Results for “high-strain rate”

NASA NTRS1982

Environmental and High-Strain Rate effects on composites for engine applications

The Lewis Research Center is conducting a series of programs intended to investigate and develop the application of composite materials to structural components for turbojet engines. A significant part of that effort is directed to establishing resistance, defect growth, and strain rate characteristics of composite materials over the wide range of environmental and load conditions found in commercial turbojet engine operations. Both analytical and experimental efforts are involved.

Chamis, C. C.↗

NASA NTRS2002

Tensile Strength of Carbon Nanotubes Under Realistic Temperature and Strain Rate

Strain rate and temperature dependence of the tensile strength of single-wall carbon nanotubes has been investigated with molecular dynamics simulations. The tensile failure or yield strain is found to be strongly dependent on the temperature and strain rate. A transition state theory based predictive model is developed for the tensile failure of nanotubes. Based on the parameters fitted from high-strain rate and temperature dependent molecular dynamics simulations, the model predicts that a defect free micrometer long single-wall nanotube at 300 K, stretched with a strain rate of 1%/hour, fails at about 9 plus or minus 1% tensile strain. This is in good agreement with recent experimental findings.

Wei, Chen-Yu↗

NASA NTRS1992

Shear failure and impact resistance in graphite fiber laminates

The multispan beam (MSB) test was evaluated as a predictor of damage resistance and damage tolerance in quasi-isotropic graphite laminates. Materials studied were five commercial prepreg system using high-strain and intermediate-modulus carbon fibers, as well as an amorphous thermoplastic system. Failure loads and displacements in the MSB tests showed little rate dependence. Values of compressive strength after a standard low-velocity impact correlated fairly well with the MSB results.

Srinivasan, Krishna↗

NASA NTRS1987

Bithermal Low-Cycle Fatigue Behavior of a NiCoCrAlY-Coated Single Crystal Superalloy

Specimens of a single crystal superalloy, PWA 1480, both bare and coated with a NiCoCrAlY alloy, PWA 276, were tested in low-cycle fatigue at 650 and 1050 C, and in bithermal thermomechanical fatigue tests. In the two bithermal test types, tensile strain was imposed at one of the two temperatures and reversed in compression at the other. In the high-strain regime, lives for both bithermal test types approached that for the 650 C isothermal test on an inelastic strain basis, all being controlled by the low ductility of the superalloy at 650 C. In the low-strain regime, coating cracking reduced life in the 650 C isothermal test. The bithermal test imposing tension at 650 C, termed out-of-phase, also produced rapid surface cracking, but in both coated and bare specimens. Increased crack growth rates also occurred for the out-of-phase test. Increased lives in vacuum suggested that there is a large environmental contribution to damage in the out-of-phase test due to the 1050 C exposure followed by tensile straining at the low temperature.

Gayda, J.↗

NASA NTRS1986

The NASA strain gage laboratory

The goal of the NASA-sponsored high-temperature high-strain gage program (which combines in-house, contract, and grant work) is to develop a gage that will measure static strains up to 2000 microstrain to within 10 percent, and at temperatures up to 1250 K (typical for combustors and turbine blades and vanes of gas turbine engines) maintained over 50-h period. The basic equipment of the NASA in-house lab is described (with special attention given to the strain-gage testing system), and some examples of recent test results are discussed. Data are presented on following tests performed on four gages: apparent strain vs temperature at different cooling rates, gage factor at various strain and temperature levels, and drift and creep tests at 133 C.

Hobart, Howard F.↗

NASA NTRS1987

Bithermal low-cycle fatigue behavior of a NiCoCrAlY-coated single crystal superalloy

Specimens of a single crystal superalloy, PWA 1480, both bare and coated with a NiCoCrAlY alloy, PWA 276, were tested in low-cycle fatigue at 650 and 1050 C, and in bithermal thermomechanical fatigue tests. In the two bithermal test types, tensile strain was imposed at one of the two temperatures and reversed in compression at the other. In the high-strain regime, lives for both bithermal test types approached that for the 650 C isothermal test on an inelastic strain basis, all being controlled by the low ductility of the superalloy at 650 C. In the low-strain regime, coating cracking reduced life in the 650 C isothermal test. The bithermal test imposing tension at 650 C, termed out-of-phase, also produced rapid surface cracking, but in both coated and bare specimens. Increased crack growth rates also occurred for the out-of-phase test. Increased lives in vacuum suggested that there is a large environmental contribution to damage in the out-of-phase test due to the 1050 C exposure followed by tensile straining at the low temperature.

Gayda, J.↗