NASA NTRS2011

Timescale Correlation between Marine Atmospheric Exposure and Accelerated Corrosion Testing

Evaluation of metal-based structures has long relied on atmospheric exposure test sites to determine corrosion resistance in marine environments. Traditional accelerated corrosion testing relies on mimicking the exposure conditions, often incorporating salt spray and ultraviolet (UV) radiation, and exposing the metal to continuous or cyclic conditions of the corrosive environment. Their success for correlation to atmospheric exposure is often a concern when determining the timescale to which the accelerated tests can be related. Accelerated laboratory testing, which often focuses on the electrochemical reactions that occur during corrosion conditions, has yet to be universally accepted as a useful tool in predicting the long term service life of a metal despite its ability to rapidly induce corrosion. Although visual and mass loss methods of evaluating corrosion are the standard and their use is imperative, a method that correlates timescales from atmospheric exposure to accelerated testing would be very valuable. This work uses surface chemistry to interpret the chemical changes occurring on low carbon steel during atmospheric and accelerated corrosion conditions with the objective of finding a correlation between its accelerated and long-term corrosion performance. The current results of correlating data from marine atmospheric exposure conditions at the Kennedy Space Center beachside corrosion test site, alternating seawater spray, and immersion in typical electrochemical laboratory conditions, will be presented. Key words: atmospheric exposure, accelerated corrosion testing, alternating seawater spray, marine, correlation, seawater, carbon steel, long-term corrosion performance prediction, X-ray photoelectron spectroscopy.

Montgomery, Eliza L.↗
NASA NTRS1976

Flaw growth of 7075, 7475, 7050 and 7049 aluminum alloy plate in stress corrosion environments

Marine atmosphere and laboratory stress corrosion test results on smooth and precracked specimens from 7075, 7475, 7050, and 7049 alloy plates (1.25 and 3.0-in. thick) are presented. It is shown that for a given strength level, alloys 7050-T7X and 7049-T7X have superior short-transverse stress corrosion resistance (SCR) to 7X75-T7X. At typical strength levels above the minimum, for example, SCR of these alloys is considerably better than that of 7075-T76, and approaches that of 7075-T73. Alloy 7475 maintains an advantage in the area of fracture toughness, however, because it can be thermally processed to give particularly clean microstructures. Results from precracked specimens are in good qualitative agreement with those obtained from smooth specimens. Although both specimen types are capable of distinguishing between -T6, -T76 and -T73 tempers in relatively short time periods the precracked specimen provides more information about crack growth rates.

Dorward, R. C.↗
NASA NTRS2015

NASA's Corrosion Technology Laboratory at the Kennedy Space Center: Anticipating, Managing, and Preventing Corrosion

The marine environment at NASAs Kennedy Space Center (KSC) has been documented by ASM International (formerly American Society for Metals) as the most corrosive in North America. With the introduction of the Space Shuttle in 1981, the already highly corrosive conditions at the launch pads were rendered even more severe by the highly corrosive hydrochloric acid (HCl) generated by the solid rocket boosters (SRBs). Numerous failures at the launch pads are caused by corrosion. The structural integrity of ground infrastructure and flight hardware is critical to the success, safety, cost, and sustainability of space missions. NASA has over fifty years of experience dealing with unexpected failures caused by corrosion and has developed expertise in corrosion control in the launch and other environments. The Corrosion Technology Laboratory at KSC evolved, from what started as an atmospheric exposure test site near NASAs launch pads, into a capability that provides technical innovations and engineering services in all areas of corrosion for NASA, external partners, and customers.This paper provides a chronological overview of NASAs role in anticipating, managing, and preventing corrosion in highly corrosive environments. One important challenge in managing and preventing corrosion involves the detrimental impact on humans and the environment of what have been very effective corrosion control strategies. This challenge has motivated the development of new corrosion control technologies that are more effective and environmentally friendly. Strategies for improved corrosion protection and durability can have a huge impact on the economic sustainability of human spaceflight operations.

Corrosion Control↗
NASA NTRS1978

Flat growth of 7075, 7475, 7050 and 7049 aluminum alloy plate in stress corrosion environments: 2-year marine atmosphere results

Marine atmospheric exposure of smooth and precracked specimens from 7075, 7475, 7050 and 7049 plates support the conclusion that for a given strength level, the short transverse stress corrosion resistance of 7050-T7X and 7049-T7X is superior to that of 7075-T7X. The threshold stress intensity (K sub Iscc) for these alloys is about 25 MPa square root m at a yield strength of about 460 MPa; the corresponding yield strength level for 7075-T7X at this SCR level is about 425 MPa. Additional tests on two lots of high-toughness 7475 plate indicate that this alloy is capable of achieving K sub Iscc values of about 35 MPa square root m at yield strengths of 400-450 MPa. Precracked specimens from all these 7XXX-series alloys are subject to self loading from corrosion product wedging. This effect causes stress corrosion cracks to continue growing at very low apparent stress intensities, and should therefore be considered a potential driving force for stress corrosion in design and materials selection.

Dorward, R. C.↗
NASA NTRS1981

Flaw growth of 7075, 7475, 7050 and 7049 aluminum alloy plate in stress corrosion environments: 4-year marine atmosphere results

After nearly 53 months of exposure to marine atmosphere, crack growth in SL DCB specimens from 7075, 7475, 7050, and 7049-T7X plate has slowed to the arbitrary 10 to the -10 power m/sec used to define threshold stress intensity. Because some specimens appear to be approaching crack arrest, the importance of self-loading from corrosion product wedging as a significant driving force for crack propagation in overaged materials is questioned. Crack length-time data were analyzed using a computer curve fitting program which minimized the effects of normal data scatter, and provided a clearer picture of material performance. Precracked specimen data are supported by the results of smooth specimen tests. Transgranular stress corrosion cracking was observed in TL DCB specimens from all four alloys. This process is extremely slow and is characterized by a striated surface morphology.

Hasse, K. R.↗
DOE OSTI2024

Understanding the Interactions of Multiple Pits Under Freely Corroding Conditions

The interactions of two propagating pits on a single cathode surface were evaluated across variations in chloride concentration, water layer (WL), pit sizes, separation distance (x 2 ), and cathode size (L Cath ) under freely corroding conditions using Finite Element Methods (FEM). Calculated FEM current was utilized to predict stability based on the Galvele pit stability product. FEM predictions were utilized to train a neural network machine learning model for rapid stability predictions. Pit one is in the center of a circular cathode while pit two moves radially from the center pit. With two pits, the overall current in each pit is decreased with respect to a single pit, however, the total current is increased. Increasing WL and L Cath generally increased overall current in each pit and increased predicted maximum pit sizes. Increasing x 2 decreased current in pit two due to less cathode being available to support dissolution in proximity to pit two. Increasing chloride concentration from 0.6 to 3 M NaCl increased current, while increasing from 3 to 5.3 M NaCl decreased current. An overall increase in predicted pit size with increase in chloride concentration is predicted. A machine learning model was created to predict current and maximum pit size and captured underlying physics and predicted stability across the multidimensional parameter space.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
NASA NTRS2002

The Effects of Chemical Wash Additives on the Corrosion of Aerospace Alloys in Marine Environments

This paper presents the methodology for comparing the relative effectiveness of four chemical products used for rinsing airplanes and helicopters. The products were applied on a weekly basis to a series of flat alloy panels exposed to an oceanfront marine environment for one year. The results are presented along with comparisons of exposures of the same alloys that were not washed, were washed with seawater, or washed with de-ionized water.

MacDowell, Louis↗
NASA NTRS2012

Timescale Correlation between Marine Atmospheric Exposure and Accelerated Corrosion Testing - Part 2

Evaluation of metals to predict service life of metal-based structures in corrosive environments has long relied on atmospheric exposure test sites. Traditional accelerated corrosion testing relies on mimicking the exposure conditions, often incorporating salt spray and ultraviolet (UV) radiation, and exposing the metal to continuous or cyclic conditions similar to those of the corrosive environment. Their reliability to correlate to atmospheric exposure test results is often a concern when determining the timescale to which the accelerated tests can be related. Accelerated corrosion testing has yet to be universally accepted as a useful tool in predicting the long-term service life of a metal, despite its ability to rapidly induce corrosion. Although visual and mass loss methods of evaluating corrosion are the standard, and their use is crucial, a method that correlates timescales from accelerated testing to atmospheric exposure would be very valuable. This paper presents work that began with the characterization of the atmospheric environment at the Kennedy Space Center (KSC) Beachside Corrosion Test Site. The chemical changes that occur on low carbon steel, during atmospheric and accelerated corrosion conditions, were investigated using surface chemistry analytical methods. The corrosion rates and behaviors of panels subjected to long-term and accelerated corrosion conditions, involving neutral salt fog and alternating seawater spray, were compared to identify possible timescale correlations between accelerated and long-term corrosion performance. The results, as well as preliminary findings on the correlation investigation, are presented.

Montgomery, Eliza L.↗
NASA NTRS2013

The Behavior of Environmentally Friendly Corrosion Preventative Compounds in an Aggressive Coastal Marine Environment

The shift to use environmentally friendly technologies throughout future space-related launch programs prompted a study aimed at replacing current petroleum and solvent-based Corrosion Preventive Compounds (CPCs) with environmentally friendly alternatives. The work in this paper focused on the identification and evaluation of environmentally friendly CPCs for use in protecting flight hardware and ground support equipment from atmospheric corrosion. The CPCs, while a temporary protective coating, must survive in the aggressive coastal marine environment that exists throughout the Kennedy Space Center, Florida. The different protection behaviors of fifteen different soft film CPCs, both common petroleum-based and newer environmentally friendly types, were evaluated on various steel and aluminum substrates. The CPC and substrate systems were subjected to atmospheric testing at the Kennedy Space Center's Beachside Atmospheric Corrosion Test Site, as well as cyclic accelerated corrosion testing. Each CPC also underwent physical characterization and launch-related compatibility testing . The initial results for the fifteen CPC systems are reported : Key words: corrosion preventive compound, CPC, spaceport, environmentally friendly, atmospheric exposure, marine, carbon steel, aluminum alloy, galvanic corrosion, wire on bolt.

Montgomery, Eliza L.↗
NASA NTRS1983

Corrosion fatigue of high strength fastener materials in seawater

Environmental effects which significantly reduce the fatigue life of metals are discussed. Corrosion fatigue is a major concern in the engineering application of high strength fasteners in marine environments. The corrosion fatigue failure of an AISI 41L4O high strength steel blade to hub attachment bolt at the MOD-OA 200 kW wind turbine generator was investigated. The reduction of fatigue strength of AISI 41L4O in marine environments and to obtain similar corrosion fatigue data for candidate replacement materials was studied. The AISI 4140, PH 13-8Mo stainless steel, alloy 718 and alloy MP-35N were tested in axial fatigue at a frequency of 20 Hz in dry air and natural seawater. The fatigue data are fitted by regression equations to allow determination of fatigue strength for a given number of cycles to failure.

Tipton, D. G.↗
NASA NTRSDate not supplied

Evaluation Of Corrosion-Resistant Alloys for Use in Acidic and Marine Launch Environments at NASA Kennedy Space Center: 20-Year Study

After the completion of an initial three-year study to qualify corrosion-resistant stainless steel tubing for use in NASA Kennedy Space Center’s acidic and marine launch environment, test specimens remained exposed at the KSC Beachside Atmospheric Corrosion Test Site for long-term exposure. NASA KSC’s lifetime requirement for most ground support equipment is twenty years. After twenty-one years of marine exposure, NASA KSC took the unique opportunity to reevaluate the tubing after long-term exposure to better understand the corrosion resistance of these alloys as they reached their expected lifetime requirement. Metallurgical and corrosion analysis was performed on the CRES tubing components and the alloys were rated on performance. A summary of CRES alloy tubing corrosion-related performance after 20 years of exposure in a marine launch environment is presented in this work.

NASA KSC↗
NASA NTRS2015

Superhydrophobic Post Treatment and Coating Extenders for Improved Asset Sustainability

Launch structures, hardware, and ground support equipment, at NASA's John F. Kennedy Space Center in Florida, are exposed to a highly corrosive natural coastal marine environment. In addition, during launches, rocket exhaust deposition is also highly corrosive. Superhydrophobic coatings are being considered for additional corrosion protection on existing structures to enhance corrosion resistance and add an additional layer of protection against harsh environmental elements. These coatings have come into their own recently, and are now being investigated as corrosion protective coatings due to their water repelling capability. These coatings can be used on existing coatings, newly coated materials, or used on bare substrates. The coatings are not suitable for permanent corrosion protection, but can be used where additional corrosion control is desired or only when temporary corrosion control is needed, such as in hardware sitting on a launch pad for 30-45 days prior to a launch. In this study, superhydrophobic coatings were applied on various coated and uncoated substrates and exposed to the spaceport environment for various times up to 60 days. This paper highlights the current results of the superhydrophobic coatings performance evaluated by X-ray photoelectron spectroscopy, and contact angle measurements.

Coating↗
NASA NTRS1995

Plasma Sprayed Bondable Stainless Surface (BOSS) Coatings for Corrosion Protection and Adhesion Treatments

Plasma-sprayed Bondable Stainless Surface (BOSS) coatings are being developed under the Solid Propulsion Integrity Program's (SPIP) Bondlines Package. These coatings are designed as a steel case preparation treatment prior to insulation lay-up. Other uses include the exterior of steel cases and bonding surfaces of nozzle components. They provide excellent bondability - rubber insulation and epoxy bonds fail cohesively within the polymer - for both fresh surfaces and surfaces having undergone natural and accelerated environmental aging. They have passed the MSFC requirements for protection of inland and sea coast environment. Because BOSS coatings are inherently corrosion resistant, they do not require preservation by greases or oils. The reduction/elimination of greases and oils, known bondline degraders, can increase SRM reliability, decrease costs by reducing the number of process steps, and decrease environmental pollution by reducing the amount of methyl chloroform used for degreasing and thus reduce release of the ozone-depleting chemical in accordance with the Clean Air Act and the Montreal Protocol. The coatings can potential extend the life of RSRM case segments and nozzle components by eliminating erosion due to multiple grit blasting during each use cycle and corrosion damage during marine recovery. Concurrent work for the Air Force show that other BOSS coatings give excellent bondline strength and durability for high-performance structures of aluminum and titanium.

Davis, G. D.↗
NASA NTRS2010

Mechanical Extraction of Power From Ocean Currents and Tides

A proposed scheme for generating electric power from rivers and from ocean currents, tides, and waves is intended to offer economic and environmental advantages over prior such schemes, some of which are at various stages of implementation, others of which have not yet advanced beyond the concept stage. This scheme would be less environmentally objectionable than are prior schemes that involve the use of dams to block rivers and tidal flows. This scheme would also not entail the high maintenance costs of other proposed schemes that call for submerged electric generators and cables, which would be subject to degradation by marine growth and corrosion. A basic power-generation system according to the scheme now proposed would not include any submerged electrical equipment. The submerged portion of the system would include an all-mechanical turbine/pump unit that would superficially resemble a large land-based wind turbine (see figure). The turbine axis would turn slowly as it captured energy from the local river flow, ocean current, tidal flow, or flow from an ocean-wave device. The turbine axis would drive a pump through a gearbox to generate an enclosed flow of water, hydraulic fluid, or other suitable fluid at a relatively high pressure [typically approx.500 psi (approx.3.4 MPa)]. The pressurized fluid could be piped to an onshore or offshore facility, above the ocean surface, where it would be used to drive a turbine that, in turn, would drive an electric generator. The fluid could be recirculated between the submerged unit and the power-generation facility in a closed flow system; alternatively, if the fluid were seawater, it could be taken in from the ocean at the submerged turbine/pump unit and discharged back into the ocean from the power-generation facility. Another alternative would be to use the pressurized flow to charge an elevated reservoir or other pumped-storage facility, from whence fluid could later be released to drive a turbine/generator unit at a time of high power demand. Multiple submerged turbine/pump units could be positioned across a channel to extract more power than could be extracted by a single unit. In that case, the pressurized flows in their output pipes would be combined, via check valves, into a wider pipe that would deliver the combined flow to a power-generating or pumped-storage facility.

Jones, Jack↗
DOE OSTI2024

Composite coatings from polycarbosilane derived SiC and Al/SiC cermet active fillers as protective barriers against steel corrosion

Stainless steel is used throughout the world as a structural material. However, it undergoes corrosion damage when exposed to extremely corrosive media, such as the marine environment. An alternative to solve this problem lies in the development of coatings that can withstand extreme conditions but also be easily deposited with inherently corrosion-resistant materials such as silicon carbide (SiC). The present study shows a simple method to produce Al/SiC cermet powders by attrition milling. The resulting cermet powders with a metallic matrix and hemispherical morphology, were employed as fillers in polycarbosilane (PCS) solutions that were sprayed on A304 stainless steel substrates. Al/SiC composite coatings were produced after heating the sprayed suspensions at 700 °C for 1 h in Ar atmosphere. The resulting composite coatings exhibited low surface energies (< 35 mN/m), water contact angles of 53°, and adhesion strength of up to 30 MPa. Finally, corrosion tests were performed in a cyclic corrosion test chamber, showing that these coatings effectively reduced the corrosion rate of stainless steel by 87%, reaching corrosion rate values of 0.007 g/cm 2 year.

36 MATERIALS SCIENCE↗