Final Status Report Confirming Completion of Mechanical Testing of HFIR Irradiated Nanocomposite Materials
This report provides a final status report on the in-cell mechanical testing of High Flux Isotope Reactor (HFIR)-irradiated nanodispersion-strengthened materials at the Irradiated Materials Examination and Testing (IMET) facility. All tension tests were performed at room temperature with a nominal strain rate of 0.018 mm/mm/min using shoulder-loading grip sets by following the standard testing procedure in ASTM E8/E8M. Round 1 (unirradiated) and round 2 (0.7 dpa) testing was completed in FY 2021. This report confirms completion of round 3 (1.4 dpa) and round 4 (2.1 dpa) tensile testing in FY 2022 with examples of test data collected on select sample conditions. Additionally, the report includes IDs of samples selected for shipment to Idaho National Laboratory (INL) for additional characterization.