Results for “hot isostatic pressing”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

At least 19 records

An Initial Evaluation of the Elevated-Temperature Cyclic Properties of Optimized 316H Stainless Steel Fabricated by Powder Metallurgy Hot Isostatic Pressing

Powder metallurgy hot isostatic pressing (PM-HIP) is a mature advanced manufacturing technology, which can consolidate metallic powder under high temperature and pressure to generate near-net shape components. This process can lower production costs and reduce component lead times for nuclear reactor construction and can be readily deployed in the near term for microreactor components because of their smaller size. The purpose of this work is to continue the evaluation of elevated-temperature cyclic material properties for PM-HIP 316H stainless steel. Prior scoping results have shown that the commercially procured PM-HIP stainless-steel materials have reduced creep-fatigue performance compared to wrought 316 stainless steels. To better understand how PM-HIP processed material properties compare to traditional manufacturing methods, additional billets of PM-HIP 316H stainless steel were procured and tested. This testing is necessary to understand how elevated-temperature properties are influenced by the PM-HIP process and what data are needed for incorporating PM HIP 316H into the American Society of Mechanical Engineers Boiler Pressure Vessel Code, Section III, Division 5 for high temperature reactor construction. Specifically, an additional PM-HIP 316H stainless steel billet with lower oxygen and nitrogen concentrations was fabricated by the Nuclear Advanced Manufacturing Research Centre of the United Kingdom and tested to understand if elevated-temperature cyclic properties can be improved. The creep-fatigue resistance of the material from this new billet did not show appreciable improvement compared to prior testing.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

A fast and robust computational modeling approach for density and shape predictions in powder metallurgy hot isostatic pressing

Powder metallurgy hot isostatic pressing (PM-HIP) is an advanced manufacturing process that produces near-net-shape parts with high material utilization and uniform microstructures. PM-HIP is frequently used for producing small-scale parts with complicated geometries and is potentially economical for producing large-scale parts. However, excessive post-HIP shape distortions can reduce its effectiveness and economic advantage, especially for larger parts. A PM-HIP computational model can predict and help mitigate these distortions. However, due to complex deformation mechanisms and thermo-mechanical coupling present in PM-HIP processes, these non-linear computational models sometimes become numerically unstable. The numerical instabilities in these models can lead to very slow convergence or no convergence at all, which often translates to slow and unreliable models. These limitations are more pronounced in large models with complicated geometries. Hence, in this work, an alternative modeling approach is presented that improves numerical stability and computational performance. The presented approach achieves these improvements through approximating the fully coupled thermo-mechanical PM-HIP model as a decoupled model and adding inertial damping to the model’s mechanical part. In conclusion, a comparison with the fully coupled model indicated a slight dip in prediction accuracy (<5% error) but significant improvements in numerical stability (>20 times larger time step size) and computational performance (5-10 times speed-up with less computational resource usage) when using the presented approach.

Hot isostatic pressing↗

A visco-plastic constitutive model for accurate densification and shape predictions in powder metallurgy hot isostatic pressing

Powder metallurgy hot isostatic pressing (PM-HIP) is an advanced manufacturing process that produces near net shape parts with high material utilization and uniform microstructures. Despite being used frequently to produce small-scale components, the application of PM-HIP to large-scale components is limited due to inadequate understanding of its complex mechanisms that cause unpredictable post-HIP shape distortions. A computational model can provide necessary information about the intermediate and final stages of the HIP process that can help understand it better and make accurate predictions. Generally, two types of computational models are employed for PM-HIP of metal powders, namely, plastic and visco-plastic models. Between these, the plastic model is preferred due to its cheaper calibration approach requiring less experimental data. However, the plastic model sometimes produces incorrect predictions when slight variations of the HIP conditions are encountered in practical situations. Therefore, this work presents a visco-plastic model that addresses these limitations of the plastic model. A novel modified calibration approach is employed for the visco-plastic model that utilizes less experimental data than existing approaches. With the new approach, the data requirement is same for both plastic and visco-plastic models. This also enables a quantitative comparison of plastic and visco-plastic models, which have been only qualitatively compared in the past. When calibrated with the same experimental data, both the models are found to produce similar results. In conclusion, the calibrated visco-plastic model is applied to several complex geometries, and the predictions are found to be in good agreement with experimental observations.

Hot isostatic pressing↗

Convergent Manufacturing of Large-Scale Components for Nuclear Applications, via Additive Manufacturing and Powder Metallurgy Hot Isostatic Pressing

Powder metallurgy (PM)–hot isostatic pressing (PM-HIP) has long been recognized as a powerful route for producing fully dense, near net shape metallic components. By consolidating powders under high temperature and pressure, HIP provides isotropic properties, uniform microstructures, and scalability to complex geometries that are vital for sectors such as aerospace, energy, and nuclear power. Yet despite these advantages, the technology has remained constrained by costly trial and error canister fabrication, limitations of conventional forging, and incomplete knowledge about how the canister design influences final part properties. Additive manufacturing (AM), by contrast, thrives on design freedom and geometric flexibility but struggles with speed, scalability, and cost when applied to very large structures. The research presented in this report investigated how a convergent manufacturing approach, combining AM with PM-HIP, can merge the strengths of both technologies, leveraging AM’s flexibility for canister design and HIP’s consolidation capability to deliver reliable, large, and complex parts. The work progressed through three case studies that built on one another in scale and complexity. Small cylindrical canisters fabricated by conventional methods, laser powder bed fusion, and directed energy deposition were filled with stainless steel powders and subjected to HIP. The resulting parts demonstrated near-full density and mechanical properties on par with wrought stainless steel, showing for the first time that AM canisters can be a direct substitute for conventional ones without sacrificing quality. The next step involved a medium-scale, noncentrosymmetric T-valve, which is an enclosed, multibranch geometry that tested the limits of AM + PM-HIP integration. The T-valve achieved predictable shrinkage and uniform densification, confirming feasibility for enclosed designs. However, this study also revealed oxide inclusions and interfacial challenges at the AM + HIP boundary, underscoring the critical importance of controlling interface chemistry and employing robust, in situ strategies, such as melt pool monitoring and thermal monitoring, coupled with nondestructive evaluation techniques such as x-ray computed tomography. Finally, the effort culminated in fabricating a large-scale impeller weighing nearly 2000 lb and spanning 5 ft in diameter. Produced via multirobot wire arc AM and hot isostatic pressed to near-full density, the impeller validated industrial-scale feasibility. Predictive models closely matched experimental shrinkage, tensile properties were spatially uniform across the component, and the AM + PM-HIP interface proved mechanically sound despite the presence of oxide-decorated prior particle boundaries. This large-scale demonstration is a major milestone, showing that hybrid AM + PM‑HIP can reliably deliver components at reactor-relevant scales. Collectively, these studies charted a logical pathway: small-scale work built scientific confidence, medium-scale work highlighted opportunities and challenges, and large-scale work proved industrial impact. The overarching conclusion of this report is that AM + PM-HIP should not be seen as a replacement for forging but as a complementary pathway that provides the US with flexibility, resilience, and new options for manufacturing nuclear-grade components. Looking ahead, several directions emerge as critical to sustaining progress. Predictive modeling must become faster, more accessible, and more accurate, with digital twins and machine learning reducing reliance on trial and error. Powders and alloys must be optimized for HIP, with improved cleanliness, reduced oxides, and tailored chemistries that enhance creep, fatigue, and irradiation resistance. Interfaces between AM and HIP regions must be better engineered through coatings, machining strategies, and surface treatments to mitigate oxide formation and ensure reliable bonding to explore opportunities for HIP of targeted compositional parts, as well as multimaterial HIP cladding applications. Monitoring and nondestructive evaluation need to expand, incorporating multimodal sensors, x-ray computed tomography, and real-time data integration through platforms such as Pelican. At the same time, the pathway to industrial adoption requires techno-economic analysis, machinability studies, and qualification frameworks aligned with industry and regulatory standards. Finally, workforce and academic engagement must be strengthened. Programs that train technicians and engineers for US Navy and US Department of Energy manufacturing challenges should be paired with academic partnerships to support fundamental research, with open sharing of non-export-controlled data to accelerate innovation and build the next generation of experts. In conclusion, this report demonstrates that hybrid AM + PM-HIP is scientifically viable and strategically important. By combining the design agility of AM with the consolidation strength of HIP and embedding modeling, monitoring, and workforce development, this approach provided a transformative new capability for US manufacturing. The path forward is clear: hybrid AM + PM-HIP is not just a promising research direction but is also potentially an industrially relevant pathway that can reshape how nuclear-grade components are designed, qualified, and deployed.

36 MATERIALS SCIENCE↗

The Elevated-Temperature Cyclic Properties of Alloy 316H Fabricated by Powder Metallurgy Hot Isostatic Pressing (Rev.1)

Powder metallurgy hot isostatic pressing (PM HIP), an advanced manufacturing technique, is viewed by the Department of Energy as a “transformational technology” for heavy section manufacturing of nuclear components. Although PM HIP is a mature technology, it has not been qualified in Section III, Division 5 for elevated-temperature nuclear construction. This work seeks to demonstrate a PM HIP qualification method for elevated-temperature nuclear construction that is based on allowable material characteristics. Specifically, the elevated-temperature cyclic properties of PM HIP 316H are investigated. The creep-fatigue properties of PM HIP 316H are significantly degraded compared to those of wrought. Current PM HIP practices are not able to fabricate elevated-temperature nuclear components with creep-fatigue properties that are equivalent to or better than traditional wrought components. A research and development program is proposed for qualifying PM HIP 316H for elevated-temperature nuclear construction.

36 MATERIALS SCIENCE↗

Powder metallurgy hot isostatic pressing - workshop report

The findings of the powder metallurgy (PM) hot isostatic pressing (HIP) workshop confirmed that the accelerated adoption of this technology requires the following action items: 1. By 2035, the HIP infrastructure must be scaled to sizes larger than 4 .0 meters for manufacturing components relevant to energy and defense industries at large. 2. The community must develop cost-effective and agile standards, qualifications, and certification pathways for these HIP parts. 3. At the same time, domestic powder production should be expanded to a wide range of metallic alloys, including Cr-Mo steels, stainless steels, and titanium- and nickel-based superalloys, as well as to emerging alloy classes in the refractory space. 4. The above initiatives can be enhanced by implementing digital modeling and controls, including AI-driven simulations, in situ monitoring, and digital twins.

36 MATERIALS SCIENCE↗

Insight into the interfacial microstructure and chemistry of hot isostatically pressed AA6061-AA6061 bonds for U-10Mo fuel cladding application

Here, in the present study, hot isostatic pressing (HIP) bonding was carried out using AA6061-AA6061 plates for U-10Mo monolithic fuel cladding application. HIP was performed at 560°C with an applied isostatic pressure of 103 MPa for 90 min. Interfacial microstructure characterizations were performed using scanning electron microscopy (SEM) combined with electron backscatter diffraction (EBSD) to quantify precipitate fractions and study recrystallization, grain growth, and orientation relationships across the interface. EBSD results confirmed that no interfacial grain growth occurred during the HIP process. Transmission electron microscopy (TEM) was also employed to quantify composition and identify phases of various precipitates and an oxide layer that formed at the interface during HIP bonding. Microstructural analyses revealed the formation of a large fraction of Mg 2 Si precipitate and a ~50 nm thick Mg-oxide layer at the interface. Further TEM analysis confirmed that the oxide layer was not continuous, and Mg 2 Al 2 O 5 oxide particles with an average size of 18 nm were present in the oxide layer. Finite element modeling analysis was performed to study the stress distribution at the interface during HIP processing.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Influence of Powder Characteristics and Processing Methods on Creep Performance of Powder Metallurgy Hot Isostatic Pressed SS316

The U.S. nuclear energy expansion goals are driving the demand for manufacturing routes that can rapidly produce large, complex, near net shape components. Powder metallurgy hot isostatic pressing (PM HIP) is an advanced manufacturing technique that can be economically scaled-up, while alleviating the supply chain challenges that forging and casting face in terms of cost and lead time constraints. This makes PM-HIP a viable technology to aid and accelerate large-scale part manufacturing for nuclear applications. However, large-scale qualification and deployment of this technology require a thorough understanding of the influence of powder feedstock quality, powder handling history, hot isostatic pressing (HIP) parameters, and subsequent heat treatment on microstructural evolution and elevated temperature mechanical performance. The present work focusses on 316 austenitic stainless steel (SS316) which is most commonly used in high temperature environments for nuclear applications Results from this study show that PM HIPed SS316 meets ASME tensile requirements at room temperature and at elevated temperature. However, creep performance of PM-HIPed SS316 remains inferior to its wrought counterpart, demonstrating that tensile performance alone is not a reliable metric for long duration high temperature integrity. Further, this report delineates powder derived microstructural features that govern creep damage, with key evidences pointing to “microstructural inheritance” from gas atomized powder feedstocks. Commercial SS316 powders of varying chemical compositions and recycling histories were studies, and the results showed large differences in elemental segregation, oxide surface layers and secondary phase distributions. Multi-scale characterization revealed segregation of chromium, molybdenum, manganese and silicon at the boundaries and the precipitation of manganese-, silicon-, and molybdenum-oxides. During HIP consolidation, these surface oxides transform into decorated prior particle boundaries (PPBs) and grain boundary inclusions that persist through conventional post-HIP solution annealing treatment. The retained oxides in post-HIP microstructures were found to influence grain growth, precipitation behavior, and ultimately creep cavitation and fracture. Such post-HIP heat treatments are therefore limited by a complex trade-off between grain growth, and oxide coarsening which aggravate creep damage by acting as nucleation sites for cavities. The objective of this work is to establish an integrated processing–structure–property framework for PM-HIP 316 stainless steel by investigating the influence of powder feedstock characteristics in pre- and post-HIP processing as well as to understand the significance of post-HIP heat treatment on microstructural evolution and creep properties. The results from this report emphasize the significance of powder feedstock integrity in improving creep performance of PM-HIPed SS316, by highlight the effect of rapid solidification, elemental segregation, oxide formation and powder recycling on microstructural defect inheritance following HIP consolidation. Rather than considering HIP processing, solution annealing, and mechanical performance independently, this report treats powder production, HIP consolidation, post-HIP thermal processing, and creep deformation as interconnected stages within a continuous metallurgical process. The resulting framework will provide a scientific basis for developing feedstock engineering strategies capable of improving long-term reliability of PM-HIP stainless steels and accelerating their qualification for advanced nuclear applications.

Ajjarapu, Pavan [Oak Ridge National Laboratory (OR↗

SA508 low alloy steel to 316L stainless steel dissimilar metal joint made by powder metallurgy hot isostatic pressing

Joining ferritic SA508 low alloy steel (LAS) and austenitic 316 L stainless steel (SS) via powder metallurgy hot isostatic pressing (PM-HIP) was evaluated as an alternative method to welding. This study investigated the mechanical and microstructural evolutions of the bimetallic interface under different joint designs and heat treatments. Here, the direct joining of dissimilar metal alloys by PM-HIP method resulted in two designs: 1) powder SA508 to solid bar 316 L (P508–B316L) and 2) powder 316 L solid bar SA508 (P316L-B508). In both cases, P508–B316L and P316L-demonstrated satisfactory tensile strength, however, high hardness and severe depreciation in toughness were located on the bimetallic interface. The mechanisms responsible for the detrimental mechanical properties were verified. Large oxides were observed in P508–B316L due to the prior powder boundary (PPB) oxides present in SA508 powder. The intense sensitization occurred from the formation of M 23 C 6 carbides, consequently from the slow cooling after PM-HIP in P316L-B508. Post-HIP heat treatments were explored to reduce the distance of carbide formation; however, the heat treatment could not eliminate the carbides. The experimental results were compared to the diffusion couple simulation as a function of carbide formation with distance. The analysis also showed the high hardness at the bimetallic interface was primarily contributed by solid solution strengthening. In conclusion, the direct joining of P316L-B508 and P508–B316L via PM-HIP was deemed to be unfeasible, and a transitional material is necessary to impede the diffusion of carbon.

316L stainless Steel↗

Understanding Oxide–Metal Interactions During Hot Isostatic Pressing to Diffusion Bond Aluminum Alloy 6061 Plates

The interaction between Mg, Si, and Al 2 O 3 during hot isostatic pressing diffusion bonding of aluminum alloy 6061 (AA6061) plates was investigated through thermodynamic calculations and experimental microstructural characterization. Thermodynamic calculations as functions of temperature, pressure, and composition revealed that the interaction among Mg, Si, and Al 2 O 3 yields Mg 2 Si and either MgO + Al or MgAl 2 O 4 + Al, facilitating the reduction of Al 2 O 3 and allowing Al/Al metallic bonds to form. Total pressure variation had a negligible influence on the oxygen partial pressure, and consequently, the reaction product formation. Oxygen partial pressure variation as a function of temperature and initial amount of Al 2 O 3 determined the formation of either MgO or MgAl 2 O 4 . Experimental Hot Isostatic Pressure (HIP) bonding at 723 K and 833 K under a constant pressure of 1017 atm documented the cooling rate-dependent formation of β–Mg 2 Si precipitates. High-resolution transmission electron microscopy imaging and selected area electron diffraction patterns verified the formation of β–Mg 2 Si and MgO at the interface but did not detect MgAl 2 O 4 . In conclusion, findings from this study clarify the role of thermochemical interactions in oxide disruption and bonding mechanisms during HIP diffusion bonding of AA6061 and provide guidance for optimizing joining processes for monolithic nuclear fuel assemblies.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Microstructure and microchemistry changes at U-10Mo fuel/AA6061 cladding interfaces with varying hot isostatic pressing conditions

Monolithic uranium - 10 wt.% molybdenum (U-10Mo) is a promising high-assay low-enriched uranium fuel system for nuclear reactors used in research, medical isotope production, and remote power applications. During manufacturing, AA6061 cladding is bonded to the U-10Mo fuel plate via hot isostatic pressing, during which diffusion and fuel/cladding chemical interaction occurs at plate edges. Furthermore, the microstructure and microchemistry changes that occur at fuel/cladding interfaces are important to understand as a function of process parameters to develop a reliable fuel fabrication process and to meet the desired specifications. Here, microstructural and microchemical changes are studied using complementary electron microscopy and atom probe tomography for two manufactured fuel plates with varied hot isostatic pressing (HIP) parameters. Results highlight that modifying thermomechanical processing parameters significantly changed the interaction layer thickness between U-10Mo and AA6061 by an order of magnitude. In addition to this the distribution and concentration of elements (i.e., Al, Si, Mg) from cladding to fuel was also investigated.

36 MATERIALS SCIENCE↗

Near-Net-Shape Hot Isostatic Press Manufacturing Modality for sCO2 CSP Capital Cost Reduction

Through this DOE funded 3.5-year research project, feasibility of fabricating supercritical carbon dioxide (sCO2) turbine components by powder metallurgy (PM) based near-net-shape (NNS) hot isostatic pressing (HIP) was demonstrated in a turbine nozzle ring, a turbine casing with Haynes 282 powder, and a bimetallic pipe with Haynes 282 and SS415 powder. As-HIP microstructure of various powders and HIP processing conditions was studied to downselect a condition for the prototype components. Tensile strength and low cycle fatigue (LCF) capability of PM HIP 282 was found to be superior to cast 282, despite a debit in creep stress capability that could be mitigated by component design modification. Near-Net-shape with minimal post machining was achieved by modeling the non-uniform shrinkage during HIP cycle and designing the HIP tooling to meet dimensional targets. The prototypes of turbine nozzle ring and bimetallic pipe were successful in achieving overall dimension, microstructure, and properties, despite dimensional tolerance affected by chemical milling rate. The prototype of a 1700lbs turbine casing was partially successful in achieving dimension, microstructure in as-HIP state, and providing consistent mechanical properties, however, cracking issue during post heat treatment required further investigation. The estimated manufacturing cost using NNS HIP was a ~50% reduction compared to forging with extensive machining, which translated into ~$100/kWe CAPEX cost reduction for concentrated solar power (CSP) power block.

14 SOLAR ENERGY↗

Binder-jetted AISI M2 tool steel during hot isostatic pressing: Densification and carbide transformation

Binder jetting (BJ) enables fabrication of complex components from high-alloy steels such as AISI M2; however, residual porosity after sintering limits mechanical performance. This study investigates the coupled effects of binder chemistry, sintering conditions, cooling rate, and subsequent hot isostatic pressing (HIP) on densification, microstructure, and mechanical response in binder-jetted M2 tool steel. HIP increased relative density from ∼93 to 95% to >99% and improved compressive strength by ∼40-70%. Densification was governed by initial pore morphology, where closed porosity was effectively eliminated, while interconnected porosity limited full consolidation. Microstructural analysis (XRD, EBSD, SEM) shows that HIP promotes dissolution of metastable carbides and redistribution of alloying elements (W, Mo, V), transforming heterogeneous carbide networks into finer and more uniformly distributed M 2 C, MC, and M 6 C phases through diffusion-assisted homogenization. Among the investigated conditions, the FluidFuse binder combined with sintering at 1270 °C for 60 min and furnace cooling produced the most balanced response, achieving ∼99.7% density, ∼855 HV hardness, ∼4130 MPa compressive strength, and ∼24% strain. In contrast, higher sintering temperatures promoted carbide coarsening, reducing ductility despite high density. HIP reduces microstructural heterogeneity and drives the system toward a near-equilibrium state with reduced sensitivity to prior processing history. A comparative assessment with conventional and additive manufacturing routes (LPBF, DED, EBM, FFF) shows that the BJ-HIP approach achieves competitive densification and mechanical performance. These findings provide a mechanistic basis for controlling densification and microstructure in high-alloy steels processed via BJAM.

AISI M2 tool steel↗

Iodosodalite synthesis with hot isostatic pressing of precursors produced from aqueous and hydrothermal processes

Iodosodalite powders were synthesized using aqueous and hydrothermal methods, with or without sodium borosilicate glass binders, and then hot isostatically pressed (HIP) at 900 ? and 175 MPa for 3 h to convert into waste forms. After HIPing, the structures, compositions, morphologies, porosities, and leach rates of the aqueous and hydrothermally produced iodosodalite samples were compared. X-ray diffraction patterns of HIPed samples showed that iodosodalite remained as the dominant phase. However, the fraction of the iodosodalite phase decreased after HIPing, indicating decomposition of the iodosodalite structure during the HIP process. Scanning electron microscopy and chemical imaging on the cross sections of HIPed samples showed homogeneous elemental distribution for aqueous-grown iodosodalite, whereas hydrothermally grown iodosodalite samples had more heterogeneity and porosity. The densities of HIPed samples with more glass binder were generally higher than sampled HIPed without binder. The leach tests on samples containing 20 mass% glass binder showed that the iodine dissolution rate of HIPed hydrothermally grown iodosodalite was about 4 times higher than iodosodalite by aqueous method. This study provides alternative techniques for immobilizing iodine-streams in iodosodalite waste forms.

38 RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCLEA↗

The Elevated-Temperature Cyclic Properties of Alloy 316L Manufactured Using Powder Metallurgy Hot Isostatic Pressing

According to developers at the GAIN 2019 microreactors workshop, advanced manufacturing (AM) is needed to fabricate microreactor components. A methodology has not been established to qualify AM for elevated-temperature nuclear construction. A potential approach is to use the wrought design methodology by establishing the AM properties as equivalent to or better than wrought. This investigation aims to understand the relationship between powder metallurgy hot isostatic pressing (PM HIP) and material characteristics for Alloy 316L as they relate to elevated-temperature component design and construction. The elevated-temperature cyclic behavior of Alloy 316L manufactured by PM HIP differs from wrought. Of particular significance is the reduced number of cycles to failure for the PM HIP Alloy 316L compared to wrought. Additional work to identify the microstructural feature that control the elevated-temperature cyclic behavior is needed.

36 MATERIALS SCIENCE↗

Micro-tensile testing of the bond line in hot isostatic pressed aluminum

Considerable effort is being devoted to development and regulatory qualification of low enriched fuels for research and test reactors by many agencies worldwide. One promising fuel configuration being examined for United States higher power research and test reactors (USHPRRs) are plate-type fuels composed of a metallic uranium-molybdenum foil clad in an aluminum alloy. The two pieces of aluminum alloy cladding are bonded using a hot isostatic pressing method. The mechanical properties of the resulting bond line in the aluminum alloy cladding will vary by the HIP'ing parameters, requiring a need to characterize the bond line. Small scale mechanical testing can provide a path for evaluating the mechanical properties and deformation behavior of the bond line both prior to and following irradiation. Here, in this research, room temperature micro-tensile specimens of non-irradiated and irradiated samples containing an Al alloy (AA 6061) bond line were tested to evaluate its strength and deformation behavior. Observations indicated that the strain rate did not affect the deformation behavior or strength and most of the micro-tensile specimens failed in a ductile mode in grains around the bond line. There was no indication that the microstructural features from the bond line affected the mechanical properties of the micro-tensile specimens. An initial examination was performed on irradiated material but further systematic studies of the effects of irradiation can be performed in the future.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Hot Isostatic Pressing Control of Tungsten-Based Composites

Metal-oxide composites are commonly used in high temperature environments for their thermal stability and high melting points. Commonly employed with refractory oxides or carbides such as ZrC and HfC, these materials may be improved with the use of a low density, high melting point ceramic such as CeO2. In this work, the consolidation of W-CeO2 metal matrix composites in the high CeO2 concentration regime is explored. The CeO2 concentrations of 50, 33, and 25 wt.%, the CeO2 particle size from nanometer to micrometer, and various hot isostatic pressing temperatures are investigated. Decreasing the CeO2 concentration is observed to increase the composite density and increase the Vickers hardness. The CeO2 oxidation state is observed to be a combination of Ce3+ and Ce4+, which is hypothesized to contribute to the porosity of the composites. The hardness of the metal-oxide composite can be improved more than 2.5 times compared to pure W processed by the same route. This work offers processing guidelines for further consolation of oxide-doped W composites.

36 MATERIALS SCIENCE↗