NASA NTRS1985

Effects of High Mean Stress on High-cycle Fatigue Behavior of PWA 1480

PWA 1480 is a potential candidate material for use in the high-pressure fuel turbine blade of the space shuttle main engine. As an engine material it will be subjected to high-cycle fatigue loading superimposed on a high mean stress due to combined centrifugal and thermal loadings. The present paper describes the results obtained in an ongoing program at the Argonne National Laboratory, sponsored by NASA Lewis, to determine the effects of a high mean stress on the high-cycle fatigue behavior of this material. Straight-gauge high-cycle fatigue specimens, 0.2 inch in diameter and with the specimen axis in the 001 direction, were supplied by NASA Lewis. The nominal room temperature yield and ultimate strength of the material were 146 and 154 ksi, respectively. Each specimen was polished with 1-micron diamond paste prior to testing. However, the surface of each specimen contained many pores, some of which were as large as 50 micron. In the initial tests, specimens were subjected to axial-strain-controlled cycles. However, very little cyclic plasticity was observed.

Majumdar, S.↗
NASA NTRS1979

Development of high-cycle fatigue design curves for a cast aluminum alloy

Life prediction curves for rocket engine pump parts were developed from the results of high-cycle fatigue tests run on cast-aluminum specimens. Notched and smooth specimens were cyclically tested at different mean stress levels at -320 F (78 K). The notch size and mean stress enveloped the design operating conditions. Local stress computed in the groove of the notched specimen was used to represent its fatigue strength. The von Mises criterion was used to determine effective cyclic stresses. The Goodman rule was applied to determine equivalent reversed alternating stresses. The procedure permitted the notched and smooth data sets to each be described by a single curve. High-cycle fatigue life curves were provided for the stress state, mean stress, and stress concentration spanned by the data.

Cooper, R. A.↗
NASA NTRS1985

Interaction of High-cycle and Low-cycle Fatigue of Haynes 188 Alloy at 1400 F Deg

The interaction of low-cycle fatigue (LCF) and high-cycle fatigue (HCF) was evaluated at the NASA Lewis Research Center on Haynes 188 alloy at 1400 F. Completely reversed, axial-load, strain-controlled fatigue tests were performed to determine the baseline data for this study. Additional specimens for interaction tests were cycled first at a high strain range for various small portions of expected LCF life followed by a step change to a low strain range to failure in HCF. Failure was defined as complete specimen separation. The resultant lives varied between 10 and 5000 cycles for the low-cycle fatigue tests and between 4500 and 3 million for the high-cycle fatigue tests. For the interaction tests the low-cycle-life portion ranged from 30 and 1000 applied cycles while the high-frequency life ranged from 300 and 300,000 cycles to failure. The step change results showed a significant nonlinear interaction in expected life. Application of a small part of the LCF life drastically decreased the available HCF life as compared with what would have been expected by the classical linear damage rule (LDR).

Peter T Bizon↗
NASA NTRS1983

Relation of cyclic loading pattern to microstructural fracture in creep fatigue

Creep-fatigue-environment interaction is discussed using the 'strainrange partitioning' (SRP) framework as a basis. The four generic SRP strainrange types are studied with a view of revealing differences in micromechanisms of deformation and fatigue degradation. Each combines in a different manner the degradation associated with slip-plane sliding, grain-boundary sliding, migration, cavitation, void development and environmental interaction; hence the approch is useful in delineating the relative importance of these mechanisms in the different loadings. Micromechanistic results are shown for a number of materials, including 316 SS, wrought heat resistant alloys, several nickel-base superalloys, and a tantalum base alloy, T-111. Although there is a commonality of basic behavior, the differences are useful in delineation several important principles of interpretation. Some quantitative results are presented for 316 SS, involving crack initiation and early crack growth, as well as the interaction of low-cycle fatigue with high-cycle fatigue.

Manson, S. S.↗
NASA NTRS1987

Fatigue damage interaction behavior of PWA 1480

The fatigue damage interaction behavior of PWA 1480 single crystal alloy has been experimentally established for the two-level loading case in which a block of low-cycle fatigue loading is followed by high-cycle fatigue loading to failure. A relative life ratio N1/N2 (where N1 and N2 are the low- and high-cycle fatigue baseline lives, respectively) of approximately 0.002 was explored to assess the interaction behavior. The experimental results thus far show evidence of a loading order interaction effect to a similar degree of detriment as has been observed in polycrystalline materials. Current generation single crystal alloys in general, and PWA 1480 in particular, contain pores; indeed, it was observed in all cases that specimen failure initiated from pores connected with or immediately below the surface. Detailed fractographic and metallographic studies are currently being made to assess the nature of the porosity in terms of its effect on fatigue life.

Mcgaw, Michael A.↗
NASA NTRS1988

Fiber reinforced superalloys for rocket engines

High-pressure turbopumps for advanced reusable liquid-propellant rocket engines such as that for the Space Shuttle Main Engine (SSME) require turbine blade materials that operate under extreme conditions of temperature, hydrogen environment, high-cycle fatigue loading, thermal fatigue and thermal shock. Such requirements tax the capabilities of current blade materials. Based on projections of properties for tungsten fiber reinforced superalloy (FRS) composites, it was concluded that FRS turbine blades offer the potential of a several-fold increase in life and over a 200C increase in temperature capability over current SSME blade material. FRS composites were evaluated with respect to mechanical property requirements for SSME blade applications. Compared to the current blade material, the thermal shock resistance of FRS materials is excellent, two to nine times better, and their thermal fatigue resistance is equal to or higher than the current blade material. FRS materials had excellent low and high-cycle fatigue strengths, and thermal shock-induced surface microcracks had no influence on their fatigue strength. The material also exhibited negligible embrittlement when exposed to a hydrogen environment.

Petrasek, Donald W.↗
NASA NTRS1989

Fiber reinforced superalloys for rocket engines

High pressure turbopumps for advanced reusable liquid propellant rocket engines such as that for the Space Shuttle Main Engine (SSME) require turbine blade materials that operate under extreme conditions of temperature, hydrogen environment, high-cycle fatigue loading, thermal fatigue and thermal shock. Such requirements tax the capabilities of current blade materials. Based on projections of properties for tungsten fiber reinforced superalloy (FRS) composites, it was concluded that FRS turbine blades offer the potential of a several fold increase in life and over a 200 C increase in temperature capability over the current SSME blade material. FRS composites were evaluated with respect to mechanical property requirements for SSME blade applications. Compared to the current blade material, the thermal shock resistance of FRS materials is excellent, two to nine times better, and their thermal fatigue resistance is equal to or higher than the current blade material. FRS materials had excellent low and high-cycle fatigue strengths, and thermal shock-induced surface microcracks had no influence on their fatigue strength. The material also exhibited negligible embrittlement when exposed to a hydrogen environment.

Petrasek, Donald W.↗
NASA NTRS1976

The influence of growth rate and temperature on high cycle fatigue of Al-Al3Ni

High-cycle fatigue tests have been conducted on specimens of an Al-Al3Ni eutectic alloy, unidirectionally solidified at selected rates from 0.000139 to 0.3 cm/sec. Tests were conducted in air at 298, 458 and 683 K. Room temperature fatigue lives were independent of growth rate at low solidification rates but were markedly improved in samples grown at 0.3 cm/sec. Materials grown at 0.00833 cm/sec exhibited fatigue lives similar to those of the lower growth rates, despite gross misalignment due to cellular growth. The dependence of fatigue life on growth rate at elevated temperatures appears to be due primarily to differences in cyclic creep rates as a result of varying interfiber spacings. Crack initiation and propagation mechanisms were established by metallographic and fractographic examination. Dislocation substructure-fiber interactions were studied by transmission electron microscopy.

Maurer, G. E.↗
NASA NTRS1985

Effects of a high mean stress on the high cycle fatigue life of PWA 1480 and correlation of data by linear elastic fracture mechanics

High-cycle fatigue tests using 5-mm-diameter smooth specimens were performed on the single crystal alloy PWA 1480 (001 axis) at 70F (room temperature) in air and at 100F (538C) in vacuum (10 to the -6 power torr). Tests were conducted at zero mean stress as well as at high tensile mean stress. The results indicate that, although a tensile mean stress, in general, reduces life, the reduction in fatigue strength, for a given mean stress at a life of one million cycles, is much less than what is predicted by the usual linear Goodman plot. Further, the material appears to be significantly more resistant to mean stress effects at 1000F than at 70F. Metallographic examinations of failed specimens indicate that failures in all cases are initiated from micropores of sizes of the order of 30 to 40 microns. Since the macroscopic stress-strain response in all cases was observed to be linear elastic, linear elastic fracture mechanics (LEFM) analyses were carried out to determine the crack growth curves of the material assuming that crack initiation from a micropore (a sub o = 40 microns) occurs very early in life. The results indicate that the calculated crack growth rates at an R (defined as the ratio between minimum stress to maximum stress) value of zero are approximately the same at 70F as at 1000F. However, the calculated crack growth rates at other R ratios, both positive and negative, tend to be higher at 70F than at 1000F. Calculated threshold effects at large R values tend to be independent of temperature in the temperature regime studied. They are relatively constant with increasing R ratio up to a value of about 0.6, beyond which the calculated threshold stress intensity factor range decreases rapidly with increasing R ratios.

Majumdar, S.↗
NASA NTRS1973

Prior-to-failure extension of flaws under monotonic and pulsating loadings.

An equation governing the prior-to-failure crack propagation is proposed. For a rate-sensitive solid containing a two-dimensional crack and subject to the tensile mode of fracture the differential equations are integrated numerically for loads increasing monotonically in time. The resulting integral curves of load vs crack length and length vs time indicate that the growth of cracks in the subcritical range is strongly rate-dependent. The fatigue growth, viewed as a sequence of slow growth periods, is simulated on an EAI 380 analog computer. The fourth-power law proposed by Paris is confirmed only within certain range of high-cycle fatigue propagation and for a rate-insensitive solid. Otherwise, i.e., for a more pronounced rate dependence induced by viscosity of a solid and/or in the proximity of the final instability point, the growth is markedly enhanced.

Wnuk, M. P.↗
NASA NTRS1971

Prior-to-failure extension of flaws under monotonic and pulsating loadings: Inelastic fatigue

An equation governing the prior to failure crack propagation is proposed. For a rate-sensitive solid containing two-dimensional crack and subject to the tensile mode of fracture, the differential equations are integrated numerically for the loads increasing monotonically in time. The resulting integral curves sigma = sigma(l) and l = l(t), i.e. load vs. crack length and length vs. time, indicate that the growth of cracks in the subcritical range is strongly rate dependent. The fatigue growth, viewed as a sequence of slow growth periods, is simulated on an EAI 380 analogue computer. The fourth power law proposed by Paris is confirmed only within a certain range of high-cycle fatigue propagation and for a rate-insensitive solid. For a more pronounced rate dependency, induced by the viscosity of a solid and/or in the proximity of the final instability point, the growth is markedly enhanced.

Wnuk, M. P.↗
NASA NTRS1970

Two-directional-flow, axial-motion-joint flow liner

Flow liner eliminates high-cycle fatigue in ducts carrying cryogenic fluids. It is capable of handling two-directional, high-velocity cryogenic liquid flow with a 3-inch axial motion without binding within a 25-inch length.

Bissing, L. L.↗
NASA NTRS1973

Properties of materials in high pressure hydrogen at cryogenic, room, and elevated temperatures

Various tests were conducted to determine the mechanical properties of 12 alloys that are commonly used or proposed for use in pressurized gaseous hydrogen or hydrogen containing environments. Properties determined in the hydrogen environments were compared to properties determined in a pure helium environment at the same conditions to establish environmental degradation. The specific mechanical properties tested include: high-cycle fatigue, low-cycle fatigue, fracture mechanics, creep-rupture, and tensile.

Harris, J. A., Jr.↗
NASA NTRS1973

High modulus filament wound vessels for cryogenic containers in spacecraft.

Compared to metallic vessels, filament-wound vessels for containment of cryogens and high pressure gases offer high potential weight savings for NASA spacecraft applications. Since carbon fiber/epoxy resin composites exhibit high strength-to-density ratios, high-cycle fatigue life, and excellent strain compatibility with internal metallic liners, filament-wound carbon fiber/epoxy resin composites were evaluated for application to cryogenic internal pressure vessels. Compared to room temperature values, the cryogenic strengths of the composites were reduced by about 15% at -423 F (with the exception of one composite) while moduli increased as much as 25%. Filament-wound carbon fiber/epoxy resin vessel specimens, made by three fabricators, defined and solved problems in the processing of these friable high-modulus fibers into structurally efficient vessel specimens.

Simon, R. A.↗
NASA NTRS1981

Thermal-barrier-coated turbine blade study

The effects of coating TBC on a CF6-50 stage 2 high-pressure turbine blade were analyzed with respect to changes in the mean bulk temperature, cooling air requirements, and high-cycle fatigue. Localized spallation was found to have a possible deleterious effect on low-cycle fatigue life. New blade design concepts were developed to take optimum advantage of TBCs. Process and material development work and rig evaluations were undertaken which identified the most promising combination as ZrO2 containing 8 w/o Y2O3 applied by air plasma spray onto a Ni22Cr-10Al-1Y bond layer. The bond layer was applied by a low-pressure, high-velocity plasma spray process onto the base alloy. During the initial startup cycles the blades experienced localized leading edge spallation caused by foreign objects.

Siemers, P. A.↗
NASA NTRS1988

Stress analysis and life prediction of gas turbine blade

A stress analysis procedure is presented for a redesign of the Space Shuttle Main Engine high pressure fuel turbopump turbine blades. The analysis consists of the one-dimensional scoping analysis to support the design layout and the follow-on three-dimensional finite element analysis to confirm the blade design at operating loading conditions. Blade life is evaluated based on high-cycle fatigue and low-cycle fatigue.

Hsiung, H. C.↗
NASA NTRS1974

Examination of the influence of coatings on thin superalloy sections. Volume 1: Description and analysis

The effects of an aluminide coating and of section thickness were investigated on two cast nickel-base superalloys. Cast section thickness ranged from 0.038 cm to 0.15 cm. Simulated engine exposures in a jet fuel burner rig with cyclic air cooling were studied. The effects of surface machining before coating and re-machining and re-coating after exposures were examined. The properties evaluated included tensile strength, stress rupture, high-cycle mechanical fatigue, and thermal fatigue. A metallurgical analysis was made of the microstructures of the coated and uncoated alloy.

Kaufman, M.↗
NASA NTRS1974

Investigation of fatigue strength of multilayer advanced fiber composites

The analytical characterization of a multilayer fiber composite plate (without hole) was accomplished for both static and dynamic loading conditions using the finite difference technique. Thornel 300/5208 composites with and without holes were subjected to static and tensile fatigue testing. Five (5) fiber orientations were submitted to test. Tensile fatigue testing also included three (3) loading conditions and two (2) frequencies. The low-cycle test specimens demonstrated a shorter tensile fatigue life than the high-cycle test specimens. Failure surfaces demonstrated effect of testing conditions. Secondary failure mechanisms, such as: delamination, fiber breakage, and edge fiber delamination were present. Longitudinal delamination between plies also occurred in these specimens.

Thornton, H. R.↗