At least 19 records

Evaluation of CO2 and CO dopants in hydrogen to reduce hydrogen permeation in the Stirling engine heater head tube alloy CG-27

Tubes of CG-27 alloy, filled with hydrogen doped with various amounts of carbon dioxide and carbon monoxide, were heated in a diesel fuel fired Stirling engine simulator materials test rig for 100 hours at 820 C and at a gas pressure of 15 MPa to determine the effectiveness of the dopants in reducing hydrogen permeation through the hot tube wall. This was done for clean as-heat treated tubes and also for tubes that had previously been exposed for 100 hours to hydrogen doped with 1.0 volume percent carbon dioxide to determine if the lower levels of dopant could maintain a low hydrogen permeation through the hot tube wall. Carbon dioxide, as a dopant in hydrogen, was most effective in reducing hydrogen permeation through clean tubes and in maintaining low hydrogen permeation after prior exposure to 1.0 volume percent carbon dioxide. Only the lowest level of carbon dioxide (0.05 volume percent) was not as effective in the clean or prior exposed tubes. Carbon monoxide as a dopant in hydrogen was less effective than carbon dioxide at a given concentration level. Of the four dopant levels studied; 1.0, 0.5, 0.2, and 0.05 volume percent carbon monoxide, only the 1.0 and 0.5 volume percent were effective in reducing and maintaining low hydrogen permeation through the CG-27.

Misencik, J. A.↗

Effect of surface pre-oxidation on hydrogen permeation in alpha titanium

The effect of a specific oxidation treatment, to which a titanium specimen was subjected, on the permeation of hydrogen through the titanium specimen was studied. The oxidation treatment involved the maintenance of the specimen in an oxygen atmosphere at a temperature of 270 C for a time of four hours. It was found that the oxidation treatment has the effect of decreasing the permeation rate. However, the first power pressure dependency is not affected.

Shah, K. K.↗

Hydrogen Permeation Analysis Tool

There is a rising need for the measurement and understanding of hydrogen transport properties in materials for the energy and transportation industries. The Hydrogen Permeation Analysis Tool (HyPAT) provides a user friendly interface for batch analysis of dynamic hydrogen permeation data to calculate the transport properties permeability, solubility, and diffusivity. A built in literature database provides an easy comparison to known values. A common method for measuring these hydrogen transport properties is dynamic pressure rise permeation experiments, for example, those done in the Static Gas Absorption and Permeation (SGAP) experiment at INL. Most laboratories develop individual, in-house codes for data analysis. HyPAT provides a platform that can be adopted by other user groups for such experimental analysis and significantly reduce personnel time spent performing data analysis.

Fuerst, ThomasF↗

Titanium Nitride as an Intermetallic Diffusion Barrier for Hydrogen Permeation in Palladium–Vanadium Composite Membranes

Hydrogen purification is a critical industrial process, and there are ongoing efforts to develop low-cost alternatives to palladium foil membranes. Titanium nitride (TiN) is studied as an interdiffusion barrier to enable hydrogen permeation in composite palladium–vanadium membranes. TiN was deposited via reactive sputtering, and films with the desired (200) orientation were obtained in the metallic regime at 400 °C under a 200 V bias to the substrate. The permeability of thin-film TiN was determined with palladium-based sandwich structures. TiN layers up to 10 nm resulted in a minimal decrease in flux (~20%) relative to a freestanding PdCu foil, which was attributed to the interfacial resistance. At greater thicknesses, the TiN layer was rate-limiting, and it was found that the effective permeability of the sputtered TiN thin films was ~6 × 10−12 mol s−1 m−1 Pa−0.5. Composite Pd|TiN|V|TiN|Pd membranes exhibited permeability values up to three times greater than pure palladium, exhibiting stability at 450 °C for over 100 h, with the lack of intermetallic diffusion and alloy formation being confirmed with XRD. The membranes were unstable at 500 °C, which was attributed to the instability of the thin Pd layer and loss of catalytic activity.

Biochemistry & Molecular Biology↗

Evaluation of dopants in hydrogen to reduce hydrogen permeation in candidate Stirling engine heater head tube alloys at 760 deg and 820 deg

Alloy tubes filled with hydrogen doped with various amounts of carbon monoxide, carbon dioxide, ethane, ethylene, methane, ammonia, or water were heated in a diesel fuel-fired Stirling engine simulator materials test rig for 100 hours at 21 MPa and 760 or 820 C to determine the effectiveness of the dopants in reducing hydrogen permeation through the hot tube walls. Ultra high purity (UHP) hydrogen was used for comparison. The tube alloys were N-155, A-286, Incoloy 800, Nitronic 40, 19-9DL, 316 stainless steel, Inconel 718, and HS-188. Carbon dioxide and carbon monoxide in the concentration range 0.2 to 5 vol % were most effective in reducing hydrogen permeation through the hot tube walls for all alloys. Ethane, ethylene, methane, ammonia, and water at the concentrations investigated were not effective in reducing the permeation below that achieved with UHP hydrogen. One series of tests were conducted with UHP hydrogen in carburized tubes. Carburization of the tubes prior to exposure reduced permeation to values similar to those for carbon monoxide; however, carbon dioxide was the most effective dopant.

Misencik, J. A.↗

Gas phase hydrogen permeation in a Ni-Fe-Co superalloy

Hydrogen permeation measurements have been conducted for the Incoloy 909 Ni-Fe-Co superalloy via the 'membrane' technique, in which the gaseous hydrogen at the entrance of a thin membrane is transposed through the bulk to the exit side of the membrane, at 400-810 C; the pressure range explored was 2.7 x 10 exp 3 to 1.3 x 10 exp 5 N/sq m. The lattice hydrogen solubility of Incoloy 909 is found to be only weakly temperature-dependent. These results are compared with those obtained for Incoloy 903.

Shanabarger, Mickey R.↗

Gas-phase hydrogen permeation through alpha iron, 4130 steel, and 304 stainless steel from less than 100 C to near 600 C

Gas phase hydrogen permeation studies were conducted on hollow, cylindrical membranes of triply zone-refined alpha iron, AISI 304 austenitic stainless steel, and AISI-SAE 4130 steel in both the normalized (ferrite and carbide) and quenched and tempered (martensite) conditions. Membrane temperature was varied from less than 100 C to near 600 C and hydrogen pressure was varied. For one membrane material, normalized 4130 steel, gas phase hydrogen transport under both steady state and nonsteady state conditions was demonstrated to be controlled by lattice diffusion. Additionally, Sievert's law was shown to be applicable. For all membrane materials, expressions for the coefficients for hydrogen permeation were determined by analysis of steady state transport; the coefficients for diffusion were determined by the lag time technique applied to nonsteady state transport; and through a knowledge of the Sievert's constants, the subsurface equilibrium lattice hydrogen concentrations were determined.

Nelson, H. G.↗

Development of an atomic layer deposition system for deposition of alumina as a hydrogen permeation barrier

Tritium permeation into and through materials poses a critical challenge for the development of nuclear fusion reactors. Minimizing tritium permeation is essential for the safe and efficient use of available fuel supplies. In this work, we present the design, construction, and validation of custom atomic layer deposition (ALD) and deuterium permeation measurement systems aimed at developing thin-film hydrogen permeation barriers. Using the ALD system, we deposited conformal $\mathrm{Al}_{2}\mathrm{O}_{3}$ films on copper foil substrates and characterized their growth behavior, morphology, and composition. ALD growth rates of ∼1.1 Å/cycle were achieved for temperatures between 100 ∘ C and 210 ∘ C. Permeation measurements on bare and alumina coated copper foils revealed a significant reduction in deuterium flux with the addition of a ∼10 nm $\mathrm{Al}_{2}\mathrm{O}_{3}$ layer. While bare copper followed diffusion-limited transport consistent with Sievert’s law, the alumina-coated samples exhibited surface-limited, pore-mediated transport with linear pressure dependence. Arrhenius analysis showed distinct differences in activation energy for the two transport regimes, and permeation reduction factors exceeding an order of magnitude were observed. These results demonstrate the potential of ALD-grown $\mathrm{Al}_{2}\mathrm{O}_{3}$ films as effective hydrogen isotope barriers and provide a foundation for future studies on film optimization and integration into fusion-relevant components.

atomic layer deposition↗

Recent Advances and Prospects in Design of Hydrogen Permeation Barrier Materials for Energy Applications—A Review

The hydrogen infrastructure involves hydrogen production, storage and delivery for utilization with clean energy applications. Hydrogen ingress into structural materials can be detrimental due to corrosion and embrittlement. To enable safe operation in applications that need protection from hydrogen isotopes, this review article summarizes most recent advances in materials design and performance characterization of barrier coatings to prevent hydrogen isotopes’ absorption ingress and permeation. Barriers are crucial to prevent hydride formation and unwanted hydrogen effects to increase safety, materials’ lifetime and reduce cost for applications within nuclear and renewable energy. The coating may be applied on a material that requires protection from hydrogen pick-up, transport and hydride formation in hydrogen storage containers, in pipelines, spent nuclear fuel storage or in nuclear reactors. While existing, commercial coatings that have been much in use may be satisfactory for various applications, it is desirable to evaluate whether alternative coating concepts can provide a greater resistance to hydrogen isotope permeation along with other improved properties, such as mechanical strength and thermal resistance. The information presented here is focusing on recent findings within the past 5–7 years of promising hydrogen barriers including oxides, nitrides, carbon, carbide, MAX-phases and metals and their mechanical strength, hydrogen pick-up, radiation resistance and coating manufacturing techniques. A brief introduction to hydrogen permeation is provided. Knowledge gaps were identified to provide guidance for material’s research prospects.

08 HYDROGEN↗

Hydrogen permeation, diffusion and solubility in IN-100 and Waspaloy

An attempt has been made to determine the permeation rate of hydrogen in IN-100 and Waspaloy by determining the evolution rate of hydrogen from a closed capsule of the test materials. Enclosed vanadium hydride was the source of hydrogen in the capsule. The presentation discusses the treatment of data and assesses the validity of the techniques in permeation measurement. In addition to permeation experiments, the solubility and diffusion of hydrogen in IN-100 and Waspaloy were also determined. For hydrogen diffusion in Waspaloy, Delta H was 38.5 kJ and D(0) was 0.0026 sq cm/sec. For IN-100, Delta H was 68.2 kJ and D(0) was 0.059 sq cm /sec. Both IN-100 and Waspaloy exhibited limited solubility of hydrogen at pressures up to 340 atmospheres hydrogen.

Khan, A. S.↗

Ab initio Screening of Refractory Nitrides and Carbides for High Temperature Hydrogen Permeation Barriers

Density functional theory was used to screen eleven refractory materials – two pure metals, six nitrides, and three carbides–as high-temperature hydrogen permeation barriers to prevent hydrogen embrittlement. Activation energies were calculated for atomic hydrogen (H) diffusion into the first subsurface layer from the lowest energy surface of the high-temperature phase of each candidate material. The candidate barrier materials with the highest activation energies are h-BN, c-BN, HfN, and ZrN with predicted barriers of 3.25 eV, 3.23 eV, 3.14 eV, and 2.76 eV, respectively. Strain energies, Bader charges, and density of states were calculated for the diffusing H at the relaxed initial state and the transition state to provide insight into contributing factors to high energy barriers. The diffusing H atom in materials with the highest predicted barriers are protic. In addition, interstitial H atoms induce mid-gap states in the density of states of both BN polymorphs. The nitrogen retention of each nitride material at high temperatures was predicted using nitrogen vacancy formation energies with respect to gaseous nitrogen. Experimental evaluation of nitrogen retention in h-BN, ZrN, and TiN confirmed their resistance to nitrogen loss at 1773 K. However, of these nitrides, TiN is predicted to be the least stable. This work identifies multiple promising materials that are predicted to be effective hydrogen barriers at high temperatures and that are stable at temperatures above 2700 K, with BN predicted to perform best.

Density Functional Theory (DFT)↗

Gas-phase hydrogen permeation through alpha-titanium - Surface film and dimensional effects

The process of hydrogen transport through alpha-Ti involves simultaneous diffusion and phase boundary reactions at both surfaces, with the relative effect on each surface depending on the extent of surface contamination as well as the physical dimensions of the titanium membrane used. It is shown by the present study that hydrogen permeation in commercially pure alpha-Ti increases exponentially with temperature and is dependent on the first power of the input pressure, whether the surface is as-polished, preoxidized or prenitrided. Permeation decreases in the case of the as-polished condition if nitride or oxide films are formed at the surface in contact with source hydrogen, while increasing slightly for the same condition if such films are formed at the hydrogen exit surface.

Shah, K. K.↗

Hydrogen Permeation in FeCrAl APMT Alloy for Accident Tolerant Fuel Cladding

Iron-chromium-aluminum (FeCrAl) alloys such as APMT (advanced powder metallurgy tubing) are candidate materials to replace zirconium alloys for the light water reactor fuel cladding. This alloy meets the requirements to be a material more tolerant of high-temperature accidents than the current zirconium alloys. One concern is that the use of FeCrAl may result in an increase in tritium presence in the coolant compared to the current design. The aim of the current research was to obtain effective diffusion coefficients (D eff ) for hydrogen through APMT using the Devanathan-Stachurski cell. Results showed that at 30°C the D eff value was 2.8 × 10 -8 cm 2 /s. Results also showed a linear relationship between the permeated hydrogen flux and the inverse of the test specimen thickness, which demonstrated the validity of the permeation measurements.

36 MATERIALS SCIENCE↗

Hydrogen permeation in iron-chromium-aluminum (FeCrAl) alloys and the effects of microstructure and surface oxide

Iron–chromium–aluminum (FeCrAl) class alloys are candidates for use as cladding for accident-tolerant fuels and moderators. In this context, hydrogen isotope permeation in FeCrAl alloys is an important material property. Here, in the present work, the apparent permeability, effective diffusivity, and apparent solubility of hydrogen in the FeCrAl alloys C26M and Kanthal D (KD) were measured with gas-driven hydrogen permeation. Permeation measurements were conducted at temperatures of 400 to 700 °C and at gas-driven pressures from 1 to 100 kPa. In particular, the effect of grain size on hydrogen transport was studied with KD samples with three different microstructures: nanocrystalline (NC), ultra-fine grained (UFG), and coarse-grained (CG). The UFG and NC specimens had higher apparent activation energies (73.4 kJ mol -1 and 65.2 kJ mol -1 , respectively) for hydrogen permeability than the CG sample (46.9 kJ mol -1 ). An aluminum oxide layer formed on the primary- and secondary-side surfaces of all samples subjected to permeation experiments which demonstrated the propensity of FeCrAl alloys to form these innate oxide permeation barriers.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Development of Hydrogen Permeation Barrier and Matrix Interaction Protection Coatings for TZM Enclosure of Hydride Moderators (Microreactor Program M3 Report)

It is important to develop a high-performance enclosure solution for hydride-based microreactor moderation components to effectively suppress hydride thermal decomposition and prevent hydrogen loss in harsh in-reactor environments. Currently, the DOE-NE Microreactor Program (MR program) is investigating the titanium-zirconium-molybdenum (TZM) canned yttrium hydride (YH 2-x ) solution, which provides acceptable hydrogen retainment performance up to ~700 °C. However, improvements in the enclosure are necessary for increasing long-term operation temperature beyond 700 °C and enhancing short-term survivability at even higher temperatures during power transients. One potential solution is the addition of a dedicated hydrogen permeation barrier, which can potentially improve the enclosure's performance. Furthermore, the hydride moderator components will be inserted into the microreactor matrix, which may consist of materials that are not chemically inert against TZM. Therefore, the TZM might need to be protected from the external environment through the application of another surface protection coating. To address these critical issues, two types of barrier coatings optimized for TZM-based moderator enclosure has been developed. A multilayer coating approach has been used to identify TZM-compatible barrier materials. Behavior of these coating designs against H 2 permeation and long-term high-temperature graphite matrix interactions has been examined in detail. Additionally, the developed coatings' behavior when exposed to both high-temperature thermal cycling and heavy-ion irradiation has also been investigated. Overall, the development of these barrier coatings is essential for achieving maturity for the metal hydride moderator technology. The results in this report will provide crucial insights into the behavior of the developed coatings and their potential for improving the long-term performance of TZM-based moderator enclosures.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

Surface effects on hydrogen permeation through Ti-14Al-21Nb alloy

Hydrogen transport through Ti-14Al-21Nb (wt percent) alloy is measured using ultrahigh vacuum permeation techniques over the temperature range of 500 to 900 C and hydrogen pressure range of 0.25 to 10 torr. Hydrogen permeability through the alloy can be described through two different mechanisms depending on th temperature of exposure. In the 675 to 900 C range, the process is diffusion-limited: the permeability has a weak temperature dependence, but the diffusivity has a strong temperature dependence. Below 675 C, the permeation rate of hydrogen is very sensitive to surface controlled processes such as the formation of a barrier layer from contaminants. A physical model explaining the role of surface films on the transport of hydrogen through Ti-14Al-21Nb alloy was described.

Sankaran, Sandara N.↗

Evaluating hydrogen permeation through medium-density and high-density polyethylene pipes to enable a hydrogen-compatible infrastructure

As the United States and the global community pursue energy abundance and resilience, hydrogen is becoming a critical energy carrier. The future of hydrogen transport depends on one thing: verifying that today’s pipelines are hydrogen ready. This study investigates the permeation behavior of medium-density polyethylene (MDPE) and high-density polyethylene (HDPE) pipelines under pure hydrogen gas environment at various pressures and temperatures. Using thermal desorption analysis (TDA) and direct pipe permeability measurements, hydrogen loss rates are quantified, revealing minimal permeation losses (< 10.5 g/km/day) under realistic operating conditions. Effects of temperature and pressure with Standard Dimension Ratios (SDR), were evaluated to determine their influence on permeation rates of MDPE and HDPE pipelines. In addition, ex-situ density and degree of crystallinity (DOC) of MDPE and HDPEs after hydrogen exposure were also investigated to understand pressure-dependency of polymer properties. The findings provide essential data for assessing polymer-based pipeline materials for safe and reliable hydrogen transport.