NASA NTRS1991

Thermochemical analysis of the silicon carbide-alumina reaction with reference to liquid-phase sintering of silicon carbide

The stabilities of different phases in the Si-Al-C-O system are calculated from thermodynamic considerations with the objective of identifying the liquid phases formed during sintering of SiC in the presence of Al2O3. It is shown that a liquid phase can form at the sintering temperatures by the reaction of SiC with Al2O3. Depending on the carbon activity, the liquid can be either of the following: Al2O3 + Al4C3, SiC + Al4C3, or molten aluminum. The stability of the aluminosilicate melts that can form by the reaction of Al2O3 with the surface silica layer on SiC powders is also evaluated. Several factors that influence liquid-phase sintering, such as the solubility of SiC in the melts and the generation of gases during sintering, are discussed. The results of the thermodynamic analysis are compared with the observed sintering behavior for SiC.

Misra, Ajay K.↗
NASA NTRS1989

The gravitational effects on liquid phase sintering

The liquid-phase sintering of heavy-metal PM alloys containing 78, 83, 88, 93, or 98 wt pct W plus Ni and Fe in a 7:3 ratio is investigated experimentally. The focus is on the potential role of gravity in phenomena such as specimen slumping and distortion, liquid migration, and microstructural coarsening. The results are presented in extensive graphs and micrographs and discussed in detail, and a preliminary grain-growth model is developed which accounts for the effects of contiguity and the volume fraction of solid.

Kipphut, C. M.↗
NASA NTRS1988

Gravity and configurational energy induced microstructural changes in liquid phase sintering

Experiments were performed with W-Ni-Fe heavy alloys in order to measure the microstructural changes vs. position that occur in liquid-phase sintering under normal gravity. The experimentally observed segregation is less than the calculated equilibrium segregation due to the retarding effect from the rigid solid skeleton formed during sintering. These results improve understanding of microstructure, mechanical properties, component shape, and dimensional stability benefits that may be realized from low-gravity sintering.

Kipphut, C. M.↗
NASA NTRS1977

Pressureless sintered beta prime-Si3N4 solid solution: Fabrication, microstructure, and strength

Si3N4, AlN, and Al2O3 were used as basic constituents in a study of the pressureless sintering of beta prime-Si3N4 solid solution as a function of temperature. Y2O3-SiO2 additions were used to promote liquid-phase sintering. The sintered specimens were characterized with respect to density, microstructure, strength, oxidation, and thermal shock resistance. Density greater than 98 percent of theoretical was achieved by pressureless sintering at 1750 C. The microstructure consisted essentially of fine-grained beta prime-Si3N4 solid solution as the major phase. Modulus of rupture strengths up to 483 MPa were achieved at moderate temperature (1000 C), but decreased to 228 MPa at 1380 C. This substantial strength loss was attributed to a glassy grain boundary phase formed during cooling from the sintering temperature. The best oxidation resistance was exhibited by a composition containing 3 mol % Y2O3-SiO2 additives. Water quench thermal shock resistance was equivalent to that of reaction sintered silicon nitride but lower than hot-pressed silicon nitride.

Dutta, S.↗
NASA NTRS1977

Pressureless sintered beta-prime-Si3N4 solid solution - Fabrication, microstructure, and strength

Pressureless sintering of beta-prime-Si3N4 solid solution was studied as a function of temperature using Si3N4, A1N, and Al2O3 as basic constituents. Y2O3-SiO2 additions were used to promote liquid-phase sintering. The sintered specimens were characterized with respect to density, microstructure, strength, oxidation, and thermal shock resistance. Density greater than 98 percent of theoretical was achieved by pressureless sintering at 1750 C. The microstructure consisted essentially of fine-grained beta-prime-Si3N4 solid solution as the major phase. Modulus of rupture strengths up to 483 M Pa were achieved at moderate temperature (1000 C), but decreased to 228 M Pa at 1380 C. This substantial strength loss was attributed to a 'glassy' grain boundary phase formed during cooling from the sintering temperature. The best oxidation resistance was exhibited by a composition containing 3 mol % Y2O3-SiO2 additives. Water quench thermal shock resistance was equivalent to that of reaction sintered silicon nitride but lower than hot-pressed silicon nitride.

Dutta, S.↗
NASA NTRS1988

Numerical simulation of morphological development during Ostwald ripening

The morphological evolution of a small number of particles undergoing Ostwald ripening in two dimensions was investigated using a boundary integral technique. The numerical calculations show that, in many cases, interparticle diffusional interactions do not induce large distortions in particle morphology from a circle, due to the strong local interaction between regions of different curvature on the same particle. Particle migration due to interparticle diffusional interactions was observed, with the migration distance larger than the initial radius of a particle, which is linked to the particle spatial arrangement. As diffusion is the mechanism for the migration, it is expected that particle movement is a generic aspect of the coarsening process at high volume fractions of coarsening phase and, possibly, at low volume fractions. The calculations support unambiguously the Ostwald ripening mechanism for flat formation during liquid-phase sintering. As such, the appearance or regions of low interfacial curvature is a dynamic phenomenon dependent on interparticle diffusion.

Voorhees, P. W.↗