mAh/g Si) in calendar life tests over 200 days compared to dried electrolytes (< 20 ppm water). Calendar aging took place at 100% state of charge. Cells with 200-300 ppm water performed comparably to cells with 20 ppm water in cycle life tests (900-1000 mAh/g Si) . Even adding 1000 ppm water did not lead to rapid capacity fade in cells undergoing cycle life tests. Nano-FTIR spectroscopy revealed chemical and structural differences in the SEI for cells with 1000 ppm water compared to 200-300 ppm water. The SEI differences, including increased Li2O concentration, may have contributed to improved calendar life. This research reveals the capabilities of LHCEs to improve the calendar and cycle life of Si-based Li-ion batteries, despite the presence of a highly reactive contaminant.
Here, the widespread use of silicon (Si)-rich anodes in lithium-ion batteries (LIBs) is impeded by an unstable solid electrolyte interphase (SEI) incurring insufficient cell life. Fluoroethylene carbonate (FEC) additive in the electrolyte significantly improves cycle life. However, the gains on calendar life remain unclear; the SEI structure still undergoes detrimental alterations at rest. Thus, elucidating the SEI dynamics during calendar aging is critical to mitigating time-dependent capacity degradation. ATR-FTIR, XPS, and ToF-SIMS are used herein to investigate the SEI structure before and after calendar aging. Si cycled without FEC exhibits no notable SEI chemistry changes Pre- and Post-aging, leaving poor passivation as the main failure pathway. Conversely, the FEC-SEI starts as short oligomeric species from FEC/EC electroreduction prior to aging; after calendar aging, polymerized carbonates become consistently more prominent. Unexpectedly, the deposition of self-polymerized FEC species results from time exposure to the delithiated Si specifically as opposed to the lithiated surface. This unexpected finding is supported by another recent Si calendar-aging research, which albeit not investigating FEC, finds global failure of the SEI upon delithiation resulting in ∼247 fold more reactive surface compared to the lithiated.
Lithium metal batteries (LMBs) are prime candidates for next-generation energy storage devices characterized by their remarkable energy storage capabilities. Despite the importance of understating the calendar aging impacts in LMBs, cycle life and calendar life have received inconsistent attention across various research and development stages. For acceptance into an application, especially electric vehicles, batteries are required to have sufficient calendar life to ensure performance over the life of vehicles which often experience extended periods of inactivity. In this study, an in-depth exploration into the calendar aging of LMB (Li/ Li[Ni 0.8 Mn 0.1 Co 0.1 ]O 2 in pouch cell format) is conducted. Specifically, the impact of calendar aging factors, state-of-charge (SOC), temperature, pressure, and operating conditions (open-circuit voltage, OCV and constant voltage, CV) on the surface morphology and thickness change rate in lithium metal anode is investigated. Notably, the results show that storing LMB pouch cells at an OCV, 80 % SOC, 25 °C, and 10 psi external pressure leads to a <1% reduction in capacity over 18 months. The results also suggest routes which can be utilized in the future for accelerated aging without altering the primary degradation modes. The results also show an accelerated calendar aging at high temperatures (45 °C), 100 % SOC, and CV suggesting they may serve as key accelerated aging methods for future studies. During calendar aging, pressure mitigates dendrite growth and extends calendar life. In conclusion, the insights from this study reinforce the viability of LMBs as a compelling solution for addressing increased energy storage needs in real-world applications.
Robust, flexible, and reusable solid electrolyte interphases and a minimal lithium/electrolyte interface area endow lithium metal batteries with a long-term calendar life.
Lithium-ion batteries with silicon anodes promise high energy density but are limited by calendar lifetime. Reducing the long iteration time to obtain experimental results requires predicting calendar lifetime early in a cell's life. In this study, we demonstrate that lightweight machine learning models with feature engineering can provide calendar lifetime estimates from early electrochemical signals. After 1 month of electrochemical aging, the best models achieve 10% error in calendar-life prediction and can separate "bad" from "good" lifetime cells with a mean F1 score of 0.857. As battery systems exhibit inherent variability, four methods for uncertainty quantification are compared, and confidence intervals are demonstrated with an uncertainty of +-3.6 months in lifetime prediction. A feature importance analysis indicates that early patterns in voltage decay are the strongest indicators of calendar lifetime. Finally, this modeling approach has high error when generalizing to new electrode chemistries or testing conditions but with appropriately low confidence.
Lithium–sulfur (Li-S) batteries with high energy density and low cost are promising for next-generation energy storage. However, their cycling stability is plagued by the high solubility of lithium polysulfide (LiPS) intermediates, causing fast capacity decay and severe self-discharge. Exploring electrolytes with low LiPS solubility has shown promising results toward addressing these challenges. However, here, we report that electrolytes with moderate LiPS solubility are more effective for simultaneously limiting the shuttling effect and achieving good Li-S reaction kinetics. We explored a range of solubility from 37 to 1,100 mM (based on S atom, [S]) and found that a moderate solubility from 50 to 200 mM [S] performed the best. Using a series of electrolyte solvents with various degrees of fluorination, we formulated the S ingle- S olvent, S ingle- S alt, S tandard S alt concentration with M oderate L i PSs so l ubility E lectrolytes (termed S 6 MILE ) for Li-S batteries. Among the designed electrolytes, Li-S cells using fluorinated-1,2-diethoxyethane S 6 MILE (F4DEE-S 6 MILE) showed the highest capacity of 1,160 mAh g −1 at 0.05 C at room temperature. At 60 °C, fluorinated-1,4-dimethoxybutane S 6 MILE (F4DMB-S 6 MILE) gave the highest capacity of 1,526 mAh g −1 at 0.05 C and an average CE of 99.89% for 150 cycles at 0.2 C under lean electrolyte conditions. This is a fivefold increase in cycle life compared with other conventional ether-based electrolytes. Moreover, we observed a long calendar aging life, with a capacity increase/recovery of 4.3% after resting for 30 d using F4DMB-S 6 MILE. Furthermore, the correlation between LiPS solubility, degree of fluorination of the electrolyte solvent, and battery performance was systematically investigated.
Silicon is a promising candidate as a next generation anode to replace or complement graphite electrodes due to its high energy density and low lithiation potential. When silicon is lithiated, it experiences over 300% expansion which stresses the silicon as well as its solid electrolyte interphase (SEI) leading to poor performance. The use of nano-sized silicon has helped to mitigate volume expansion and stress in the silicon, yet the silicon SEI is still both mechanically and chemically unstable. Identifying the mechanical failure mechanism of the SEI will help enhance calendar and cycle life performance through improved SEI design. In situ moiré interferometry was investigated to try and track the in-plane strain in the SEI and silicon electrode for this purpose. Moiré can detect on the order of 10 nm changes in displacement and is therefore a useful tool in the measurement of strain. As the sample undergoes small deformations, large changes in the moiré fringe allow for measurements of displacement below the diffraction limit of light. Figure 1a shows how the moiré fringe changes as the sample grating deforms. As the sample contracts or expands, the frequency of the moiré fringe changes, and this change is proportional to the strain in the sample.
Silicon (Si) is a promising high-capacity anode in lithium-ion batteries but suffers from chronic chemical degradation and capacity fading during calendar aging, greatly hindering its automobile applications. Electrolyte engineering currently relies on conventional evaluation criteria of reducing coulombic consumption, which implicitly presume its equivalence to irreversible capacity loss and complicates battery development. Here, we introduce the detrimental ratio p to quantify the fraction of parasitic species that permanently degrades active material. This metric is independent and crucially complements total coulombic consumption for accurate performance evaluation. We systematically investigate multiple electrolyte formulations using high-precision leakage current measurements, open-circuit-voltage experiments, and post-mortem characterizations. Although some electrolytes exhibit similarly low coulombic consumption, they diverge significantly incapacity retention and p. Especially, dimethyl-carbonate-based localized-high concentration electrolyte can synergically achieve low coulombic consumption and detrimental ratio p during calendar aging, owing to its chemically inert and structurally resilient solidelectrolyte interface with minimal isolated Si material. By contrast, increasing fluoroethylene carbonate (FEC) additive content suppresses electrolyte breakdown but suffers aggravated chemical degradation of more LixSi isolation for irreversible capacity loss with arising p. This study critically reveals that the chemistry-characteristic detrimental ratio p establishes physically informed performance evaluation to pave the way for accelerating battery development.
Not Available
Over the past decades, Lithium-ion batteries have seen extensive improvements, and as a result are now the primary choice in many applications for their power, energy, and durability. In recent years, battery cost has reduced by orders of magnitude through adoption of new materials and processes. Despite these advances, interfaces in these battery systems are yet to be fully understood. This is seen as a major limitation to further increase cycle life, calendar life, abuse tolerance, and performances. A major obstacle is a lack of comprehensive understanding of the complex dynamic chemical processes occurring at the electrolyte/electrode interface. In this context, vibrational sum frequency generation (vSFG) spectroscopy possesses the unique capability of probing a molecularly thin interfacial layer to obtain molecular-level information through nonlinear optical interaction. Probing the molecular level processes at the interfaces using such a versatile technique would be a game changer in the advancement of current battery research knowledge. This review article summarizes recent vSFG studies on the electrolyte/electrode interface of various electrode materials and nonaqueous electrolytes for LIBs and discusses future research perspectives. Finally, overall, this focused review highlights the advantages and versatility of vSFG that can be used to further advance present-day battery research.
Lithium hexafluorophosphate (LiPF 6 )-based carbonate electrolytes are widely used in commercial lithium-ion batteries (LIBs), but their thermal instability limits the cycle life and safety of LIBs at elevated temperatures. Few studies have yielded insight into the initial PF 6 — decomposition reaction that promotes thermal instability of LiPF6-based electrolytes. Here, we find that lithium-ion hopping assisted by the overall reorientational motion of propylene carbonate molecules facilitates PF 6 — decomposition at elevated temperatures in 1 M LiPF 6 /propylene carbonate electrolyte. Further, we demonstrate that urea additives, by preventing lithium-ion hopping, suppress the initial LiPF 6 decomposition reaction and enhance the thermal stability of the electrolyte. LIB cell tests with LiNi 0.6 Mn 0.2 Co 0.2 O 2 ||Li 4 Ti 5 O 12 show improved LIB performance at elevated temperatures with the thermally stabilized electrolyte. This study provides key insights into the design of thermally stable LiPF 6 -based carbonate electrolytes for improving the cycle life, calendar life, and safety of LIBs in elevated-temperature applications.