Interesting facts about graphite. Graphite within HTRs and how long they will last, potential issues prediction, model building to predict expected behavior, and frequent and thorough inspection and monitoring strategy.
Achieving precise control over crack propagation in nuclear graphite and conducting quantitative analysis remain challenging. In this study, the through-thickness fracture behavior of pristine and neutron-irradiated (700 °C, ∼7 dpa) NBG-17 nuclear graphite was investigated using split-disc testing coupled with micro-computed tomography (micro-CT). A notably lower number of micropores was observed in the neutron-irradiated specimen. The fracture toughness of neutron-irradiated NBG-17 was measured to be 1.45 MPa√m, compared to 1.17 ± 0.05 MPa√m for the pristine specimen. In both materials, cracks were found to initiate at the filler–binder interface, and often correlated with microstructural features such as pores and thermal cracks. Crack bridging and deflections emerged as the primary toughening mechanisms in both unirradiated and irradiated NBG-17. However, compared with the pristine specimen, the cracks in the neutron-irradiated specimen were more likely to grow trans granularly, resulting in less deflected crack paths. The reduced micro-porosity and strengthened filler–binder boundaries were considered to be the cause of the observed differences in crack morphologies. In conclusion, this study provides a qualitative analysis of the fracture behavior of neutron-irradiated nuclear graphite in the absence of radiolytic oxidation.
Low dose reactor irradiation effect on temperature dependence of dynamic modulus and internal friction of as-deposited pyrolytic graphite
This report describes the specimen loading order and documents all preirradiation examination material property measurement data for graphite specimens contained within the Second Advanced Graphite Capsule (AGC 2) irradiation capsule. The AGC 2 capsule is the second in six planned irradiation capsules comprising the Advanced Graphite Creep (AGC) test series. The AGC test series is used to irradiate graphite specimens in order to garner quantitative data necessary for predicting the irradiation behavior and operating performance of new nuclear grade graphites. This testing will ascertain the in service behavior of the graphite for pebble bed and prismatic very high temperature reactor designs. Similar to the First Advanced Graphite Capsule (AGC 1) preirradiation examination report, material property tests were conducted on specimens from 18 nuclear grade graphite types. However, AGC 2 tested an increased number of specimens (i.e., 512) prior to loading them into the AGC 2 irradiation assembly. All AGC 2 specimen testing was conducted at Idaho National Laboratory from July 2009 to August 2010. This report also details the specimen loading methodology for graphite specimens inside the AGC 2 irradiation capsule. The AGC 2 capsule design requires “matched pair” creep specimens that have similar dose levels above and below the neutron flux profile mid plane. This provides similar specimens with and without an applied load. Analysis in this document utilizes the neutron flux profile calculated for the AGC 2 capsule design, the capsule dimensions, and the size (i.e., length) of the selected graphite specimens to create a stacking order that produces “matched pairs” of graphite specimens above and below the AGC 2 capsule elevation mid point, thus providing specimens with similar neutron dose levels.
This interim report documents preliminary results of the post-irradiation examination material property testing from the fourth advanced graphite creep (AGC), AGC 4, capsule specimens. This is the fourth of a series of six irradiation test trains planned as part of the AGC experiment to fully characterize the neutron irradiation effects and radiation creep behavior of current nuclear graphite grades to moderate dose levels (=7 dpa). The AGC 4 capsule was irradiated in the Idaho National Laboratory Advanced Test Reactor at a nominal temperature of 800°C and to a peak dose of 8 dpa. Half of the AGC-4 specimens were subjected to compressive stresses to induce irradiation creep. Post-irradiation testing and measurement results are reported with the exception of thermal testing, which is still in progress, and irradiation mechanical strength testing. Additionally, some specimens initially deemed too hot to be examined in the ART Graphite laboratory may still be measured. The data reported includes specimen dimensions for both stressed and unstressed specimens to establish the irradiation creep rates, mass and dimensional data necessary to derive density, elastic constants (Young?s modulus, shear modulus, and Poisson?s ratio) from ultrasonic time of flight velocity measurements, Young?s modulus from the fundamental frequency of vibration, and electrical resistivity. A more complete evaluation of trends in the material property changes, as well as irradiation-induced creep due to the irradiation environment and applied load on the specimens, will be discussed later in AGC 4 post-irradiation examination analysis reports.
Glassy carbon, a monoatomic allotrope of carbon, is a candidate material for components in fission nuclear power systems due to its radiation tolerance. This article presents comprehensive electron microscopy data revealing the effects of neutron and electron irradiation on glassy carbon. For comparison, additional data are provided for pyrolytic graphite and carbon fibers, materials that exhibit similar structural behavior under irradiation. In situ electron irradiation experiments further illustrate the real-time microstructural evolution of glassy carbon during exposure. The dataset is organized into five parts: (1) transmission electron microscopy (TEM) micrographs of as-received and neutron-irradiated glassy carbon; (2) TEM micrographs of neutron-irradiated graphite; (3) TEM micrographs of unirradiated and irradiated carbon–carbon composites; (4) TEM micrographs of pyrolytic carbon specimens in both conditions; (5) scanning transmission electron microscopy (STEM) micrographs of as-received and neutron-irradiated glassy carbon and (6) in situ electron irradiation data of a glassy carbon particle. These datasets provide valuable insights into radiation-induced structural changes in carbon-based materials relevant to nuclear applications.
This report documents all pre-irradiation examination material-property measurement data for graphite specimens that are going to be used within the first high dose graphite (HDG) -1 irradiation capsule. The two new HDG capsules signify a major change to the AGC Experiment. HDG-1 and HDG-2 will replace the last two Advanced Graphite Creep (AGC) capsules (AGC-5 and AGC-6) which were designed to irradiate graphite at the extreme upper operational temperatures for a very-high-temperature reactor (VHTR) design, 1100°C. These very high temperature AGC-5 and AGC-6 capsules have been repurposed to re-irradiated specimens (from AGC-2, AGC-3, and AGC-4) at the lower temperatures of 600°C and 800°C. HDG-1 will be irradiated at 600°C and HDG-2 will be irradiated at 800°C. By re-irradiating the previous AGC specimens a total maximum neutron dose of around 15 dpa (displacements per atom) can be achieved for all major graphite grades at irradiation temperatures of 600°C and 800°C. Specimens in the HDG-1 capsule are made up of previously irradiated specimens from the AGC-2 capsule and unirradiated specimens prepared for the now discontinued AGC-5 capsule. Utilizing the irradiated specimens, a maximum neutron dose of around 15 dpa is anticipated. These new maximum dose levels will provide irradiated material property data over a total neutron dose range of 1-15 dpa at a temperature of 600°C when combined with the previous AGC-1 and AGC-2 irradiation data. This will provide quantitative data necessary for predicting the irradiation behavior and operating performance of new nuclear graphite grades for use within high temperature reactor designs. Similar to previous AGC test trains, HDG-1 includes the major graphite grades (IG-110, NBG-17, NBG-18, PCEA, and 2114) as well as adding the very fine-grain grade IG-430 which is of interest to the Molten Salt Reactor (MSR) designs. Also new to the HDG-1 capsule are 90 smaller geometry specimens designated as pencil specimens. These specimens take up only one third the space of a standard creep size specimen. This increased number of specimens will enhance property measurement statistics because they will provide 3 times the control specimen data at a position that would otherwise only have a single measurement.
Nuclear graphite is a critical material for the performance and safety of high-temperature reactors, making its study essential for the successful deployment of next-generation reactors in the United States. During the past year, Oak Ridge National Laboratory (ORNL) has contributed extensively to advancing the understanding of nuclear graphite’s properties, behavior, and applications; particular focus has been given to irradiation effects, oxidation mechanisms, thermal and mechanical performance, and long-term stability under reactor conditions. This report provides an update on the ongoing publications being prepared at ORNL. These studies are collectively intended to build a comprehensive knowledge base on nuclear graphite. The studies focus on key aspects such as microstructural characterization, oxidation behavior, advanced analytical techniques, molten salt infiltration, technique development, and billet-to-billet variability. By summarizing the progress of these publications, this report outlines ORNL’s contributions to the field, identifies knowledge gaps, and proposes future research directions. The findings presented in these studies will help enhance the understanding of nuclear graphite’s behavior, support the qualification of nuclear graphite materials, further the development of new techniques and guidelines for using microscopy techniques, and improve reactor safety and performance.
Publications and theses generated on composite research are listed. Surface energy changes of an epoxy based on tetraglycidyl diaminodiphenyl methane (TGDDM)/diaminodiphenyl sulfone (DDS), T-300 graphite fiber and T-300/5208 (graphite fiber/epoxy) composites were investigated after irradiation with 0.5 MeV electrons. Electron spin resonance (ESR) investigations of line shapes and the radical decay behavior were made of an epoxy based on tetraglycidyl diaminodiphenyl methane (TGDDM)/diaminodiphenyl sulfone (DDS), T-300 graphite fiber, and T-300/5208 (graphite fiber/epoxy) composites after irradiation with Co(60) gamma-radiation or 0.5 MeV electrons. The results of the experiments are discussed.
Molten-salt reactors (MSRs) are Generation IV nuclear reactors that use liquid salt as a coolant and/or fuel. In several MSR designs, graphite serves as a moderator and/or reflector. However, due to limited experimental data and operational experience, our understanding of graphite behavior in molten salt environments remains incomplete. This report aims to identify the degradation mechanisms of nuclear graphite in MSRs, detail the mechanisms of each factor, and provide an initial assessment of their impact on the structural integrity of graphite components. This assessment is based on an extensive literature review and insights from subject matter experts. Furthermore, given the limited data, a modeling strategy using existing Grizzly software is proposed for a more thorough analysis where appropriate. Additionally, it presents mitigation strategies where applicable. The report covers physical degradation mechanisms such as infiltration, erosion, and abrasion, as well as chemical degradation mechanisms including fluorination, intercalation, corrosion, and oxidation. Molten salt can infiltrate the porous structure of graphite, leading to several detrimental effects. Entrapment of fissile products within the graphite pores can cause radiation damage and could pose challenges in the handling and disposal of contaminated components. The differential thermal expansion between the infiltrated salt and graphite, along with internal stress from pressurized molten salt and volumetric heating, can compromise the structural integrity of graphite. To mitigate these effects, employing ultra-fine graphite grades and applying sealants and coatings are effective strategies. A computational model based on coupled solid mechanics and heat transfer phenomena could be used to predict the internal stresses using Grizzly software. In pebble-bed MSRs, graphite fuel pebbles can cause abrasion against reactor components due to friction and wear. The severity of wear is influenced by various factors such as temperature, environment, and the presence of lubricants. Tribological studies reveal that higher temperatures and molten salt environments, such as FLiBe, significantly reduce wear rates compared to dry conditions. Additionally, the chemical composition of the salt can further optimize graphite's tribological performance. Long-term wear effects can be modeled by incorporating surface defects into the geometry and predict stresses under thermal and radiation effects using Grizzly software. Chemical degradation of graphite in a molten salt environment can occur through fluorination and intercalation. Fluorination can occur via replacement of hydrogen or oxygen atoms, or at the active sites, but does not cause structural degradation. Intercalation, on the other hand, can lead to exfoliation, where layers of graphite separate and peel away, damaging the graphite. Protective coatings can enhance graphite's resistance to intercalation. Graphite generally exhibits good chemical stability in molten salt environments, though it can corrode under specific conditions, particularly in the presence of impurities or oxidants. Studies have shown that protective coatings, such as plasma-sprayed partially stabilized zirconia (PSZ), can effectively prevent such degradation. Corrosion behavior varies significantly with different graphite grades and coating applications, underscoring the need for detailed studies on uncoated and coated graphite to understand and mitigate corrosion mechanisms in MSRs. Research indicates that the presence of oxidants and impurities can accelerate graphite degradation in molten salts, making it essential to explore acceptable impurity limits. Oxidation is another critical degradation mechanism, leading to weight loss and structural damage due to the formation of CO and CO 2 from the reaction of carbon atoms with oxygen. This process creates new porosity and compromises graphite's integrity. While extensive research on graphite oxidation has been conducted for gas-cooled reactors, studies specific to MSRs are limited. Findings from the coal industry suggest that molten alkali metal salts can significantly accelerate graphite oxidation, a hypothesis worth exploring for fluoride salts in MSRs. Understanding oxidation behavior in MSRs is vital for developing protective measures. The analysis of post-irradiated graphite from the MSRE experiment demonstrated exceptional chemical compatibility with molten fluoride salt, suggesting that the extent of chemical attack on graphite largely depends on the salt's infiltration capability. Therefore, the use of ultra-fine grade graphite could help mitigate chemical degradation effects. Existing oxidation modeling capabilities in Grizzly, which use reaction-diffusion equations to model graphite-air interactions, could be adapted to simulate the chemical degradation effects of graphite in molten salt environments.
Using standardized uniaxial tensile test specimens is not practical due to the limited volumes in irradiation capsules, molten salt degradation facilities, or oxidation apparatus. The ASTM International Standard Test Method for Tensile Strength Estimate by Disc Compression of Manufactured Graphite (ASTM D8289) was developed to provide a convenient way for estimating tensile strength. Unlike the traditional uniaxial tensile test in ASTM C749 (International Standard Test Method for Tensile Stress–Strain of Carbon and Graphite), which uses dog-bone shaped specimens larger than 12.95 mm × 120.65 mm, the ASTM D8289 standard uses smaller discs with diameters of 6–12.7 mm. A digital image correlation (DIC) system, which uses a full-field noncontact surface displacement measurement technique, was applied along with the ASTM D8289 disc splitting test on IG-110 samples and compared with previous measurements from Mersen 2114 samples. Results confirmed that the DIC technique can measure the surface displacement/strain on these small (Ø6 mm × 3 mm) graphite specimens with good repeatability. However, Mersen 2114 and IG-110 samples exhibited strain discrepancies when DIC measurements were compared with analytical and finite element simulation values. The loading history and strain results also indicated different mechanical behaviors between Mersen 2114 and IG-110, particularly the nonlinear behavior of the IG-110 samples. Good agreement was observed by comparing the splitting tensile strengths of two superfine-grained grades with results from other work. The specimen size effect is discussed when comparing the splitting tensile strength with corresponding uniaxial tensile strength of these two graphite grades.
Beryllium carbide (Be 2 C) is an attractive alternative to graphite as a moderator material because of its high melting point, moderating efficiency, and theoretical environmental compatibility in MSRs, FHRs and HTGRs. However, its behavior under neutron irradiation is not yet known. Research on otherwise promising beryllium compounds are restricted because of the toxic nature of the material. For this work, a novel experiment was designed to safely irradiate beryllium-containing samples at The Michigan Ion Beam Laboratory (MIBL). Using this new capability, Be 2 C samples were irradiated with 9 MeV C 3+ ions from 2 dpa to 30 dpa, at temperatures up to 500 °C. Samples were characterized to investigate radiation tolerance. No evidence of phase precipitation, dislocation loops, or amorphization was observed up to 30 dpa, suggesting good radiation tolerance. One sample left in air for ~3 months oxidized slowly and lost structural integrity, while a sample kept in argon did not, suggesting that Be 2 C is not suitable for service in moist environments, but maintains its integrity in dry environments.
Nuclear graphite plays a pivotal role in the advanced reactor program. Consequently, developing a viable method to measure and evaluate small samples is essential. The Digital Image Correlation (DIC) technique allows for the examination of much smaller components in real-time applications, particularly concerning reactor capsule design and placement within the reactor. These samples become crucial for understanding the behavior of nuclear graphite before and after radiation exposure. They serve as a means to analyze changes and effectively measure the mechanical strength properties, which may or may not alter following irradiation.
In parabolic dish solar collectors, walk-off of the spot of concentrated sunlight is a hazard if a malfunction causes the concentrator to stop following the Sun. Therefore, a test program was carried out to evaluate the behavior of various ceramics, metals, and polymers under solar irradiation of about 7000 kW/sq m. (peak) for 15 minutes. The only materials that did not slump or shatter were two grades of medium-grain extruded graphite. High purity, slip-cast silica might be satisfactory at somewhat lower flux. Oxidation of the graphite appeared acceptable during tests simulating walk-off, acquisition (2000 cycles on/off Sun), and spillage (continuous on-Sun operation).
Time-dependent deformation in nuclear graphite is influenced by the creation and migration of radiation-induced defects in the reactor environment. This study investigates the role of pre-existing defects such as point defect clusters and Mrozowski cracks in nuclear graphite IG-110. Separate specimens were irradiated with a 2.8 MeV Au 2+ beam with a fluence of 4.38 × 10 14 cm −2 and an 8 MeV C 2+ beam with a fluence of 1.24 × 10 16 cm −2 . Microscopic specimens were either mechanically loaded inside a transmission electron microscope (TEM) or subjected to ex situ indentation-based creep loading. In situ TEM tests showed significant plasticity in regions highly localized around the Mrozowski cracks, resembling slip or ripplocation bands. Slip bands were also seen near regions without pre-existing defects but at very high stresses. Ex situ self-ion irradiation embrittled the specimens and decreased the creep displacement and rate, while heavy ion irradiation resulted in the opposite behavior. We hypothesize that the large-sized gold ions (compared to the carbon atoms) induced interplanar swelling as well as cross-plane channels for increased defect mobility. These findings illustrate the role of pre-existing defects in the dynamic relaxation of stresses during irradiation and the need for more studies into the radiation environment’s impact on the mechanical response of nuclear graphite.
We used a combination of x-ray photoelectron spectroscopy (XPS) and density functional theory (DFT) to investigate how the presence of a ruthenium (Ru) metal substrate modifies the N-D bond strength of the pyridinic nitrogen species in nitrogen (N)-doped graphene (Gr) on Ru(0001) compared to metal-free highly-oriented pyrolytic graphite (HOPG) substrate. The N-dopants were introduced through low-energy N+/N2+ irradiation. N is embedded in the carbon materials in two predominant configurations: as graphitic N (GN: N substituted in the hexagonal C lattice) and pyridinic N (PN: substitutional N adjacent to a C vacancy). XPS data showed that upon atomic deuterium (D) exposure at 220 K, the PN peak shifted to a higher binding energy by +1.2 eV for HOPG and +1.0 eV for N-doped graphene on Ru(0001), while the GN peak remained unchanged, indicating that the D atoms bound solely to pyridinic N. 85% of PN sites on HOPG can be saturated with D atoms, whereas only ~30% of pyridinic N sites are able to bind D atoms in N-doped Gr/Ru(0001). Our DFT analysis shows that this difference is due to the coordination of PN to Ru atoms, which necessitates bond cleavage of the N-Ru interaction prior to D atom adsorption. D begins desorbing from N-HOPG at ~573 K and is fully desorbed by ~973 K, whereas desorption from N-doped graphene on Ru(0001) begins at ~290 K, with complete desorption observed at ~700 K, indicating that the Ru metal weakens the N-D bond strength. We also studied a high-surface-area, layered, and porous N-doped carbon material, internally labeled NC900, which was synthesized by pyrolysis of glucose and graphitic carbon nitride (g-C3N4) at 1173 K. D exposure caused a +1.1 eV PN peak shift in NC900, with no change in the GN peak. Moreover, the NC900 exhibited the same desorption behavior as HOPG, demonstrating that well-defined model systems can effectively capture the behavior of more complex N-doped carbon materials.
Beam-intercepting devices such as beam windows and particle-production targets are critical components of accelerator target facilities for High Energy Physics (HEP) experiments. The high-power, pulsed structure of the particle beams used for these experiments leads to thermal shock and high-cycle fatigue in addition to radiation damage resulting from the accumulated particle fluence. This can lead to degradation of the target system s mechanical and thermal properties; considerably reducing their lifetimes and presenting substantial challenges to reliable operation of multi-MW class facilities. Recently several major accelerator facilities have been forced to operate at reduced power levels due to target survivability concerns. Furthermore, at Fermilab it is planned to increase the neutrino production beam power up to 2.4 MW in coming years. Therefore, timely R&D on the irradiated behavior of target system materials is critical to efficient operation of accelerator facilities and full utilization of recent accelerator power upgrades for HEP research. This talk will begin with an overview of high-power targetry, and the significant challenges presented by beam power increases expected for future HEP experiments. We will then cover several past materials irradiation studies that have been completed by the High-Power Targetry R&D group at Fermilab and its collaborators on common accelerator and target materials such as graphite, beryllium, titanium, and tungsten. Finally, we will conclude with a discussion of two novel materials investigations under way within the group; high-entropy alloys for beam window applications, and electrospun nanofibers to serve as particle production targets.
Here, this work investigates the option of modifying the Advanced Test Reactor by replacing the current beryllium reflector with heavy water. Such a change may provide some potential benefits for not only increasing the thermal irradiation capabilities but also resolving other problems such as reflector integrity issues due to fast fluence damage, which is always a limiting factor in the lifetime of the current beryllium reflector. This paper presents the analysis and estimation of the ATR core physics parameters by replacing the current beryllium reflector with heavy water (D 2 O). The paper first describes the details of two selected conceptual designs, which are partially reflected with either beryllium or graphite, and how they are derived from the baseline beryllium reflector concept. Then, reactor physics performance parameters for the two new concepts are assessed by comparing with those of the baseline concept. The performance parameters considered in this paper include in-pile tube neutron and gamma fluxes and heating rates, maximum loop voiding reactivity, core power behavior with different power splits, predicted cycle length with a given fuel loading, and thermal hydraulic analysis with a higher lobe power split. It is important to note that this study focuses on the reactor physics aspects and does not delve into the engineering challenges associated with such a design modification.