Failure modes and damage accumulation in laminated composites with free edges

The influence of fiber orientation, stacking sequence, material properties and edge effects on the accumulation of damage and modes of failure in angle-ply and quasi-isotropic composite laminates are studied. Experimental results are presented for graphite-epoxy and graphite-polyimide coupons subjected to tensile load. It is shown that all the parameters studied can have a significant influence on the behavior of the composite.

Herakovich, Carl T.↗

An advanced test technique to quantify thermomechanical fatigue damage accumulation in composite materials

A mechanical test technique was developed to assist in quantifying the accumulation of damage in composite materials during thermomechanical fatigue (TMF) cycling. This was accomplished by incorporating definitive elastic mechanical property measurements into an ongoing load-controlled TMF test without disturbing the test specimen or significantly altering the test conditions. The technique allows two fundamental composite properties consisting of the isothermal elastic static moduli and the macroscopic coefficient of thermal expansion (CTE) to be measured and collected as functions of the TMF cycles. The specific implementation was incorporated into the commonly employed idealized in-phase and out-of-phase TMF cycles. However, the techniques discussed could be easily implemented into any form of load-controlled TMF mission cycle. By quantifying the degradations of these properties, tremendous insights are gained concerning the progression of macroscopic composite damage and often times the progression of damage within a given constituent. This information should also be useful for the characterization and essential for the verification of analytical damage modeling methodologies. Several examples utilizing this test technique are given for three different fiber lay-ups of titanium metal matrix composites.

Castelli, Michael G.↗

Microscale Characterization of Damage Accumulation in CMCs

The developing roles of damage mechanisms in the failure response of SiC/SiC minicomposites was investigated by the characterization of microscale damage accumulation with respect to microstructure. A multi-modal approach combining spatially resolved acoustic emission (AE) with tensile testing in-SEM (scanning electron microscope) was used to simultaneously examine surface (observed in-SEM) and bulk damage (monitored via AE). Strong agreement was shown between the evolving crack density estimated by AE and in-SEM measurements. The following were observed: (i) in-plane matrix content and distribution impacted crack growth; (ii) spatially-distributed matrix cracks generated varying stress-dependent AE; and (iii) certain individual cracks became more probable failure locations due to unique combinations of damage mechanisms that drove their growth. This approach enabled characterizing potential failure determinants and suggests that early damage behavior is related to certain microstructural features (e.g. surface flaws), while subsequent damage behavior is coupled to interactions of local mechanisms evolving with stress.

ceramic matrix composites↗

Acoustic Emission and Damage Accumulation for Various Woven C/SiC Composites Tested in Tension at Room Temperature

Modal acoustic emission (AE) has proven to be an excellent technique to monitor damage accumulation in ceramic matrix composites. In this study, AE was used to monitor tensile load-unload-reload hysteresis tests for a variety of C fiber reinforced, SiC matrix composites. C/SiC composites were reinforced with T300 and IM7 fibers, had C, multilayer, or pseudo-porous C interphases, and had chemical vapor infiltrated SiC or melt-infiltrated SiC matrices. All of the composites exhibited considerable AE during testing. The extent and nature of the AE activity will be analyzed and discussed in light of matrix cracking and the variety of composite constituents. It is hoped that understanding the nature of stress dependent damage accumulation in these materials can be of use in life modeling for these types of composites.

Morscher, Gregory N.↗

Acoustic Emission and Damage Accumulation for Various Woven C/SiC Composites Tested in Tension at Room Temperature

Modal acoustic emission (AE) has proven to be an excellent technique to monitor damage accumulation in ceramic matrix composites. In this study, AE was used to monitor tensile load-unload-reload hysteresis tests for a variety of C fiber reinforced, Sic matrix composites. C/SiC composites were reinforced with T-300 and IM7 fibers, had C, multilayer, or pseudo-porous C interphases, and had chemical vapor infiltrated Sic or melt-infiltrated SiC matrices. All of the composites exhibited considerable AE during testing. The extent and nature of the AE activity will be analyzed and discussed in light of matrix cracking and the variety of composite constituents. It is hoped that understanding the nature of stress-dependent damage accumulation in these materials can be of use in life-modeling for these types of composites.

Morscher, Gregory↗

Modal Acoustic Emission of Damage Accumulation in Woven SiC/SiC at Elevated Temperatures

Ceramic matrix composites exhibit significant nonlinear stress-strain behavior that makes them attractive as potential materials for many high temperature applications. The mechanisms for this nonlinear stress-strain behavior are all associated with various types of damage in the composites, e.g. transverse matrix cracks and individual fiber failures. Modal acoustic emission has been employed to aid in discerning the damage accumulation that occurs during elevated temperature tensile stress-rupture of woven Hi-Nicalon fiber, BN interphase, SiC matrix composites. It is shown that modal acoustic emission is an effective monitor of the relative damage accumulation in the composites and locator of the damage and failure events as a function of strain (stress), time at temperature, and temperature gradients along the length of the elevated temperature test specimen.

Morscher, G. N.↗

X ray attenuation measurements for high-temperature materials characterization and in-situ monitoring of damage accumulation

The scope of this dissertation is to develop and apply x ray attenuation measurement systems that are capable of: (1) characterizing density variations in high-temperature materials, e.g., monolithic ceramics, ceramic and intermetallic matrix composites, and (2) noninvasively monitoring damage accumulation and failure sequences in ceramic matrix composites under room temperature tensile testing. This dissertation results in the development of: (1) a point scan digital radiography system, and (2) an in-situ x ray material testing system. Radiographic evaluation before, during, and after loading shows the effect of preexisting volume flaws on the fracture behavior of composites. Results show that x ray film radiography can monitor damage accumulation during tensile loading. Matrix cracking, fiber matrix debonding, fiber bridging, and fiber pullout are imaged throughout the tensile loading of the specimens. Further in-situ radiography is found to be a practical technique for estimating interfacial shear strength between the silicon carbide fibers and the reaction bonded silicon nitride matrix. It is concluded that pretest, in-situ, and post test x ray imaging can provide for greater understanding of ceramic matrix composite mechanical behavior.

Baaklini, George Y.↗

Damage Accumulation in SiC/SiC Composites with 3D Architectures

The formation and propagation of multiple matrix cracks in relatively dense ceramic matrix composites when subjected to increasing tensile stress is necessary for high strength and tough composites. However, the occurrence of matrix cracks at low stresses may limit the usefulness of some non-oxide composite systems when subjected to oxidizing environments for long times at stresses sufficient to cause matrix cracking. For SiC fiber-reinforced composites with two-dimensional woven architectures and chemically vapor infiltrated (CVI) SiC matrix and melt-infiltrated (MI) Si/SiC matrix composites, the matrix cracking behavior has been fairly well characterized for different fiber-types and woven architectures. It was found that the occurrence, degree, and growth of matrix cracks depends on the material properties of the composite constituents as well as other physical properties of the composite or architecture, e.g., matrix porosity and size of the fiber bundle. In this study, matrix cracking in SiC fiber reinforced, melt-infiltrated SiC composites with a 3D orthogonal architecture was determined for specimens tested in tension at room temperature. Acoustic emission (AE) was used to monitor the matrix cracking activity, which was later confirmed by microscopic examination of specimens that had failed. The determination of the exact location of AE demonstrated that initial cracking occurred in the matrix rich regions when a large z-direction fiber bundle was used. For specimens with large z-direction fiber tows, the earliest matrix cracking could occur at half the stress for standard 2D woven composites with similar constituents. Damage accumulation in 3D architecture composites will be compared to damage accumulation in 2D architecture composites and discussed with respect to modeling composite stress-strain behavior and use of these composites at elevated temperatures.

Morscher, Gregory N.↗

Fatigue damage accumulation in nickel prior to crack initiation

The accumulation of lattice defects during fatigue cycling of nickel was investigated by electrical resistivity measurements, positron annihilation lifetime spectroscopy and transmission electron microscopy. Dislocations and vacancy clusters were found to be the main defect types. During cycling of axial and flexural samples at constant load amplitude, the dislocations form a saturated structure early in the fatigue life. This saturated structure consists of a cellular dislocation matrix, in which persistent slip bands (PSBs) begin to operate after the saturation has been established. Vacancies and vacancy clusters are formed during fatigue as a consequence of repetitive dislocation glide in the PSB structure. When PSBs operate, the matrix is assumed to be dormant, allowing vacancies to accumulate preferentially in the PSBs. The increase in vacancy concentration then accounts for the monotonic accumulation of fatigue damage, which points to the importance of vacancy accumulation as a precursor to crack nucleation.

Grobstein, T. L.↗

Evaluation of Fatigue Damage Accumulation Functions for Delamination Initiation and Propagation

The present report follows on the cohesive fatigue damage model methodology proposed in NASA-TP-2018-219838. In that report, an empirical function describing the incremental damage due to cyclic loading was used to calculate fatigue damage within a cohesive formulation. The form of the function was developed such that, when integrated at a constant stress amplitude from no damage to failure, it produces a life versus load response that is consistent with an S-N diagram. Therefore, the parameters of the damage model could be obtained by fitting the model predictions to an S-N diagram. The finite element analyses performed demonstrate that the cohesive fatigue accumulation function provides a link between the S-N diagram that describes crack initiation, and the Paris law that characterizes the rate of crack propagation. However, when the model was proposed, it was not known whether the form of the damage accumulation function associated with a desired S-N diagram is unique and, if not, if the link between S-N and the Paris law is unique and independent of the fatigue function selected. In the effort described herein, several alternative forms of the damage function that reproduce the desired features of S-N diagrams were found and evaluated. The effects of each of these functions on the predicted parameters of the Paris law and the propagation threshold are discussed. The results indicate that the predicted exponent m of the Paris law is indeed independent of the damage accumulation function. However, different functions predict different values for the pre-factor C of the Paris law. Therefore, the proper damage accumulation function must be selected by comparison with experiments. One of the new damage accumulation functions proposed herein was found to be particularly useful for analysis because of the ease with which the model parameters can be determined with a minimal amount of experimental information. The effectiveness of the proposed methodology and damage function was demonstrated by conducting analyses of a double cantilever beam test, a mixed-mode bending test, and a three-point bending test of a skin/doubler specimen. The results indicate that the same set of model parameters can provide accurate predictions of the rate of fatigue crack propagation for a variety of material interfaces, mode mixities, load levels, and stress ratios.

Cohesive elements↗

Life prediction modeling based on cyclic damage accumulation

A high temperature, low cycle fatigue life prediction method was developed. This method, Cyclic Damage Accumulation (CDA), was developed for use in predicting the crack initiation lifetime of gas turbine engine materials, where initiation was defined as a 0.030 inch surface length crack. A principal engineering feature of the CDA method is the minimum data base required for implementation. Model constants can be evaluated through a few simple specimen tests such as monotonic loading and rapic cycle fatigue. The method was expanded to account for the effects on creep-fatigue life of complex loadings such as thermomechanical fatigue, hold periods, waveshapes, mean stresses, multiaxiality, cumulative damage, coatings, and environmental attack. A significant data base was generated on the behavior of the cast nickel-base superalloy B1900+Hf, including hundreds of specimen tests under such loading conditions. This information is being used to refine and extend the CDA life prediction model, which is now nearing completion. The model is also being verified using additional specimen tests on wrought INCO 718, and the final version of the model is expected to be adaptable to most any high-temperature alloy. The model is currently available in the form of equations and related constants. A proposed contract addition will make the model available in the near future in the form of a computer code to potential users.

Nelson, Richard S.↗

Application of cyclic damage accumulation life prediction model to high temperature components

A high temperature, low cycle fatigue life prediction method was developed. This method, Cyclic Damage Accumulation (CDA), was developed for use in predicting the crack initiation lifetime of gas turbine engine materials, but it can be applied to other materials as well. The method is designed to account for the effects on creep-fatigue life of complex loading such as thermomechanical fatigue, hold periods, waveshapes, mean stresses, multiaxiality, cumulative damage, coatings, and environmental attack. Several features of this model were developed to make it practical for application to actual component analysis, such as the ability to handle nonisothermal loading (including TMF), arbitrary cycle paths, and multiple damage modes. The CDA life prediction model was derived from extensive specimen tests conducted on cast nickel-base superalloy B1900 + Hf. These included both monotonic tests (tensile and creep) and strain-controlled fatigue experiments (uniaxial, biaxial, TMF, mixed creep-fatigue, and controlled mean stress). Additional specimen tests were conducted on wrought INCO 718 to verify the applicability of the final CDA model to other high-temperature alloys. The model will be available to potential users in the near future in the form of a FORTRAN-77 computer program.

Nelson, Richard S.↗

Isothermal Fatigue, Damage Accumulation, and Life Prediction of a Woven PMC

This dissertation focuses on the characterization of the fully reversed fatigue behavior exhibited by a carbon fiber/polyimide resin, woven laminate at room and elevated temperatures. Nondestructive video edge view microscopy and destructive sectioning techniques were used to study the microscopic damage mechanisms that evolved. The residual elastic stiffness was monitored and recorded throughout the fatigue life of the coupon. In addition, residual compressive strength tests were conducted on fatigue coupons with various degrees of damage as quantified by stiffness reduction. Experimental results indicated that the monotonic tensile properties were only minimally influenced by temperature, while the monotonic compressive and fully reversed fatigue properties displayed noticeable reductions due to the elevated temperature. The stiffness degradation, as a function of cycles, consisted of three stages; a short-lived high degradation period, a constant degradation rate segment composing the majority of the life, and a final stage demonstrating an increasing rate of degradation up to failure. Concerning the residual compressive strength tests at room and elevated temperatures, the elevated temperature coupons appeared much more sensitive to damage. At elevated temperatures, coupons experienced a much larger loss in compressive strength when compared to room temperature coupons with equivalent damage. The fatigue damage accumulation law proposed for the model incorporates a scalar representation for damage, but admits a multiaxial, anisotropic evolutionary law. The model predicts the current damage (as quantified by residual stiffness) and remnant life of a composite that has undergone a known load at temperature. The damage/life model is dependent on the applied multiaxial stress state as well as temperature. Comparisons between the model and data showed good predictive capabilities concerning stiffness degradation and cycles to failure.

Gyekenyesi, Andrew L.↗

Use of Acoustic Emission to Monitor Progressive Damage Accumulation in Kevlar (R) 49 Composites

Acoustic emission (AE) data acquired during intermittent load hold tensile testing of epoxy impregnated Kevlar(Registeres TradeMark) 49 (K/Ep) composite strands were analyzed to monitor progressive damage during the approach to tensile failure. Insight into the progressive damage of K/Ep strands was gained by monitoring AE event rate and energy. Source location based on energy attenuation and arrival time data was used to discern between significant AE attributable to microstructural damage and spurious AE attributable to noise. One of the significant findings was the observation of increasing violation of the Kaiser effect (Felicity ratio < 1.0) with damage accumulation. The efficacy of three different intermittent load hold stress schedules that allowed the Felicity ratio to be determined analytically is discussed.

Waller, Jess M.↗

Three dimensional finite element analysis of damage accumulation in composite laminate

A three dimensional finite-element computer program has been developed to analyze layered fiber-reinforced composite laminate. This program is capable of: (1) calculating the detailed stress distribution, (2) identifying the damage zone and mode of failure, (3) analyzing the damage accumulation, and (4) determining the ultimate strength of the composite laminate.

Lee, J. D.↗

Room Temperature Tensile Behavior and Damage Accumulation of Hi-Nicalon Reinforced SiC Matrix Composites

Composites consisting of woven Hi-Nicalon fibers, BN interphases, and different SiC matrices were studied in tension at room temperature. Composites with SiC matrices processed by CVI and melt infiltration were compared. Monotonic and load/unload/reload tensile hysteresis experiments were performed. A modal acoustic emission (AE) analyzer was used to monitor damage accumulation during the tensile test. Post test polishing of the tensile gage sections was performed to determine the extent of cracking. The occurrence and location of cracking could easily be determined using modal AE. The loss of modulus could also effectively be determined from the change in the velocity of sound across the sample. Finally, the stresses where cracks appear to intersect the load-bearing fibers correspond with high temperature low cycle fatigue run out stresses for these materials.

Morscher, G. N.↗

In-situ x-ray monitoring of damage accumulation in SiC/RBSN tensile specimens

The room-temperature tensile testing of silicon carbide fiber reinforced reaction-bonded silicon nitride (SiC/RBSN) composite specimens was monitored by using in-situ x ray film radiography. Radiographic evaluation before, during, and after loading provided data on the effect of preexisting volume flaws (high density impurities, and local density variations) on the fracture behavior of composites. Results from (0)1, (0)3, (0)5, and (0)8 composite specimens, showed that x ray film radiography can monitor damage accumulations during tensile loading. Matrix cracking, fiber-matrix debonding, and fiber pullout were imaged throughout the tensile loading history of the specimens. Further, in-situ film radiography was found to be a helpful and practical technique for estimating interfacial shear strength between the SiC fiber and the RBSN matrix by the matrix crack spacing method. It is concluded that pretest, in-situ, and post-test radiography can provide for a greater understanding of ceramic matrix composite mechanical behavior, a verification of related experimental procedures, and a validation and development of related analytical models.

Baaklini, George Y.↗

In situ X-ray monitoring of damage accumulation in SiC/RBSN tensile specimens

The room-temperature tensile testing of silicon carbide fiber reinforced reaction-bonded silicon nitride (SiC/RBSN) composite specimens was monitored by using in-situ X-ray film radiography. Radiographic evaluation before, during, and after loading provided data on the effect of preexisting volume flaws (high density impurities, and local density variations) on the fracture behavior of composites. Results from (O)1, (O)3, (O)5, and (O)8 composite specimens showed that X-ray film radiography can monitor damage accumulations during tensile loading. Matrix cracking, fiber-matrix debonding, and fiber pullout were imaged throughout the tensile loading history of the specimens. Further, in-situ film radiography was found to be a helpful and practical technique for estimating interfacial shear strength between the SiC fiber and the RBSN matrix by the matrix crack spacing method. It is concluded that pretest, in-situ, and post-test radiography can provide for a greater understanding of ceramic matrix composite mechanical behavior, a verification of related experimental procedures, and a validation and development of related analytical models.

Baaklini, George Y.↗