DOE OSTI2022

Behavior of helium cavities in ion-irradiated W-Ni-Fe ductile-phase toughened tungsten

This study reports on the distribution of helium (He) cavities in a hot-rolled W-Ni-Fe ductile-phase toughened tungsten (DPT W) composite irradiated to a dose and a helium concentration that are comparable to those in the material after 5-year irradiation in a conceptual fusion power plant. Here, the DPT W sample consists of W particles embedded in a ductile-phase NiFeW matrix with a nominal composition of 90W-7Ni-3Fe by weight. It was hot-rolled to a thickness reduction by 87% (87R DPT W). Sequential irradiation of the material with 1.2 MeV Ni + ions to a fluence of 2.15×10 16 Ni + /cm 2 and 90 keV He + ions to 6.5×10 15 He + /cm 2 was performed at 973 K. Larger He cavities with a lower number density are observed in NiFeW than W. Helium cavities are aggregated preferentially along the NiFeW/W interphase boundary. This behavior is not observed along the W/W grain boundary under the same irradiation conditions. A similar distribution of He cavities with comparable sizes is observed in 87R DPT W irradiated with He + ions only, suggesting that the He cavity distribution is not significantly affected by pre-irradiation of Ni + ions at 973 K. The data from this study does not provide any evidence for formation of visible voids or Ni precipitates in W phase irradiated with Ni + ions only. Diffusion and clustering of He atoms and mobile vacancies during ion irradiation at 973 K are responsible for the formation and growth of the He cavities.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Tailoring ductile-phase toughened tungsten hierarchical microstructures for plasma-facing materials

Biological materials, such as bones, nacre, etc., have been found to show attractive and unique combinations of stiffness, strength and fracture toughness. Research has been conducted in various engineering areas to mimic the naturally hierarchical microstructures or nanostructures of these materials to produce materials with optimum stiffness, high strength and fracture toughness for their intended structural applications. In the same objective, this work applies a multiscale microstructural approach recently developed to investigate the deformation and fracture behavior of ductile phase toughened tungsten (W) materials such as tungsten-nickel/iron (W-Ni/Fe) composites that possess lamellar-like and hierarchical “brick-and-mortar” (BAM) microstructures. First, the approach is used to simulate tensile loading of W-Ni/Fe specimens cut out from hot-rolled W-Ni/Fe plates which possess lamellar-like microstructures. The finite element model of the gage section of the specimen consists of a W-Ni/Fe dual-phase microstructural domain in which the constitutive behaviors of W and Ni/Fe phases are described by an elastic-plastic damage model. The predicted material stress-strain response and crack pattern development as a function of loading are then compared to the corresponding experimental results to determine the constitutive model parameters for W and Ni/Fe. Subsequently, the model parameters are used to analyze W-Ni/Fe BAM microstructures that are artificially created to investigate the effects of microstructural features and morphologies on the composite stress-strain response, damage, and fracture patterns. The modeling shows that regular BAM microstructures that experience bridging mechanism combined with crack penetration across W-phase regions exhibit significantly higher strengths than the rather random lamellar-like microstructures. More significantly, however adjusting the brick’s length-to-height ratio, the BAM microstructure can be designed to allow a more distributed damage zone which leads to increased strength, ductility and fracture energy.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Temperature effects of ion irradiation on the nanostructural features in ductile-phase-toughened tungsten composites

Ductile-phase toughened tungsten (DPT W) composites have emerged as promising candidates for load-bearing components behind the plasma-facing tungsten armor in fusion reactors due to their enhanced thermomechanical properties. This study focuses on a composite consisting of W particles embedded in a ductile NiFeW solution matrix, hot-rolled to a thickness reduction of 87% (87R DPT W). Sequential irradiations with Ni2+ and He+ ions were performed to identical doses and helium concentrations at room temperature (RT) and 1273 K. Irradiation at RT produced no discernible nanostructural features due to the immobility of mono-vacancies, whereas cavity formation was observed at 973 K. At 1273 K, the W phase exhibited larger cavities, reduced cavity number density, and lower volumetric swelling compared to 973 K. Notably, nanosized NiFeW precipitates formed within the W phase at 1273 K, a phenomenon absent at 973 K. A new phase of cubic (NiFe)6W6C was also observed at the interphase boundary. In contrast, the NiFeW matrix showed no nanostructural changes at 1273 K, likely due to cavity dissociation. Separate irradiations at 1273 K indicated that Ni2+ ions induced precipitate formation in the W phase, while He+ ions exclusively caused cavity formation. The microstructure of 87R DPT W irradiated at RT and subsequently annealed at 1273 K closely resembled that of material irradiated directly at 1273 K. Like oxide-dispersion-strengthened steels, the observed nanoparticle-embedded W can inhibit dislocation propagation, potentially delaying the ductile-to-brittle transition temperature. These findings highlight the potential of NiFeW nanoparticle-reinforced W composites as irradiation-resistant materials for fusion reactors.

Jiang, Weilin (ORCID:0000000183028313)↗
DOE OSTI2023

Behavior and properties of helium cavities in ductile-phase-toughened tungsten irradiated with He + ions at an elevated temperature

Ductile-phase toughened tungsten (DPT W) composites have demonstrated a great potential for plasma-facing components in fusion power systems. These materials can retain the outstanding thermomechanical properties of W while significantly enhancing the fracture toughness. The DPT W composite in this study consists of W particles (88 wt.%) embedded in a ductile NiFeW (12 wt.%) solution matrix. Irradiation of the composite was performed with 90 keV He + ions to 1.0 × 10 17 He + /cm 2 at 973 K. The He cavities formed in both W and NiFeW phases are examined using convergent-beam scanning transmission electron microscopy (CB-STEM) at an atomic-level resolution. Full-range depth profiles of the He cavity diameters and number densities are analyzed. The results show that the average cavity diameter in NiFeW is ~2.7 times that in W, while the number density is an order of magnitude lower. A quantitative analysis of the He density and pressure in the cavities is also achieved using STEM electron energy loss spectroscopy (STEM-EELS) mapping. The He atoms in the cavities in NiFeW are found to be under-pressurized, while those in similar-sized cavities in W are not detectable. Further, the He energy-loss shift exhibits a linear relationship with the He density in cavities in NiFeW, with the slope comparable to that for martensitic steel.

36 MATERIALS SCIENCE↗
NASA NTRS1990

Intermetallic matrix composites; Proceedings of the MRS Symposium, San Francisco, CA, Apr. 18-20, 1990

The present volume on intermetallic matrix composites discusses the modeling, processing, microstructure/property relationships, and compatibility of intermetallic matrix composites. Attention is given to models for the strength of ductile matrix composites, innovative processing techniques for intermetallic matrix composites, ductile phase toughening of brittle intermetallics, and reactive synthesis of NbAl3 matrix composites. Topics addressed include solidification processing of NbCr2 alloys, Ta and Nb reinforced MoSi2, the microstructure and mechanical behavior of Ni3Al-matrix composites, and ductile-phase toughening of Cr3Si with chromium. Also discussed are dislocation morphologies in TiB2/NiAl, the development of highly impact resistant NiAl matrix composites, the effect of notches on the fatigue life of the SCS-6Ti3Al composite, and the chemical stability of fiber-metal matrix composites.

Anton, D. L.↗