A Hybrid Physics-Based, Data-Driven Approach to Model Damage Accumulation in Corrosion of Polymeric Adhesives
The degradation of polymeric adhesives in dissimilar joints is a menace to electric and structural components of the automotive industry. In polymeric adhesives, failure often occurs due to damage accumulated from discrete environmental sources—thermal degradation, oxidation, hydrolysis, radiation, and moisture—that are combined with progressive damage mechanisms, such as aging and fatigue. Because most damage mechanisms that lead to degradation act in parallel, the estimation of the lifetime of a polymeric material becomes a significant reliability issue, no study currently exists that can simultaneously consider even two of these phenomena. Most current efforts are directed toward a single-phenomenon, single-model approach in which a model is developed to cover one specific damage mechanism. While this approach is advantageous in exploring single mechanisms, it is strongly inconclusive for degradation that occurs by multiple damage mechanisms. Our team plans to take a fresh perspective by designing a hybrid constitutive/data-driven approach that allows models of different damage mechanisms to be integrated into one model and then used to explore the degradation-induced failure of polymeric adhesives. The theoretical-computational part of this work is divided into four research components as described in the Approach section below.