NASA NTRS2010

Performance Testing of Molten Regolith Electrolysis with Transfer of Molten Material for the Production of Oxygen and Metals on the Moon

Previously, we have demonstrated the production of oxygen by electrolysis of molten regolith simulants at temperatures near 1600 C. Using an inert anode and suitable cathode, direct electrolysis (no supporting electrolyte) of the molten silicate is carried out, resulting in the production of molten metallic products at the cathode and oxygen gas at the anode. Initial direct measurements of current efficiency have confirmed that the process offer potential advantages of high oxygen production rates in a smaller footprint facility landed on the moon, with a minimum of consumables brought from Earth. We now report the results of a scale-up effort toward the goal of achieving production rates equivalent to 1 metric ton O2/year, a benchmark established for the support of a lunar base. We previously reported on the electrochemical behavior of the molten electrolyte as dependent on anode material, sweep rate and electrolyte composition in batches of 20-200g and at currents of less than 0.5 A. In this paper, we present the results of experiments performed at currents up to 10 Amperes) and in larger volumes of regolith simulant (500 g - 1 kg) for longer durations of electrolysis. The technical development of critical design components is described, including: inert anodes capable of passing continuous currents of several Amperes, container materials selection, direct gas analysis capability to determine the gas components co-evolving with oxygen. To allow a continuous process, a system has been designed and tested to enable the withdrawal of cathodically-reduced molten metals and spent molten oxide electrolyte. The performance of the withdrawal system is presented and critiqued. The design of the electrolytic cell and the configuration of the furnace were supported by modeling the thermal environment of the system in an effort to realize a balance between external heating and internal joule heating. We will discuss the impact these simulations and experimental findings have on the design of a suitable prototype for lunar applications

Sibille, Laurent↗
NASA NTRSDate not supplied

Degradation of Yttria-Stabilized Zirconia in Molten Regolith Electrolysis Applications

The generation of oxygen from lunar resources is an enabling technology to support a sustained human presence on the lunar surface. Molten regolith electrolysis is a promising process for directly electrolyzing lunar regolith, which is primarily a mixture of oxide minerals. During electrolysis, metallic products (Fe, Si) are formed at the cathode and oxygen is produced at the anode. In order to perform electrolysis, the regolith must be molten to enable ionic transport of metallic cations and oxygen anions, requiring an operating temperature of 1600C. Common refractory oxide materials, such as Al2O3 and MgO, undergo rapid degradation due to the high operating temperature and contact with the corrosive molten regolith. This work investigates yttria-stabilized zirconia (YSZ) for molten regolith electrolysis applications. Corrosion studies are presented to elucidate the degradation mechanism of YSZ powders and crucibles exposed to lunar regolith simulants at 1600C. Two regolith simulants are used to represent regolith from the lunar maria (JSC-1A) and the lunar highlands (LHS-1). Degradation of YSZ in contact with regolith simulants is evaluated using SEM/EDS, XRD, and EBSD. Furthermore, a modified molten regolith electrolysis reactor is presented utilizing YSZ at the anode to enable facile collection of oxygen produced during electrolysis.

Kevin Yu↗
NASA NTRSDate not supplied

Development of a Cold-Walled Molten Regolith Electrolysis Reactor for Lunar Oxygen Production

On the lunar surface, production of commodi-ties to support human presence, such as water, food and oxygen, and sustain the growth of a per-manent outpostwill likely require the use oflocal resources. The moon is covered almost entirely withfragmented oxide minerals known as regolithhundreds of meter thick.As a resource, it is rich in oxygen (> 42 wt.%) bound in a solid state with a variety of metals. The molten regolith electrolysis (MRE)reactor is a promising technology for the production of gaseous oxygen from the lunar reg-olithin a simple, single-stepreaction that requires minimalconsumable materials, produces oxygen and metals with high electrical efficiency and high yields from any regolithcomposition.This process involvesmelting regolith to~1600°C then electro-lyzing the molten pool to separate metal and oxy-gen ions that are then collected as liquid metal and gaseous oxygen at the respective electrodes. Lab-scale demonstrations of the MRE technology have previously reliedon external heating sources to bring the entirety of the reactor up to the operating temperaturewhich creates corrosive interfaces be-tween the molten regolith and the containment ma-terial in the reactor, limiting the overall lifespan of a reactor[1]. The Gaseous Lunar Oxygen from Regolith Electrolysis (GaLORE) project is focused on the development of a “cold-walled” or “Joule-heated” reactor design in which an internal heating source is used to selectively melt a pool of regolith between the electrodes of the reactor, leaving a shell of solidified regolith between the molten pool and the containment vessel of the reactor. This next generation reactor concept has been under development as molten oxide electrolysis (MOE) by MIT and Boston Metal for the production of iron from pure ores for terrestrial application [2]. The GaLORE project in engaged in early development of the technology for use with varying lunar regolith compositionsin the lunar environment. Thermal modelling of a proposed cold-walledreac-tor design were used as a scaffold to develop pa-rameters for a feasible reactor shape and size as well as target energy consumption[3]. The current development effort for the cold-walled reactor de-sign will be presented as a trade study of the most promising techniques for melting regolithwithin the constraints imposed by the lunar environment.Heater devices are designed to accommodate lim-ited electrical power availabilityon the moon, a wide range of regolith compositions that may be seen on the moon, limited metals available for re-placing consumed parts,and the low thermal con-ductivity of granular regolith in vacuum.Heater de-vices will be down-selectedbased on performance measurements within the above operationalcon-straints,and selected devices will be integrated into a reactor with electrodes to begin producing oxygen. [1]Sibille,L.,Sadoway, D.R.,Sirk, A., Tripathy,P.,Melendez, O., Standish, E., Dominguez, J. A., Stefanescu, D.M.,Curreri, P.A., Poizeau,S.,2009. “Recent Advancesin Scale-up Development of Molten Regolith Electrolysis for Oxygen Production in support of a Lunar Base.”AIAA 2009-659, 47th AIAA Aerospace Sciences Meeting, 5 -8 January 2009, Orlando, FL. [2] Boston Metal, https://www.boston-metal.com/moe-technology/#moe-process[3]Schreiner, S.S.,Sibille, L., Dominguez, J.A., Hoffman, J.A., 2016. "A parametric sizing model for Molten Regolith Electrolysis reactors to pro-duce oxygen on the Moon." Advances in Space Research 57.,7,1585-1603.

K D Grossman↗
NASA NTRS2012

Joule-Heated Molten Regolith Electrolysis Reactor Concepts for Oxygen and Metals Production on the Moon and Mars

The maturation of Molten Regolith Electrolysis (MRE) as a viable technology for oxygen and metals production on explored planets relies on the realization of the self-heating mode for the reactor. Joule heat generated during regolith electrolysis creates thermal energy that should be able to maintain the molten phase (similar to electrolytic Hall-Heroult process for aluminum production). Self-heating via Joule heating offers many advantages: (1) The regolith itself is the crucible material, it protects the vessel walls (2) Simplifies the engineering of the reactor (3) Reduces power consumption (no external heating) (4) Extends the longevity of the reactor. Predictive modeling is a tool chosen to perform dimensional analysis of a self-heating reactor: (1) Multiphysics modeling (COMSOL) was selected for Joule heat generation and heat transfer (2) Objective is to identify critical dimensions for first reactor prototype.

Sibille, Laurent↗
NASA NTRS2023

Galvanic Protected Anode Materials for Molten Regolith Electrolysis

This effort aimed to explore the use of refractory alloys as long-lifetime electrode materials for use in a molten regolith electrolysis (MRE) reactor, a technology that can produce oxygen (O2) from regolith. To find a material capable of withstanding the high temperatures and corrosive nature of molten regolith, first-principles thermodynamic calculations were performed on platinum group metals in the presence of iron (Fe) and silicon (Si) to determine favorable compositions for resisting unwanted secondary phases that could form on the surface of the material. As a result of these first-principles calculations, the kinetic properties of elements such as aluminum (Al), Fe, and Si can be more easily derived, which would provide insight into the longevity of such a material when used in an MRE reactor. The effort funded by this CIF project mapped the entire phase diagram of platinum group metals, which is beneficial not only to MRE where high temperatures and molten material are present, but also aerospace applications like turbine materials, terrestrial metal processing techniques, and energy storage applications. This project narrowed a broad spectrum of refractory metals down to a small list of alloys that would be able to survive not only the high temperatures of an MRE reactor, but also the thermodynamic forces that would cause inferior alloys to form secondary phases, which would ultimately consume the electrodes of the reactor. This research needs to be followed up with experimental demonstrations of these alloys in an MRE environment.

Kevin Grossman↗
NASA NTRS2010

Multiphysics Modeling for Dimensional Analysis of a Self-Heated Molten Regolith Electrolysis Reactor for Oxygen and Metals Production on the Moon and Mars

The technology of direct electrolysis of molten lunar regolith to produce oxygen and molten metal alloys has progressed greatly in the last few years. The development of long-lasting inert anodes and cathode designs as well as techniques for the removal of molten products from the reactor has been demonstrated. The containment of chemically aggressive oxide and metal melts is very difficult at the operating temperatures ca. 1600 C. Containing the molten oxides in a regolith shell can solve this technical issue and can be achieved by designing a self-heating reactor in which the electrolytic currents generate enough Joule heat to create a molten bath.

Dominguez, Jesus↗
NASA NTRS2010

Multiphysics Modeling for Dimensional Analysis of a Self-Heated Molten Regolith Electrolysis Reactor for Oxygen and Metals Production on the Moon and Mars

The technology of direct electrolysis of molten lunar regolith to produce oxygen and molten metal alloys has progressed greatly in the last few years. The development of long-lasting inert anodes and cathode designs as well as techniques for the removal of molten products from the reactor has been demonstrated. The containment of chemically aggressive oxide and metal melts is very difficult at the operating temperatures ca 1600 C. Containing the molten oxides in a regolith shell can solve this technical issue and can be achieved by designing a self-heating reactor in which the electrolytic currents generate enough Joule heat to create a molten bath. In a first phase, a thermal analysis model was built to study the formation of a melt of lunar basaltic regolith irradiated by a focused solar beam This mode of heating was selected because it relies on radiative heat transfer, which is the dominant mode of transfer of energy in melts at 1600 C. Knowing and setting the Gaussian-type heat flux from the concentrated solar beam and the phase and temperature dependent thermal properties, the model predicts the dimensions and temperature profile of the melt. A validation of the model is presented in this paper through the experimental formation of a spherical cap melt realized by others. The Orbitec/PSI experimental setup uses an 3.6-cm diameter concentrated solar beam to create a hemispheric melt in a bed of lunar regolith simulant contained in a large pot. Upon cooling, the dimensions of the vitrified melt are measured to validate the thermal model. In a second phase, the model is augmented by multiphysics components to compute the passage of electrical currents between electrodes inserted in the molten regolith. The current through the melt generates Joule heating due to the high resistivity of the medium and this energy is transferred into the melt by conduction, convection and primarily by radiation. The model faces challenges in two major areas, the change of phase as temperature increases, and the dominance of radiative heat flux as heat transfer mechanism within the melt the change of phase concerns the regolith itself which is present in states ranging from a fine grain regolith with low thermal conductivity and low density to a vitrified melt with much higher thermal conductivity, and higher density. As the regolith is heated, it starts to soften around 1300 C the melt iS very viscous and evolving gas bubbles out in thick, lava-like fashion. By 1600 C the regolith is completely melted and the viscosity is low The second challenge resides in the proper modeling of the radiative heat flux requiring the addition of the computing-demanding radiative-heat-transfer function to the general heat transfer equation. The model Includes temperature-dependent properties (density, thermal conductivity, heat capacity, and viscosity, and absorption coefficients) and solves the radiative heat flux equation assuming gray (fine grains) and semi-transparent (melt) media and using an absorption coefficient spectral found in the literature for terrestrial minerals similar in composition to those of lunar regolith simulant

Dominguez, Jesus A.↗
NASA NTRS2012

Joule-Heated Molten Regolith Electrolysis Reactor Concepts for Oxygen and Metals Production on the Moon and Mars

The technology of direct electrolysis of molten lunar regolith to produce oxygen and molten metal alloys has progressed greatly in the last few years. The development of long-lasting inert anodes and cathode designs as well as techniques for the removal of molten products from the reactor has been demonstrated. The containment of chemically aggressive oxide and metal melts is very difficult at the operating temperatures ca. 1600 C. Containing the molten oxides in a regolith shell can solve this technical issue and can be achieved by designing a Joule-heated (sometimes called 'self-heating') reactor in which the electrolytic currents generate enough Joule heat to create a molten bath. Solutions obtained by multiphysics modeling allow the identification of the critical dimensions of concept reactors.

Sibille, Laurent↗
NASA NTRS2024

System Modeling of a Lunar Molten Regolith Electrolysis Plant

In-Situ Resource Utilization (ISRU) is the process of extracting local resources to produce commodities for propulsion, life support systems, and off-planet construction rather than transporting consumables from Earth. Molten Regolith Electrolysis (MRE) is a novel ISRU method of extracting oxygen gas and metal alloy from lunar regolith. The MRE process involves placing lunar regolith between two electrodes, through which current is passed, to melt the regolith and reduce the metal oxide constituents by direct electrolysis (e.g. FeO, SiO 2 , MgO, Al 2 O 3 ) into oxygen gas and metal alloys. The oxygen is liquefied and used as propellant for landers, while the metals (e.g. Ferro-alloys) are further processed and used in structural building materials and parts manufacturing. A system model was developed that accounted for the major processes of an MRE plant (from excavation of raw materials to storage of products) to assess the feasibility of a lunar MRE plant. The S ystem Engineering and Integration ( S E&I) I SRU M odeling and A nalysis (SIMA) team utilized its previously documented system sizing model, the Mission Analysis and Integration Tool (MAIT) as framework of the system model. MAIT uses MATLAB/Simulink to integrate subsystem models into a complete system model of the MRE plant. Total mass, volume, and power requirements were computed for numerous iterations of a MRE plant.

In-Situ Resource Utilization↗
NASA NTRSDate not supplied

System Modeling of a Lunar Molten Regolith Electrolysis Plant

Introduction: In-Situ Resource Utilization (ISRU) is the process of extracting local resources to produce commodities for propulsion, life support systems, and off-planet construction rather than transporting consumables from Earth. Molten Regolith Electrolysis (MRE) is a novel ISRU method of extracting oxygen gas and metal alloy from lunar regolith. The MRE process involves placing lunar regolith between two electrodes, through which current is passed, to melt the regolith and reduce the metal oxide constituents by direct electrolysis (e.g. FeO, SiO2, MgO, Al2O3) into oxygen gas and metal alloys. The oxygen is liquefied and used as propellant for landers, while the metals (e.g. Ferro-alloys) are further processed and used in structural building materials and parts manufacturing. A system model was developed that accounted for the major processes of an MRE plant (from excavation of raw materials to storage of products) to assess the feasibility of a lunar MRE plant. The System Engineering and Integration (SE&I) ISRU Modeling and Analysis (SIMA) team utilized its previously documented system sizing model, the Mission Analysis and Integration Tool (MAIT) [1] as framework of the system model. MAIT uses MATLAB/Simulink to integrate subsystem models into a complete system model of the MRE plant. Total mass, volume, and power requirements were computed for numerous iterations of a MRE plant. System Model: Figure 1: MRE Plant Block Diagram The regolith excavation model determines the mass and power needed to excavate sufficient regolith. The preheating auger initiates the regolith heating process before regolith enters the MRE re-actor to reduce the energy required to turn the solid into a molten liquid. The MRE reactor is modeled in COMSOL Multiphysics and based on the research by Dominguez, Sibille, and Schreiner [2, 3, 4]. This preliminary reactor model provides an accurate calculation of thermal equilibrium during electrochemical operation of the reactor system to assess the optimal mass and power required to process the inlet flow of regolith. The model also computes the outlet flowrates of oxygen and molten products. For this analysis, the primary components of the metal alloy considered were iron and silicon. The oxygen is then purified using an Yttrium Stabilized Zirconia (YSZ) electrode, followed by liquefaction using a 90K cryocooler to be stored as liquid oxygen in insulated cylindrical tanks. In future iterations of the system model, the molten metal tapped from the MRE reactor will undergo additional processing or refinement. However, downstream handling of metals is currently a technology gap that is missing a high TRL subsystem model. Therefore, for this analysis, the accumulated metal alloy stream terminates after leaving the MRE reactor. Study Goals: This analysis investigates multiple input variables to the system to determine the sensitivity of a (near) complete plant at full-scale. This preliminary investigation ran parametric sweeps on the MRE reactor geometry, electrical current supply, layers of multi-layer insulation (MLI) on the reactor, size of the electrodes in the oxygen purification model, and regolith composition (based on landing site location). Three production targets of oxygen (1,000, 10,000, and 50,000 kg/yr) were investigated for this analysis. The parametric sweeps conducted in this analysis provide valuable insight into the expected impact of the various model inputs on plant size. This information can be used to identify the most critical components of the plant and guide future decisions on allocating funding for research and development, providing subsystem developers with appropriate interfaces with downstream and upstream processes, and assessing the overall feasibility of MRE when compared to other ISRU plants. References: [1] Carlson, A. et al. (2024) ICES, ICES-2024-53. [2] Dominguez, D.A., and Sibille, L. (2011) AIAA, AIAA-2011-700. [3] Schreiner, S.S. (2015) MIT, Dissertation. [4] Schreiner, S.S. et al. (2016) ASR, 57(7), pp.1585-1603.

ISRU↗
NASA NTRS2009

Production of Oxygen from Lunar Regolith using Molten Oxide Electrolysis

This slide presentation reviews the possible use of molten oxide electrolysis to extract oxygen from the Lunar Regolith. The presentation asserts that molten regolith electrolysis has advanced to be a useful method for production of oxygen and metals in situ on the Moon. The work has demonstrated an 8 hour batch of electrolysis at 5 amps using Iridium inert anodes.

Sibille, Laurent↗
NASA NTRSDate not supplied

Gaseous By-Product of Thermal Vacuum Processing of Lunar Highland Simulant

Scientists at Kennedy Space Center are advancing technologies to achieve oxygen extraction on the Lunar surface. One such technology is Molten Regolith Electrolysis (MRE) in which regolith simulant is melted under high temperatures to perform oxygen extraction through electrolysis of the melt pool. A study was conducted to understand the molten formation and proper-ties of Lunar Highlands Simulants (LHS-1) under high vacuum environments ranging between 10-6 Torr. These studies include investigating the regolith melt behavior and by-product gas analysis systems to prepare for pilot plant development and operations. The off-gassing rates and pressure build-up, gaseous compounds, and material compatibility may be a risk to MRE systems. The KSC findings are reported here for inclusion into future mis-sion architecture and operational planning. The four stages of the experiment were vacuum, resistive heating, regolith melt and gas detection. The regolith mass of 70 g was melted in a 40 cm tall x 50 cm diameter vacuum chamber at temperature increase rate 47 ℃ /min and ramp rate of 1 ampere/3 min up to an 18-amp maximum. The test is conducted for about 60 minutes and the constituent gases produced during heating of regolith is monitored with a re-sidual gas analyzer. During the molten formation, primary off-gassing volatiles included water vapor (18 amu), a peak at 44 amu (FeO2 – expected), and atomic oxygen (16 amu), among a series of other compounds that could create compatibility issues such as magnesium, chlorine, and silicon oxide. These results add to the knowledge required for successful oxygen extraction on the moon.

Molten Regolith Electrolysis↗
NASA NTRS2009

Ceramics for Molten Materials Containment, Transfer and Handling on the Lunar Surface

As part of a project on Molten Materials Transfer and Handling on the Lunar Surface, molten materials containment samples of various ceramics were tested to determine their performance in contact with a melt of lunar regolith simulant. The test temperature was 1600 C with contact times ranging from 0 to 12 hours. Regolith simulant was pressed into cylinders with the approximate dimensions of 1.25 dia x 1.25cm height and then melted on ceramic substrates. The regolith-ceramic interface was examined after processing to determine the melt/ceramic interaction. It was found that the molten regolith wetted all oxide ceramics tested extremely well which resulted in chemical reaction between the materials in each case. Alumina substrates were identified which withstood contact at the operating temperature of a molten regolith electrolysis cell (1600 C) for eight hours with little interaction or deformation. This represents an improvement over alumina grades currently in use and will provide a lifetime adequate for electrolysis experiments lasting 24 hours or more. Two types of non-oxide ceramics were also tested. It was found that they interacted to a limited degree with the melt resulting in little corrosion. These ceramics, Sic and BN, were not wetted as well as the oxides by the melt, and so remain possible materials for molten regolith handling. Tests wing longer holding periods and larger volumes of regolith are necessary to determine the ultimate performance of the tested ceramics.

Standish, Evan↗
NASA NTRSDate not supplied

Thermochemical Interactions of Yttria-Stabilized Zirconia and Molten Lunar Regolith Simulants

Oxygen produced from lunar resources through in-situ resource utilization (ISRU) is critical to maintaining a permanent human presence on the lunar surface. Molten regolith electrolysis and carbothermal reduction are two promising ISRU techniques for generating oxygen directly from lunar regolith, which is primarily a mixture of oxide minerals; however, both processes require operating temperatures of 1600C to melt lunar regolith and dissociate the molten oxides. These conditions limit the use of many oxide refractory materials, such as Al2O3 and MgO, due to rapid degradation resulting from reactions between the refractory materials and molten lunar regolith. Yttria-stabilized zirconia (YSZ) is a promising refractory oxide to provide containment of molten regolith while demonstrating limited reactivity. This work focuses on corrosion studies of YSZ powders and dense YSZ crucibles in contact with molten lunar mare and highlands regolith simulants at 1600C. The interactions between YSZ and molten regolith are characterized using SEM/EDS, XRD, and EBSD with an emphasis on elemental and microstructural analysis to assess reactivity and degradation of YSZ. Due to lunar regolith’s similar composition to calcium-magnesium-aluminosilicates (CMAS) and YSZ’s usage as a thermal barrier coating, these interactions can serve to inform YSZ/CMAS behavior by simulating cases of elevated CMAS/YSZ ratios and for higher than intended gas turbine temperatures.

Kevin Yu↗
NASA NTRS2024

Thermochemical Interactions Between Yttria-Stabilized Zirconia and Molten Lunar Regolith Simulants

Oxygen produced through in-situ resource utilization (ISRU) is critical to maintaining a permanent human presence on the lunar surface. Molten regolith electrolysis and carbothermal reduction are two promising ISRU techniques for generating oxygen directly from lunar regolith, which is primarily a mixture of oxide minerals; however, both processes require operating temperatures of 1600 C to melt lunar regolith and dissociate the molten oxides. These conditions limit the use of many oxide refractory materials, such as Al2O3 and MgO, due to rapid degradation resulting from reactions between the refractory materials and molten lunar regolith. Yttria-stabilized zirconia (YSZ) is shown here to be a promising refractory oxide to provide containment of molten regolith while demonstrating limited reactivity. This work focuses on corrosion studies of YSZ powders and dense YSZ crucibles in contact with molten lunar maria and highlands regolith simulants at 1600 C. The interactions between YSZ and molten regolith are characterized using SEM/EDS, XRD, and EBSD. A FactSage thermochemical model is created to compare with the experimental results. These combined analyses suggest that lunar maria regolith will degrade YSZ faster than lunar highlands regolith due to the lower viscosity of the maria regolith. The feasibility of long-term molten regolith containment with YSZ is discussed based on the YSZ powder and crucible results.

Kevin Yu↗
NASA NTRSDate not supplied

Advanced Metal Separation (AMS) via Marangoni Effect-driven Separation

For practical, economical, and sustainable human missions to the Moon, processing of lunar regolith and metal oxides is necessary for localized production of oxygen (O2) and metals that can be repurposed as rocket propellant, life support O2, and in-space manufactured parts. The primary candidates for in-situ resource utilization (ISRU) regolith processing are carbothermic reductions and molten regolith electrolysis (MRE) which both produce oxygen and a reduced, deoxygenated metallic slag. A metal separation technique is still required to capture and purify metals from the deoxygenated slag for reuse in areas such as metallic part fabrication, structural or design frameworks, and metal catalyst production. The Marangoni Effect is best explained as mass transfer along an interface driven by surface tension gradients induced by temperature and concentration differences. Due to the temperature gradients, molten metal can be transported in this fashion to create thin films. This method can transport molten metal in the absence of gravity or mechanical motion and greatly increases the available surface area for a vacuum fractional separation process. In this study, a novel vacuum furnace induces the Marangoni Effect to fractionally decompose and separate valuable metals (e.g., aluminum) from thin films of molten metal via vacuum distillation. The proposed work will examine lunar regolith, metal-based recycling feedstocks, and metallic slags produced from the carbothermal reduction of regolith. Data and observations from this study could produce a simple yet effective method of refining lunar derived metals by taking advantage of the high vacuum environment present on the lunar surface.

ISRU↗