Vacuum thermal-mechanical fatigue testing of two iron base high temperature alloys
Ultrahigh vacuum elevated temperature low cycle fatigue and thermal fatigue tests of 304 stainless steel and A-286 alloy have shown significant effects of frequency and combined temperature-strain cycling on fatigue life. At constant temperature, the cyclic life of both alloys was lower at lower frequencies. Combined temperature-strain cycling reduced fatigue life with respect to isothermal life at the maximum temperature of the thermal cycle. Life reductions with in-phase thermal cycling (tension at high temperature, compression at low temperature) were attributed to grain boundary cavitation caused by unreversed tensile grain boundary sliding. The proposed mechanism for out-of-phase cavity generation involved accumulation of unreversed compressive grain boundary displacements which could not be geometrically accomodated by intragranular deformation in the low-ductility A-286 alloy.