Stabilizing perovskite-substrate interfaces for high-performance perovskite modules

The interfaces of perovskite solar cells (PSCs) are important in determining their efficiency and stability, but the morphology and stability of imbedded perovskite-substrate interfaces have received less attention than have top interfaces. We found that dimethyl sulfoxide (DMSO), which is a liquid additive broadly applied to enhance perovskite film morphology, was trapped during film formation and led to voids at perovskite-substrate interfaces that accelerated the film degradation under illumination. Partial replacement of DMSO with solid-state carbohydrazide reduces interfacial voids. A maximum stabilized power conversion efficiency (PCE) of 23.6% was realized for blade-coated p-type/intrinsic/n-type (p-i-n) structure PSCs with no efficiency loss after 550-hour operational stability tests at 60°C. The perovskite mini-modules showed certified PCEs of 19.3 and 19.2%, with aperture areas of 18.1 and 50.0 square centimeters, respectively.

Chen, Shangshang↗
DOE OSTI2024

Multifunctional entinostat enhances the mechanical robustness and efficiency of flexible perovskite solar cells and minimodules

Flexible perovskite solar cells (F-PSCs), prized for their nature of soft and high power-weight compatibility, have attracted intensive attention. However, inferior buried perovskite-substrate interfaces due to low interfacial adhesion between perovskites and substrates and large deformation of flexible substrates have greatly limited the performance of F-PSCs. Here, we add organic molecule Entinostat (ET) into hole extraction material Poly[bis(4-phenyl)(2,4,6-trimethylphenyl)amine] (PTAA) to enhance the adhesion at the perovskite/substrate interface using the interactions of ET with perovskites, PTAA and indium tin oxide (ITO) through its multiple function groups. Meanwhile, ET added into perovskites reduces the voids at the bottom perovskite film, due to its capability to tune the crystallization of perovskites by forming adduct with lead. Consequently, the inverted small area F-PSCs achieved an efficiency of 23.4%. The flexible perovskite minimodule with an area of 9 cm 2 achieved an aperture efficiency of ~19.0% certified by National Renewable Energy Laboratory. Furthermore, the optimized unencapsulated flexible minimodule retained 84% of the initial efficiency after 5000 bending cycles and retained 90% of the initial PCE (T90) after light soaking for >750 hours.

14 SOLAR ENERGY↗
DOE OSTI2022

Hot-Casting-Assisted Liquid Additive Engineering for Efficient and Stable Perovskite Solar Cells

High-performance inorganic–organic lead halide perovskite solar cells (PSCs) are often fabricated with a liquid additive such as dimethyl sulfoxide (DMSO), which retards crystallization and reduces roughness and pinholes in the perovskite layers. However, DMSO can be trapped during perovskite film formation and induce voids and undesired reaction byproducts upon later processing steps. Here, it is shown that the amount of residual DMSO can be reduced in as-spin-coated films significantly through use of preheated substrates, or a so-called hot-casting method. Hot casting increases the perovskite film thickness given the same concentration of solutions, which allows for reducing the perovskite solution concentration. By reducing the amount of DMSO in proportion to the concentration of perovskite precursors and using hot casting, it is possible to fabricate perovskite layers with improved perovskite–substrate interfaces by suppressing the formation of byproducts, which increase trap density and accelerate degradation of the perovskite layers. The best-performing PSCs exhibit a power conversion efficiency (PCE) of 23.4% (23.0% stabilized efficiency) under simulated solar illumination. Furthermore, encapsulated devices show considerably reduced post-burn-in decay, retaining 75% and 90% of their initial and post-burn-in efficiencies after 3000 h of operation with maximum power point tracking (MPPT) under high power of ultraviolet (UV)-containing continuous light exposure.

perovskite-substrate interface↗