Search NASA⌕ Search

SEARCH · Search NASA

Results for “k dot p method”

Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.

Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.

4 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS2003

Spurious States-Free Solution of the k dot p Hamiltonian for Heterostructures

A method for eliminating spurious solution in the k dot p Hamiltonian has been proposed. Introduction of additional off-diagonal alpha k(exp 2) term converts spurious solution with large real wave vector to evanescent solution with large imaginary wave vector. This modification keeps the same effective masses at Gamma point and introduces negligible deviation from original nonparabolicity. A set of unphysical fast oscillation eigenfunctions in confined states of heterostructures are removed.

Kolokolov, Konstantin I.↗
NASA NTRS2001

Band Anticrossing in Highly Mismatched Compound Semiconductor Alloys

Compound semiconductor alloys in which metallic anions are partially replaced with more electronegative isoelectronic atoms have recently attracted significant attention. Group IIIN(sub x)V(sub 1-x) alloys with a small amount of the electronegative N substituting more metallic column V elements has been the most extensively studied class of such Highly Mismatched Alloys (HMAs). We have shown that many of the unusual properties of the IIIN(sub x)V(sub 1-x) alloys can be well explained by the Band Anticrossing (BAC) model that describes the electronic structure in terms of an interaction between highly localized levels of substitutional N and the extended states of the host semiconductor matrix. Most recently the BAC model has been also used to explain similar modifications of the electronic band structure observed in Te-rich ZnS(sub x)Te(sub 1-x) and ZnSe(sub y)Te(sub 1-y) alloys. To date studies of HMAs have been limited to materials with relatively small concentrations of highly electronegative atoms. Here we report investigations of the electronic structure of ZnSe(sub y)Te(sub 1-y) alloys in the entire composition range, y between 0 and 1. The samples used in this study are bulk ZnSe(sub y)Te(sub 1-y) crystals grown by either a modified Bridgman method or by physical vapor transport. Photomodulated reflection (PR) spectroscopy was used to measure the composition dependence of optical transitions from the valence band edge and from the spin-orbit split off band to the conduction band. The pressure dependence of the band gap was measured using optical absorption in a diamond anvil cell. We find that the energy of the spin-orbit split off valence band edge does not depend on composition and is located at about 3 eV below the conduction band edge of ZnSe. On the Te-rich side the pressure and the composition dependence of the optical transitions are well explained by the BAC model which describes the downward shift of the conduction band edge in terms of the interaction between localized Se states and the conduction band. On the other hand we show that the large band gap reduction observed on the Se-rich side of the alloy system is a result of an interaction between the localized Te level and the valence bands. This interaction leads to the formation of a Te-like valence band edge that strongly interacts with the light hole valence band. Calculations based on a modified k(sup dot)p model account for the reduction of the band gap and the large increase of the spin-orbit splitting observed in Se-rich ZnSe(sub y)Te(sub 1-y) alloys. We will also discuss the importance of these new results for understanding of the electronic structure and band offsets in other highly mismatched alloy systems.

Yu, Kin Man↗
NASA NTRS2003

An Experimental Investigation To Determine Interaction Between Rotating Bodies

A brass (copper+zinc) wheel, with a 4-in diameter and 1.4 in thick, was used for this investigation. Ceramic ball bearings were used to safely spin the wheel up to 40,000 rpm. The wheel was also electrically insulated from the rest of the armature. For spinning, an air turbine was used. The rotational velocity was measured by two methods: (1) A simple strobe light and (2) a photodiode that detected laser beam pulses as they passed through a slot in the rotating shaft. The magnetic sensor is based on a giant magnetoresistivity, and consists of a balanced bridge circuitry. The position of the sensor was as close as possible to the rim of the wheel. The linear dimension of the sensor is approximately equal to 8 mm so that the offset from the surface is on the order of 15 percent. We did not use any goniometer system, so the accuracy of the angular position is not high, being estimated within a few degrees, with the main uncertainty being the direction of Earth's magnetic field. We attempted to fit the experimental data with the presented theory by selecting the best value for the electrical conductivity of the wheel. The results of this procedure are displayed, where the black dots represent experimental values. A slight misfit on the right shoulder can be due to slight angular misalignment from a 90 degree position. The obtained value for the resistivity is 43 n(OMEGA)m, which compares well with those listed. We can conclude, based on these measurements, that the proposed theory satisfactorily explains our experiments.

Grugel, R. N.↗
NASA NTRS2021

Microstructural Observations on Advanced Multilayer Protective Coatings for Nuclear Thermal Propulsion

The present research discusses the microstructures of a new multilayered coating concept proposed to solve the “midrange corrosion” problem observed in NbC and ZrC-coated graphite (Gr) nuclear fuels during the NERVA/Rover programs. The concept envisions designing a compliant multilayered coatings architecture to accommodate the thermal expansion mismatch strains between the ZrC outer coating and the Gr/(U,Zr)C fuel matrix along with using a diffusion barrier to minimize carbon and hydrogen diffusion, respectively. Multilayered coatings were deposited on Gr substrates by chemical vapor deposition (CVD). Graphite disks, as well as the inner channels of a 19-hole hexagonal rod 152.4 mm long, were coated by CVD in proof-of concept process demonstration studies. Coated disk specimens were thermally-cycled between ambient and 1900 K for as long as 20 cycles with a 1h hold time at the temperature using both stepped and non-interrupted thermal cycling methods. Detailed cross-sectional microstructural analyses were conducted on the thermally-cycled coated disks. These results showed that the coatings were intact after 20 thermal cycles at 1900 K although the bonding of the overlay Mo coating appeared to be influenced by the oxygen content in the layer. Seven transverse sections were cut along the length from the coated hexagonal rod for microstructural studies. All the nineteen channels were observed to have been coated in all the sections. This paper reports the results of detailed microstructural analyses, compositional line scans and x-ray dot maps conducted on three coated channels from a mid-section of the rod. The measured values of carbon (C) were observed to be exceptionally high in all the specimens, which were attributed to hydrocarbon contamination of the specimen surfaces. It was observed that the oxygen (O) levels were high in all the coating layers even after approximately correcting for the observed high values of C. The source of O contamination of the CVD reactor system was attributed to either the presence of oxychloride impurities in the precursor salts or a pin hole leak in the coating system. It is concluded that high values of O result in poor bonding of the Mo overlay to the ZrC layer. These trials have established that it is possible to deposit multilayered coatings by CVD in 19-hole hexagonal rods 152.4 mm long similar to the NERVA fuel rod design although the quality of the coatings and the uniformity of their thicknesses require further improvement.

Nuclear thermal propulsion, multilayer coatings, m↗