Self-healable Copolymer Composites for Extended Service H 2 Dispensing Hoses
In this project, we designed, synthesized and fabricated using X-winder technologies precommercialized novel, self-healingable commodity copolymer fiber-reinforced composites to extend the H 2 hose service life beyond the current target of 1000 fills. These studies demonstrated that these composites are able to withstand over 25,000 damage-repair cycles, which was the main objective of the proposed project, in the temperature range of -40 to +80 °C under variable pressures. When micro-cracks are formed after about 1,000 cycles/fueling per hose in the inner composite layer, these micro-cracks self-heal, thus extending the lifetime of a prototype inner layer of the hose. These composites were tested by exposure to H 2 fuel and demonstrated the ability to recover from mechanical damage. Thermomechanical testing combined with analysis of the stress and strain fields across the cross-section of the inner layer composite hoses also identified the ring-like stresses on the edge of inner layers arising from changes of the fiber winding angle directions from +45° to -45°. The developed novel concept that self-healing commodity copolymers can be used in the development of prototype composites for the extended service of H 2 dispensing hoses will have major implications for other energy-related technologies, where the extended service life in harsh environments is expected. In this project, we optimized, validated, and demonstrated novel copolymer fiber-reinforced composites for H 2 dispensing hose applications, which can be utilized in future manufacturing using commodity materials. The estimated cost of materials (exluding labor) is in the range of < $1.0/ft.