NASA NTRS1954

Relation Between Roughness of Interface and Adherence of Porcelain Enamel to Steel

Porcelain-enamel ground coats were prepared and applied under conditions that gave various degrees of adherence between enamel and a low-carbon steel (enameling iron). The variations in adherence were produced by (a) varying the amount of cobalt-oxide addition in the frit, (b) varying the type of metallic-oxide addition in the frit, keeping the amount constant at 0.8 weight percent, (c) varying the surface treatment of the metal before application of the enamel, by pickling, sandblasting, and polishing, and (d) varying the time of firing of the enamel containing 0.8 percent of cobalt oxide. Specimens of each enamel were given the standard adherence test of the Porcelain Enamel Institute. Metallographic sections were made on which the roughness of interface was evaluated by counting the number of anchor points (undercuts) per centimeter of specimen length and also by measuring the length of the interface and expressing results as the ratio of this length to the length of a straight line parallel to the over-all direction of the interface.

Richmond, J C↗
NASA NTRS1973

Development of porcelain enamel passive thermal control coatings

A white porcelain enamel coating was developed for application to high temperature metallic alloy substrates on spacecraft. The coating consists of an optically opacifying zirconia pigment, a lithia-zirconia-silica frit, and an inorganic pigment dispersant. The coating is fired at 1000 to 1150 C to form the enamel. The coating has a solar absorptance of 0.22 and a total normal emittance of 0.82 for a 0.017 cm thick coating. The coating exhibits excellent adhesion, cleanability, and integrity and is thermal shock resistant to 900 C. Capability to coat large panels has been demonstrated by successful coating of 30 cm x 30 cm Hastelloy X alloy panels. Preliminary development of low temperature enamels for application to aluminum and titanium alloy substrates was initiated. It was determined that both leaded and leadless frits were feasible when applied with appropriate mill fluxes. Indications were that opacification could be achieved at firing temperatures below 540 C for extended periods of time.

Levin, H.↗
NASA NTRS1987

Practical significance and calculation of surface tension of glass, enamels and glazes

Surface tension is important in the formation of streaks in the whole procedure of enameling and glazing., in the action of TiO2 as opacifier, in the addition of borax to enamels, or metals to glasses, and in the corrosion of refractories by molten charges. By the use of known methods for measuring surface tension additive constants are found which give correct results within 1% with no discrepancy due to B2O3.

Dietzel, A.↗
NASA NTRS1966

Copper-acrylic enamel serves as lubricant for cold drawing of refractory metals

Acrylic enamel spray containing metallic copper pigment lubricates refractory metal tubing during cold drawing operations so that the tubing surface remains free from scratches and nicks and does not seize in the die. Zirconium alloys, zirconium, tantalum alloys, niobium alloys, vanandium alloys and titanium alloys have been drawn using this lubricant.

Beane, C.↗
NASA NTRS1977

Enamel for high-temperature superalloys

Desired optical and high temperature enamel properties are obtained with glasses prepared from the system Li2O-ZrO2-nSiO2. Molar compositions range from n=4 to n=1.3, to which are added minor amounts in varying combinations of alumina, alkali fluorides, boric oxide, alkali oxides, and akaline earth oxides.

Levin, H.↗
NASA NTRS1978

Porcelain enamel passive thermal control coatings

This paper discusses the development and evaluation of a highly adherent, low solar absorptance, porcelain enamel thermal control coating applied to 6061 and 1100 aluminum for space vehicle use. The coating consists of a low index of refraction, transparent host frit and a high volume fraction of titania as rutile, crystallized in-situ, as the scattering medium. Solar absorptance is 0.21 at a coating thickness of 0.013 cm. Hemispherical emittance is 0.88. The change in solar absorptance is 0.03, as measured in-situ, after an exposure of 1000 equivalent sun hours in vacuum.

Leggett, H.↗
NASA NTRS1974

New tooth enamel from brushite crystals

Appropriate nutrient gel solution could be used to precipitate brushite, which becomes hydroxyapatite, mineral found in bones and teeth. Gel can be made from sodium metasilicate and phosphoric acid, or gelatin, or other organic materials that polymerize in presence of acid to get gelantinous medium.

Rubin, B.↗
NASA NTRS1981

Method for applying photographic resists to otherwise incompatible substrates

A method for applying photographic resists to otherwise incompatible substrates, such as a baking enamel paint surface, is described wherein the uncured enamel paint surface is coated with a non-curing lacquer which is, in turn, coated with a partially cured lacquer. The non-curing lacquer adheres to the enamel and a photo resist material satisfactorily adheres to the partially cured lacquer. Once normal photo etching techniques are employed the lacquer coats can be easily removed from the enamel leaving the photo etched image. In the case of edge lighted instrument panels, a coat of uncured enamel is placed over the cured enamel followed by the lacquer coats and the photo resists which is exposed and developed. Once the etched uncured enamel is cured, the lacquer coats are removed leaving an etched panel.

Fuhr, W.↗
NASA NTRS1974

Survey of coatings for solar collectors

Ceramic enamel is found to be more solar selective, (i.e., has high solar absorptance in combination with low infrared emittance) than organic enamel, but neither is as solar selective as black chrome, black copper, black zinc, or black nickel. Ceramic enamel is matched only by black chrome in durability and wide availability. Ceramic enamel and organic enamel have approximately the same cost, and both are currently slightly lower in cost than black chrome, black copper, or black zinc. Black nickel is relatively unavailable and, because of that, realistic cost comparisons are not possible.

Mcdonald, G. E.↗