Lessons from the IEC Durability of Adhesion Accelerated Test Sequence

The IEC 62788-1-1 and IEC 63209-2 standards use aging sequences for durability of adhesion in photovoltaic (PV) modules, which may be evaluated using the single cantilever beam (SCB) test. Because the encapsulant forms critical interfaces with the front glass and solar cells, degradation at those interfaces under ultraviolet (UV) exposure, elevated temperature, and humidity can lead to interfacial delamination - compromising the long-term reliability. In this work, adhesion durability of UV-transmitting poly(ethylene-co-vinyl acetate) (EVA) encapsulant to glass and to silicon solar cells is evaluated after sequenced UV and damp heat aging (85C/85%RH). Laminates were prepared using StarPhire solar front glass with thin glass or PERC cells, and two EVA formulations with different concentrations of siloxane coupling agent. Adhesion was quantified by measuring critical debond energy using the SCB method. Both formulations exhibit similar qualitative trends, while different adhesion is observed at the periphery despite the use of low-shrink manufacturing. The results show that while glass/EVA adhesion remains stable or increases after UV exposure and shows only moderate changes after damp heat, the EVA/cell interface exhibits an irreversible loss of adhesion following UV and then damp heat exposure. Although glass/EVA interfaces generally exhibit lower debond energies, the EVA/cell interface is significantly more vulnerable to UV-driven degradation, identifying it as the dominant reliability risk location through early- and intermediate-module life. These results demonstrate that accelerated aging sequences can expose large, interface-specific losses in adhesion durability and underscore the importance of interface engineering for long-term PV module reliability.

14 SOLAR ENERGY↗

DOE OSTI2020

Characterizing photovoltaic backsheet adhesion degradation using the wedge and single cantilever beam tests, Part I: Field Modules

Photovoltaic backsheets are exposed to harsh outdoor weathering conditions throughout their service lives that can compromise their protective function, through adhesive debonding between their constituent layers and between the backsheet and the module. We report a large-scale study on adhesive degradation was conducted on 37 field-exposed modules, that spanned 19 different module manufacturers, that were deployed among six Köppen–Geiger climatic zones, and that were fielded between 0 and 28 years. Six outer layer polymer classes were identified among the backsheets: polyamide (PA), polyethylene terephthalate (PET), polyvinyl fluoride (PVF), polyvinylidene fluoride (PVDF), fluoroethylene vinyl ether copolymer (FEVE), and tetrafluoroethylene hexafluoropropylene vinylidene fluoride copolymer (THV). Two adhesion tests were used to measure the adhesive strength: the wedge test and the width-tapered single-cantilever beam (SCB) test. Adhesion energies were compared across exposure time and Köppen–Geiger climatic zone. Many of the PET-, PVF-, and PVDF-based backsheets experienced degradation of the adhesive layer between the backsheet outer and core layers. A consistent trend of decreasing adhesion energy with exposure time was observed in five out of the six backsheet types. Trends among adhesion energy and climatic zone, while expected, were not observed, possibly due to broad ranges in temperature, humidity, and precipitation defining Köppen–Geiger climatic zones. The cantilever beam measurements produced an upper cutoff of approximately 100 J/m 2 , above which no modules exhibited field delamination. The results are part of a two-part study quantifying adhesion in both field-weathered and indoor-exposed PV backsheets.

14 SOLAR ENERGY↗

DOE OSTI2021

Cohesive and adhesive degradation in PET-based photovoltaic backsheets subjected to ultraviolet accelerated weathering

Delamination between layers in photovoltaic (PV) backsheets is often reported in the literature, causing voids that can collect moisture, diminish module backside heat dissipation, and reduce the backsheet’s effectiveness as a physical barrier. While backsheets with weathering-resistant fluoropolymer outer layers have traditionally been used in modules, more recent backsheets using non-fluoropolymer outer layers, such as polyethylene terephthalate (PET), have been developed. These backsheets have shown signs of premature degradation, and their adhesion degradation, in particular, has not been widely studied. In the present work, the single cantilever beam (SCB) adhesion test was used to quantify the adhesion energy in two commercially available PET-based backsheets. To study the effect of minor changes in formulation, the backsheets were obtained from same manufacturer and product line but during different years. To study the effect of environmental variables on adhesion degradation, the backsheets were subjected to artificial weathering at controlled temperature, humidity, and ultraviolet (UV) radiation in an indoor weathering chamber, and the adhesion energy was quantified at several intervals of exposure time. Layering structure, composition, and adhesion failure mode were compared between the backsheets, using Raman and infrared spectroscopy and thermogravimetric analysis. The results show a large difference in initial (unexposed) adhesion energy between the backsheets, despite very similar structures and compositions. Following exposure, adhesion energy dropped significantly, primarily due to thermo-hydrolytic degradation of the polyurethane (PU)-based adhesive layers. Significant UV-induced adhesion degradation of the PET outer layer surface was also observed. The study represents an important step in understanding adhesion degradation in PET-based backsheets, suggesting ways in which adhesion integrity – and, correspondingly, module service life – can be improved.

14 SOLAR ENERGY↗